JP6688162B2 - イルミナイト系被覆アーク溶接棒 - Google Patents
イルミナイト系被覆アーク溶接棒 Download PDFInfo
- Publication number
- JP6688162B2 JP6688162B2 JP2016114176A JP2016114176A JP6688162B2 JP 6688162 B2 JP6688162 B2 JP 6688162B2 JP 2016114176 A JP2016114176 A JP 2016114176A JP 2016114176 A JP2016114176 A JP 2016114176A JP 6688162 B2 JP6688162 B2 JP 6688162B2
- Authority
- JP
- Japan
- Prior art keywords
- oxide
- total
- arc
- welding
- welding rod
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
鋼心線中のCは、溶接時のアークの吹付けを強くして溶込みを深くし、溶接部の融合不良やブローホール等の溶接欠陥を防止する効果を有する。鋼心線中のCが0.03%未満であると、アークの吹付けが弱くなって溶込みが浅くなり、融合不良等の溶接欠陥が発生しやすくなる。一方、鋼心線のCが0.15%を超えると、アークの吹付けが強くなりすぎ、ビード形状が不良になる。また鋼心線のCが0.15%を超えると、溶接金属の強度が過剰に高くなって靭性が低下する。したがって、鋼心線中のCは0.03〜0.15%とする。
金属炭酸塩は、炭酸カルシウム、炭酸マグネシウム、炭酸バリウム、炭酸マンガン等から添加され、アーク中で分解してCO2ガスを発生させて溶着金属を大気から遮蔽して保護するとともに、アークの吹付けを強くして溶込みを深くし、溶接欠陥を防止する効果を有する。金属炭酸塩の1種又は2種以上の合計が9%未満であると、シールド効果が不足するとともに、アークの吹付けが弱いので、ブローホール等の溶接欠陥が発生しやすくなる。一方、金属炭酸塩の1種又は2種以上の合計が20%を超えると、アークが不安定となり、ビード形状も不良になる。したがって、被覆剤中の金属炭酸塩の1種又は2種以上の合計は9〜20%とする。
硫化鉄は、溶融スラグの表面張力を下げて溶融池とのなじみを良好にし、溶融スラグを溶融池全面に均一に被包させることで、溶接ビード表面へのスラグ焼き付きを防止してスラグ剥離性を改善する効果を有する。硫化鉄が0.005%未満では、その効果が得られず、ビード表面にスラグ焼き付きが発生してスラグ剥離性が不良となる。一方、硫化鉄が0.1%を超えると、溶接金属の靭性が低下するとともに、高温割れが発生しやすくなる。したがって、被覆剤中の硫化鉄は0.005〜0.1%とする。
Ti酸化物は、ルチール、酸化チタン、チタン酸ソーダ、チタンスラグ、イルミナイト等から添加され、スラグ生成剤及びアーク安定剤として作用し、アーク安定性及びビード形状を改善する効果を有する。Ti酸化物のTiO2換算値の合計が15%未満であると、アークが不安定になるとともに、スラグ流動性が悪くなってビード形状が不良となる。一方、Ti酸化物のTiO2換算値の合計が35%を超えると、スラグが緻密になってスラグ剥離性が不良となる。したがって、被覆剤中のTi酸化物のTiO2換算値の合計は15〜35%とする。
Si酸化物は、珪砂、長石、水ガラス等から添加され、スラグ生成剤及びアーク安定剤として作用し、アーク安定性及びスラグ剥離性を改善する効果を有する。Si酸化物のSiO2換算値の合計が15%未満であると、アークが不安定になるとともに、生成したスラグのガラス質が少なくなってスラグ剥離性が不良になる。一方、Si酸化物のSiO2換算値の合計が35%を超えると、スラグの粘性が高くなってビード形状が不良となる。したがって、被覆剤中のSi酸化物のSiO2換算値の合計は15〜35%とする。
Al酸化物は、アルミナ、砂鉄、長石、珪砂、マイカ等から添加され、アークを安定にする効果を有する。Al酸化物のAl2O3換算値の合計が2%未満であると、アークが弱くなって不安定になる。一方、Al酸化物のAl2O3換算値の合計が6%を超えると、スラグ剥離性が不良となる。したがって、被覆剤中のAl酸化物のAl2O3換算値の合計は2〜6%とする。
Mn酸化物は、酸化マンガン、二酸化マンガン等から添加され、棒焼けを防止する効果を有する。Mn酸化物のMnO換算値の合計が1%未満であると、その効果が得られず、棒焼けが発生しやすくなる。一方、Mn酸化物のMnO換算値の合計が5%を超えると、ビード形状が不良となる。したがって、被覆剤中のMn酸化物のMnO換算値の合計は1〜5%とする。
有機物は、セルロース、デキストリン、小麦粉、澱粉、コーンスターチ等から添加され、アーク吹付けを強くして溶込みを深くし、ブローホール等の溶接欠陥を防止する効果がある。有機物の1種又は2種以上の合計が3%未満であると、アークの吹付けが弱くなり、溶込みが浅くなってブローホール等の溶接欠陥が発生しやすくなる。一方、有機物の1種又は2種以上の合計が8%を超えると、棒焼けが発生しやすくなる。したがって、被覆剤中の有機物の1種又は2種以上の合計は3〜8%とする。
金属Mn及びMn合金は、金属Mn、Fe−Mn、Fe−Si−Mn等から添加され、脱酸剤として添加する他、溶接金属の強度及び靭性向上に有効である。金属Mn及びMn合金の1種又は2種以上のMn換算値の合計が6%未満では、脱酸不足となり、ブローホールが発生しやすくなり、また溶接金属の強度及び靭性が低下する。一方、金属Mn及びMn合金の1種又は2種以上のMn換算値の合計が15%を超えると、溶接金属の強度が過剰に高くなって靭性が低下する。したがって、被覆剤中の金属Mn及びMn合金の1種又は2種以上のMn換算値の合計は6〜15%とする。
Na酸化物及びK酸化物は、水ガラス中の珪酸ソーダ、珪酸カリウム、カリ長石、カリガラス及びソーダ長石等から添加され、アークを安定にする効果を有する。Na酸化物及びK酸化物のNa2O換算値及びK2O換算値の合計が2.5%未満では、アークが不安定になる。一方、Na酸化物及びK酸化物のNa2O換算値及びK2O換算値の合計が5.5%を超えると、アークの吹付けが強くなりすぎ、ビード形状が不良になる。したがって、被覆剤中のNa酸化物及びK酸化物のNa2O換算値及びK2O換算値の合計は2.5〜5.5%とする。
、硫化鉄、Ti酸化物のTiO2換算値の合計、Si酸化物のSiO2換算値の合計、Al酸化物のAl2O3換算値の合計、Mn酸化物のMnO換算値の合計、有機物の合計、金属MnとMn合金のMn換算値の合計、Na酸化物及びK酸化物のNa2O換算値及びK2O換算値の合計が適正であるので、アークの吹付けが適正で深い溶込みが得られたので溶接部の溶接欠陥が無く、アークが安定し、スラグ剥離性に優れ、ビード形状が良好であった。また、棒焼けも発生せず、高温割れもなく、溶着金属の引張強さ及び吸収エネルギーも良好で、極めて満足な結果であった。
Claims (1)
- 鋼心線に被覆剤が被覆されているイルミナイト系被覆アーク溶接棒において、
前記鋼心線は、鋼心線全質量に対する質量%で、
C:0.03〜0.15%を含有し、
前記被覆剤は、被覆剤全質量に対する質量%で、
金属炭酸塩の1種又は2種以上の合計:9〜20%、
硫化鉄:0.005〜0.1%、
Ti酸化物のTiO2換算値の合計:15〜35%、
Si酸化物のSiO2換算値の合計:15〜35%、
Al酸化物のAl2O3換算値の合計:2〜6%、
Mn酸化物のMnO換算値の合計:1〜5%、
有機物の1種又は2種以上の合計:3〜8%、
金属Mn及びMn合金の1種又は2種以上のMn換算値の合計:6〜15%、
Na酸化物及びK酸化物のNa2O換算値及びK2O換算値の合計:2.5〜5.5%を含有し、残部は塗装剤、鉄合金からのFe分及び不可避不純物からなることを特徴とするイルミナイト系被覆アーク溶接棒。