JP6143825B2 - 磁気テープ及びその製造方法 - Google Patents
磁気テープ及びその製造方法 Download PDFInfo
- Publication number
- JP6143825B2 JP6143825B2 JP2015203363A JP2015203363A JP6143825B2 JP 6143825 B2 JP6143825 B2 JP 6143825B2 JP 2015203363 A JP2015203363 A JP 2015203363A JP 2015203363 A JP2015203363 A JP 2015203363A JP 6143825 B2 JP6143825 B2 JP 6143825B2
- Authority
- JP
- Japan
- Prior art keywords
- magnetic
- magnetic tape
- blade
- cutting
- tape
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
前記非磁性支持体と前記磁性層との間に、無機粉末及び結合剤を含有する下塗り層をさらに有し、
前記非磁性支持体の長手方向のヤング率が9〜22GPaであり、
前記磁気テープの裁断面の厚さ方向の粗さ曲線における中心線平均粗さ(Ra)が0.08〜0.25μmであることを特徴とする。
また、本発明は、幅広の原反を裁断装置により裁断して上記磁気テープを製造する製造方法であって、
前記裁断装置は、薄刃及び前記薄刃と噛み合わせ状態で対向配置される厚刃を有する裁断手段と、前記磁気原反を前記薄刃と厚刃との間に搬送する巻出し手段及び巻取り手段とを備え、
前記薄刃と厚刃との噛み合わせ深さ(L)が0.05〜0.1mm、前記薄刃と厚刃とが互いに噛み合う側面の最大表面粗さ(P−V)がいずれも0.05μm以下であり、
前記磁気原反を、前記裁断手段近傍における磁気原反の幅方向の変動が100μm以下になるように搬送させて所定幅に裁断するものである。
非磁性支持体としては、高容量化のために4μm以下の厚さを有する薄い高分子樹脂フィルムが用いられる。非磁性支持体の厚さは、薄いほど好ましいが、余りに薄くなると均一な厚みの非磁性支持体が得られ難くなるため、1μm以上が好ましい。このような非磁性支持体としては、具体的には、例えば、ポリアミドフィルムやポリイミドフィルムなどが挙げられる。また、上記した長手方向と幅方向とで等方的なヤング率を有する磁気原反を作製するために、幅方向のヤング率が8〜20GPa、長手方向のヤング率が9〜22GPaの非磁性支持体が好ましい。
下記の表1に示す組成を有する磁性塗料(I)成分をニーダで混練した後、混練物をサンドミルを用いて分散処理を行い(滞留時間:60分)、得られた分散液にポリイソシアネート6部を加え、撹拌し、ろ過して磁性塗料(I)を調製した。
下記表2の下塗り層塗料(i)成分をニーダで混練した後、混練物をサンドミル(滞留時間:60分)で分散した。得られた分散液に、電子線硬化性樹脂であるジペンタエリスリトールヘキサアクリレート6部を加え、撹拌し、ろ過して、下塗り層塗料(i)を調製した。
電子線硬化性樹脂を添加しなかった以外は、下塗り層塗料(i)と同様にして、下塗り層塗料(ii)を調製した。
下記表3のバックコート層塗料成分を、サンドミルで分散処理(滞留時間:45分)を行い、得られた分散液にポリイソシアネート8.5部を加え、撹拌し、ろ過して、バックコート層塗料を調製した。
下記の表4に示す各非磁性支持体を用い、表5に示す塗料の組み合わせで、まず、上記の下塗り層塗料(i)または(ii)を、非磁性支持体上に、乾燥及びカレンダ処理後の厚さが2μmとなるように塗布して下塗り塗膜を形成し、この下塗り塗膜上に、さらに、乾燥及びカレンダ処理後の厚さが100nmとなるように上記の磁性塗料(I)を同時重層塗布し、長手方向に配向処理を行いながら、乾燥して下塗り層及び磁性層を形成した。なお、結合剤として電子線硬化性樹脂を含有する下塗り層塗料(i)を用いたものについては、乾燥後、4MRadの電子線を照射した。
精密変位測定器を設置した引っ張り試験機を用いて、1/2インチ角の正方形状にした測定試料を引っ張り、歪み0.3%の時の伸び量からヤング率を算出した。
磁気テープの裁断面を治具で固定し、裁断面の粗さ曲線をレーザー顕微鏡(レーザーテック(株)製のリアルタイム走査型レーザ顕微鏡1LM21D,He−Neレーザ,CW型,波長:632.8mm,最大出力:0.1mW)で測定した。測定条件は、顕微鏡倍率を1000倍、解像度を0.3μm、スロースキャンを8、スキャンタイムを40秒とした。各サンプルの裁断面の10箇所から粗さ曲線を得て、得られた粗さ曲線のデータ処理を行い、中心線平均粗さ(Ra)を求めた。
LTO用のガイドローラー(SUS製)を有し、両端にテンションゲージを設置した評価装置を用いて、磁気テープを上部フランジに0.5°の角度で巻き付け、1.2m/分でテープを走行させたときの、両端のテンションゲージの張力差から摩擦係数を算出した。
磁気テープをLTOカートリッジに組み込み、これをLTOドライブ装置のシャトルモード(単純走行、録再無し、テープ速度:6m/s)で走行させた。ドライブ内のガイドローラと摺接している磁気テープの走行性を目視により観察し、以下の基準で直進走行性を評価した。
○:テープエッジの振れ無し
△:テープエッジに振動が見られる
×:テープエッジに折れ曲がりが見られる
磁気テープをLTOカートリッジに組み込み、これをLTOドライブ装置のシャトルモード(テープ速度:6m/s)で2000パス走行させた。走行後、ガイドローラのフランジ部の汚れを目視により観察し、以下の基準で粉落ちを評価した。
○:明確な粉落ちは見られない
△:フランジ部が黒色に変色している
×:フランジ部に黒色の粉末状の汚れが見られる
3a 磁性層
3b 非磁性支持体
3c バックコート層
6 ガイドローラ
6a フランジ部
10 裁断手段
11 薄刃
11a 薄刃の側面
12 厚刃
12a 厚刃の側面
20 巻出し部
30 巻取り部
M 磁気原反
L 噛み合せ深さ
S 裁断面
Claims (4)
- 4μm以下の厚さを有する非磁性支持体上の一面上に磁性粉末及び結合剤を含有する磁性層を有し、裁断面を有する、リニアサーペンタイン方式の磁気記録再生システムに利用される磁気テープであって、
前記非磁性支持体と前記磁性層との間に、無機粉末及び結合剤を含有する下塗り層をさらに有し、
前記非磁性支持体の長手方向のヤング率が9〜22GPaであり、
前記磁気テープの裁断面の厚さ方向の粗さ曲線における中心線平均粗さ(Ra)が0.08〜0.25μmである磁気テープ。 - 前記磁気テープの裁断面の厚さ方向の粗さ曲線における中心線平均粗さ(Ra)が、0.09〜0.12μmである請求項1に記載の磁気テープ。
- 前記下塗り層の結合剤は、電子線硬化性樹脂を含有する請求項1または2に記載の磁気テープ。
- 幅広の磁気原反を裁断装置によって裁断することにより製造される請求項1〜3のいずれか1項に記載の磁気テープの製造方法であって、
前記裁断装置は、薄刃及び前記薄刃と噛み合わせ状態で対向配置される厚刃を有する裁断手段と、前記磁気原反を前記薄刃と厚刃との間に搬送する巻出し手段及び巻取り手段とを備え、
前記薄刃と厚刃との噛み合わせ深さ(L)が0.05〜0.1mm、前記薄刃と厚刃とが互いに噛み合う側面の最大表面粗さ(P−V)がいずれも0.05μm以下であり、
前記磁気原反を、前記裁断手段近傍における磁気原反の幅方向の変動が100μm以下になるように搬送させて所定幅に裁断する、製造方法。