JP6175367B2 - オフセット印刷用インキ組成物、及び当該組成物を用いた方法 - Google Patents
オフセット印刷用インキ組成物、及び当該組成物を用いた方法 Download PDFInfo
- Publication number
- JP6175367B2 JP6175367B2 JP2013261711A JP2013261711A JP6175367B2 JP 6175367 B2 JP6175367 B2 JP 6175367B2 JP 2013261711 A JP2013261711 A JP 2013261711A JP 2013261711 A JP2013261711 A JP 2013261711A JP 6175367 B2 JP6175367 B2 JP 6175367B2
- Authority
- JP
- Japan
- Prior art keywords
- ink composition
- oil
- printing
- naphthenic
- dry
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
本発明のオフセット印刷用インキ組成物(上記のように、「インキ組成物」又は「インキ」と適宜省略する。)は、オフセット印刷用として使用されるものであり、特にオフセット輪転印刷を浸透乾燥方式で行った際のドライダウンや、ガイドローラー汚れを軽減することができるので、新聞印刷用として好ましく用いられる。本発明のインキ組成物は、ナフテン系ベースオイルと、ナフテン系減圧蒸留残渣と、を必須の構成成分として含み、その他、通常のオフセット印刷用インキ組成物と同様に、着色成分である着色顔料、バインダー樹脂及び油成分を含む。以下、各成分について説明する。
ナフテン系ベースオイル及びナフテン系減圧蒸留残渣は、いずれもナフテン系原油を出発原料として得ることができるものである。ナフテン系ベースオイル及びナフテン系減圧蒸留残渣は、好ましくは、両者が混合された状態でインキ組成物の構成成分として添加される。ナフテン系ベースオイル及びナフテン系減圧蒸留残渣の混合物中におけるナフテン系減圧蒸留残渣の混合比率としては、当該混合物の100質量部中に10〜90質量部程度を挙げることができるが特に限定されない。このような混合物は、これまでゴム用の可塑剤としての使用が提案されてきており、例えば特許第3703468号公報にその製造方法が記載されているのでその製造方法に準じて製造することも可能であるし、市販されている製品を購入して入手することもできる。市販されている製品の一例としては、三共油化株式会社製のA/OMIX(製品名)を挙げることができる。
着色顔料は、インキ組成物に着色力を付与するための成分(着色成分)である。着色顔料としては、従来からインキ組成物に使用される有機及び/又は無機顔料を特に制限無く挙げることができる。
バインダー樹脂(以下、単に「樹脂」とも呼ぶ。)は、印刷用紙の表面で上記着色顔料を固定するバインダーとして機能する成分であり、また、上記着色顔料をインキ組成物中に分散させるために用いられる成分でもある。このような樹脂としては、インキ組成物の分野で通常使用されるものを特に制限なく挙げることができ、ロジン変性フェノール樹脂、ロジン変性マレイン酸樹脂、ロジン変性アルキド樹脂、ロジン変性石油樹脂、ロジンエステル樹脂、石油樹脂変性フェノール樹脂、アクリル変性フェノール樹脂、アルキド樹脂、植物油変性アルキド樹脂、石油樹脂等が例示される。これらの樹脂の重量平均分子量としては、3000〜30万程度を好ましく例示することができる。
油成分は、上記樹脂を溶解させてワニスとしたり、インキ組成物の粘度を調節したりするために使用される。油成分としては、植物油及び/又は鉱物油を挙げることができ、これまでインキ組成物の調製に使用されてきたものを特に制限なく使用できる。
本発明のインキ組成物には、印刷性能を向上させる等の観点から、必要に応じて上記の各成分の他に各種成分を添加することができる。このような各種成分としては、無色顔料、リン酸塩等の塩類、ポリエチレン系ワックス・オレフィン系ワックス・フィッシャートロプシュワックス等のワックス類、アルコール類、酸化防止剤等が例示される。
上記のインキ組成物を用いることを特徴とする、浸透乾燥方式により印刷を行ったときの印刷紙面の経時におけるドライダウンを抑制する方法もまた本発明の一つである。既に述べたように、浸透乾燥方式にてオフセット印刷を行った場合、印刷紙面におけるドライダウンの抑制と、オフセット輪転機にて用いられるガイドローラーの汚れの抑制とはトレードオフの関係になる。つまり、ドライダウンの抑制という観点ではインキ組成物のセット時間(浸透乾燥方式における乾燥時間)が短いほど有利である一方で、ガイドローラー汚れの抑制という観点ではインキ組成物のセット時間が長いほど有利であるので、両者は互いに真逆の特性を要求するものであり、これまでのインキ組成物ではこれらを両立するのが難しかったのが実情である。
冷却管、温度計及び撹拌機を装着した4つ口フラスコに、重量平均分子量10万のロジン変性フェノール樹脂(荒川化学工業株式会社製)35部、大豆油20部及びAFソルベント6号(JX日鉱日石エネルギー株式会社製)44.5部を仕込んだ後200℃に昇温し、同温度を1時間維持することにより樹脂を溶解させた後、エチルアセトアセテートアルミニウムジイソプロピレート(川研ファインケミカル株式会社製、ALCH)を0.5部仕込み、その後170℃で60分間加熱保持して、ワニスを得た。
表1及び2に示す処方にて各種の材料を混合し、三本ロールにて練肉することで実施例1〜5、及び比較例1〜6のインキ組成物を調製した。表1及び2において、「カーボンブラック」は三菱化学株式会社製のカーボンブラック#32であり、「ワニス」は上記手順にて調製したワニスであり、「ナフテン系混合物」はナフテン系ベースオイルとナフテン系減圧蒸留残渣との混合物(三共油化株式会社製、製品名:A/OMIX)であり、「ギルソナイトワニス」はギルソナイト(American Gilsonite Company社製、製品名:ギルソナイト S325L)20部をAFソルベント6号(JX日鉱日石エネルギー株式会社製)40部及びナフテン系ベースオイル(三共油化株式会社製、製品名:SNH540)40部の混合油で溶解させたものであり、「分散ワニス1」はビチューメン(TOSAS(Pty) Limited製、製品名:Penetration grade bitumen)30部をナフテン系ベースオイル(三共油化株式会社製、製品名:SNH540)70部で溶解させたものであり、「分散ワニス2」は上記ビチューメン30部を大豆油70部で溶解させたものであり、「分散ワニス3」は上記ビチューメン30部を上記AFソルベント6号70部で溶解させたものであり、「分散ワニス4」はビチューメン(中国産)30部を上記ナフテン系ベースオイル(製品名SNH540)70部で溶解させたものであり、「ベースオイル」は上記ナフテン系ベースオイル(製品名SNH540)である。また、表1及び2に示す処方量は、いずれも質量部である。また、表1及び2において大豆油の添加量が各サンプルで異なっているのは、出来上がりのインキ組成物の25℃におけるラレー粘度を7.0±0.5Pa・sとなるようにオイル成分の量を調節したためである。
各実施例及び比較例のインキ組成物におけるセット時間の測定は、以下のようにして行った。まず、インキ組成物の試料0.1ccをRI展色機(4分割ロール、株式会社明製作所製)を用いて更紙(王子製紙株式会社製、SL+)に展色した。次に、展色直後の各展色物の展色面にあて紙を被せてセット試験機(AUTO INKSETTING TESTER、東洋精機株式会社製)にセットし、セット試験を3分間隔で行って、あて紙に対するインキ付着の様子を目視で確認した。あて紙にインキが付着しなくなるのに要した時間をセット時間とした。その結果を表1及び2に示す。なお、セット時間の長いものほど、インキ組成物の乾燥が遅いことになり、ガイドローラー汚れの抑制という観点では有利となる。
各実施例及び比較例のインキ組成物のドライダウンの評価は、以下のようにして行った。まず、インキ組成物の試料0.1ccをRI展色機(2分割ロール、株式会社明製作所製)を用いて更紙(王子製紙株式会社製、SL+)に展色し、展色直後の濃度をSpectroeye濃度計(Gretagmacbeth社製)により測定した後に、室内で24時間放置してから再度濃度を測定した。そして、展色直後の濃度値から24時間経過後の濃度値を引いたものをドライダウン量とした。その結果を表1及び2に示す。
Claims (5)
- ナフテン系ベースオイルと、ナフテン系減圧蒸留残渣と、を構成成分として含むことを特徴とするオフセット印刷用インキ組成物。
- 前記ナフテン系減圧蒸留残渣の25℃における針入度が300を超えることを特徴とする請求項1記載のオフセット印刷用インキ組成物。
- 前記ナフテン系ベースオイルが、OSHA基準及びPCA3質量%未満の基準の両方を満足することを特徴とする請求項1又は2記載のオフセット印刷用インキ組成物。
- 浸透乾燥型である請求項1〜3のいずれか1項記載のオフセット印刷用インキ組成物。
- 請求項1〜4のいずれか1項記載のオフセット印刷用インキ組成物を用いることを特徴とする、浸透乾燥方式により印刷を行ったときの印刷紙面の経時におけるドライダウンを抑制する方法。