JP5650933B2 - ジメチルエーテル製造用触媒およびその製造方法、並びにジメチルエーテルの製造方法 - Google Patents
ジメチルエーテル製造用触媒およびその製造方法、並びにジメチルエーテルの製造方法 Download PDFInfo
- Publication number
- JP5650933B2 JP5650933B2 JP2010124521A JP2010124521A JP5650933B2 JP 5650933 B2 JP5650933 B2 JP 5650933B2 JP 2010124521 A JP2010124521 A JP 2010124521A JP 2010124521 A JP2010124521 A JP 2010124521A JP 5650933 B2 JP5650933 B2 JP 5650933B2
- Authority
- JP
- Japan
- Prior art keywords
- catalyst
- mass
- dimethyl ether
- alumina
- terms
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Description
しかしながら、前述の工程を経ると、触媒製造時に発熱するという問題がある。また、廃液も発生するので、触媒を大量に製造するには問題があった。
(1)アルミナをAl2O3として80質量%以上含有し、さらにケイ素およびマグネシウムを含有することを特徴とするジメチルエーテル製造用触媒。
(2)ケイ素含有量は、Al2O3換算で100質量部のアルミナに対して、SiO2換算で0.5質量部以上である前記(1)記載のジメチルエーテル製造用触媒。
(3)マグネシウム含有量は、Al2O3換算で100質量部のアルミナに対して、Mg換算で0.01〜1.2質量部である前記(1)または(2)記載のジメチルエーテル製造用触媒。
(4)1100℃で2時間空気中に保持した後の重量減少率が、保持前の触媒重量に対して5質量%以下である前記(1)〜(3)のいずれかに記載のジメチルエーテル製造用触媒。
(5)アルミニウム源、ケイ素源およびマグネシウム源を混合して原料粉を得、原料粉を焼成することを特徴とする前記(1)〜(4)のいずれかに記載のジメチルエーテル製造用触媒の製造方法。
(6)原料粉の中心粒径が20μm以下である前記(5)記載のジメチルエーテル製造用触媒の製造方法。
(7)前記(1)〜(4)のいずれかに記載のジメチルエーテル製造用触媒の存在下にメタノールを脱水反応させることを特徴とするジメチルエーテルの製造方法。
本発明のジメチルエーテル製造用触媒(以下、「触媒」と言うことがある。)は、主成分としてアルミナを含有する。アルミナは、アルミニウムの酸化物であり、通常は化学式:Al2O3・nH2O〔式中、nは0≦n≦0.5を示す。〕で示されるものである。アルミナは、例えばχ,γ,η等の結晶相を有する活性アルミナである。アルミナは、χ,γ,η以外の結晶相として、例えばκ,δ,θ,ρ等の結晶相を含んでいてもよい。
触媒は、例えばアルミニウム源、ケイ素源およびマグネシウム源を混合して原料粉を得、原料粉を焼成する方法により製造することができる。この製造方法によれば、中和析出工程を経ることにより発生する発熱および廃液の発生を抑制することができるので、触媒を大量に製造することができる。
本発明のジメチルエーテルの製造方法は、本発明の触媒の存在下にメタノールを脱水反応させてジメチルエーテルを得る方法である。具体的には、メタノールを気化させたメタノールガスを、脱水反応温度で触媒と接触させる。
まず、触媒を粉砕し、炭酸ナトリウムおよびホウ酸を加えて1050℃で焼成した後、硝酸を加えてサンプル液を作製した。次いで、このサンプル液についてICP(Inductively Coupled Plasma)発光分析を実施し、ケイ素元素量およびマグネシウム元素量を求めた。次いで、当該触媒がAl2O3、MgおよびSiO2のみからなるものとして、ケイ素含有量については、Al2O3換算で100質量部のアルミナに対するSiO2の含有量を、マグネシウム含有量については、Al2O3換算で100質量部のアルミナに対するMgの含有量を、それぞれ算出した。
全自動BET比表面積測定装置((株)マウンテック製の「Macsorb Model−1201」)を用いて、1点法により測定した。
XRD(X線回折)測定により触媒の結晶相を確認した。具体的には、粉末X線回折装置((株)リガク製の「RINT2200HL」)を用いて、X線出力を40kV、30mAとし、X線源にCuKα線を用い、10°から80°まで0.02°/秒の速度で走査して測定した。
まず、アルミナ前駆体であるベーマイト水酸化アルミニウム(サソール社製の「Catapal C1」)を150℃で6時間乾燥させた。乾燥後のベーマイト水酸化アルミニウムの水分量は、9.0質量%であった。水分量は次のようにして測定した。まず、触媒5gを電気炉にて200℃の温度をかけながら2時間加熱した。次いで、加熱前後の触媒重量を式:(加熱後の触媒重量)/(加熱前の触媒重量)×100に当てはめ、水分量(質量%)を算出した。
まず、ベーマイト結晶水酸化アルミニウム(アルマティス社製の「HIQ−40」)を振動ミルにて中心粒径が7.5μmになるまで粉砕し、粉砕品を得た。この粉砕品を600℃で2時間焼成したところ、得られたアルミナの結晶形はγアルミナで、Na2O量は0.001質量%以下であった。
まず、比較例1と同様にして水酸化アルミニウム成形体を得た。次いで、得られた水酸化アルミニウム成形体122gに、シリカゾル液を充分に吸収させた。シリカゾル液は、シリカゾル(日産化学工業(株)製の「スノーテックスN」)5.0gと水25.2gとを混合して得た。
実施例1〜7および比較例1,2の各触媒(A1)〜(A7),(C1),(C2)について、メタノール反応率および維持率を評価した。各評価方法を以下に示すとともに、その結果を表2に併せて示す。
各触媒をそれぞれ使用してメタノールの脱水反応を行い、ジメチルエーテルを製造した。すなわち、固定床流通式の反応装置を用い、温度290℃、圧力1MPaGの条件で、メタノール液(和光純薬(株)製、特級)を気化させ、空間速度(SV)2000h-1で供給してメタノールの脱水反応を行い、ジメチルエーテルを連続製造した。
初期および7日間経過後のメタノール反応率を下記式(II)に当てはめ、維持率(%)を算出した。
Claims (6)
- アルミナをAl2O3として80質量%以上含有し、さらにケイ素およびマグネシウムを含有し、
1100℃で2時間空気中に保持した後の重量減少率が、保持前の触媒重量に対して5質量%以下であることを特徴とするジメチルエーテル製造用触媒。 - ケイ素含有量は、Al2O3換算で100質量部のアルミナに対して、SiO2換算で0.5質量部以上である請求項1記載のジメチルエーテル製造用触媒。
- マグネシウム含有量は、Al2O3換算で100質量部のアルミナに対して、Mg換算で0.01〜1.2質量部である請求項1または2記載のジメチルエーテル製造用触媒。
- アルミニウム源、ケイ素源およびマグネシウム源を混合して原料粉を得、原料粉を焼成することを特徴とする請求項1〜3のいずれかに記載のジメチルエーテル製造用触媒の製造方法。
- 原料粉の中心粒径が20μm以下である請求項4記載のジメチルエーテル製造用触媒の製造方法。
- 請求項1〜3のいずれかに記載のジメチルエーテル製造用触媒の存在下にメタノールを脱水反応させることを特徴とするジメチルエーテルの製造方法。