JP6451265B2 - タイヤ用ゴム組成物 - Google Patents
タイヤ用ゴム組成物 Download PDFInfo
- Publication number
- JP6451265B2 JP6451265B2 JP2014243328A JP2014243328A JP6451265B2 JP 6451265 B2 JP6451265 B2 JP 6451265B2 JP 2014243328 A JP2014243328 A JP 2014243328A JP 2014243328 A JP2014243328 A JP 2014243328A JP 6451265 B2 JP6451265 B2 JP 6451265B2
- Authority
- JP
- Japan
- Prior art keywords
- silica
- rubber
- weight
- rubber composition
- tire
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
i)シリカを水に100分間以上、浸漬する。
ii)そのシリカを乾燥器に入れ、110℃で16時間乾燥する。
iii)乾燥したシリカを、坩堝に入れ秤量する。
iv)その坩堝を電気炉に入れ、110℃から1100℃まで強熱減量させる。
v)その後、坩堝を秤量し、シリカ1g当たりの重量減少M(g)を求める。
vi)上記重量減少が水の蒸発によるものとし、蒸発した水1分子をヒドロキシ基2個として下記一般式によりシリカ表面のヒドロキシ基数(OH)を算出する。
OH=2×M×6.02×1023/18/(N2SA×1018)
ただし、OHは、シリカ表面のヒドロキシ基数(個/nm2)、
Mは、シリカ1g当たりの重量減少量(g)、
N2SAは、シリカの窒素吸着比表面積(m2/g)である。
5:シリカのゴムへの取込み時間が120秒未満
4:シリカのゴムへの取込み時間が120秒以上180秒未満
3:シリカのゴムへの取込み時間が180秒以上240秒未満
2:シリカのゴムへの取込み時間が240秒以上300秒未満
1:シリカのゴムへの取込み時間が300秒以上
得られた試験片のゴム硬度を、JIS K6253に準拠しデュロメータのタイプAにより温度20℃で測定した。得られた結果は、表1,2では標準例1の値を100、表3では標準例2の値を100とする指数で表わし表1〜3の「ゴム硬度」の欄に示した。この指数が大きいほどゴム硬度が高く、タイヤにしたとき操縦安定性が優れることを意味する。
得られた試験片の動的粘弾性を、東洋精機製作所社製粘弾性スペクトロメーターを用いて、初期歪み10%、振幅±2%、周波数20Hzで測定し、雰囲気温度60℃におけるtanδを測定した。得られた結果は、表1,2では標準例1の値を100、表3では標準例2の値を100とする指数で表わし、表1〜3の「tanδ(60℃)」の欄に示した。この値が小さいほどtanδ(60℃)が小さく、タイヤにしたとき転がり抵抗が小さく燃費性能が優れることを意味する。
・SBR:スチレンブタジエンゴム、旭化成社製E581、スチレンブタジエンゴム100重量部にオイル37.5重量部を配合した油展製品
・BR:ブタジエンゴム、日本合成ゴム社製Nipol BR1220
・乾式シリカ−1:シリコーンオイルで表面処理した乾式シリカ、トクヤマ社製KS−30SC、窒素吸着比表面積が300m2/g、表面のヒドロキシ基数が1.5個/nm2、シリコーンオイルの種類がジメチルシリコーン、シリコーンオイルの添加量はシリカ重量の3重量%
・乾式シリカ−2:シリコーンオイルで表面処理した乾式シリカ、トクヤマ社製KS−20SC、窒素吸着比表面積が200m2/g、表面のヒドロキシ基数が1.5個/nm2、シリコーンオイルの種類がジメチルシリコーン、シリコーンオイルの添加量はシリカ重量の3重量%
・未変性乾式シリカ:シリコーンオイルの表面処理を施していない乾式シリカ、トクヤマ社製QS−30、窒素吸着比表面積が300m2/g、表面のヒドロキシ基数が1.5個/nm2
・湿式シリカ:Solyay社製Zeosil 1165MP、窒素吸着比表面積が160m2/g、表面のヒドロキシ基数が6個/nm2
・変性−湿式シリカ:シリコーンオイルで表面処理表面処理したSolyay社製Zeosil 1165MP、シリコーンオイルの種類がジメチルシリコーン、シリコーンオイルの添加量はシリカ重量の3重量%
・カップリング剤:シランカップリング剤、Evonik社製Si69
・酸化亜鉛:正同化学社製酸化亜鉛3種
・ステアリン酸:日油社製ビーズステアリン酸YR
・老化防止剤:精工化学社製オゾノン6C
・オイル:昭和シェル石油社製エキストラクト4号S
・硫黄:鶴見化学工業社製金華印油入微粉硫黄
・加硫促進剤1:大内新興化学社製ノクセラーCZ−G
・加硫促進剤2:住友化学社製ソクシノールD−G
Claims (3)
- ジエン系ゴム100重量部に、シリカを30〜160重量部、シランカップリング剤を前記シリカの重量の3〜20重量%配合したタイヤ用ゴム組成物であって、前記シリカが、シリコーンオイルで処理された乾式シリカ5〜80重量%と湿式シリカとを含み、前記乾式シリカの表面のヒドロキシ基数が2個/nm2未満であることを特徴するタイヤ用ゴム組成物。
- 前記乾式シリカの窒素吸着比表面積が200〜450m2/gであることを特徴する請求項1に記載のタイヤ用ゴム組成物。
- 前記乾式シリカが、前記シリコーンオイルを1.0〜20重量%含むことを特徴する請求項1または2に記載のタイヤ用ゴム組成物。