JP6492494B2 - 樹脂組成物、樹脂シート、積層シート及び発泡壁紙 - Google Patents
樹脂組成物、樹脂シート、積層シート及び発泡壁紙 Download PDFInfo
- Publication number
- JP6492494B2 JP6492494B2 JP2014200871A JP2014200871A JP6492494B2 JP 6492494 B2 JP6492494 B2 JP 6492494B2 JP 2014200871 A JP2014200871 A JP 2014200871A JP 2014200871 A JP2014200871 A JP 2014200871A JP 6492494 B2 JP6492494 B2 JP 6492494B2
- Authority
- JP
- Japan
- Prior art keywords
- resin
- resin composition
- density polyethylene
- sheet
- base material
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
本実施形態に係る樹脂組成物は、基材と、該基材上に設けられた発泡樹脂層と、を備える発泡壁紙の発泡樹脂層を形成するための樹脂組成物であって、発泡剤と、低密度ポリエチレンと、超低密度ポリエチレンと、を含み、低密度ポリエチレンのメルトフローレートが100以上であり、且つ、超低密度ポリエチレンのメルトフローレートが20以上である。
本実施形態に係る樹脂シートは、上記本実施形態に係る樹脂組成物から形成されるものである。本実施形態に係る樹脂シートは、例えば、上記本実施形態に係る樹脂組成物を押出製膜して得ることができる。
本実施形態に係る積層シートは、基材と、基材上に設けられた上記樹脂シートと、を備える。当該積層シートは、樹脂シートを、基材上にラミネートして得ることができる。ラミネートの方法としては、特に限定されるものではないが、樹脂シートと基材とを、熱プレス機等を用いて熱圧着を行う方法、過熱蒸気を用いて圧着を行う方法等が挙げられる。過熱蒸気を用いて圧着を行う方法によれば、過熱蒸気によってシート状物の表面の溶融状態を保ったまま基材上へラミネートすることが可能となり、そのレベリング効果によって、密着させる基材の表面の凹凸が樹脂シートに転写されることを抑制することができる。また、樹脂シートがシラン架橋性樹脂を含む場合は、過熱蒸気によってシラン架橋性樹脂を効率よく架橋させることができる。
本実施形態に係る発泡壁紙は、基材と、基材上に設けられた発泡樹脂層と、を備える。このような発泡壁紙は、例えば、上述した樹脂シートを、基材上にラミネートして積層シートを得る工程と、上記樹脂シートに含まれる発泡剤を発泡させることにより、発泡樹脂層を形成する工程と、を備える、製造方法によって得ることができる。
(実施例1〜4、比較例1〜4)
スクリュー径65mm、L/D=32の単軸Tダイ押出成形機を用い、表1に示される組成(表中の数値は質量部を示す)を有する樹脂組成物を、押出設定温度130℃、厚み80μmで製膜し、樹脂シートをそれぞれ得た。なお、製膜は、シート製膜を安定的に行うことができる最大速度で行い、このときの押出機のトルク、樹脂温度、及び樹脂圧力を表1に示す。なお、これらの意味は下記のとおりである。
シート成膜品の幅方向中央部の厚みを、流れ方向におおよそ2mに渡って測定し、その厚み公差が5μm以内となる場合を、シート製膜を安定的に行うことができる最大速度とした。
押出機にかかる負荷の指標として、押出機スクリューのモータートルク(単位:A(アンペア))を押出機のトルクと規定した。この数値が高いほど、押出機にかかる負荷は高くなるため、押出条件としては好ましくない。
樹脂温度は、Tダイ直下の中央部にて、接触式の温度計を使用して測定した。
押出圧力は、押出機先端に取り付けた備え付けの樹脂圧力計を用いて測定した。
作製した発泡壁紙について、下記の方法に従い、耐傷性及びカッティング性を評価した。結果を表2に示す。
ホフマンスクラッチテスターを用いて以下の耐傷試験を行い、傷がつかない最大の荷重(g)を確認した。ただし、実施例及び比較例は全て発泡樹脂層を含むため、傷の評価においては、凹みを除外して判定を行った。
[耐傷試験]
BYK−Gardener社製のホフマンスクラッチ試験機を用いて、試験体表面に対して45度の角度で接するようにスクラッチ刃(直径7mmの円柱のエッジ部)をセットし、スクラッチ刃を引っ張るように移動させて、表面を擦った。その際、スクラッチ刃にかける荷重を変化させて、傷がつかない最大の荷重を確認した。
実際の壁紙施工作業において、壁紙を表面側からカッター刃を入れてカットすることによって、カッターでカットした際の切れやすさを評価した。問題なくカットできる場合には「○」、カット不良により、樹脂層の伸長が発生した場合には「×」と評価した。
樹脂A−1:ペトロセン353(東ソー製、MFR=145、密度=0.917)
樹脂A−2:ペトロセン249(東ソー製、MFR=70、密度=0.916)
樹脂A−3:ペトロセン202(東ソー製、MFR=24、密度=0.918)
樹脂B−1:タフマー DF7350(三井化学製、MFR=35、密度=0.870)
樹脂B−2:エクセレンFX CX5508(住友化学製、MFR=75、密度=0.890)
樹脂C−1:ウルトラセン 680(東ソー製、MFR=160)
樹脂C−2:ウルトラセン 633(東ソー製、MFR=20)
シラン架橋性樹脂:リンクロン SS732N(三菱化学製)
炭酸カルシウム1:ソフトン1200(備北粉化工業製、50%平均粒径2.2μm)
炭酸カルシウム2:Vigot−15(白石カルシウム性、50%平均粒径0.15μm)
二酸化チタン:タイペークCR−60(石原産業製、50%平均粒径0.21μm)
アゾ系発泡剤:ビニホールAC#3C−K2(永和化成工業製、平均粒径5μm)
亜鉛系発泡助剤:アデカスタブOF101(ADEKA製)
シラン架橋助剤:LZ013(三菱化学製、ポリエチレンベース)
Claims (6)
- 基材と、該基材上に設けられた発泡樹脂層と、を備える発泡壁紙の前記発泡樹脂層を形成するための樹脂組成物であって、
発泡剤と、低密度ポリエチレンと、超低密度ポリエチレンと、を含み、
前記低密度ポリエチレンの含有量が、前記樹脂組成物全量を基準として、10〜70質量%であり、
前記超低密度ポリエチレンの含有量が、前記樹脂組成物全量を基準として、5〜50質量%であり、
前記低密度ポリエチレンのメルトフローレートが100以上であり、且つ、
前記超低密度ポリエチレンのメルトフローレートが20以上である、樹脂組成物。 - 50%平均粒径が0.15〜0.3μmである第1の充填剤と、50%平均粒径が0.3〜10μmである第2の充填剤と、を含有する、請求項1に記載の樹脂組成物。
- 請求項1又は2に記載の樹脂組成物を押出製膜して得られる、樹脂シート。
- 架橋処理が施されている、請求項3に記載の樹脂シート。
- 基材と、該基材上に設けられた、請求項3又は4に記載の樹脂シートと、を備える、積層シート。
- 基材と、該基材上に設けられた発泡樹脂層と、を備える発泡壁紙であって、
請求項5に記載の積層シートにおける前記樹脂シートに含まれる発泡剤を発泡させて得られる、発泡壁紙。