JP6260807B2 - 固体電池 - Google Patents
固体電池 Download PDFInfo
- Publication number
- JP6260807B2 JP6260807B2 JP2012267291A JP2012267291A JP6260807B2 JP 6260807 B2 JP6260807 B2 JP 6260807B2 JP 2012267291 A JP2012267291 A JP 2012267291A JP 2012267291 A JP2012267291 A JP 2012267291A JP 6260807 B2 JP6260807 B2 JP 6260807B2
- Authority
- JP
- Japan
- Prior art keywords
- positive electrode
- solid electrolyte
- binder
- layer
- negative electrode
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
0<B<A<1
0.1<B<0.5<A<0.9
まず、図1に基づいて、本実施形態に係る固体電池1の構成について説明する。固体電池1は、正極集電体2、接着層3、正極層4、固体電解質層5、負極層6、負極集電体7を備えて構成されている。接着層3及び正極層4により固体電池1の正極10が構成される。また、負極層6が固体電池1の負極20を構成する。なお、固体電池1は接着層3を含んでいなくてもよい。
次に、固体電池1の製造方法の一例について説明する。まず、第1の結着剤と、第2の結着剤と、接着層導電性物質と、第1の結着剤及び第2の結着剤を溶解するための第1の溶媒と、を含む接着層塗工液を生成する。ここで、第1の溶媒としては、例えば、NMP(N−メチルピロリドン)、DMF(N、N−ジメチルホルムアミド)、N,N−ジメチルアセトアミド、等のアミド溶媒、酢酸ブチル、酢酸エチル等のアルキルエステル溶媒、アセトン、メチルエチルケトン、メチルイソブチルケトン等のケトン類溶媒、テトラフドロフラン、ジエチルエーテル等のエーテル類溶媒、メタノール、エタノール、イソプロピルアルコール等のアルコール類溶媒等がある。後述するように、接着層3には硫化物系固体電解質が含まれないか、正極層4から膨潤した硫化物系固体電解質が少量含まれる程度であるので、第1の溶媒には極性溶媒を使用することができる。
次に、本実施形態の実施例について説明する。なお、以下の各実施例、参考例及び比較例での作業は、全て露点温度−55℃以下のドライルーム内で行われた。
[実施例1]
[接着層の生成]
接着層導電性物質としてのグラファイト(ティムカル社KS−4、以下同じ)及びアセチレンブラック(電気化学工業、以下同じ)と、第1の結着剤としてのスチレン系熱可塑性エラストマー(以下、結着剤A)(旭化成S.O.E1611、以下同じ)と、第2の結着剤としての酸変性PVDF(以下、結着剤B)(クレハKF9200、以下同じ)とを60:10:15:15の質量%比で秤量した。そして、これらの材料と適量のNMPとを自転公転ミキサに投入し、3000rpmで5分撹拌することで、接着層塗工液を生成した。
正極活物質としてのLiNiCoAlO2三元系粉末と、硫化物系固体電解質としてのLi2S−P2S5(80:20モル%)と、正極層導電性物質(導電助剤)としての気相成長炭素繊維粉末とを60:35:5の質量%比で秤量し、これらを自転公転ミキサを用いて混合した。
負極活物質としての黒鉛粉末(80℃で24時間真空乾燥したもの)と、第1の結着剤としての結着剤Aと、硫化物系固体電解質としてのLi2S−P2S5(70:30モル%)を69.0:1.0:30.0の質量%比で秤量した。そして、これらの材料と適量のキシレンとを自転公転ミキサに投入し、3000rpmで3分撹拌した後、1分脱泡処理することで、負極層塗工液を生成した。硫化物系固体電解質の非晶質と結晶質との割合は正極の場合と同じにした。
硫化物系固体電解質としてのLi2S−P2S5(70:30モル%)に、結着剤A(電解質結着剤)のキシレン溶液を+結着剤Aが非晶質粉末の質量に対して1質量%となるように添加することで、1次混合液を調整した。さらに、この1次混合液に、粘度調整のための脱水キシレンを適量添加することで、2次混合液を生成した。さらに、混合粉の分散性を向上させるために、直径5mmのジルコニアボールを、空間、混合粉、ジルコニアボールがそれぞれ混練容器の全容積に対して1/3ずつを占めるように2次混合液に投入した。これにより生成された3次混合液を自転公転ミキサに投入し、3000rpmで3分撹拌することで、電解質層塗工液を生成した。固体電解質層の硫化物固体電解質における非晶質体と結晶質体との割合は20:80とした。
負極構造体及び電解質層5からなるシート及び正極構造体をそれぞれトムソン刃で打ちぬき、シートの電解質層5と正極構造体の正極層4とをロールギャップ50μmのロールプレス機を用いたドライラミネーション法により貼り合わせることで、固体電池1の単セル(単電池)を生成した。
割合を後述の表1のように変更して固体電池を作製した(参考例、比較例1〜12)。
既述のようにして製造された単セルを東洋システム製充放電評価装置 TOSCAT−3100により0.05mA/cm2の定電流密度で充電、引き続いて放電を行い、放電容量(mAh)を測定した(充電上限電圧4.0V、放電下限電圧2.5V)。実施例及び比較例の放電下限電圧2.5V時での放電容量(mAh/g)を下記表1に示す。
室温で0.05Cの定電流充放電サイクル試験を実施し、初回放電容量に対する容量維
持率を評価した。実施例、参考例、比較例の結果を表1に示す。
2 正極集電体
3 接着層
4 正極層
5 電解質層
6 負極層
7 負極集電体
Claims (2)
- 正極と、
負極と、
前記正極と前記負極との間に存在する固体電解質を有する固体電解質層と、
を備え、
前記正極及び前記負極は前記固体電解質を有し、
前記固体電解質は非晶質体と結晶質体とから構成され、
前記正極及び前記負極の前記固体電解質における前記非晶質体の割合(A)と、前記固体電解質層の固体電解質における前記非晶質体の割合(B)とが下記の関係に設定された固体電池。
0.1<B<0.5<A<0.9 - 前記固体電解質は硫化物系固体電解質からなり、当該硫化物系固体電解質は、硫化リチウムと硫化リンとの混合物から形成される、請求項1記載の固体電池。