JP5796142B2 - 鋼板材の溶融めっき法 - Google Patents
鋼板材の溶融めっき法 Download PDFInfo
- Publication number
- JP5796142B2 JP5796142B2 JP2014555957A JP2014555957A JP5796142B2 JP 5796142 B2 JP5796142 B2 JP 5796142B2 JP 2014555957 A JP2014555957 A JP 2014555957A JP 2014555957 A JP2014555957 A JP 2014555957A JP 5796142 B2 JP5796142 B2 JP 5796142B2
- Authority
- JP
- Japan
- Prior art keywords
- atmosphere
- holding
- steel
- dew point
- steel sheet
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Links
- 229910000831 Steel Inorganic materials 0.000 title claims description 140
- 239000010959 steel Substances 0.000 title claims description 140
- 238000007598 dipping method Methods 0.000 title claims description 11
- 238000000034 method Methods 0.000 claims description 77
- 239000000463 material Substances 0.000 claims description 71
- 238000007747 plating Methods 0.000 claims description 59
- 238000010438 heat treatment Methods 0.000 claims description 33
- 229910052751 metal Inorganic materials 0.000 claims description 21
- 239000002184 metal Substances 0.000 claims description 19
- XEEYBQQBJWHFJM-UHFFFAOYSA-N Iron Chemical compound [Fe] XEEYBQQBJWHFJM-UHFFFAOYSA-N 0.000 claims description 18
- 238000001816 cooling Methods 0.000 claims description 18
- 239000012535 impurity Substances 0.000 claims description 16
- 230000008569 process Effects 0.000 claims description 13
- 101100492805 Caenorhabditis elegans atm-1 gene Proteins 0.000 claims description 10
- 229910052742 iron Inorganic materials 0.000 claims description 10
- 230000001681 protective effect Effects 0.000 claims description 10
- 229910052759 nickel Inorganic materials 0.000 claims description 8
- 229910052804 chromium Inorganic materials 0.000 claims description 7
- 238000011282 treatment Methods 0.000 claims description 7
- 238000005097 cold rolling Methods 0.000 claims description 2
- 238000005098 hot rolling Methods 0.000 claims description 2
- PXHVJJICTQNCMI-UHFFFAOYSA-N nickel Substances [Ni] PXHVJJICTQNCMI-UHFFFAOYSA-N 0.000 description 28
- 229910052782 aluminium Inorganic materials 0.000 description 12
- 230000003647 oxidation Effects 0.000 description 10
- 238000007254 oxidation reaction Methods 0.000 description 10
- 239000011701 zinc Substances 0.000 description 10
- 229910045601 alloy Inorganic materials 0.000 description 9
- 239000000956 alloy Substances 0.000 description 9
- 238000002844 melting Methods 0.000 description 9
- 230000008018 melting Effects 0.000 description 9
- 239000000203 mixture Substances 0.000 description 9
- 229910052710 silicon Inorganic materials 0.000 description 9
- 239000010410 layer Substances 0.000 description 8
- 229910052748 manganese Inorganic materials 0.000 description 8
- 229910000990 Ni alloy Inorganic materials 0.000 description 7
- 238000000137 annealing Methods 0.000 description 7
- 230000001590 oxidative effect Effects 0.000 description 6
- 229910000599 Cr alloy Inorganic materials 0.000 description 5
- 230000015572 biosynthetic process Effects 0.000 description 5
- 239000007789 gas Substances 0.000 description 5
- 229910052749 magnesium Inorganic materials 0.000 description 5
- 239000011777 magnesium Substances 0.000 description 5
- UQSXHKLRYXJYBZ-UHFFFAOYSA-N Iron oxide Chemical compound [Fe]=O UQSXHKLRYXJYBZ-UHFFFAOYSA-N 0.000 description 4
- HCHKCACWOHOZIP-UHFFFAOYSA-N Zinc Chemical compound [Zn] HCHKCACWOHOZIP-UHFFFAOYSA-N 0.000 description 4
- 238000005275 alloying Methods 0.000 description 4
- 239000010953 base metal Substances 0.000 description 4
- 239000000470 constituent Substances 0.000 description 4
- 238000002474 experimental method Methods 0.000 description 4
- 229910052725 zinc Inorganic materials 0.000 description 4
- 229910000851 Alloy steel Inorganic materials 0.000 description 3
- 229910001566 austenite Inorganic materials 0.000 description 3
- 238000010276 construction Methods 0.000 description 3
- 230000007547 defect Effects 0.000 description 3
- 230000007613 environmental effect Effects 0.000 description 3
- 238000001953 recrystallisation Methods 0.000 description 3
- 229910052719 titanium Inorganic materials 0.000 description 3
- 238000009736 wetting Methods 0.000 description 3
- XAGFODPZIPBFFR-UHFFFAOYSA-N aluminium Chemical compound [Al] XAGFODPZIPBFFR-UHFFFAOYSA-N 0.000 description 2
- QVGXLLKOCUKJST-UHFFFAOYSA-N atomic oxygen Chemical compound [O] QVGXLLKOCUKJST-UHFFFAOYSA-N 0.000 description 2
- 229910002091 carbon monoxide Inorganic materials 0.000 description 2
- 239000010960 cold rolled steel Substances 0.000 description 2
- 239000000567 combustion gas Substances 0.000 description 2
- 238000002485 combustion reaction Methods 0.000 description 2
- 238000011109 contamination Methods 0.000 description 2
- 229910052802 copper Inorganic materials 0.000 description 2
- 238000005260 corrosion Methods 0.000 description 2
- 230000007797 corrosion Effects 0.000 description 2
- 238000005246 galvanizing Methods 0.000 description 2
- 229910052745 lead Inorganic materials 0.000 description 2
- 229910052760 oxygen Inorganic materials 0.000 description 2
- 239000001301 oxygen Substances 0.000 description 2
- 239000011241 protective layer Substances 0.000 description 2
- 230000009467 reduction Effects 0.000 description 2
- 238000005096 rolling process Methods 0.000 description 2
- 239000000126 substance Substances 0.000 description 2
- 239000000758 substrate Substances 0.000 description 2
- 238000004804 winding Methods 0.000 description 2
- 229910016943 AlZn Inorganic materials 0.000 description 1
- 229910000789 Aluminium-silicon alloy Inorganic materials 0.000 description 1
- 229910000760 Hardened steel Inorganic materials 0.000 description 1
- FYYHWMGAXLPEAU-UHFFFAOYSA-N Magnesium Chemical compound [Mg] FYYHWMGAXLPEAU-UHFFFAOYSA-N 0.000 description 1
- 229910000914 Mn alloy Inorganic materials 0.000 description 1
- 229910001297 Zn alloy Inorganic materials 0.000 description 1
- 230000009471 action Effects 0.000 description 1
- 238000005269 aluminizing Methods 0.000 description 1
- 238000013459 approach Methods 0.000 description 1
- 230000008901 benefit Effects 0.000 description 1
- 229910052797 bismuth Inorganic materials 0.000 description 1
- 229910052793 cadmium Inorganic materials 0.000 description 1
- 238000006388 chemical passivation reaction Methods 0.000 description 1
- 238000006243 chemical reaction Methods 0.000 description 1
- 238000004140 cleaning Methods 0.000 description 1
- 239000011248 coating agent Substances 0.000 description 1
- 238000000576 coating method Methods 0.000 description 1
- 238000010924 continuous production Methods 0.000 description 1
- 238000009713 electroplating Methods 0.000 description 1
- 238000005516 engineering process Methods 0.000 description 1
- 238000000605 extraction Methods 0.000 description 1
- 238000005244 galvannealing Methods 0.000 description 1
- 239000011261 inert gas Substances 0.000 description 1
- 238000012423 maintenance Methods 0.000 description 1
- 229910001092 metal group alloy Inorganic materials 0.000 description 1
- 150000002739 metals Chemical class 0.000 description 1
- 229910052750 molybdenum Inorganic materials 0.000 description 1
- 229910000480 nickel oxide Inorganic materials 0.000 description 1
- 229910052758 niobium Inorganic materials 0.000 description 1
- GNRSAWUEBMWBQH-UHFFFAOYSA-N oxonickel Chemical compound [Ni]=O GNRSAWUEBMWBQH-UHFFFAOYSA-N 0.000 description 1
- 238000002161 passivation Methods 0.000 description 1
- 238000012545 processing Methods 0.000 description 1
- 229910052761 rare earth metal Inorganic materials 0.000 description 1
- 150000002910 rare earth metals Chemical class 0.000 description 1
- 230000000717 retained effect Effects 0.000 description 1
- 238000002791 soaking Methods 0.000 description 1
- 239000010935 stainless steel Substances 0.000 description 1
- 229910001220 stainless steel Inorganic materials 0.000 description 1
- 239000007858 starting material Substances 0.000 description 1
- 239000000725 suspension Substances 0.000 description 1
- 230000007704 transition Effects 0.000 description 1
- 229910052720 vanadium Inorganic materials 0.000 description 1
- 239000013585 weight reducing agent Substances 0.000 description 1
Images
Classifications
-
- C—CHEMISTRY; METALLURGY
- C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
- C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
- C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
- C23C2/02—Pretreatment of the material to be coated, e.g. for coating on selected surface areas
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B32—LAYERED PRODUCTS
- B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
- B32B15/00—Layered products comprising a layer of metal
- B32B15/01—Layered products comprising a layer of metal all layers being exclusively metallic
- B32B15/012—Layered products comprising a layer of metal all layers being exclusively metallic one layer being formed of an iron alloy or steel, another layer being formed of aluminium or an aluminium alloy
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B32—LAYERED PRODUCTS
- B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
- B32B15/00—Layered products comprising a layer of metal
- B32B15/01—Layered products comprising a layer of metal all layers being exclusively metallic
- B32B15/013—Layered products comprising a layer of metal all layers being exclusively metallic one layer being formed of an iron alloy or steel, another layer being formed of a metal other than iron or aluminium
-
- C—CHEMISTRY; METALLURGY
- C21—METALLURGY OF IRON
- C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
- C21D8/00—Modifying the physical properties by deformation combined with, or followed by, heat treatment
- C21D8/02—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips
- C21D8/0221—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips characterised by the working steps
- C21D8/0226—Hot rolling
-
- C—CHEMISTRY; METALLURGY
- C21—METALLURGY OF IRON
- C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
- C21D8/00—Modifying the physical properties by deformation combined with, or followed by, heat treatment
- C21D8/02—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips
- C21D8/0221—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips characterised by the working steps
- C21D8/0236—Cold rolling
-
- C—CHEMISTRY; METALLURGY
- C21—METALLURGY OF IRON
- C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
- C21D9/00—Heat treatment, e.g. annealing, hardening, quenching or tempering, adapted for particular articles; Furnaces therefor
- C21D9/46—Heat treatment, e.g. annealing, hardening, quenching or tempering, adapted for particular articles; Furnaces therefor for sheet metals
-
- C—CHEMISTRY; METALLURGY
- C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
- C22C—ALLOYS
- C22C18/00—Alloys based on zinc
-
- C—CHEMISTRY; METALLURGY
- C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
- C22C—ALLOYS
- C22C18/00—Alloys based on zinc
- C22C18/04—Alloys based on zinc with aluminium as the next major constituent
-
- C—CHEMISTRY; METALLURGY
- C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
- C22C—ALLOYS
- C22C21/00—Alloys based on aluminium
- C22C21/02—Alloys based on aluminium with silicon as the next major constituent
-
- C—CHEMISTRY; METALLURGY
- C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
- C22C—ALLOYS
- C22C21/00—Alloys based on aluminium
- C22C21/10—Alloys based on aluminium with zinc as the next major constituent
-
- C—CHEMISTRY; METALLURGY
- C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
- C22C—ALLOYS
- C22C30/00—Alloys containing less than 50% by weight of each constituent
-
- C—CHEMISTRY; METALLURGY
- C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
- C22C—ALLOYS
- C22C38/00—Ferrous alloys, e.g. steel alloys
-
- C—CHEMISTRY; METALLURGY
- C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
- C22C—ALLOYS
- C22C38/00—Ferrous alloys, e.g. steel alloys
- C22C38/001—Ferrous alloys, e.g. steel alloys containing N
-
- C—CHEMISTRY; METALLURGY
- C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
- C22C—ALLOYS
- C22C38/00—Ferrous alloys, e.g. steel alloys
- C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
- C22C38/40—Ferrous alloys, e.g. steel alloys containing chromium with nickel
-
- C—CHEMISTRY; METALLURGY
- C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
- C22C—ALLOYS
- C22C38/00—Ferrous alloys, e.g. steel alloys
- C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
- C22C38/40—Ferrous alloys, e.g. steel alloys containing chromium with nickel
- C22C38/44—Ferrous alloys, e.g. steel alloys containing chromium with nickel with molybdenum or tungsten
-
- C—CHEMISTRY; METALLURGY
- C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
- C22C—ALLOYS
- C22C38/00—Ferrous alloys, e.g. steel alloys
- C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
- C22C38/40—Ferrous alloys, e.g. steel alloys containing chromium with nickel
- C22C38/58—Ferrous alloys, e.g. steel alloys containing chromium with nickel with more than 1.5% by weight of manganese
-
- C—CHEMISTRY; METALLURGY
- C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
- C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
- C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
- C23C2/003—Apparatus
- C23C2/0038—Apparatus characterised by the pre-treatment chambers located immediately upstream of the bath or occurring locally before the dipping process
- C23C2/004—Snouts
-
- C—CHEMISTRY; METALLURGY
- C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
- C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
- C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
- C23C2/02—Pretreatment of the material to be coated, e.g. for coating on selected surface areas
- C23C2/022—Pretreatment of the material to be coated, e.g. for coating on selected surface areas by heating
- C23C2/0222—Pretreatment of the material to be coated, e.g. for coating on selected surface areas by heating in a reactive atmosphere, e.g. oxidising or reducing atmosphere
-
- C—CHEMISTRY; METALLURGY
- C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
- C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
- C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
- C23C2/02—Pretreatment of the material to be coated, e.g. for coating on selected surface areas
- C23C2/022—Pretreatment of the material to be coated, e.g. for coating on selected surface areas by heating
- C23C2/0224—Two or more thermal pretreatments
-
- C—CHEMISTRY; METALLURGY
- C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
- C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
- C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
- C23C2/02—Pretreatment of the material to be coated, e.g. for coating on selected surface areas
- C23C2/024—Pretreatment of the material to be coated, e.g. for coating on selected surface areas by cleaning or etching
-
- C—CHEMISTRY; METALLURGY
- C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
- C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
- C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
- C23C2/04—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor characterised by the coating material
- C23C2/06—Zinc or cadmium or alloys based thereon
-
- C—CHEMISTRY; METALLURGY
- C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
- C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
- C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
- C23C2/34—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor characterised by the shape of the material to be treated
- C23C2/36—Elongated material
- C23C2/40—Plates; Strips
Landscapes
- Chemical & Material Sciences (AREA)
- Engineering & Computer Science (AREA)
- Mechanical Engineering (AREA)
- Organic Chemistry (AREA)
- Metallurgy (AREA)
- Materials Engineering (AREA)
- Chemical Kinetics & Catalysis (AREA)
- Physics & Mathematics (AREA)
- Thermal Sciences (AREA)
- Crystallography & Structural Chemistry (AREA)
- Coating With Molten Metal (AREA)
- Heat Treatment Of Sheet Steel (AREA)
- Oil, Petroleum & Natural Gas (AREA)
Applications Claiming Priority (3)
| Application Number | Priority Date | Filing Date | Title |
|---|---|---|---|
| DE102012101018.8 | 2012-02-08 | ||
| DE102012101018A DE102012101018B3 (de) | 2012-02-08 | 2012-02-08 | Verfahren zum Schmelztauchbeschichten eines Stahlflachprodukts |
| PCT/EP2012/075402 WO2013117273A1 (de) | 2012-02-08 | 2012-12-13 | Verfahren zum schmelztauchbeschichten eines stahlflachprodukts |
Publications (2)
| Publication Number | Publication Date |
|---|---|
| JP2015509556A JP2015509556A (ja) | 2015-03-30 |
| JP5796142B2 true JP5796142B2 (ja) | 2015-10-21 |
Family
ID=47504886
Family Applications (1)
| Application Number | Title | Priority Date | Filing Date |
|---|---|---|---|
| JP2014555957A Expired - Fee Related JP5796142B2 (ja) | 2012-02-08 | 2012-12-13 | 鋼板材の溶融めっき法 |
Country Status (9)
| Country | Link |
|---|---|
| US (1) | US9803270B2 (enExample) |
| EP (1) | EP2812458B8 (enExample) |
| JP (1) | JP5796142B2 (enExample) |
| KR (1) | KR101994989B1 (enExample) |
| CN (1) | CN104245995B (enExample) |
| DE (1) | DE102012101018B3 (enExample) |
| ES (1) | ES2593531T3 (enExample) |
| IN (1) | IN2014MN01579A (enExample) |
| WO (1) | WO2013117273A1 (enExample) |
Families Citing this family (12)
| Publication number | Priority date | Publication date | Assignee | Title |
|---|---|---|---|---|
| ES2851199T3 (es) * | 2013-07-03 | 2021-09-03 | Outokumpu Nirosta Gmbh | Procedimiento para recubrir productos planos de acero con una capa protectora metálica |
| JP6131919B2 (ja) * | 2014-07-07 | 2017-05-24 | Ｊｆｅスチール株式会社 | 合金化溶融亜鉛めっき鋼板の製造方法 |
| DE102014109943B3 (de) | 2014-07-16 | 2015-11-05 | Thyssenkrupp Ag | Stahlprodukt mit einer Korrosionsschutzbeschichtung aus einer Aluminiumlegierung sowie Verfahren zu dessen Herstellung |
| EP3356572B1 (de) * | 2015-09-30 | 2020-03-11 | ThyssenKrupp Steel Europe AG | Verfahren zur herstellung eines stahlflachprodukts mit einer zn-galvannealing-schutzbeschichtung |
| JP6237937B2 (ja) * | 2016-03-11 | 2017-11-29 | Ｊｆｅスチール株式会社 | 高強度溶融亜鉛めっき鋼板の製造方法 |
| JP6323628B1 (ja) | 2016-10-25 | 2018-05-16 | Ｊｆｅスチール株式会社 | 高強度溶融亜鉛めっき鋼板の製造方法 |
| DE102016222993A1 (de) * | 2016-11-22 | 2018-05-24 | Volkswagen Aktiengesellschaft | Verfahren zur Herstellung eines beschichteten Stahlbauteils |
| DE102018100842B3 (de) * | 2018-01-16 | 2019-05-09 | Ebner Industrieofenbau Gmbh | Durchlaufofen für Aluminiumbänder |
| CN112522591B (zh) * | 2019-09-19 | 2022-03-18 | 宝山钢铁股份有限公司 | 一种薄带连铸生产高强高耐蚀钢的方法 |
| WO2021224662A1 (en) * | 2020-05-07 | 2021-11-11 | Arcelormittal | Annealing method of steel |
| CN113969336B (zh) * | 2020-07-23 | 2023-03-28 | 宝山钢铁股份有限公司 | 一种热镀锌钢板的制造方法、钢板及车用构件 |
| CN115351295B (zh) * | 2022-08-26 | 2023-10-27 | 河北建筑工程学院 | 一种复合板制备工艺 |
Family Cites Families (29)
| Publication number | Priority date | Publication date | Assignee | Title |
|---|---|---|---|---|
| JPS60262950A (ja) | 1984-06-08 | 1985-12-26 | Nippon Steel Corp | 耐熱性と耐食性にすぐれた溶融アルミニウムメツキ鋼板の製造法 |
| JPS61147865A (ja) | 1984-12-18 | 1986-07-05 | Nisshin Steel Co Ltd | 溶融アルミめつき鋼板およびその製造法 |
| US5066549A (en) | 1986-05-20 | 1991-11-19 | Armco Inc. | Hot dip aluminum coated chromium alloy steel |
| US4675214A (en) | 1986-05-20 | 1987-06-23 | Kilbane Farrell M | Hot dip aluminum coated chromium alloy steel |
| US4883723A (en) | 1986-05-20 | 1989-11-28 | Armco Inc. | Hot dip aluminum coated chromium alloy steel |
| US5023113A (en) * | 1988-08-29 | 1991-06-11 | Armco Steel Company, L.P. | Hot dip aluminum coated chromium alloy steel |
| AT392089B (de) | 1988-09-14 | 1991-01-25 | Andritz Ag Maschf | Verfahren zum ein- und beidseitigen elektrolytischen verzinken von edelstahl |
| US5246563A (en) | 1988-09-14 | 1993-09-21 | Andritz-Patentverwaltungs-Gesellschaft M.B.H. | Process for the electrolytic zinc coating of stainless steel |
| JPH02285057A (ja) * | 1989-04-27 | 1990-11-22 | Sumitomo Metal Ind Ltd | 溶融亜鉛めっき用鋼板の連続焼鈍方法 |
| JP2727529B2 (ja) | 1989-09-27 | 1998-03-11 | 新日本製鐵株式会社 | メッキ密着性に優れた高耐蝕性アルミメッキＣｒ含有鋼板の製造方法 |
| FR2664617B1 (fr) | 1990-07-16 | 1993-08-06 | Lorraine Laminage | Procede de revetement d'aluminium par trempe a chaud d'une bande d'acier et bande d'acier obtenue par ce procede. |
| JP2743228B2 (ja) | 1992-05-11 | 1998-04-22 | 新日本製鐵株式会社 | 加工性とめっき密着性に優れた溶融アルミめっきＣｒ含有鋼板の製造方法 |
| US5447754A (en) | 1994-04-19 | 1995-09-05 | Armco Inc. | Aluminized steel alloys containing chromium and method for producing same |
| CA2336373C (en) * | 1999-02-22 | 2007-02-27 | Nippon Steel Corporation | High strength galvanized steel plate excellent in adhesion of plated metal and formability in press working and high strength alloy galvanized steel plate and method for production thereof |
| US6902829B2 (en) * | 2001-11-15 | 2005-06-07 | Isg Technologies Inc. | Coated steel alloy product |
| JP2003253413A (ja) * | 2002-03-06 | 2003-09-10 | Nippon Steel Corp | 高強度冷延鋼板とめっき鋼板の兼用製造設備および兼用製造方法 |
| WO2004063410A1 (en) * | 2003-01-15 | 2004-07-29 | Nippon Steel Corporation | High-strength hot-dip galvanized steel sheet and method for producing the same |
| RU2312162C2 (ru) | 2003-04-10 | 2007-12-10 | Ниппон Стил Корпорейшн | Высокопрочный стальной лист с покрытием из расплавленного цинка и способ его изготовления |
| ES2350931T3 (es) | 2003-07-29 | 2011-01-28 | Voestalpine Stahl Gmbh | Procedimiento para la fabricación de componentes templados de chapa de acero. |
| JP4192051B2 (ja) * | 2003-08-19 | 2008-12-03 | 新日本製鐵株式会社 | 高強度合金化溶融亜鉛めっき鋼板の製造方法と製造設備 |
| JP2006051543A (ja) | 2004-07-15 | 2006-02-23 | Nippon Steel Corp | 冷延、熱延鋼板もしくはＡｌ系、Ｚｎ系めっき鋼板を使用した高強度自動車部材の熱間プレス方法および熱間プレス部品 |
| DE102004059566B3 (de) | 2004-12-09 | 2006-08-03 | Thyssenkrupp Steel Ag | Verfahren zum Schmelztauchbeschichten eines Bandes aus höherfestem Stahl |
| EP1693477A1 (de) | 2005-02-22 | 2006-08-23 | ThyssenKrupp Steel AG | Beschichtetes Stahlblech oder -band |
| CA2625790C (en) * | 2005-10-14 | 2010-10-12 | Nippon Steel Corporation | Continuous annealing and hot dip plating method and continuous annealing and hot dip plating system of steel sheet containing si |
| PL1857566T3 (pl) | 2006-05-15 | 2017-10-31 | Thyssenkrupp Steel Europe Ag | Płaski wyrób stalowy z powłoką chroniącą przed korozją i sposób jego wytwarzania |
| EP2009128A1 (en) | 2007-06-29 | 2008-12-31 | ArcelorMittal France | Galvanized or galvannealed silicon steel |
| JP2009035756A (ja) | 2007-07-31 | 2009-02-19 | Nisshin Steel Co Ltd | 高温強度に優れた二輪車排ガス経路部材用Ａｌ系めっき鋼板および部材 |
| EP2055799A1 (de) | 2007-11-05 | 2009-05-06 | ThyssenKrupp Steel AG | Stahlflachprodukt mit einem vor Korrosion schützenden metallischen Überzug und Verfahren zum Erzeugen eines vor Korrosion schützenden metallischen Zn-Mg Überzugs auf einem Stahlflachprodukt |
| DE102010037254B4 (de) * | 2010-08-31 | 2012-05-24 | Thyssenkrupp Steel Europe Ag | Verfahren zum Schmelztauchbeschichten eines Stahlflachprodukts |
-
2012
- 2012-02-08 DE DE102012101018A patent/DE102012101018B3/de not_active Expired - Fee Related
- 2012-12-13 JP JP2014555957A patent/JP5796142B2/ja not_active Expired - Fee Related
- 2012-12-13 IN IN1579MUN2014 patent/IN2014MN01579A/en unknown
- 2012-12-13 US US14/377,337 patent/US9803270B2/en not_active Expired - Fee Related
- 2012-12-13 ES ES12810177.1T patent/ES2593531T3/es active Active
- 2012-12-13 KR KR1020147025029A patent/KR101994989B1/ko not_active Expired - Fee Related
- 2012-12-13 CN CN201280069241.0A patent/CN104245995B/zh not_active Expired - Fee Related
- 2012-12-13 WO PCT/EP2012/075402 patent/WO2013117273A1/de not_active Ceased
- 2012-12-13 EP EP12810177.1A patent/EP2812458B8/de not_active Not-in-force
Also Published As
| Publication number | Publication date |
|---|---|
| KR101994989B1 (ko) | 2019-07-02 |
| IN2014MN01579A (enExample) | 2015-05-15 |
| CN104245995A (zh) | 2014-12-24 |
| US20150345002A1 (en) | 2015-12-03 |
| JP2015509556A (ja) | 2015-03-30 |
| EP2812458B8 (de) | 2016-08-24 |
| CN104245995B (zh) | 2016-08-03 |
| WO2013117273A1 (de) | 2013-08-15 |
| DE102012101018B3 (de) | 2013-03-14 |
| US9803270B2 (en) | 2017-10-31 |
| KR20140128416A (ko) | 2014-11-05 |
| EP2812458B1 (de) | 2016-06-29 |
| EP2812458A1 (de) | 2014-12-17 |
| ES2593531T3 (es) | 2016-12-09 |
Similar Documents
| Publication | Publication Date | Title |
|---|---|---|
| JP5796142B2 (ja) | 鋼板材の溶融めっき法 | |
| JP5720856B2 (ja) | 熱間成形用亜鉛系めっき鋼板 | |
| JP3527092B2 (ja) | 加工性の良い高強度合金化溶融亜鉛めっき鋼板とその製造方法 | |
| US10287440B2 (en) | Steel product with an anticorrosive coating of aluminum alloy and method for the production thereof | |
| JP5636683B2 (ja) | 密着性に優れた高強度合金化溶融亜鉛めっき鋼板および製造方法 | |
| WO2010114174A1 (ja) | 高強度溶融亜鉛めっき鋼板およびその製造方法 | |
| JP5799819B2 (ja) | めっき濡れ性及び耐ピックアップ性に優れる溶融亜鉛めっき鋼板の製造方法 | |
| JP2010519415A (ja) | 冷間圧延されかつ連続的に焼きなましされた高強度鋼ストリップ及び該鋼の製造方法 | |
| JP4329639B2 (ja) | 耐液体金属脆性に優れた熱処理用鋼板 | |
| CN105960480B (zh) | 合金化热镀锌钢板及其制造方法 | |
| US11702729B2 (en) | Method for producing a steel strip with improved bonding of metallic hot-dip coatings | |
| CN111433385A (zh) | 热浸涂钢基材 | |
| JP4264373B2 (ja) | めっき欠陥の少ない溶融Ａｌ系めっき鋼板の製造方法 | |
| JP6874163B2 (ja) | 溶融メッキされた中マンガン鋼及びその製造方法 | |
| WO2018079124A1 (ja) | 高強度溶融亜鉛めっき鋼板の製造方法 | |
| JP7480928B2 (ja) | 合金化溶融亜鉛めっき鋼板の製造方法 | |
| JP4882446B2 (ja) | 溶融亜鉛めっき鋼板および合金化溶融亜鉛めっき鋼板の製造方法 | |
| JP4306427B2 (ja) | 合金化溶融亜鉛めっき鋼板およびその製造方法 | |
| KR101736640B1 (ko) | 도금성 및 점용접성이 우수한 아연계 도금강판 및 그 제조방법 | |
| JP4816068B2 (ja) | めっき密着性に優れた溶融亜鉛めっき鋼板の製造方法 | |
| JP2005200711A (ja) | 合金化溶融亜鉛めっき鋼板の製造方法 | |
| JP4592000B2 (ja) | 加工性に優れた高強度合金化溶融亜鉛めっき鋼板の製造方法 | |
| JP4817749B2 (ja) | 加工性に優れた高強度合金化溶融亜鉛めっき鋼板の製造方法 | |
| JP6777045B2 (ja) | 高強度溶融亜鉛めっき鋼板の製造方法 | |
| WO2024224638A1 (ja) | 合金化溶融亜鉛めっき鋼板の製造方法 |
Legal Events
| Date | Code | Title | Description |
|---|---|---|---|
| A975 | Report on accelerated examination |
Free format text: JAPANESE INTERMEDIATE CODE: A971005 Effective date: 20150109 |
|
| A131 | Notification of reasons for refusal |
Free format text: JAPANESE INTERMEDIATE CODE: A131 Effective date: 20150123 |
|
| A601 | Written request for extension of time |
Free format text: JAPANESE INTERMEDIATE CODE: A601 Effective date: 20150423 |
|
| A521 | Request for written amendment filed |
Free format text: JAPANESE INTERMEDIATE CODE: A523 Effective date: 20150522 |
|
| TRDD | Decision of grant or rejection written | ||
| A01 | Written decision to grant a patent or to grant a registration (utility model) |
Free format text: JAPANESE INTERMEDIATE CODE: A01 Effective date: 20150803 |
|
| A61 | First payment of annual fees (during grant procedure) |
Free format text: JAPANESE INTERMEDIATE CODE: A61 Effective date: 20150817 |
|
| R150 | Certificate of patent or registration of utility model |
Ref document number: 5796142 Country of ref document: JP Free format text: JAPANESE INTERMEDIATE CODE: R150 |
|
| R250 | Receipt of annual fees |
Free format text: JAPANESE INTERMEDIATE CODE: R250 |
|
| R250 | Receipt of annual fees |
Free format text: JAPANESE INTERMEDIATE CODE: R250 |
|
| R250 | Receipt of annual fees |
Free format text: JAPANESE INTERMEDIATE CODE: R250 |
|
| LAPS | Cancellation because of no payment of annual fees |