JP6149148B1 - かつら用粘着剤、及びかつら用粘着剤の使用方法 - Google Patents
かつら用粘着剤、及びかつら用粘着剤の使用方法 Download PDFInfo
- Publication number
- JP6149148B1 JP6149148B1 JP2016237339A JP2016237339A JP6149148B1 JP 6149148 B1 JP6149148 B1 JP 6149148B1 JP 2016237339 A JP2016237339 A JP 2016237339A JP 2016237339 A JP2016237339 A JP 2016237339A JP 6149148 B1 JP6149148 B1 JP 6149148B1
- Authority
- JP
- Japan
- Prior art keywords
- wig
- pressure
- sensitive adhesive
- adhesive
- filler
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
Description
また、特許文献2に記載のかつら用固定剤は、感温性粘着剤を用いることで、かつらを頭皮に高い固定力で固定できると共に、取外しも簡単にでき、また耐水性や耐汗性にも優れたものとされている。かつらを頭皮に接着するのにより適したものとするためには、上述の通り、さらに多くの優れた性能や機能を備えたものとすることが望ましい。
また、本発明のかつら用粘着剤の使用方法は、上記のかつら用粘着剤を、頭皮に塗布し、ネット地からなるかつらベースを備えたかつらにおけるかつらベースを、前記頭皮に接着させる方法としてある。
本実施形態のかつら用粘着剤は、粘着剤のベース樹脂と、タッキファイヤーと、増粘剤と、フィラーとを混合してなり、フィラーとして、シリカ、アルギン酸カルシウム、及びナイロンパウダーからなる群から選択された一又は二以上を有効成分として含むことを特徴とする。
アクリル酸エステル系共重合体樹脂を構成する(メタ)アクリル酸エステル系モノマーは、特に限定されず、種々のものを用いることができる。例えば、メチル(メタ)アクリレート、エチル(メタ)アクリレート、n−プロピル(メタ)アクリレート、イソプロピル(メタ)アクリレート、n−ブチル(メタ)アクリレート、イソブチル(メタ)アクリレート、n−ヘキシル(メタ)アクリレート、2−エチルヘキシル(メタ)アクリレート、シクロヘキシル(メタ)アクリレート、イソオクチル(メタ)アクリレート、n−オクチル(メタ)アクリレート、ノニル(メタ)アクリレート、イソノニル(メタ)アクリレート、デシル(メタ)アクリレート、イソデシル(メタ)アクリレート、ウンデシル(メタ)アクリレート、イソウンデシル(メタ)アクリレート、ドデシル(メタ)アクリレート、イソドデシル(メタ)アクリレート、トリデシル(メタ)アクリレート、イソトリデシル(メタ)アクリレート、テトラデシル(メタ)アクリレート等の脂肪族(メタ)アクリレート、ベンジル(メタ)アクリレート、フェニル(メタ)アクリレート等の芳香族(メタ)アクリレート等が挙げられ、炭素数4〜12、特には4〜10、更には4〜8のアルキル基を含有する(メタ)アクリル酸アルキルエステルが好ましく、具体的にはn−ブチル(メタ)アクリレート、2−エチルヘキシル(メタ)アクリレート等が好ましく用いられ、2−エチルヘキシル(メタ)アクリレートが特に好ましく用いられる。これらの2種類以上を混合して用いても良い。
ここで、フィラーは、一般に粉体の原料であり、粘着剤や接着剤に補助的に添加することにより、嵩増し、増粘、凝集力の向上を図るためのものである。本実施形態のかつら用粘着剤では、このフィラーの材質の選択と、その添加量を調整することによって、かつら用粘着剤の接着力、色調、塗りやすさ、べたつき、乾燥性、吸水及び吸油性、並びに安定性等のバランスを最適化している。
本実施形態のかつら用粘着剤では、上記のフィラーを適量添加することで、接着力を高めつつ、その他の性質や機能を合せて向上させることが可能となっている。
例えば、粘着剤が乾燥した後の状態に光沢が生じたり、あるいは白化したり、その他の色調が生じることによって、かつらの自然さが阻害される場合がある。
そこで、本実施形態のかつら用粘着剤においては、上記のフィラーを適量添加することで、フィラーによって生じた粘着剤表面の凹凸が光を乱反射させ、つやを抑えることを可能にしている。ただし、フィラーの種類や添加量によっては、フィラー自体が光ったり、過度に白くなったりするなど、外観が不自然となることから、適切な種類の選定と適性量の添加が重要である。
そこで、本実施形態のかつら用粘着剤においては、上記のフィラーを適量添加することで、塗布厚を確保するために十分な粘度が得られ、かつ塗布しやすいクリーム状のなめらかな液性を実現している。
そこで、本実施形態のかつら用粘着剤においては、上記のフィラーを適量添加することで、このようなべたつきの問題を改善することを可能としている。
本実施形態のかつら用粘着剤は、上記のフィラーを適量添加することで、乾燥性に優れたものとなっている。
本実施形態のかつら用粘着剤は、上記のフィラーを適量添加することで、吸水及び吸油性に優れたものとなっている。
本実施形態のかつら用粘着剤における上記のフィラーは分散性が良好であり、沈降が少なく、吸水性(保水性)を有するため、水性エマルションタイプの粘着剤に特有の離水現象を改善することが可能となっている。
例えば、抗炎症剤、殺菌剤、及び防腐剤等を含有させることができる。このとき、これらの成分としては、かつら用粘着剤の粘着力や頭皮への悪影響が認められないものを選択することが重要である。
抗炎症剤、殺菌剤としては、レゾルシン及び/又は塩化セチルピリジニウムを好適に配合させることができる。
また、防腐剤としては、フェノキシエタノールを好適に配合させることが可能である。かつら用粘着剤に当該防腐剤を使用した場合に、粘着力が安定的に保たれること、及び経時安定性が保たれることが確認されている。
具体的には、かつら用粘着剤を塗布部材に少量取り出して、これを頭皮に軽くパッティングすることで塗布し、さらにこれを引き延ばす。このとき、かつらベースの周縁に対応する頭皮上に円周状に塗布し、その円内において格子状に塗布することが好ましい。そして、1回目の塗布を完了すると、所定の時間(5分間から10分間程度)、自然乾燥させた後、2回目の塗布を行うことが好ましい。これにより、乾燥させた状態において十分な被膜強度を得るために必要な塗布厚を確保することができる。
そして、2回目の塗布の完了後に、さらに所定の時間(5分間から10分間程度)、自然乾燥させ、かつらにおけるかつらベースを、かつら用粘着剤が塗布された頭皮に載せて接着させる。
本発明の実施形態に係るかつら用粘着剤を以下のように製造した。
真空乳化釜を使用して、常温で、ベース樹脂組成物、タッキファイヤー、フィラー、増粘剤の順で混合し、十分に乳化するまで攪拌して、本実施形態に係るかつら用粘着剤を得た。配合成分の割合は、図1〜3、及び図5〜7に示す通りである。
具体的には、ベース樹脂組成物としては、日本カーバイド工業株式会社のニカゾールTS620(2-エチルヘキシルアクリレート(58%)、ポリ=ノニルフェニルエーテル(2.2%)、水(39.8%))(ベース樹脂組成物a)と、日本カーバイド工業株式会社のニカゾールMH-6010(2-エチルヘキシルアクリレート(58%)、ポリオキシエチレン=ラウリルエーテル(2.0%)、水(40%))(ベース樹脂組成物b)の2種類のうちの一方を、100g配合した。
比較例のかつら用粘着剤を以下のように製造した。
真空乳化釜を使用して、常温で、ベース樹脂組成物、タッキファイヤー、増粘剤の順で混合し、十分に乳化するまで攪拌して、比較例のかつら用粘着剤を得た。配合成分の割合は、図4、8に示す通りである。
具体的には、ベース樹脂組成物としては、上記のベース樹脂組成物aとベース樹脂組成物bの一方を100g配合した。また、タッキファイヤーとしては、上記のタッキファイヤーaとタッキファイヤーbの一方を5g又は25g配合した。また、増粘剤としては、上記の増粘剤aと増粘剤bの一方を、1g又は7g配合した。また、フィラーは、配合しなかった。
(1)粘着力
かつら用粘着剤の粘着力は、引っ張り試験機による測定と、指による粘着力の官能評価とを総合して評価した。具体的には、引っ張り試験機による測定の評価結果と官能評価結果の平均値(小数点以下は四捨五入)を粘着力の評価結果とした。
・29Nより大きい 5
・25〜29N 4
・20〜24N 3
・15〜19N 2
・15N未満 1
官能評価の結果は、3名の評価結果の平均値の小数点以下を四捨五入して得た。以下の官能評価についても同様である。
・強い 5
・やや強い 4
・普通 3
・やや弱い 2
・弱い 1
かつら用粘着剤の色調は、かつら用粘着剤をフィルムに塗布して乾燥させた状態を目視で観察することによる官能評価により評価した。
具体的には、易接着フィルム(東洋紡株式会社、コスモシャインA4100,A4300)上に、かつら用粘着剤を100μmの厚みで塗布して評価用のサンプルを作製した。そして、各サンプルにおけるかつら用粘着剤の透明度及び表面のツヤ等を考慮し、見た目の自然さについて総合的に評価した。
・極めて良好 5
・非常に良好 4
・良好 3
・やや不自然 2
・不自然 1
かつら用粘着剤の塗りやすさは、粘着剤の厚みを確保する上での塗りやすさであり、上記の色調を評価するためのサンプルを作製する際の塗布のし易さと塗布状態を目視で観察することによる官能評価により評価した。
・良好 5
・やや良好 4
・普通 3
・やや不良 2
・不良 1
かつら用粘着剤のべたつきは、ボールタックテスター(株式会社安田精機製作所、ボールタックテスター183-BT)を用いて測定した。測定方法は以下の通りである。
かつら用粘着剤を2回塗布して得られた粘着シート(縦200mm、横150mm)を、30°の斜面上に長手方向に傾斜するように固定した。粘着シートの上側半分をカバーシートで覆い、測定用ボールの滑走をスタートさせる滑走基点から100mmの区間を助走距離とした。粘着シートの下側半分は粘着シートが露出した100mmの区間であり、これを滑走距離とした。
・1〜4 5
・5〜8 4
・9〜12 3
・13〜16 2
・17〜20 1
かつら用粘着剤の乾燥性は、かつら用粘着剤をフィルムに塗布して、その乾燥具合を目視で観察することによる官能評価により評価した。
・早い 5
・やや早い 4
・普通 3
・やや遅い 2
・遅い 1
総合評価の判定基準は、評価結果の合計値の範囲ごとに、以下の通りである。
・23〜25 極めて良い(☆)
・20〜22 非常に良い(◎)
・17〜19 良い(○)
・14〜16 やや悪い(△)
・0〜13 悪い(×)
一方、比較例1〜26のフィラーを含まないかつら用粘着剤は、悪いものとなっている。
このように実施例1〜90のかつら用粘着剤は、接着力、色調、塗りやすさ、べたつき、及び乾燥性のバランスが優れたものとなっていることが分かる。
Claims (5)
- 頭皮に塗布して使用するかつら用粘着剤であって、
粘着剤のベース樹脂と、タッキファイヤーと、増粘剤と、フィラーとを混合してなり、前記フィラーとして、シリカ、アルギン酸カルシウム、及びナイロンパウダーからなる群から選択された一又は二以上を有効成分として含み、
前記フィラーが、前記ベース樹脂に対して、1.0重量%〜28.0重量%含有された
ことを特徴とするかつら用粘着剤。 - 前記タッキファイヤーが、テルペンフェノール樹脂及び/又はロジンエステル樹脂であることを特徴とする請求項1記載のかつら用粘着剤。
- 前記増粘剤が、ポリエーテルポリオール系ウレタンポリマーであることを特徴とする請求項1又は2記載のかつら用粘着剤。
- 前記ベース樹脂が、アクリル酸エステル系共重合体樹脂であることを特徴とする請求項1〜3のいずれかに記載のかつら用粘着剤。
- 請求項1〜4のいずれかに記載のかつら用粘着剤を、頭皮に塗布し、ネット地からなるかつらベースを備えたかつらにおけるかつらベースを、前記頭皮に接着させることを特徴とするかつら用粘着剤の使用方法。