CN104245995B - 扁钢产品的热浸镀层方法 - Google Patents

扁钢产品的热浸镀层方法 Download PDF

Info

Publication number
CN104245995B
CN104245995B CN201280069241.0A CN201280069241A CN104245995B CN 104245995 B CN104245995 B CN 104245995B CN 201280069241 A CN201280069241 A CN 201280069241A CN 104245995 B CN104245995 B CN 104245995B
Authority
CN
China
Prior art keywords
atmosphere
flat steel
steel product
dew point
volume
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
CN201280069241.0A
Other languages
English (en)
Chinese (zh)
Other versions
CN104245995A (zh
Inventor
马克·布卢梅瑙
克里斯托弗·古泽克
弗莱德·金德拉
鲁道夫·舍嫩贝格
汉斯-约阿希姆·克劳特希克
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
ThyssenKrupp Steel Europe AG
Outokumpu Nirosta GmbH
Original Assignee
ThyssenKrupp Steel Europe AG
Outokumpu Nirosta GmbH
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by ThyssenKrupp Steel Europe AG, Outokumpu Nirosta GmbH filed Critical ThyssenKrupp Steel Europe AG
Publication of CN104245995A publication Critical patent/CN104245995A/zh
Application granted granted Critical
Publication of CN104245995B publication Critical patent/CN104245995B/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Links

Classifications

    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
    • C23C2/02—Pretreatment of the material to be coated, e.g. for coating on selected surface areas
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B32—LAYERED PRODUCTS
    • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
    • B32B15/00—Layered products comprising a layer of metal
    • B32B15/01—Layered products comprising a layer of metal all layers being exclusively metallic
    • B32B15/012—Layered products comprising a layer of metal all layers being exclusively metallic one layer being formed of an iron alloy or steel, another layer being formed of aluminium or an aluminium alloy
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B32—LAYERED PRODUCTS
    • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
    • B32B15/00—Layered products comprising a layer of metal
    • B32B15/01—Layered products comprising a layer of metal all layers being exclusively metallic
    • B32B15/013—Layered products comprising a layer of metal all layers being exclusively metallic one layer being formed of an iron alloy or steel, another layer being formed of a metal other than iron or aluminium
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D8/00—Modifying the physical properties by deformation combined with, or followed by, heat treatment
    • C21D8/02—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips
    • C21D8/0221—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips characterised by the working steps
    • C21D8/0226—Hot rolling
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D8/00—Modifying the physical properties by deformation combined with, or followed by, heat treatment
    • C21D8/02—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips
    • C21D8/0221—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips characterised by the working steps
    • C21D8/0236—Cold rolling
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D9/00—Heat treatment, e.g. annealing, hardening, quenching or tempering, adapted for particular articles; Furnaces therefor
    • C21D9/46—Heat treatment, e.g. annealing, hardening, quenching or tempering, adapted for particular articles; Furnaces therefor for sheet metals
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C18/00—Alloys based on zinc
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C18/00—Alloys based on zinc
    • C22C18/04—Alloys based on zinc with aluminium as the next major constituent
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C21/00—Alloys based on aluminium
    • C22C21/02—Alloys based on aluminium with silicon as the next major constituent
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C21/00—Alloys based on aluminium
    • C22C21/10—Alloys based on aluminium with zinc as the next major constituent
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C30/00—Alloys containing less than 50% by weight of each constituent
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/001—Ferrous alloys, e.g. steel alloys containing N
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
    • C22C38/40—Ferrous alloys, e.g. steel alloys containing chromium with nickel
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
    • C22C38/40—Ferrous alloys, e.g. steel alloys containing chromium with nickel
    • C22C38/44—Ferrous alloys, e.g. steel alloys containing chromium with nickel with molybdenum or tungsten
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
    • C22C38/40—Ferrous alloys, e.g. steel alloys containing chromium with nickel
    • C22C38/58—Ferrous alloys, e.g. steel alloys containing chromium with nickel with more than 1.5% by weight of manganese
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
    • C23C2/003—Apparatus
    • C23C2/0038—Apparatus characterised by the pre-treatment chambers located immediately upstream of the bath or occurring locally before the dipping process
    • C23C2/004—Snouts
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
    • C23C2/02—Pretreatment of the material to be coated, e.g. for coating on selected surface areas
    • C23C2/022—Pretreatment of the material to be coated, e.g. for coating on selected surface areas by heating
    • C23C2/0222—Pretreatment of the material to be coated, e.g. for coating on selected surface areas by heating in a reactive atmosphere, e.g. oxidising or reducing atmosphere
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
    • C23C2/02—Pretreatment of the material to be coated, e.g. for coating on selected surface areas
    • C23C2/022—Pretreatment of the material to be coated, e.g. for coating on selected surface areas by heating
    • C23C2/0224—Two or more thermal pretreatments
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
    • C23C2/02—Pretreatment of the material to be coated, e.g. for coating on selected surface areas
    • C23C2/024—Pretreatment of the material to be coated, e.g. for coating on selected surface areas by cleaning or etching
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
    • C23C2/04—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor characterised by the coating material
    • C23C2/06—Zinc or cadmium or alloys based thereon
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
    • C23C2/34—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor characterised by the shape of the material to be treated
    • C23C2/36—Elongated material
    • C23C2/40—Plates; Strips

Landscapes

  • Chemical & Material Sciences (AREA)
  • Engineering & Computer Science (AREA)
  • Mechanical Engineering (AREA)
  • Organic Chemistry (AREA)
  • Metallurgy (AREA)
  • Materials Engineering (AREA)
  • Chemical Kinetics & Catalysis (AREA)
  • Physics & Mathematics (AREA)
  • Thermal Sciences (AREA)
  • Crystallography & Structural Chemistry (AREA)
  • Coating With Molten Metal (AREA)
  • Heat Treatment Of Sheet Steel (AREA)
  • Oil, Petroleum & Natural Gas (AREA)
CN201280069241.0A 2012-02-08 2012-12-13 扁钢产品的热浸镀层方法 Expired - Fee Related CN104245995B (zh)

Applications Claiming Priority (3)

Application Number Priority Date Filing Date Title
DE102012101018.8 2012-02-08
DE102012101018A DE102012101018B3 (de) 2012-02-08 2012-02-08 Verfahren zum Schmelztauchbeschichten eines Stahlflachprodukts
PCT/EP2012/075402 WO2013117273A1 (de) 2012-02-08 2012-12-13 Verfahren zum schmelztauchbeschichten eines stahlflachprodukts

Publications (2)

Publication Number Publication Date
CN104245995A CN104245995A (zh) 2014-12-24
CN104245995B true CN104245995B (zh) 2016-08-03

Family

ID=47504886

Family Applications (1)

Application Number Title Priority Date Filing Date
CN201280069241.0A Expired - Fee Related CN104245995B (zh) 2012-02-08 2012-12-13 扁钢产品的热浸镀层方法

Country Status (9)

Country Link
US (1) US9803270B2 (enExample)
EP (1) EP2812458B8 (enExample)
JP (1) JP5796142B2 (enExample)
KR (1) KR101994989B1 (enExample)
CN (1) CN104245995B (enExample)
DE (1) DE102012101018B3 (enExample)
ES (1) ES2593531T3 (enExample)
IN (1) IN2014MN01579A (enExample)
WO (1) WO2013117273A1 (enExample)

Families Citing this family (12)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
ES2851199T3 (es) * 2013-07-03 2021-09-03 Outokumpu Nirosta Gmbh Procedimiento para recubrir productos planos de acero con una capa protectora metálica
JP6131919B2 (ja) * 2014-07-07 2017-05-24 Ｊｆｅスチール株式会社 合金化溶融亜鉛めっき鋼板の製造方法
DE102014109943B3 (de) 2014-07-16 2015-11-05 Thyssenkrupp Ag Stahlprodukt mit einer Korrosionsschutzbeschichtung aus einer Aluminiumlegierung sowie Verfahren zu dessen Herstellung
EP3356572B1 (de) * 2015-09-30 2020-03-11 ThyssenKrupp Steel Europe AG Verfahren zur herstellung eines stahlflachprodukts mit einer zn-galvannealing-schutzbeschichtung
JP6237937B2 (ja) * 2016-03-11 2017-11-29 Ｊｆｅスチール株式会社 高強度溶融亜鉛めっき鋼板の製造方法
JP6323628B1 (ja) 2016-10-25 2018-05-16 Ｊｆｅスチール株式会社 高強度溶融亜鉛めっき鋼板の製造方法
DE102016222993A1 (de) * 2016-11-22 2018-05-24 Volkswagen Aktiengesellschaft Verfahren zur Herstellung eines beschichteten Stahlbauteils
DE102018100842B3 (de) * 2018-01-16 2019-05-09 Ebner Industrieofenbau Gmbh Durchlaufofen für Aluminiumbänder
CN112522591B (zh) * 2019-09-19 2022-03-18 宝山钢铁股份有限公司 一种薄带连铸生产高强高耐蚀钢的方法
WO2021224662A1 (en) * 2020-05-07 2021-11-11 Arcelormittal Annealing method of steel
CN113969336B (zh) * 2020-07-23 2023-03-28 宝山钢铁股份有限公司 一种热镀锌钢板的制造方法、钢板及车用构件
CN115351295B (zh) * 2022-08-26 2023-10-27 河北建筑工程学院 一种复合板制备工艺

Citations (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN1040828A (zh) * 1988-08-29 1990-03-28 阿姆科公司 热浸镀铝的铬合金钢
US20040033386A1 (en) * 2001-11-15 2004-02-19 Isg Technologies Inc. Coated steel alloy product
WO2005017214A1 (en) * 2003-08-19 2005-02-24 Nippon Steel Corporation Process of production and production system of high strength galvannealed steel sheet
CN101287854A (zh) * 2005-10-14 2008-10-15 新日本制铁株式会社 含Si钢板的连续退火热浸镀方法以及连续退火热浸镀装置

Family Cites Families (25)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPS60262950A (ja) 1984-06-08 1985-12-26 Nippon Steel Corp 耐熱性と耐食性にすぐれた溶融アルミニウムメツキ鋼板の製造法
JPS61147865A (ja) 1984-12-18 1986-07-05 Nisshin Steel Co Ltd 溶融アルミめつき鋼板およびその製造法
US5066549A (en) 1986-05-20 1991-11-19 Armco Inc. Hot dip aluminum coated chromium alloy steel
US4675214A (en) 1986-05-20 1987-06-23 Kilbane Farrell M Hot dip aluminum coated chromium alloy steel
US4883723A (en) 1986-05-20 1989-11-28 Armco Inc. Hot dip aluminum coated chromium alloy steel
AT392089B (de) 1988-09-14 1991-01-25 Andritz Ag Maschf Verfahren zum ein- und beidseitigen elektrolytischen verzinken von edelstahl
US5246563A (en) 1988-09-14 1993-09-21 Andritz-Patentverwaltungs-Gesellschaft M.B.H. Process for the electrolytic zinc coating of stainless steel
JPH02285057A (ja) * 1989-04-27 1990-11-22 Sumitomo Metal Ind Ltd 溶融亜鉛めっき用鋼板の連続焼鈍方法
JP2727529B2 (ja) 1989-09-27 1998-03-11 新日本製鐵株式会社 メッキ密着性に優れた高耐蝕性アルミメッキＣｒ含有鋼板の製造方法
FR2664617B1 (fr) 1990-07-16 1993-08-06 Lorraine Laminage Procede de revetement d'aluminium par trempe a chaud d'une bande d'acier et bande d'acier obtenue par ce procede.
JP2743228B2 (ja) 1992-05-11 1998-04-22 新日本製鐵株式会社 加工性とめっき密着性に優れた溶融アルミめっきＣｒ含有鋼板の製造方法
US5447754A (en) 1994-04-19 1995-09-05 Armco Inc. Aluminized steel alloys containing chromium and method for producing same
CA2336373C (en) * 1999-02-22 2007-02-27 Nippon Steel Corporation High strength galvanized steel plate excellent in adhesion of plated metal and formability in press working and high strength alloy galvanized steel plate and method for production thereof
JP2003253413A (ja) * 2002-03-06 2003-09-10 Nippon Steel Corp 高強度冷延鋼板とめっき鋼板の兼用製造設備および兼用製造方法
WO2004063410A1 (en) * 2003-01-15 2004-07-29 Nippon Steel Corporation High-strength hot-dip galvanized steel sheet and method for producing the same
RU2312162C2 (ru) 2003-04-10 2007-12-10 Ниппон Стил Корпорейшн Высокопрочный стальной лист с покрытием из расплавленного цинка и способ его изготовления
ES2350931T3 (es) 2003-07-29 2011-01-28 Voestalpine Stahl Gmbh Procedimiento para la fabricación de componentes templados de chapa de acero.
JP2006051543A (ja) 2004-07-15 2006-02-23 Nippon Steel Corp 冷延、熱延鋼板もしくはＡｌ系、Ｚｎ系めっき鋼板を使用した高強度自動車部材の熱間プレス方法および熱間プレス部品
DE102004059566B3 (de) 2004-12-09 2006-08-03 Thyssenkrupp Steel Ag Verfahren zum Schmelztauchbeschichten eines Bandes aus höherfestem Stahl
EP1693477A1 (de) 2005-02-22 2006-08-23 ThyssenKrupp Steel AG Beschichtetes Stahlblech oder -band
PL1857566T3 (pl) 2006-05-15 2017-10-31 Thyssenkrupp Steel Europe Ag Płaski wyrób stalowy z powłoką chroniącą przed korozją i sposób jego wytwarzania
EP2009128A1 (en) 2007-06-29 2008-12-31 ArcelorMittal France Galvanized or galvannealed silicon steel
JP2009035756A (ja) 2007-07-31 2009-02-19 Nisshin Steel Co Ltd 高温強度に優れた二輪車排ガス経路部材用Ａｌ系めっき鋼板および部材
EP2055799A1 (de) 2007-11-05 2009-05-06 ThyssenKrupp Steel AG Stahlflachprodukt mit einem vor Korrosion schützenden metallischen Überzug und Verfahren zum Erzeugen eines vor Korrosion schützenden metallischen Zn-Mg Überzugs auf einem Stahlflachprodukt
DE102010037254B4 (de) * 2010-08-31 2012-05-24 Thyssenkrupp Steel Europe Ag Verfahren zum Schmelztauchbeschichten eines Stahlflachprodukts

Patent Citations (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN1040828A (zh) * 1988-08-29 1990-03-28 阿姆科公司 热浸镀铝的铬合金钢
US20040033386A1 (en) * 2001-11-15 2004-02-19 Isg Technologies Inc. Coated steel alloy product
WO2005017214A1 (en) * 2003-08-19 2005-02-24 Nippon Steel Corporation Process of production and production system of high strength galvannealed steel sheet
CN101287854A (zh) * 2005-10-14 2008-10-15 新日本制铁株式会社 含Si钢板的连续退火热浸镀方法以及连续退火热浸镀装置

Also Published As

Publication number Publication date
KR101994989B1 (ko) 2019-07-02
IN2014MN01579A (enExample) 2015-05-15
CN104245995A (zh) 2014-12-24
US20150345002A1 (en) 2015-12-03
JP5796142B2 (ja) 2015-10-21
JP2015509556A (ja) 2015-03-30
EP2812458B8 (de) 2016-08-24
WO2013117273A1 (de) 2013-08-15
DE102012101018B3 (de) 2013-03-14
US9803270B2 (en) 2017-10-31
KR20140128416A (ko) 2014-11-05
EP2812458B1 (de) 2016-06-29
EP2812458A1 (de) 2014-12-17
ES2593531T3 (es) 2016-12-09

Similar Documents

Publication Publication Date Title
CN104245995B (zh) 扁钢产品的热浸镀层方法
EP4108793B1 (en) Method for producing high-strength hot dipped galvanized steel sheet
KR101940250B1 (ko) 용융 침지 코팅에 의하여 금속 보호 층이 제공된 판상 강 제품을 제조하는 방법
JP6025867B2 (ja) メッキ表面品質及びメッキ密着性に優れた高強度溶融亜鉛メッキ鋼板及びその製造方法
RU2736476C2 (ru) Горячеоцинкованная алюминизированная стальная полоса с полимерным покрытием, пределом текучести не менее 500 мпа и высокой величиной относительного удлинения и способ ее изготовления
CN100385019C (zh) 高强度镀锌钢板的生产方法和生产系统
CN101506403B (zh) 为含有6重量%至30重量%的Mn的热轧或冷轧钢带镀覆金属保护层的方法
CN103080363B (zh) 对扁钢制品进行热浸镀层的方法
CN105283573B (zh) 热冲压成形体及热冲压成形体的制造方法
CN105814229B (zh) 高强度合金化热镀锌钢板的制造方法
JP5513216B2 (ja) 合金化溶融亜鉛めっき鋼板の製造方法
JP5636683B2 (ja) 密着性に優れた高強度合金化溶融亜鉛めっき鋼板および製造方法
JP5799819B2 (ja) めっき濡れ性及び耐ピックアップ性に優れる溶融亜鉛めっき鋼板の製造方法
JP4918044B2 (ja) 高張力鋼ストリップを溶融浸漬コーティングする方法
CN108603263B (zh) 高屈服比型高强度镀锌钢板及其制造方法
CN106715726A (zh) 高强度熔融镀锌钢板的制造方法和制造设备
CN102325907A (zh) 钢板退火装置、含有该装置的制备镀覆钢板的设备，和使用所述装置制备镀覆钢板的方法
KR102635881B1 (ko) 금속 용융 도금 코팅의 개선된 접착을 갖는 강 스트립을 제조하는 방법
CN105026599B (zh) 高强度熔融镀锌钢板及其制造方法
WO2018214683A1 (zh) 一种热浸镀高锰钢及其制造方法
CN103814148B (zh) 涂装后耐腐蚀性优良的合金化热镀锌钢板
JP4264373B2 (ja) めっき欠陥の少ない溶融Ａｌ系めっき鋼板の製造方法
CN100580130C (zh) 合金化热浸镀锌钢板及其制造方法
CN112195416B (zh) 一种含铝高强钢及其制备方法、应用
JP5533730B2 (ja) 合金化溶融亜鉛めっき鋼板の製造方法

Legal Events

Date Code Title Description
C06 Publication
PB01 Publication
C10 Entry into substantive examination
SE01 Entry into force of request for substantive examination
C14 Grant of patent or utility model
GR01 Patent grant
CF01 Termination of patent right due to non-payment of annual fee

Granted publication date: 20160803

Termination date: 20211213

CF01 Termination of patent right due to non-payment of annual fee