JP6746969B2 - 多層樹脂シート、積層シート、多層樹脂シートの製造方法、積層シートの製造方法及び発泡壁紙の製造方法 - Google Patents
多層樹脂シート、積層シート、多層樹脂シートの製造方法、積層シートの製造方法及び発泡壁紙の製造方法 Download PDFInfo
- Publication number
- JP6746969B2 JP6746969B2 JP2016045645A JP2016045645A JP6746969B2 JP 6746969 B2 JP6746969 B2 JP 6746969B2 JP 2016045645 A JP2016045645 A JP 2016045645A JP 2016045645 A JP2016045645 A JP 2016045645A JP 6746969 B2 JP6746969 B2 JP 6746969B2
- Authority
- JP
- Japan
- Prior art keywords
- resin
- foaming agent
- layer
- resin composition
- sheet
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
本実施形態に係る多層樹脂シートは、第1の樹脂分と、発泡剤と、を含む発泡剤含有樹脂組成物からなる第1層と、第2の樹脂分を含み、発泡剤を含まない発泡剤非含有樹脂組成物からなる第2層とを有する。
発泡剤含有樹脂組成物における第1の樹脂分は、エチレン単独重合体、又はエチレン単位を50モル%以上含有する、エチレンと他のオレフィンとの共重合体を含む。このような樹脂分を用いることで、ポリ塩化ビニル樹脂等のハロゲン系樹脂を用いる場合と比較して、環境への影響をより小さくすることができる。さらに、押出成形の際の製膜安定性がより優れたものとなるほか、発泡剤を発泡させた際の発泡セルが細密になり、より良好な発泡状態を有する発泡壁紙を実現するための多層樹脂シートを得ることができる。また、上記のほか、ベース樹脂の表面エネルギーが大きいためにブリードアウトの低減による親インク性の向上効果がより大きく発揮される。
本実施形態に係る発泡剤非含有樹脂組成物は、第2の樹脂分を含み、発泡剤を含まない。
本実施形態に係る多層樹脂シートは、上述した発泡剤含有樹脂組成物及び発泡剤非含有樹脂組成物、並びに、所望により第2の発泡剤非含有樹脂組成物を押出成形することにより得ることができる。
本実施形態に係る積層シートは、基材と、該基材上に設けられた上記多層樹脂シートと、を備える。
本実施形態に係る積層シートは、例えば、基材上に、上記の方法により得られた多層樹脂シートをラミネートする工程を備える。本発明の効果がより有効に得られる観点から、積層シートは、多層樹脂シートにおける上記第1層を基材上にラミネートする工程を備えることが好ましい。
本実施形態に係る発泡壁紙は、基材と、基材上に設けられた発泡樹脂層と、を備える。このような発泡壁紙は、上記積層シートにおける第1層に含まれる発泡剤を発泡させることにより発泡樹脂層を形成する発泡工程を備える、発泡壁紙の製造方法により得ることができる。
同方向噛み合い型二軸押出機を用いて、発泡剤が分解しないように樹脂温度を120℃に制御しながら、表1の配合(単位は質量部)で発泡剤含有樹脂組成物のペレットを作製した。
樹脂A:ノバテックLD LJ802A(日本ポリエチレン株式会社製、商品名、融点=107℃、MFR=27(190℃)、密度=0.919g/cm3、エチレン単位含有量=100モル%)
樹脂B:カーネル KJ−640T(日本ポリエチレン株式会社製、商品名、融点=58℃、MFR=30(190℃)、密度=0.885g/cm3、エチレン単位含有量=88モル%)
樹脂C:リンクロン SS732N(三菱化学株式会社製、商品名、ポリエチレンベース、融点=58℃、MFR=13(190℃)、密度=0.885g/cm3)
充填剤A:タイペークCR−60−2(石原産業株式会社製、商品名)
充填剤B:ソフトン1000(備北粉化工業株式会社製、商品名)
同方向噛み合い型2軸押出機を用いて、樹脂温度を150℃に制御しながら、表2の配合(単位は質量部)で発泡剤非含有樹脂組成物のペレットを作製した。
樹脂D:ノバテックHD HJ490(日本ポリエチレン株式会社製、商品名、融点=133℃、MFR=25(190℃)、密度=0.958g/cm3、エチレン単位含有量=100モル%)
樹脂E:ウインテックWSX03(日本ポリプロ株式会社製、商品名、エチレンランダムポリプロピレン、融点=125℃、MFR=25(230℃)、密度=0.9g/cm3、プロピレン含有量=96モル%)
樹脂F:リンクロン HM600A(三菱化学株式会社製、商品名、ポリエチレンベース、融点=132℃、MFR=9(190℃)、密度=0.955g/cm3)
第2の発泡剤非含有樹脂組成物のペレットとして、上記樹脂Bを用意した。
(実施例1〜4、比較例1〜2)
上記で作製した発泡剤含有樹脂組成物1〜3のペレット、発泡剤非含有樹脂組成物4〜9のペレット及び第2の発泡剤非含有樹脂組成物のペレットを、表3に示す組合せで用いて、多層樹脂シートを作製した。具体的には、スクリュー1(スクリュー径(D)50mm、L/D(スクリュー長をスクリュー径で除したもの)=28の単軸押出機)を用いて発泡剤非含有樹脂組成物のペレットを押出し、スクリュー2(スクリュー径(D)65mm、L/D=28の単軸押出機)を用いて発泡剤含有樹脂組成物のペレットを押出し、スクリュー3(スクリュー径(D)50mm、L/D=28の単軸押出機)を用いて第2の発泡剤非含有樹脂組成物のペレットを押出し、それぞれをフィードブロックタイプで合流させた後に巾700mmのTダイでライン速度20m/分にてシート製膜し、発泡剤非含有樹脂組成物からなる第2層(厚み20μm)と、発泡剤含有樹脂組成物からなる第1層(厚み60μm)と、第2の発泡剤非含有樹脂組成物からなる第3層(厚み10μm)と、からなる多層樹脂シートを得た。また、フィードブロックタイプで合流させる際の各スクリューの温度設定値は、スクリュー1を130℃、スクリュー2を130℃、スクリュー3を130℃とした。
(層間密着性)
実施例1〜4、比較例1〜2で作製した多層樹脂シートについて、第2層側に巾1インチのテープを貼り付けしたのちに剥離し、第2層がテープに追従して剥離した場合を「B」、剥離しなかった場合を「A」と評価した。結果を表3に示す。
温度40℃、湿度90%で1週間保存した実施例1〜4、比較例1〜3の多層樹脂シート、及び温度80℃で1週間保存した実施例1〜4、比較例1〜3の多層樹脂シートについて、第2層側に巾1インチのテープを貼り付けしたのちに剥離し、第2層がテープに追従して剥離した場合を「B」、剥離しなかった場合を「A」と評価した。結果を表3に示す。
(耐傷性)
コインスクラッチ試験機を用いて、耐傷性の評価を行った。具体的には、水平な面に発泡壁紙を置き、10円硬貨を用いて45°の角度で発泡壁紙を荷重800g及び1000gで引っ掻き、表面状態を観察した。試験表面に傷がない場合を「A」、傷がついた場合を「B」と評価した。結果を表3に示す。
サンシャインフェードメーターを用いて、288時間及び576時間の耐候試験を行った後、それぞれに荷重200g、400g、600g及び800gで上記と同様に引っ掻き、表面状態を観察した。試験表面に傷がない場合を「A」、傷がついた場合を「B」と評価した。結果を表3に示す。
Claims (8)
- 第1の樹脂分と、発泡剤と、を含む発泡剤含有樹脂組成物からなる第1層と、第2の樹脂分を含み、発泡剤を含まない発泡剤非含有樹脂組成物からなる第2層とを有する多層樹脂シートであって、
前記第1の樹脂分が、0.91g/cm 3 以上0.94g/cm 3 以下の密度を有する低密度ポリエチレン、0.85g/cm 3 以上0.91g/cm 3 未満の密度を有する超低密度ポリエチレン、及びシラン架橋性樹脂を含み、
前記第2の樹脂分が、0.950g/cm3以上の密度を有するポリエチレン及びシラン架橋性樹脂を含む、多層樹脂シート。 - 前記発泡剤非含有樹脂組成物が、フェノール系ラジカル捕捉剤及びヒンダードアミン系ラジカル捕捉剤からなる群より選択される少なくとも1種を更に含む、請求項1に記載の多層樹脂シート。
- 前記発泡剤非含有樹脂組成物が、紫外線吸収剤を更に含む、請求項1又は2に記載の多層樹脂シート。
- 基材と、該基材上に設けられた請求項1〜3のいずれか一項に記載の多層樹脂シートと、を備える、積層シート。
- 請求項1〜3のいずれか一項に記載の多層樹脂シートの製造方法であって、
前記発泡剤含有樹脂組成物及び前記発泡剤非含有樹脂組成物をそれぞれ押出成形することにより前記第1層及び前記第2層を形成する工程、又は少なくとも前記発泡剤含有樹脂組成物及び前記発泡剤非含有樹脂組成物を共押出成形することにより前記第1層及び前記第2層を形成する工程、
を備える、多層樹脂シートの製造方法。 - 請求項4に記載の積層シートの製造方法であって、
基材上に請求項5に記載の方法により得られた多層樹脂シートをラミネートする工程を備える、積層シートの製造方法。 - 前記基材上にラミネートされる前若しくはラミネート中の前記多層樹脂シートに含まれる前記樹脂分の一部若しくは全部を架橋する架橋工程、又は前記積層シートにおける前記多層樹脂シートに含まれる前記樹脂分の一部若しくは全部を架橋する架橋工程を更に備える、請求項6に記載の積層シートの製造方法。
- 基材と、該基材上に設けられた発泡樹脂層と、を備える発泡壁紙の製造方法であって、
請求項4に記載の積層シートにおける前記第1層に含まれる前記発泡剤を発泡させることにより発泡樹脂層を形成する発泡工程を備える、発泡壁紙の製造方法。