JP6501829B2 - ゴルフクラブ用グリップおよびゴルフクラブ - Google Patents
ゴルフクラブ用グリップおよびゴルフクラブ Download PDFInfo
- Publication number
- JP6501829B2 JP6501829B2 JP2017125258A JP2017125258A JP6501829B2 JP 6501829 B2 JP6501829 B2 JP 6501829B2 JP 2017125258 A JP2017125258 A JP 2017125258A JP 2017125258 A JP2017125258 A JP 2017125258A JP 6501829 B2 JP6501829 B2 JP 6501829B2
- Authority
- JP
- Japan
- Prior art keywords
- grip
- less
- golf club
- mass
- rubber
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
前記微細突起は、高さが0.07mm〜0.15mmであり、かつ、底部の最小幅が0.2mm〜0.7mmである。前記微細突起の高さおよび底部の最小幅が上記範囲内であれば、使用者がグリップを握った際に、微細突起が使用者の指紋の溝に入り込むことができる。そのため、前記微細突起が、使用者の指紋の溝内部でアンカー効果を発揮し、防滑性能が向上する。
前記ゴルフクラブ用グリップの円筒部は、単層構造でもよいし、多層構造でもよい。円筒部が単層構造の場合は、微細突起存在領域と、微細突起存在領域以外の他の領域(以下、単に「他の領域」と称する場合がある。)とを異なる組成物から形成してもよいし、同一の組成物から形成してもよい。なお、単層構造の円筒部は、微細突起存在領域および他の領域が、いずれも中実層であることが好ましい。
前記円筒部の材質は特に限定されず、従来ゴルフクラブ用グリップに使用されているゴム組成物、樹脂組成物から形成できる。
本発明には、前記ゴルフクラブ用グリップを用いたゴルフクラブも含まれる。前記ゴルフクラブは、シャフトと、前記シャフトの一端に取り付けられたヘッドと、前記シャフトの他端に取り付けられたグリップとを備え、前記グリップが前記ゴルフクラブ用グリップである。前記シャフトは、ステンレス鋼製や炭素繊維強化樹脂製が使用できる。前記ヘッドとしては、ウッド型、ユーティリティ型、アイアン型が挙げられる。前記ヘッドを構成する材料は、特に限定されるものではなく、例えばチタン、チタン合金、炭素繊維強化プラスチック、ステンレス鋼、マルエージング鋼、軟鉄などが挙げられる。
(1)アクリロニトリル含有率
アクリロニトリル含有率は、水素添加前のアクリロニトリル−ブタジエンゴムについて、ISO 24698−1(2008)により測定した。
二重結合含有量は、共重合体中のブタジエン含有率(質量%)と残存二重結合量(%)から算出した。前記残存二重結合量とは、水素添加前の共重合体中の二重結合と水素添加後の共重合体中の二重結合との質量比(水素添加後の二重結合量/水素添加前の二重結合量)であり、赤外分光法により測定できる。アクリロニトリル−ブタジエンゴムが、アクリロニトリル−ブタジエン2元共重合体の場合、共重合体中のブタジエン含有率は100からアクリロニトリル含有率(質量%)を減ずることで求められる。
二重結合量={ブタジエン含有率/45}×残存二重結合量×10
アクリロニトリル−ブタジエンゴムを1g量りとり、クロロホルム50mlに溶解させ、ここにチモールブルー指示薬を滴下した。この溶液を攪拌しながら、水酸化ナトリウムの0.05mol/Lメタノール溶液を滴下し、最初に変色するまでの滴下量(Vml)を記録した。ブランクとしてアクリロニトリル−ブタジエンゴムを含有しないクロロホルム50mlについても、チモールブルーを指示薬として、水酸化ナトリウムの0.05mol/Lメタノール溶液を滴下し、最初に変色するまでの滴下量(Bml)を記録した。下記式により、カルボキシ基含有率を算出した。
カルボキシ基含有単量体含有率={0.05×(V−B)×PM}/(10×X)
(式中、V:試験溶液の水酸化ナトリウム溶液滴下量(ml)、B:ブランクの水酸化ナトリウム溶液滴下量(ml)、PM:カルボキシ基含有単量体の分子量、X:カルボキシ基含有単量体の価数)
ゴム組成物を用いて、160℃で8〜20分間プレスして、厚み2mmのシートを作製した。なお、ゴム組成物がマイクロバルーンを含有する場合は、グリップを形成した際と同様の発泡倍率となるようにマイクロバルーンを膨張させてシートを作製した。このシートを、23℃で2週間保存し、測定基板などの影響が出ないように、3枚重ねた状態で、自動硬度計(H.バーレイス社製、デジテストII)を用いて硬度を測定した。検出器は、「Shore A」を用いた。
耐摩耗性は、学振形摩耗試験機(安田精機製作所製、摩擦試験機II型)を用いて評価した。具体的には、グリップの表層を構成するゴム組成物を用いてプレス成形(成形温度160℃、成形時間15分)により、厚さ2mmのシートを作製した。このシートを長さ130mm、幅40mmの長方形状に切り出して試験片を作製し、試験片台(かまぼこ形(表面半径R200mm))に固定した。摩擦子(表面半径R45mm、20×20mm)の表面に紙やすり(番手240番)を取り付け、1.96Nの荷重で、試験片の中央部10cmの間を毎分30回往復の速度で500回往復摩擦した。その後、試験片の試験前後の質量変化により耐摩耗性を評価した。なお、耐摩耗性は、グリップNo.9の耐摩耗性を100として、指数化した値で示した。
動摩擦係数は、静・動摩擦測定機(トリニティーラボ社製、TL201Ts)を用いて測定した。具体的には、ゴルフクラブ用グリップからゴム片(幅2cm、長さ6cm)を切り出し、これを試験片とした。ゴム片は、グリップの突起が形成されている領域から切り出した。なお、グリップNo.9については、微細突起が形成されていないため、グリップの軸方向の中央付近からゴム片を切り出した。試験片を装置の移動テーブルに固定し、幾何学指紋パターンが施された触覚接触子を使用し、試験片の動摩擦を測定した。試験は、移動距離1cm、移動速度1mm/秒、荷重25gとした。動摩擦係数は、ずれ運動を開始した位置を0cmとして、0.35cm〜0.65cmの平均値を求めた。なお、摩擦係数は、グリップNo.9の摩擦係数を100として、指数化した値で示した。
グリップをシャフトに装着し、ゴルフクラブを作製した。このゴルフクラブについて10名のゴルファーに対してフィーリング試験を行った。評価は、打撃時の感触および防滑性能の総合評価について行い、評価基準は下記の3段階とした。
○;良好と判断した人が8人以上
△:良好と判断した人が5〜7人
×:良好と判断した人が4人以下
グリップをシャフトに装着し、ゴルフクラブを作製した。このゴルフクラブについて、5000回の実打耐久評価を行った。打撃後のグリップの突起を観察し、突起にチッピングが見られた場合を「×」、チッピングが見られなかった場合を「○」と評価した。
表1、2に示す配合で各原料を混練し、外層用ゴム組成物および内層用ゴム組成物を調製した。なお、外層用ゴム組成物は、全ての原料をバンバリーミキサーで混練した。内層用ゴム組成物は、マイクロバルーン以外の原料をバンバリーミキサーで混練し、その後、ロールを用いてマイクロバルーンを配合した。内層用ゴム組成物のバンバリーミキサーの混練時の材料温度およびロールによりマイクロバルーンを配合する際の材料温度は、マイクロバルーンの膨張開始温度未満とした。
HXNBR:カルボキシ変性水素添加アクリロニトリル−ブタジエンゴム(ランクセス社製、Therban XT VPKA 8889(残存二重結合量3.5%、アクリロニトリル含有率33.0質量%、二重結合含有量0.40mmol/g、カルボキシ基含有単量体含有率5.0質量%))
HNBR:水素添加アクリロニトリル−ブタジエンゴム(ランクセス社製、Therban 3446(残存二重結合量4.0%、アクリロニトリル含有率34.0質量%))
NR(天然ゴム):TSR20
EPDM(エチレン−プロピレン−ジエンゴム):住友化学社製、エスプレン(登録商標)505A
IIR:JSR社製、JSR BUTYL065
シースト(SEAST)(登録商標)SO:東海カーボン社製、カーボンブラック
DIABLACK(登録商標)N220:三菱化学社製、カーボンブラック
ウルトラジルVN3 GR:エボニック社製、造粒シリカ(不定形)
硫黄:鶴見化学工業社製、5%油入微粉硫黄(200メッシュ)
サンセラー(登録商標)TBzTD:三新化学工業社製、テトラベンジルチウラムジスルフィド
ノクセラーNS:大内新興化学工業社製、N−t−ブチル−2−ベンゾチアゾリルスルフェンアミド
ノクセラーCZ:大内新興化学工業社製、N−シクロヘキシル−2−ベンゾチアゾリルスルフェンアミド
ソクシノールD:住友化学社製、1,3−ジフェニルグアニジン
スクラトールZP 1014:struktol社製、struktol ZP 1014(過酸化亜鉛含有量29質量%)
酸化亜鉛:PT.INDO LYSAGHT社製、ホワイトシール
ノクラック(登録商標)NS−6:大内新興化学工業社製、2,2’−メチレンビス(4−メチル−6−t−ブチルフェノール)
ノクラック TBTU:大内新興化学工業社製、トリブチルチオ尿素
ステアリン酸:日油社製、ビーズステアリン酸つばき
アデカサイザー(登録商標) RS735:アデカ社製
PW380:出光興産社製、ダイアナプロセスオイルPW380
ハリタックSE10:ハリマ化成社製、水素添加ロジンエステル(軟化点78℃〜87℃、酸価2mgKOH/g〜10mgKOH/g)
サントガードPVI:三新化学工業社製、N−シクロヘキシルチオフタルイミド
安息香酸:Aldrich社製
Koresin(登録商標):BASF社製、ブチルフェノール−アセチレン縮合物(軟化点135℃〜150℃)
マイクロバルーン:Akzo Nobel社製、「エクスパンセル(登録商標)909−80DU」(熱可塑性樹脂の殻に低沸点炭化水素が内包された樹脂カプセル、体積平均粒子径18μm〜24μm、膨張開始温度120℃〜130℃)
Claims (8)
- シャフトが挿嵌される円筒部を有し、
前記円筒部の最表層がゴム組成物または樹脂組成物から形成されており、
前記円筒部の表面に、高さ(h)が0.07mm〜0.15mmであり、かつ、底部の最小幅(w1)が0.2mm〜0.7mmである微細突起を複数有することを特徴とするゴルフクラブ用グリップ。 - 前記微細突起の立体形状が、錐台状であり、
上底の最小幅(w3)と下底の最小幅(w1)との比(w3/w1)が、0.5以上、1.0未満である請求項1に記載のゴルフクラブ用グリップ。 - シャフトが挿嵌される円筒部を有し、
前記円筒部の表面に、高さ(h)が0.07mm〜0.15mmであり、かつ、底部の最小幅(w1)が0.2mm〜0.7mmである微細突起を複数有し、
前記微細突起の立体形状が、錐台状であり、
上底の最小幅(w3)と下底の最小幅(w1)との比(w3/w1)が、0.5以上、1.0未満であることを特徴とするゴルフクラブ用グリップ。 - 前記円筒部は、前記微細突起が1cm2あたりに200個〜2500個存在する微細突起存在領域を有する請求項1〜3のいずれか一項に記載のゴルフクラブ用グリップ。
- 前記円筒部は、チップ側端部からの軸方向の距離が全長の10%〜60%までの範囲において、表面積中の微細突起存在領域の面積率が50面積%以上である請求項1〜4のいずれか一項に記載のゴルフクラブ用グリップ。
- 前記微細突起の高さ(h)と底部の最小幅(w1)との比(h/w1)が、0.1〜0.75である請求項1〜5のいずれか一項に記載のゴルフクラブ用グリップ。
- 前記円筒部が、基材ゴムとして、カルボキシ変性アクリロニトリルブタジエンゴム、水素添加アクリロニトリル−ブタジエンゴム、および、カルボキシ変性水素添加アクリロニトリル−ブタジエンゴムよりなる群から選択されるアクリロニトリル−ブタジエン系ゴムを含有するゴム組成物から形成されている請求項1〜6のいずれか一項に記載のゴルフクラブ用グリップ。
- シャフトと、前記シャフトの一端に取り付けられたヘッドと、前記シャフトの他端に取り付けられたグリップとを備え、
前記グリップが、請求項1〜7のいずれか1項に記載のゴルフクラブ用グリップであることを特徴とするゴルフクラブ。