JP6437168B2 - ミリ波帯域用電波吸収シート及びミリ波電波吸収方法 - Google Patents
ミリ波帯域用電波吸収シート及びミリ波電波吸収方法 Download PDFInfo
- Publication number
- JP6437168B2 JP6437168B2 JP2018525485A JP2018525485A JP6437168B2 JP 6437168 B2 JP6437168 B2 JP 6437168B2 JP 2018525485 A JP2018525485 A JP 2018525485A JP 2018525485 A JP2018525485 A JP 2018525485A JP 6437168 B2 JP6437168 B2 JP 6437168B2
- Authority
- JP
- Japan
- Prior art keywords
- radio wave
- wave absorption
- layer
- lower layer
- absorption
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
このように電波吸収体は広く利用され、目的や用途に応じて種々の材質、形状の電波吸収体が開発されてきた。
電波反射層(A)と、前記電波反射層(A)の上部に平行に配置された電波吸収下層(B)と、前記電波吸収下層(B)の上部に平行に配置された電波吸収上層(C)とを備えてなり、
前記電波吸収下層(B)の周波数79GHzにおける比誘電率の実数部が5〜45であり、虚数部の絶対値が0.5〜15の範囲内であり、前記電波吸収下層(B)の膜厚が0.10〜1.5mmの範囲内にあり、
前記電波吸収上層(C)の周波数79GHzにおける比誘電率の実数部が2〜20の範囲内であり、虚数部の絶対値が2未満であり、前記電波吸収上層(C)の膜厚が0.3〜2.2mmの範囲内にある、ミリ波帯域用電波吸収シート、並びに、この電波吸収シートを用いる、ミリ波帯域の電波吸収方法、に関する。
電波吸収下層(B)の比誘電率の実数部ε’が5未満では、本電波吸収シートのミリ波帯域の電波吸収性が低下し、一方45を超えると本電波吸収シートのミリ波帯域の電波吸収性が低下するとともに、本電波吸収シートの可とう性も低下する傾向にあり好ましくない。
Zin:電波吸収シートの表面インピーダンス(Ω)
d:膜厚(mm)
λ:波長(mm)
εr:比誘電率
μr:比透磁率。
ここで、垂直入射(θ=0°)の場合には式(6)、(7)の関係になる。
Znは、2層型電波吸収層(本発明における電波吸収上層(C)の表面に相当する)の表面インピーダンスであり、Zn+1は、上記電波反射層(本発明における電波反射層(A)に該当する)に最も近く積層された電波吸収層(本発明における電波吸収下層(B)の表面に相当する)の表面インピーダンスであり、上記式(4)より求めるものである。
また、電波吸収下層(B)の周波数79GHzにおける比誘電率の実数部が電波吸収上層(C)の周波数79GHzにおける比誘電率の実数部よりも大きいことが好ましい。そして電波吸収下層(B)の周波数79GHzにおける比誘電率の虚数部の絶対値が電波吸収上層(C)の周波数79GHzにおける比誘電率の虚数部の絶対値よりも大きいことが好ましい。
電波吸収下層(B)と電波吸収上層(C)の合計の膜厚としては、ミリ波帯域の電波吸収性及び設置作業性の点から0.6〜3.7mmの範囲内が好ましい。
意匠層(D)は、結合剤としてポリマー(合成樹脂)を含むフィルムが好ましい。かかるポリマーとしては電波吸収下層(B)の説明で例示した化合物と同様のものを挙げることができる。
上記した接着剤の中でも、本電波吸収シートの可とう性、ミリ派帯域の電波吸収性の観点から合成系接着剤の使用が好ましい。
電波吸収上層(C)/電波吸収下層(B)膜厚比が3.0以下にあるミリ波帯域用電波吸収シート。
電波吸収上層(C)/電波吸収下層(B)膜厚比が、3.0を超えるミリ波帯域用電波吸収シート。
電波吸収上層(C)/電波吸収下層(B)膜厚比としては1.3〜2.5の範囲内にあり、電波吸収下層(B)の膜厚としては、0.1〜1.5mm、好ましくは0.2〜1.2mm、さらに好ましくは0.4〜1.0mmの範囲内にあり、
電波吸収上層(C)の膜厚としては0.3〜2.2mm、好ましくは0.5〜1.5mm、さらに好ましくは0.7〜1.2mmの範囲内にあり、
電波吸収下層(B)と電波吸収上層(C)の合計の膜厚としては0.5〜3.7mm、好ましくは1.0〜2.0mmの範囲内にあることが適している。
電波吸収下層(C)/電波吸収下層(B)膜厚比としては3.0を超えること、好ましくは3.0を超えて且つ15以下の範囲内にあり、
電波吸収下層(B)の膜厚としては0.1〜1.5mm、好ましくは0.15〜0.3mmの範囲内にあり、
電波吸収上層(C)の膜厚としては0.3〜2.2mm、1.2〜2.15mm、好ましくは1.4〜2.1mmの範囲内にあり、
電波吸収下層(B)と電波吸収上層(C)の合計の膜厚としては、0.5〜3.7mm、好ましくは2.0を超えて且つ3.7mm以下の範囲内にあることが適している。
実施例1
タテが30cm、ヨコが30cm、厚さが50μmのアルミニウム箔に、10μmシアノアクリレート系接着層を設け、EPDMゴム(エチレンプロピレンジエンゴム)100部に対してマンガン−亜鉛系フェライト700部を混練りし、成型した膜厚550μmのシートを積層し、さらにその上にエチレンプロピレンジエンゴム100部に対してバリウム系フェライト300部を混練りし、成形した膜厚950μmのシートを積層し、さらにその上に、80μmの市販の白色マーキングフィルム(ファンタックシート:(株)カンペファンタックセンター)を貼り付けて電波吸収シート(X−1)を得た。
上層、下層、意匠層の材質、厚さを表1〜表8記載の通りとする以外は実施例1と同様にして、シート状の電波吸収シート(X−2)〜(X−51)を得た。尚、表中PHRは結合剤100質量部に対する各成分の比率を意味する。
(注)絶縁カーボン:平均粒子径0.02μm、
(注)Siゴム:シリコン系樹脂、
(注)導電カーボン:平均粒子径(一次粒子径)34nm
(注)Baフェライト:バリウム系フェライト、平均粒子径2μm、
(注)MnNiフェライト:マンガン・ニッケル系フェライト、平均粒子径0.4μm、
(注)NiZnフェライト:ニッケル・亜鉛系フェライト、平均粒子径0.9μm、
(注)ストロンチウムフェライト:平均粒子径1.5μm、
(注)コバルトフェライト:平均粒子径1.2μm。
上記実施例及び比較例で作成した電波吸収シート(X−1)〜(X−51)を下記基準、方法にて評価し、各電波吸収シートが有する性状値と共に表1〜表8に示した。尚、表1〜表8中、電波吸収下層(B)及び電波吸収上層(C)の比誘電率は、周波数79GHzのときの比誘電率を明細書記載の方法にて求めたものである。
電波吸収量が−30dB以上の電波吸収体を部屋の壁面及び床面に設置した電波暗室にてミリ波電波吸収測定装置を用いて測定した。具体的には、電波吸収測定装置に備えられた送信用ホーンアンテナと受信用ホーンアンテナの入射及び反射角度が床面からの垂直面に対し、それぞれ10°となるように設置し、それぞれのアンテナから、45cmの距離となるように金属反射板を置き、反射してくる信号を受信用ホーンアンテナで受信してその電波反射率を100%とする。次に金属反射板を取除き反射してくる信号を受信用ホーンアンテナで受信してその電波反射率を0%とする。そして金属反射板を置いた位置に測定試料を置き、種々の周波数について測定試料表面から反射してくる電波反射量を測定し、周波数(GHz)を横軸とし、電波吸収量(dB)を縦軸とする電波吸収特性チャートを得た。図3に電波吸収特性チャートの一例を示す。
上記電波吸収量測定で得られた電波吸収特性チャートにおいて、最も電波吸収量が多い周波数をピーク周波数とし、該ピーク周波数における電波吸収量を求め、表中に記載した。尚、表中の電波吸収量は数値が低いほど、電波吸収量が多く、良好であることを意味する。
電波吸収量−20dBにおける、最大吸収周波数fuと最小吸収周波数flとの差であり、次式で表される。bw=fu−fl
表中の数値が大きいほどミリ波領域での帯域幅が広いことを意味し、良好である。尚、表中「−」の記号は電波吸収量が−20dBに達していないために、幅が測定できないことを意味する。
各電波吸収シート(X−1)〜(X−51)を電波反射層が下となるように180°手で折り曲げ、折り曲げ作業性と折り曲げ部の表面状態を下記基準にて評価した。
A:折り曲げ作業性は良好であり、折り曲げ部に破損が全く認められない、
B:折り曲げ作業性は良好であるが、折り曲げ部に破損が若干認められる、
C:折り曲げ作業が困難であり、折り曲げ部に著しい破損が認められる。
表1の結果より、本発明の効果について以下に考察する。
Claims (13)
- 電波反射層(A)と、前記電波反射層(A)の上部に平行に配置された電波吸収下層(B)と、前記電波吸収下層(B)の上部に平行に配置された電波吸収上層(C)とを備えてなる、ミリ波帯域用電波吸収シートであって、
前記電波吸収下層(B)の周波数79GHzにおける比誘電率の実数部が5〜45の範囲内であり、虚数部の絶対値が0.5〜15の範囲内であり、前記電波吸収下層(B)の膜厚が0.10〜1.5mmの範囲内にあり、
前記電波吸収上層(C)の周波数79GHzにおける比誘電率の実数部が2〜20の範囲内であり、虚数部の絶対値が2未満であり、前記電波吸収上層(C)の膜厚が0.3〜2.2mmの範囲内にあり、
前記電波吸収下層(B)の周波数79GHzにおける比誘電率の実数部が、前記電波吸収上層(C)の周波数79GHzにおける比誘電率の実数部よりも大きく、
前記電波吸収下層(B)の周波数79GHzにおける比誘電率の虚数部の絶対値が、前記電波吸収上層(C)の周波数79GHzにおける比誘電率の虚数部の絶対値よりも大きく、
前記電波吸収下層(B)及び前記電波吸収上層(C)は、誘電性粉末及び結合剤を含むシートであり、
前記誘電性粉末は、以下の材料:
センダスト、Fe−Cr−Al合金、Fe−Si−Cr合金、マンガン・亜鉛系フェライト、マンガン・ニッケル系フェライト、ニッケル・亜鉛系フェライト、銅・亜鉛系フェライト、亜鉛フェライト、コバルトフェライト、マグネタイト、バリウムフェライト、ストロンチウムフェライト、M型フェライト、Y型フェライト、Z型フェライト、W型フェライト、U型フェライト、イットリウム鉄ガーネット、カルボニル鉄、微細還元鉄粉及びパーマロイ、ITO粉末、α−アルミナ、β−アルミナ、炭化ケイ素、酸化クロム、酸化セリウム、酸化鉄、コランダム、人造ダイアモンド、窒化珪素、炭化珪素、チタンカーバイト、酸化チタン、二酸化珪素、窒化ホウ素、炭酸カルシウム、硫酸バリウム、ベンゾグアナミン、架橋ポリスチレン、ポリエチレン、シリコン樹脂、ポリテトラフルオロエチレン、導電カーボン、絶縁カーボン、並びにこれらの組み合わせ、
からなる群から選択される誘電性を有する粉末である、ミリ波帯域用電波吸収シート。 - 前記電波吸収下層(B)が、前記電波吸収下層(B)に含まれる前記結合剤100質量部を基準として、前記誘電性粉末を100〜1000質量部含む、請求項1に記載の電波吸収シート。
- 前記電波吸収下層(B)が、前記電波吸収下層(B)に含まれる前記結合剤100質量部を基準として、前記誘電性粉末の成分の一部としてカーボンを1〜100質量部含む、請求項1または2に記載の電波吸収シート。
- 前記電波吸収上層(C)が、前記電波吸収上層(C)に含まれる前記結合剤100質量部を基準として、前記誘電性粉末を5〜800質量部含む、請求項1ないし3のいずれか1項に記載の電波吸収シート。
- 前記電波吸収上層(C)が、前記電波吸収上層(C)に含まれる前記結合剤100質量部を基準として、前記誘電性粉末の成分の一部としてカーボンを1〜50質量部含む、請求項1ないし4のいずれか1項に記載の電波吸収シート。
- 前記電波吸収下層(B)と前記電波吸収上層(C)の膜厚比が、電波吸収上層(C)/電波吸収下層(B)膜厚比で1を超える、請求項1ないし5のいずれか1項に記載の電波吸収シート。
- 前記電波吸収下層(B)と前記電波吸収上層(C)の膜厚を合計した合計膜厚が、0.6〜3.7mmの範囲内にある、請求項1ないし6のいずれか1項に記載の電波吸収シート。
- 前記電波吸収下層(B)と前記電波吸収上層(C)の膜厚比が、電波吸収上層(C)/電波吸収下層(B)膜厚比で3.0以下にある、請求項1〜7のいずれか1項に記載の電波吸収シート。
- 前記電波吸収下層(B)と前記電波吸収上層(C)の膜厚比が、電波吸収上層(C)/電波吸収下層(B)膜厚比で3.0を越える、請求項1〜7のいずれか1項に記載の電波吸収シート。
- さらに最表面の位置に意匠層(D)を備え、電波反射層(A)、電波吸収下層(B)、電波吸収上層(C)及び意匠層(D)の順に平行に配置されてなる、請求項1ないし9のいずれか1項に記載の電波吸収シート。
- 各層間のうち、少なくとも1つの層間に接着層(P)を設けてなる、請求項1ないし10のいずれか1項に記載の電波吸収シート。
- 請求項1ないし11のいずれか1項に記載の電波吸収シートを用いる、ミリ波帯域の電波吸収方法。
- 誤作動の電波障害を生じる原因となる電波反射体に、請求項1〜11のいずれか1項に記載の電波吸収シートを設置するか、または、前記電波反射体と電波受信装置との間に、請求項1〜11のいずれか1項に記載の電波吸収シートを設置する、電波障害の防止方法。