JP6860899B2 - ガラスクロス複合不燃シート材及びそれを用いた建築物 - Google Patents
ガラスクロス複合不燃シート材及びそれを用いた建築物 Download PDFInfo
- Publication number
- JP6860899B2 JP6860899B2 JP2016228495A JP2016228495A JP6860899B2 JP 6860899 B2 JP6860899 B2 JP 6860899B2 JP 2016228495 A JP2016228495 A JP 2016228495A JP 2016228495 A JP2016228495 A JP 2016228495A JP 6860899 B2 JP6860899 B2 JP 6860899B2
- Authority
- JP
- Japan
- Prior art keywords
- sheet material
- glass cloth
- bulky
- glass
- glass fiber
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
旧A種、旧B種とは、膜構造の建築物・膜材料等の技術基準及び同解説編集委員会・ほか編(2003)『膜構造の建築物・膜材料等の技術基準及び同解説』海文堂出版株式会社による膜材料の分類である。
しかし、プラスチック系サイジング剤のガラス繊維糸は、特殊で、汎用のデンプン系のサイジング剤のガラス繊維糸よりも高価である。
すなわち、本発明は以下のとおりである。
(2)前記バルキー(嵩高)加工されたガラス繊維糸を緯糸に用い、前記バルキー加工(嵩高)されていないガラス繊維糸を経糸に用いて製織してなる上記(1)のガラスクロス複合不燃シート材。
(3)前記ガラス繊維糸の番手は50tex以上、かつ前記ガラスクロスの質量が250g/m2以上である(1)または(2)のガラスクロス複合不燃シート材。
(4)前記ガラスクロスの織り組織が平織変化組織の斜子織、または畝織である前記(1)〜(3)いずれかのガラスクロス複合不燃シート材。
(5)前記樹脂被覆層が、塩化ビニル系樹脂、ポリウレタン系樹脂、ふっ素系樹脂、クロロプレンゴム、クロロスルフォン化ポリエチレンゴムまたはオレフィン系樹脂から選ばれた1種以上である上記(1)〜(4)のいずれかのガラスクロス複合不燃シート材。
(6)前記(1)〜(5)のいずれかのガラスクロス複合不燃シート材を用いる膜構造の建築物またはテント倉庫建築物。
<ガラスクロス(1)>
プラスチック系サイジング剤のバルキー(嵩高)加工されていないガラス繊維糸の67.5texを経糸に、デンプン系サイジング剤のバルキー(嵩高)加工されたガラス繊維糸の135.0 Btex(JIS R 3414−2012に記載されているが、Bはバルキー(嵩高)加工糸を表す。)を緯糸に用い、経糸の織り密度:44本/25mm、緯糸の織り密度:44本/25mm、織り組織:2×2正則斜子織とした質量370g/m2のガラスクロスを製織した。このガラスクロスをフッ素系撥水剤9%の水系処理浴中にディッピングしゴムマングルで絞り、これを190℃の乾燥機中で1分間乾燥し、吸水防止処理が施されたガラスクロス(1)を得た。
<ガラスクロス複合不燃シート材>
前記、吸水防止処理が施されたガラスクロス(1)に下記組成:
塩化ビニル樹脂 100.0質量部
ジ−2−エチルヘキシルフタレート 80.0質量部
三酸化アンチモン 20.0質量部
Ba−Zn系安定剤 2.0質量部
紫外線吸収剤 0.3質量部
の塩化ビニル系樹脂ペーストゾルをディップコートし、150℃の乾燥機中で1分間熱処理し、
引き続き連続して、下記組成:
塩化ビニル樹脂 100.0質量部
ジ−2−エチルヘキシルフタレート 60.0質量部
三酸化アンチモン 20.0質量部
Ba−Zn系安定剤 2.0質量部
紫外線吸収剤 0.3質量部
顔料(酸化チタン) 20.0質量部
の塩化ビニル系樹脂ペーストゾルをディップコートし、190℃の乾燥機中で1分間熱処理し、質量850g/m2のガラスクロス複合不燃シート材を得た。
<ガラスクロス(2)>
経糸、緯糸ともプラスチック系サイジング剤のバルキー(嵩高)加工されていないガラス繊維糸とし、67.5texを経糸に、135.0texを緯糸に用い、経糸の織り密度:44本/25mm、緯糸の織り密度:44本/25mm、織り組織:2×2正則斜子織とした質量380g/m2のガラスクロスを製織した。このガラスクロスをフッ素系撥水剤9%の水系処理浴中にディッピングしゴムマングルで絞り、これを190℃の乾燥機中で1分間乾燥し、吸水防止処理が施されたガラスクロス(2)を得た。
<ガラスクロス複合シート材>
前記、ガラスクロス(2)を実施例1と同様に塩化ビニル系樹脂ペーストゾルを連続してディップコートを行い、質量523g/m2のシート材を得た。
更に、下記組成:
塩化ビニル樹脂 100.0質量部
ジ−2−エチルヘキシルフタレート 50.0質量部
三酸化アンチモン 10.0質量部
Ba−Zn系安定剤 1.0質量部
紫外線吸収剤 0.3質量部
顔料(酸化チタン) 5.0質量部
の塩化ビニル系樹脂コンパウンドを170℃〜180℃でカレンダー成形で厚さ0.15mmのフィルムを別途生産し、ラミネーターで前記質量523g/m2のシート材の両面に前記フィルムを175℃の熱ロール条件で貼り合せ、質量854g/m2のガラスクロス複合シート材を得た。
比較例1で用いたガラスクロス(2)を下記ガラスクロス(3)に変更した以外は比較例1と同様にして、質量856g/m2のガラスクロス複合シート材を得た。
<ガラスクロス(3)>
経糸、緯糸ともデンプン系サイジング剤のバルキー(嵩高)加工されていないガラス繊維糸とし、67.5texを経糸に、135.0texを緯糸に用い、経糸の織り密度:44本/25mm、緯糸の織り密度:44本/25mm、織り組織:2×2正則斜子織とした質量382g/m2のガラスクロスを製織した。このガラスクロスをフッ素系撥水剤9%の水系処理浴中にディッピングしゴムマングルで絞り、これを190℃の乾燥機中で1分間乾燥し、吸水防止処理が施されたガラスクロス(3)を得た。
(前記、ガラスクロス(3)を実施例1と同様に塩化ビニル系樹脂ペーストゾルを連続してディップコートした後のシート材の質量は525g/m2であった。)
JIS L 1096(2010年)に従いシート材の厚さを測定した。
[質量]
JIS L 1096(2010年)に従いシート材の質量を測定した。
[引張強さ]
JIS L 1096(2010年)のA法(ストリップ法)に従いシート材の経糸方向と緯糸方向の引張強さを測定した。
[引裂強さ]
JIS L 1096(2010年)のA法(シングルタング法)に従いシート材の経糸方向と緯糸方向の引裂強さを測定した。
[剥離強さ:常態]
JIS K 6406−5(1999年)の試験方法Bに従い、シート材の経糸方向と緯糸方向の剥離強さを測定した。
[剥離強さ:湿潤時]
JIS K 6406−5(1999年)の試験方法Bに従い、25℃の水に24時間浸漬直後のシート材の経糸方向と緯糸方向の剥離強さを測定した。
[耐吸水性]
30mm幅にカットしたシート材を経糸方向および緯糸方向それぞれについて5枚を、下端部の5mmを市販の赤インクの3%水溶液の温度25℃で72時間後の吸水長を測定した。
[発熱速度200kW/m2超過継続時間]
シート材の表面に、輻射電気ヒ−タ−を用い50kW/m2の輻射熱を照射する発熱性試験(ASTM−E1354:コーンカロリーメーター試験)において、加熱開始後20分間の発熱速度200kW/m2超過継続時間を測定した。
Claims (6)
- バルキー(嵩高)加工されたガラス繊維糸と、バルキー(嵩高)加工されていないガラス繊維糸を用いて製織したガラスクロスの両面に樹脂被覆層が設けられた複合シート材であって、前記バルキー(嵩高)加工されたガラス繊維糸にデンプン系サイジング処理が施され、前記バルキー(嵩高)加工されていないガラス繊維糸にプラスチック系サイジング処理が施されていて、ASTM−E1354に規定される発熱性試験において、前記複合シート材に50kW/m2の輻射熱を照射した時の、加熱開始後20分間の発熱速度が、8秒以上継続して200kW/m2を超えないことを特徴とするガラスクロス複合不燃シート材。
- 前記バルキー(嵩高)加工されたガラス繊維糸を緯糸に用い、前記バルキー加工(嵩高)されていないガラス繊維糸を経糸に用いて製織してなる請求項1記載のガラスクロス複合不燃シート材。
- 前記ガラス繊維糸の番手は50tex以上、かつ前記ガラスクロスの質量が250g/m2以上である請求項1または2に記載いずれか1項のガラスクロス複合不燃シート材。
- 前記ガラスクロスの織り組織が平織変化組織の斜子織、または畝織である請求項1〜3に記載いずれか1項のガラスクロス複合不燃シート材。
- 前記樹脂被覆層が、塩化ビニル系樹脂、ポリウレタン系樹脂、ふっ素系樹脂、クロロプレンゴム、クロロスルフォン化ポリエチレンゴムまたはオレフィン系樹脂から選ばれた1種以上である請求項1〜4に記載いずれか1項のガラスクロス複合不燃シート材。
- 請求項1〜5に記載いずれか1項のガラスクロス複合不燃シート材を用いる膜構造の建築物またはテント倉庫建築物。