JP5423034B2 - この上に更に上塗り塗装を行うための一液型熱硬化性組成物及びそれを用いた鋼板接合構造体の被覆、塗装方法 - Google Patents
この上に更に上塗り塗装を行うための一液型熱硬化性組成物及びそれを用いた鋼板接合構造体の被覆、塗装方法 Download PDFInfo
- Publication number
- JP5423034B2 JP5423034B2 JP2009034923A JP2009034923A JP5423034B2 JP 5423034 B2 JP5423034 B2 JP 5423034B2 JP 2009034923 A JP2009034923 A JP 2009034923A JP 2009034923 A JP2009034923 A JP 2009034923A JP 5423034 B2 JP5423034 B2 JP 5423034B2
- Authority
- JP
- Japan
- Prior art keywords
- compound
- thermosetting composition
- coating
- steel plate
- group
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
例えば、ブロック化剤によりイソシアネート基をブロックしたウレタンプレポリマーと微粉体コーティングアミンを組み合わせて硬化反応を抑制する方法(特許文献1)、有機ポリイソシアネートとポリオールとの反応で得られる末端イソシアネート基ウレタンプレポリマーのイソシアネート基がオキシム等のブロック化剤でブロックされた化合物と芳香族アミン系化合物からなる接着性付与剤をアクリル共重合体に配合し接着性を改善する方法(特許文献2)等が提案されている。しかし、ウレタンプレポリマーを用いる被覆材は貯蔵安定性が十分ではなかったり接着性が不十分だったりする問題があり、また、高温焼付け時の膨れ(被覆材の発泡)による塗膜外観の不具合が生じたり、同じく高温焼付け時に軟化するという問題があり、その解決が求められている。
すなわち、本発明は、以下の(1)〜(8)に示されるものである。
硬化促進剤(C)が、オキサゾリジン環の加水分解を促進する開環触媒と、オキサゾリジン環の加水分解の結果生成する活性水素基とイソシアネート基との反応促進触媒とからなり、かつ、
イソシアネート基含有ウレタンプレポリマー(A)100質量部に対して、オキサゾリジン環を有する化合物(B)の使用量が5〜25質量部の割合であり、硬化促進剤(C)の使用量については、前記開環触媒が0.1〜2.0質量部の割合であり、前記反応促進触媒が0.005〜0.04質量部の割合であり、ポリウレア化合物を少なくとも含有する揺変性付与剤(D)の使用量が5〜110質量部の割合であること、
を特徴とする前記のこの上に更に上塗り塗装を行うための一液型熱硬化性組成物。
(2) 前記イソシアネート基含有ウレタンプレポリマー(A)が、アルコール成分とイソシアネート成分とを活性水素(基)に対してイソシアネート基過剰の条件で反応させて得られるものであり、かつ、該アルコール成分が、ポリオキシアルキレン系ポリオール又は該ポリオキシアルキレン系ポリオールと分子内にエチレン性不飽和結合を有する水酸基含有化合物との混合物である、前記のこの上に更に上塗り塗装を行うための一液型熱硬化性組成物。
(3) 前記ポリオキシアルキレン系ポリオールが、総不飽和度0.04meq/g以下かつ数平均分子量3,000〜10,000のポリオキシアルキレン系ポリオールであり、かつ、前記の分子内にエチレン性不飽和結合を有する水酸基含有化合物が、平均分子量1,000以下の分子内にエチレン性不飽和結合を有する水酸基含有化合物である、前記のこの上に更に上塗り塗装を行うための一液型熱硬化性組成物。
(4) 前記のオキサゾリジン環を有する化合物(B)が、ウレタン結合及びオキサゾリジン環を有する化合物である、前記それぞれのこの上に更に上塗り塗装を行うための一液型熱硬化性組成物。
(5) 前記硬化促進剤(C)が、鉄(III)アセチルアセトネートとp-トルエンスルホニルイソシアネートとからなる、前記それぞれのこの上に更に上塗り塗装を行うための一液型熱硬化性組成物。
(6) 前記ポリウレア化合物が、ポリイソシアネートとモノアミンとの反応生成物である、前記それぞれのこの上に更に上塗り塗装を行うための一液型熱硬化性組成物。
(7) 更に、耐候安定剤、充填剤、接着性付与剤、保存安定性改良剤、可塑剤、着色剤及び溶剤からなる群から選ばれる1種又は2種以上の添加剤を含有する、前記それぞれのこの上に更に上塗り塗装を行うための一液型熱硬化性組成物。
(8) 前記それぞれのこの上に更に上塗り塗装を行うための一液型熱硬化性組成物からなる被覆材を鋼板接合構造体の少なくとも鋼板接合部に塗布し、次いで該鋼板接合部を含む鋼板接合構造体の表面に塗料を塗装し、前記被覆材と前記塗料とを同時に焼き付け硬化させること、を特徴とする鋼板接合構造体の被覆、塗装方法。
本発明におけるイソシアネート基含有ウレタンプレポリマー(A)は、そのイソシアネート基がオキサゾリジン環を有する化合物(B)や湿気(水分)と反応し、尿素結合を形成して架橋、硬化するものであり、アルコール成分とイソシアネート成分とを活性水素(基)に対してイソシアネート基過剰の条件で反応させて得ることができる。
具体的には、アルコール成分とイソシアネート成分とを、原料合計のイソシアネート基/活性水素(基)の当量比が1.3〜3.0/1.0、更には1.6〜2.5/1.0となる範囲で同時或いは逐次に反応させて、好適に製造することができる。当量比が1.3/1.0を下回ると、得られるウレタンプレポリマーの粘度が上昇し一液型熱硬化性組成物の作業性が低下する傾向になり、また、架橋点が少なくなりすぎ、一液型熱硬化性組成物の硬化後の伸びや引張強度などが低下し、ゴム弾性物性や接着性が乏しいものとなる。当量比が3.0/1.0を超えると、オキサゾリジン環を有する化合物(B)の配合が多く必要となり経済的に好ましくなく、また硬化後のゴム弾性物性が硬いものとなり好ましくない。
開始剤としては、例えば、メタノール、エタノール、プロパノール、エチレングリコール、ジエチレングリコール、プロピレングリコール、ジプロピレングリコール、ネオペンチルグリコール、1,4−ブタンジオール、1,6−ヘキサンジオール、グリセリン、トリメチロールプロパン、ペンタエリスリトール、ジグリセリン等の低分子アルコール類、ソルビトール、シュークロース、グルコース、ラクトース、ソルビタン等の糖類系低分子アルコール類、ビスフェノールA、ビスフェノールF等の低分子フェノール類、エチレンジアミン、ブチレンジアミン等の低分子ポリアミン類、モノエタノールアミン、ジエタノールアミン等の低分子アミノアルコール類、アジピン酸、テレフタル酸等の低分子ポリカルボン酸類、これらの少なくとも1種にアルキレンオキシドを反応させて得られる低分子量のポリオキシアルキレンアルコールが挙げられる。
アルキレンオキシドとしては、例えば、エチレンオキシド、プロピレンオキシド、ブチレンオキシド、テトラヒドロフランなどが挙げられる。
すなわち、ポリオキシアルキレン系ポリオールは、具体的には、ポリオキシエチレンポリオール、ポリオキシプロピレンポリオール、ポリテトラメチレンエーテルポリオール、ポリ(オキシエチレン)−ポリ(オキシプロピレン)−ランダム或いはブロック共重合ポリオール、ポリ(オキシプロピレン)−ポリ(オキシブチレン)−ランダム或いはブロック共重合ポリオールなどを挙げることができ、また、これらの各種ポリオールと有機ポリイソシアネートとを、イソシアネート基に対し水酸基過剰で反応させて、分子末端を水酸基としたものも挙げられる。
ポリオキシアルキレン系ポリオールは、良好な作業性などの理由で、数平均分子量が1,000〜20,000、特に3,000〜10,000のものが好ましく、また、1分子当たり平均の水酸基の個数は2個以上、特に2〜3個が好ましく、水酸基はアルコール性水酸基が好ましい。このようにすることでイソシアネート基含有ウレタンプレポリマー(A)の粘度が低く、したがって一液型熱硬化性組成物としたときの粘度が低く作業性が良好な点と、加熱処理後の耐発泡性(膨れ)、耐軟化性が良好となり、硬化後のゴム弾性物性や接着性が高いものとすることができる。数平均分子量が1,000未満では貯蔵安定性に問題が生じ、また数平均分子量が20,000を超えると加熱硬化後の一液型熱硬化性組成物が軟化する傾向が生じ好ましくない。
更に、ポリオキシアルキレン系ポリオールは、複合金属シアン化錯体などの触媒を使用して得られる、総不飽和度が0.1meq/g以下、更に0.07meq/g以下、特に0.04meq/g以下のものが好ましく、分子量分布〔ゲルパーミエーションクロマトグラフィー(GPC)によるポリスチレン換算の重量平均分子量(Mw)と数平均分子量(Mn)との比=Mw/Mn〕が1.6以下、特に1.0〜1.3の狭いものが好ましい。
なお、本発明において、ポリオキシアルキレン系ポリオールとは、分子1モルの水酸基を除いた部分の50質量%以上、更に80質量%以上、特に好ましくは90質量%以上がポリオキシアルキレンで構成されていれば、残りの部分がエーテル、ウレタン、エステル、ポリカーボネート、ポリアミド、ポリアクリレート、ポリオレフィンなどで変性されていてもよいことを意味するが、本発明においては、水酸基を除いた分子の95質量%以上がポリオキシアルキレンからなるものが最も好ましい。
具体的には、PO、ECH(=エピクロルヒドリン)変性ビスフェノールAジメタクリレート(共栄社油脂社製、エポキシエステル3002A)、ECH変性ジエチレングリコールジメタクリレート(長瀬産業社製、テナコールDM−851)、グリセロールアクリレート/メタクリレート(日本油脂社製、ブレンマーGAM)、グリセロールメタクリレート(日本油脂社製、ブレンマーGLM)、ECH変性グリセロールトリアクリレート(長瀬産業社製、テナコールDA−314)、ECH変性1,6−ヘキサンジオールジアクリレート(日本化薬社製、カヤラッドR−167)、2−ヒドロキシエチルアクリレート(共栄社油脂社製、ライトエステルHOA)などを挙げることができる。
これらのうち、得られるイソシアネート基含有ウレタンプレポリマー(A)の粘度が低く、硬化後の物性が良好なため、これから得られる一液型熱硬化性組成物の粘度が低く作業性が良好な点と、加熱処理後の鋼板接合部、間隙部或いはエッジ部などへの接着性、上塗り塗料の密着性、ゴム弾性物性に優れている点で、ポリオキシアルキレン系トリオール又は該ポリオキシアルキレン系トリオールと分子内にエチレン性不飽和結合を有する水酸基含有化合物の混合物が好ましく、特にポリオキシプロピレントリオール又は該ポリオキシプロピレントリオールと分子内にエチレン性不飽和結合を有しかつ水酸基を2つ含有する化合物との混合物が好ましい。同様の理由から、分子内にエチレン性不飽和結合を有する水酸基含有化合物の平均分子量は1,000以下であることが好ましい。
ポリオキシアルキレン系トリオールと分子内にエチレン性不飽和結合を有する水酸基含有化合物の混合比率は、質量比=〔ポリオキシアルキレン系トリオール〕/〔分子内にエチレン性不飽和結合を有する水酸基含有化合物〕が100/0〜95/5以下であることが好ましい。分子内にエチレン性不飽和結合を有する水酸基含有化合物の割合が95/5を超えて多くなると、ウレタンプレポリマーがゲル化し易くなったり、一液型熱硬化性組成物の貯蔵安定性が低下する。
これらは単独で或いは2種以上を混合して使用できる。
また、これらの有機ポリイソシアネートを変性して得られる、ウレトジオン結合、イソシアヌレート結合、アロファネート結合、ビュレット結合、ウレトンイミン結合、カルボジイミド結合、ウレタン結合、ウレア結合などを1個以上含有する変性イソシアネート化合物も使用できる。
これらは単独で或いは2種以上を組み合わせて使用できる。
これらのうち、芳香脂肪族ジイソシアネート、脂肪族ジイソシアネート及び脂環族ジイソシアネートからなる群から選ばれる1種又は2種以上が好ましく、イソホロンジイソシアネートが更に好ましい。
また、更に公知の有機溶媒を用いることもできる。
オキサゾリジン環を有する化合物(B)は、第1級アミノ基や第2級アミノ基を有するアミノアルコールとアルデヒドとの脱水反応で得られる水酸基とオキサゾリジン環を有する化合物に、イソシアネート成分を反応させることにより得ることができる。このようにすることで、イソシアネート基含有ウレタンプレポリマー(A)と共存させておいても水分の無い状態では反応しない、貯蔵安定性に優れた一液型熱硬化性組成物を製造することができる。この場合、使用するイソシアネート成分としては、得られるオキサゾリジン環を有する化合物(B)の粘度が低い点で、脂肪族ポリイソシアネートが好ましく、特にヘキサメチレンジイソシアネートが好ましい。
アミノアルコールとしては、例えば、モノエタノールアミン、ジエタノールアミン、ジプロパノールアミン、N−(2−ヒドロキシエチル)−N−(2−ヒドロキシプロピル)アミンなどが挙げられる。
アルデヒドとしては、例えば、プロピオンアルデヒド、n−ブチルアルデヒド、イソブチルアルデヒド、n−ペンチルアルデヒド、2−メチルブチルアルデヒド、n−ヘキシルアルデヒド、2−メチルペンタナール、n−ヘプチルアルデヒド、n−オクチルアルデヒド、ベンズアルデヒド、クミンアルデヒドなどが挙げられる。
これらはいずれも単独で或いは2種以上を組み合わせて使用できる。
オキサゾリジン環を有する化合物(B)の製造方法は公知の方法を適用できるが、例えば、ジエタノールアミンとイソブチルアルデヒドからオキサゾリジン環を有する化合物を製造する方法は、反応温度60〜150℃で、溶媒としてキシレン、トルエン等のイソシアネート基に対して不活性である有機溶媒の存在下で、イソブチルアルデヒドを滴下して反応させる。滴下終了後、反応混合物を5〜10時間還流させ、生成する水を系外へ除去する。次に、反応生成物であるN−ヒドロキシエチルオキサゾリジンにイソシアネート成分を加えて混合し、60〜90℃で5〜10時間反応させて製造することができる。
オキサゾリジン環を有する化合物(B)の使用量は、イソシアネート基含有ウレタンプレポリマー(A)100質量部に対して、5〜25質量部である。又は、〔オキサゾリジン環の加水分解の結果生成する第2級アミノ基〕/〔イソシアネート基〕(モル比)=0.5/1.0〜2.0/1.0が好ましく、特に0.5/1.0〜1.8/1.0が好ましい。オキサゾリジン環を有する化合物(B)が5質量部未満又は0.5未満/1.0(モル比)では発泡の抑制が低く、25質量部又は2.0/1.0(モル比)を超えると一液型熱硬化性組成物の硬化物が軟化する傾向を示し、ゴム弾性物性が低下し、また、コストが上昇し経済的でない。
前記オキサゾリジン環の加水分解を促進する(開環)触媒は、その結果として、オキサゾリジン環の加水分解の結果生成する活性水素基と、イソシアネート基との反応が促進されるため、間接的にイソシアネート基含有ウレタンプレポリマー(A)の硬化をも促進させているといえる。
具体的には、有機カルボン酸、有機スルホン酸、有機リン酸、有機亜リン酸などの有機酸や、これらのエステル又は酸無水物、有機スルホニルイソシアネート、有機スルホン酸アミドなどが挙げられる。更に具体的に例示すれば、ギ酸、酢酸、プロピオン酸、カプロン酸、シュウ酸、コハク酸、アジピン酸、2−エチルヘキサン酸、オクチル酸、ラウリン酸、オレイン酸、ステアリン酸等の脂肪族カルボン酸、マレイン酸、アクリル酸等のα,β−不飽和カルボン酸、フタル酸、安息香酸、サリチル酸等の芳香族カルボン酸などやこれらの酸無水物が挙げられ、また、p−トルエンスルホン酸、p−トルエンスルホン酸無水物、JP−508(城北化学社製)、p−トルエンスルホニルイソシアネート、p−トルエンスルホン酸アミドなどが挙げられる。また、塩酸、リン酸などの無機酸及び三フッ化ホウ素、三フッ化ホウ素エチルエーテル、三塩化第二鉄、三塩化アルミニウム、オクチル酸第一錫、錫アセチルアセトネート、鉄アセチルアセトネートなどのルイス酸も挙げられる。これらは単独で或いは2種以上を組み合わせて使用できる。
また、オキサゾリジン環の加水分解の結果生成する活性水素基とイソシアネート基との反応を促進させる効果を有する触媒として、ジルコニウム、ビスマス、鉄、コバルト、ニッケルなどの各種金属の有機カルボン酸塩、キレート化合物などが好適に挙げられる。具体的には、ジルコニウムアセチルアセトネート、ビスマストリス(2−エチルヘキサノエート)、アセチルアセトンビスマス、鉄(II)アセチルアセトネート、鉄(III)アセチルアセトネート、アセチルアセトンコバルト、アセチルアセトンニッケルなどが挙げられる。これらは単独で或いは2種以上を組み合わせて使用できる。
これらのうち、オキサゾリジン環の加水分解を促進する開環触媒と、オキサゾリジン環の加水分解の結果生成する活性水素基とイソシアネート基との反応促進触媒との組合せが、一液型熱硬化性組成物の加熱処理時の硬化性、耐発泡性、貯蔵安定性が優れている点で好ましく、鉄(III)アセチルアセトネートとp−トルエンスルホニルイソシアネートとの組合せが特に好ましい。
硬化促進剤(C)の使用量は、イソシアネート基含有ウレタンプレポリマー(A)100質量部に対して、オキサゾリジン環の加水分解を促進する開環触媒は0.1〜2.0質量部であり、特に0.2〜1.0質量部が好ましく、オキサゾリジン環の加水分解の結果生成する活性水素基とイソシアネート基との反応促進触媒は0.005〜0.04質量部であり、特に0.01〜0.04質量部が好ましい。オキサゾリジン環の加水分解を促進する開環触媒が0.1質量部未満では硬化が遅れ、2.0質量部を超えるとイソシアネート基の反応を抑制し硬化が遅れる。また、オキサゾリジン環の加水分解の結果生じる活性水素基とイソシアネート基との反応促進触媒が0.005質量部未満では硬化が遅れ、0.04質量部を超えると一液型熱硬化性組成物の貯蔵安定性に悪影響を及ぼすため好ましくない。
ポリウレア化合物を少なくとも含有する揺変性付与剤(D)は、具体的には、少なくともポリウレア化合物を含有し、更に微粉状シリカ、脂肪酸で表面処理した炭酸カルシウム等の無機系揺変剤や、有機ベントナイト、変性ポリエステルポリオール、脂肪酸アマイド、塩化ビニル系重合体粒子などの有機系揺変剤を含有することができる。これらのうち、この上に更に上塗り塗装を行うための一液型熱硬化性組成物のタレがなく、加熱処理後の硬化物が鋼板へよく接着し、上塗り塗料の密着性が良好で、膨れ(発泡)などがなく外観に優れる点で、ポリウレア化合物単独が好ましい。
ポリウレア化合物を少なくとも含有する揺変性付与剤(D)の使用量は、イソシアネート基含有ウレタンプレポリマー(A)100質量部に対して5〜110質量部であり、特に15〜80質量部であることが好ましい。5質量部未満では、一液型熱硬化性組成物の揺変性が不十分でありタレや糸引きなどを起こし施工時に被覆部分の周囲を汚してしまったり、鋼板接合部などをビード状(かまぼこ状−断面が半月状)に被覆することができなくなる。また、110質量部を超えると一液型熱硬化性組成物が軟化する傾向を示し、揺変性付与剤(D)の分散媒などが分離することがあり好ましくない。
ヒンダートフェノール系酸化防止剤としては、ペンタエリストール−テトラキス[3−(3,5−ジ−tert−ブチル−4−ヒドロキシフェニル)プロピオネート]、オクタデシル−3−(3,5−ジ−tert−ブチル−4−ヒドロキシフェニル)プロピオネート]、N,N′−ヘキサン−1,6−ジイルビス[3−(3,5−ジ−tert−ブチル−4−ヒドロキシフェニルプロピオナミド)]、ベンゼンプロパン酸3,5−ビス(1,1−ジメチルエチル)−4−ヒドロキシC7−C9側鎖アルキルエステル、2,4−ジメチル−6−(1−メチルペンタデシル)フェノールなどが挙げられる。
塩化ビニル系重合体は塩化ビニルの単独重合体又は他のビニル系モノマーとの共重合体が好ましい。
カップリング剤としては、シラン系、アルミニウム系、ジルコアルミネート系などの各種カップリング剤及び/又はその部分加水分解縮合物が挙げられる。これらのうちシラン系カップリング剤及び/又はその部分加水分解縮合物が接着性に優れている点で好ましい。
シランカップリング剤としては、メチルトリメトキシシラン、ジメチルジメトキシシラン、トリメチルメトキシシラン、n−プロピルトリメトキシシラン、エチルトリメトキシシラン、ジエチルジエトキシシラン、n−ブチルトリメトキシシラン、n−ヘキシルトリエトキシシラン、n−オクチルトリメトキシシラン、フェニルトリメトキシシラン、ジフェニルジメトキシシラン、シクロヘキシルメチルジメトキシシランなどの炭化水素基結合アルコキシシラン類、ジメチルジイソプロペノキシシラン、メチルトリイソプロペノキシシランなどの炭化水素基結合イソプロペノキシシラン類、3−グリシドキシプロピルメチルジメトキシシラン、3−グリシドキシプロピルトリメトキシシラン、ビニルトリメトキシシラン、ビニルジメチルメトキシシラン、3−アミノプロピルトリメトキシシラン、N−(2−アミノエチル)−3−アミノプロピルメチルジメトキシシラン、3−メルカプトプロピルトリメトキシシラン、3−メルカプトプロピルメチルジメトキシシラン、3−グリシドキシプロピルメチルジイソプロペノキシシラン、3−グリシドキシプロピルトリエトキシシラン、N−(2−アミノエチル)−3−アミノプロピルトリメトキシシラン、3−アクリロキシプロピルトリメトキシシラン、3−メタクリロキシプロピルトリメトキシシラン、3−アクリロキシプロピルトリエトキシシラン、N−フェニル−3−アミノプロピルトリメトキシシラン等の官能基を有するアルコキシシラン類やイソプロペノキシシラン類などの分子量500以下、好ましくは400以下の低分子化合物及び/又はこれらシランカップリング剤の1種又は2種以上の部分加水分解縮合物で分子量200〜3,000の化合物が挙げられる。
溶剤としては、n−ヘキサンなどの脂肪族系溶剤、シクロヘキサンなどの脂環族系溶剤、トルエンやキシレンなどの芳香族系溶剤、石油系溶剤など従来公知の有機溶剤が挙げられ、これらは組成物の各成分に反応しないものであればどのようなものでも使用することができる。有機溶剤は安全性の点で、一液型熱硬化性組成物中に10質量%未満、更に5質量%未満、特に1質量%未満となるように使用するのが好ましく、最も好ましいのは0質量%と使用しないことである。
自動販売機、家電機器等の器箱等の被塗装物、例えば自動販売機の塗装方法は、一般に被覆材を鋼板接合構造体の少なくとも鋼板接合部(これ以外には例えば、間隙部或いはエッジ部、以下「等」という。)に塗布する被覆材塗布工程と、被覆材が塗布された部分を含む鋼板接合構造体の表面に塗料を塗装する塗装工程と、これらの塗布された被覆材と塗装された塗料を同時に加熱し焼き付け硬化させる焼付硬化工程とからなっている。鋼板接合構造体の表面に塗料を塗装する塗装工程では、下塗り塗装、上塗り塗装などに分けて塗装することがある。また、焼付硬化工程は一般的に加熱処理温度が120℃〜180℃であり、焼付時間は通常10〜40分である。塗料としては、例えば、ポリエステル樹脂塗料、エポキシ樹脂塗料、アクリル樹脂塗料等を使用することができる。また、使用される鋼板には通常防錆油が塗布されているが、本発明の一液型熱硬化性組成物を上記の加熱処理条件内で下記方法により施工することにより十分な接着性を得ることができる。
前記被覆材塗布工程について更に具体的に説明する。まず、予め本発明のこの上に更に上塗り塗装を行うための一液型熱硬化性組成物からなる被覆材の入ったカートリッジ容器(ノズル付き円筒容器)のノズルを内径が5〜10mmにカットする。次に、スポット溶接等で突合せ状や重ね合わせ状などに接合された鋼板接合部等に対して、カートリッジ容器が装填された被覆材打設用カートリッジガンを鋼板に対して30〜60度の角度に保持して、カットしたノズル先端を鋼板接合部等に接触させたままカートリッジから被覆材を押し出し、鋼板接合部等に沿って手前に引きながら被覆材がビード状(断面形状が高さ約5mm幅約10mmのカマボコ様)に形成されるように鋼板接合部等を被覆する。このようにすることで、被覆材が鋼板接合部等を覆うように被覆することができ、気密性、水密性、防錆性等を保持することができる。
本発明のこの上に更に上塗り塗装を行うための一液型熱硬化性組成物からなる被覆材は、自動販売機の鋼板接合構造体の鋼板接合部等に特に好適に使用することができるが、他に家電機器、自動車車体などの鋼板接合構造体の鋼板接合部等また自動車などのアンダーコート剤としても好適に使用することができる。
攪拌機、温度計、窒素シール管、還流冷却器及び加熱、冷却装置付き反応容器中に、ジエタノールアミン(分子量105)を435.0g入れた後、トルエンを183.3g加えた。この中に攪拌しながら更にイソブチルアルデヒド(分子量72.1)328.3gを加えた後、加温して110〜150℃で3時間脱水反応を続けて、エステル管により水74.5gを系外に除いた。次いで加熱減圧して、未反応のイソブチルアルデヒド及びトルエンを除去して、水酸基とオキサゾリジン環を有する化合物を得た。この水酸基とオキサゾリジン環を有する化合物658.9g中にヘキサメチレンジイソシアネート(分子量168)341.0gを加え、80℃で8時間加熱し、NCO基濃度が0.01質量%以下となった時点をウレタン化反応の終点(実測NCO基濃度0.0質量%)として、ウレタン結合とオキサゾリジン環を有する化合物O−1を合成した。得られたウレタン結合とオキサゾリジン環を有する化合物O−1は常温で透明な液体であった。
ジフェニルメタンジイソシアネート(分子量250.2)100.0gをジオクチルフタレート(DOP)300.0g中に溶解した溶液と、n−ブチルアミン(分子量73.1)55.0gをジオクチルフタレート(DOP)320.0g中に溶解した溶液を常温において反応させてポリウレア化合物のDOP分散ペーストを得た。この分散ペーストは、ポリウレア化合物20質量%とジオクチルフタレート(DOP)80質量%からなる。
塩化ビニル樹脂粒子(VESTOLIT社製、VESTOLIT E7031)120.0gをジオクチルフタレート(DOP)80.0g中に分散し、塩化ビニル樹脂粒子のDOP分散ペーストを得た。
攪拌機、温度計、窒素シール管及び加温・冷却装置の付いた反応容器に、窒素ガスを流しながら、石油系溶剤(エクソンモービル社製、エクソールD110)47.0gと、ポリオキシプロピレントリオール(旭硝子社製PML−S3008、数平均分子量8370、総不飽和度0.005meq/g)を800.0g(OH当量:0.2867)仕込み、攪拌しながらイソホロンジイソシアネート(テグサジャパン社製IPDI、分子量222.2)を78.7g(NCO当量:0.7084)(R値(NCO当量/OH当量)=2.47)仕込み、更に反応触媒としてオクチル酸錫(日東化成社製)0.1gを加え、加温して70〜80℃で4時間攪拌して、滴定によるイソシアネート基含有量が理論値1.85質量%以下となった時点で反応を終了し(実測値1.79質量%)、冷却して、イソシアネート基含有ウレタンプレポリマーPU−1を製造した。このPU−1は、粘度8,780mPa・s/25℃の常温で液体であった。
合成例4において、ポリオキシプロピレントリオール(旭硝子社製PML−S3008)800.0gに替えて、ポリオキシプロピレントリオール(三井化学社製MN−4000、数平均分子量4000、総不飽和度0.02meq/g)を800.0g(OH当量:0.6000)、さらにイソホロンジイソシアネート(テグサジャパン社製IPDI)を115.1g(NCO当量:1.036)(R値(NCO当量/OH当量)=1.73)とした以外は同様にして、滴定によるイソシアネート基含有量が理論値1.91質量%以下となった時点で反応を終了し(実測値1.88質量%)、冷却して、イソシアネート基含有ウレタンプレポリマーPU−2を製造した。このPU−2は、粘度8,100mPa・s/25℃の常温で液体であった。
攪拌機、温度計、窒素シール管及び加温・冷却装置の付いた反応容器に、窒素ガスを流しながら、石油系溶剤(エクソンモービル社製、エクソールD110)47.0gと、ポリオキシプロピレントリオール(旭硝子社製PML−S3008)790.0g(OH当量:0.2832)と、ECH変性1,6−ヘキサンジオールジアクリレート(日本化薬社製、カヤラッドR167、平均分子量374)10.0g(OH当量:0.0535)を仕込み、攪拌しながらイソホロンジイソシアネート(テグサジャパン社製IPDI)を85.8g(NCO当量:0.7723)(R値(NCO当量/OH当量)=2.29)仕込み、更に反応触媒としてオクチル酸錫(日東化成社製)0.1gを加え、加温して70〜80℃で4時間攪拌して、滴定によるイソシアネート基含有量が理論値1.87質量%以下となった時点で反応を終了し(実測値1.85質量%)、冷却して、イソシアネート基含有ウレタンプレポリマーPU−3を製造した。このPU−3は、粘度8,500mPa・s/25℃、常温で液体であった。
合成例6において、ポリオキシプロピレントリオール(旭硝子社製PML−S3008)800.0gに替えて、ポリオキシプロピレントリオール(三井化学社製MN−4000)を780.0g(OH当量:0.5850)、ECH変性1,6−ヘキサンジオールジアクリレート(日本化薬社製、カヤラッドR167)を20.0g(OH当量:0.1070)、イソホロンジイソシアネートを124.9g(NCO当量=1.124)(R値(NCO当量/OH当量)=1.63)とした以外は同様にして、滴定によるイソシアネート基含有量が理論値1.88質量%以下となった時点で反応を終了し(実測値1.83質量%)、冷却して、イソシアネート基含有ウレタンプレポリマーPU−4を製造した。このPU−4は、粘度9,000mPa・s/25℃の常温で液体であった。
加熱、冷却装置付き及び窒素シール管付き混練容器に、窒素気流下で、合成例4で得たイソシアネート基含有ウレタンプレポリマーPU−1 100.0g、予め90〜100℃の乾燥器中で乾燥して含有水分0.05質量%以下にした重質炭酸カルシウム108.0gを仕込み、内容物が均一になるまで攪拌、混合した。次に、ヒンダートフェノール系酸化防止剤(チバスペシャリティケミカルズ社製、イルガノックス1010)1.4g、ヒンダートアミン系酸化防止剤(三共社製、サノールLS−292)1.4g、合成例1で得たウレタン結合とオキサゾリジン環を有する化合物O−1 6.2gを仕込み、内容物が均一になるまで攪拌、混合した。次いで、合成例2で得たポリウレア化合物のDOP分散ペースト105.6g、鉄(III)アセチルアセトネート0.02g、p−トルエンスルホニルイソシアネート0.5gを仕込み、内容物が均一になるまで攪拌、混合し、減圧脱泡し、容器に充填密封して、この上に更に上塗り塗装を行うための一液型熱硬化性組成物を調製した。
実施例1において、ウレタン結合とオキサゾリジン環を有する化合物O−1を10.2gとした以外は同様にして、この上に更に上塗り塗装を行うための一液型熱硬化性組成物を調製した。
実施例1において、ウレタン結合とオキサゾリジン環を有する化合物O−1を16.4gとした以外は同様にして、この上に更に上塗り塗装を行うための一液型熱硬化性組成物を調製した。
実施例1において、ウレタン結合とオキサゾリジン環を有する化合物O−1を8.2gとした以外は同様にして、この上に更に上塗り塗装を行うための一液型熱硬化性組成物を調製した。
実施例1において、ウレタン結合とオキサゾリジン環を有する化合物O−1を8.2g、鉄(III)アセチルアセトネートを0.04gとした以外は同様にして、この上に更に上塗り塗装を行うための一液型熱硬化性組成物を調製した。
実施例1において、イソシアネート基含有ウレタンプレポリマーPU−1を100.0gの替わりに合成例5で得たイソシアネート基含有ウレタンプレポリマーPU−2を100.0g、ウレタン結合とオキサゾリジン環を有する化合物O−1を10.2gとした以外は同様にして、この上に更に上塗り塗装を行うための一液型熱硬化性組成物を調製した。
実施例1において、イソシアネート基含有ウレタンプレポリマーPU−1を100.0gの替わりに合成例6で得たイソシアネート基含有ウレタンプレポリマーPU−3を100.0g、ウレタン結合とオキサゾリジン環を有する化合物O−1を10.2gとした以外は同様にして、この上に更に上塗り塗装を行うための一液型熱硬化性組成物を調製した。
実施例1において、イソシアネート基含有ウレタンプレポリマーPU−1を100.0gの替わりに合成例7で得たイソシアネート基含有ウレタンプレポリマーPU−4を100.0g、ウレタン結合とオキサゾリジン環を有する化合物O−1を10.2gとした以外は同様にして、この上に更に上塗り塗装を行うための一液型熱硬化性組成物を調製した。
実施例1において、更に石油系溶剤(エクソールD110)36.2g、可塑剤ジオクチルフタレート(DOP)16.1g、塩化ビニル樹脂粒子(VESTOLIT社製、VESTOLIT E7031)48.3gを加え、ウレタン結合とオキサゾリジン環を有する化合物O−1を8.6gとした以外は同様にして、この上に更に上塗り塗装を行うための一液型熱硬化性組成物を調製した。
実施例1において、ウレタン結合とオキサゾリジン環を有する化合物O−1を用いない以外は同様にして、この上に更に上塗り塗装を行うための一液型熱硬化性組成物を調製した。
実施例1において、更に石油系溶剤20.1g、ポリウレア化合物のDOP分散ペースト105.6gの替わりに合成例3で得た塩化ビニル樹脂粒子のDOP分散ペーストを200.0g、ウレタン結合とオキサゾリジン環を有する化合物O−1を8.2gとした以外は同様にして、この上に更に上塗り塗装を行うための一液型熱硬化性組成物を調製した。
実施例1において、鉄(III)アセチルアセトネート、p−トルエンスルホニルイソシアネートを使用しない以外は同様にして、この上に更に上塗り塗装を行うための一液型熱硬化性組成物を調製した。
前記実施例1〜9、比較例1〜3と比較例4(一液型熱硬化性組成物の原料組成は表2に表示)として1成分形湿気硬化性ウレタン系シール材(オート化学社製)を用いて以下の各性能試験を行った。
〔作業性〕
JIS A1439−1997、2002改正「建築用シーリング材の試験方法」4.14試験用カートリッジによる押出し試験に準拠し23℃で測定した。
押出すのに要した時間(秒)が10秒以内を○、10秒を超えた場合を×と評価した。
〔タレ性(チクソ性)〕
製造後、製造後の焼き付け後、50℃、10日間保管後、50℃、10日間保管後の焼き付け後のそれぞれにおいて、TI=vis(25℃・10rpm)/vis(25℃・100rpm)≧4.0を○、TI<4.0を×と評価した。
〔タックフリータイム〕
JIS A1439−1997、2002改正「建築用シーリング材の試験方法」4.19タックフリー試験に準拠し測定した。
30分以上120分以内を○(可)、前記以外を×(不可)と評価した。
〔耐発泡性〕
亜鉛鋼板の表面に一液型熱硬化性組成物をおおよそ幅5mm×頂点の高さ5mm×長さ100mmのビード状に塗布し、次に、室温養生30分→上塗り塗装→焼付け170℃、30分の操作を行なった。続いて、ビード状の一液型熱硬化性組成物を目視により観察した。
フクレが認められないか又は極めて少なく、また、分離(液状物のブリード)のないものを○、フクレが多数認められたり分離(液状物のブリード)が認められるものを×と評価した。
〔硬度〕
JIS K6253−1997「加硫ゴム及び熱可塑性ゴムの硬さ試験方法」5.デュロメーター硬さ試験5.2測定範囲(2)タイプAデュロメーターに準拠し測定した。
45以上を○、45未満を×と評価した。
製造後;製造後23℃、50%相対湿度の標準状態で7日間養生して測定。
50℃、10日保存後;製造後50℃、10日保存後、23℃、50%相対湿度の標準
状態で7日間養生して測定。
製造後熱処理;製造後170℃、30分間熱処理し、23℃、50%相対湿度の標準状
態で冷却し測定。
50℃、10日保存後熱処理;製造後50℃、10日保存後、170℃、30分間熱処
理し、23℃、50%相対湿度の標準状態で冷却し測定
。
〔貯蔵安定性〕
50℃、10日間保管後の粘度(100rpm)/製造後粘度(100rpm)≦1.5を○、1.5を超えたものを×と評価した。
〔接着強さ〕
亜鉛鋼板を用いてピールテストを行なった。亜鉛鋼板の表面に一液型熱硬化性組成物をおおよそ幅10mm×頂点の高さ10mm×長さ50mmのビード状に塗布し、次に、室温養生30分→上塗り塗装→焼付け170℃、30分の操作を行なった。次に、ビード状硬化物端部と鋼板の界面にカッターで傷を入れ、手で180度折り返して引っ張り試験した。
一液型熱硬化性組成物の凝集破壊となったものを○、一液型熱硬化性組成物が亜鉛鋼板の表面から剥離したものを×と評価した。
〔上塗り塗装の密着性〕
亜鉛鋼板を用いてピールテストを行なった。亜鉛鋼板の表面に一液型熱硬化性組成物をおおよそ幅10mm×頂点の高さ10mm×長さ50mmのビード状に塗布し、室温養生30分後アクリル系塗料(日本ペイント社製、スーパーラック100)を一液型熱硬化性組成物上に塗布した。次に、室温養生30分→上塗り塗装→焼付け170℃、30分の操作を行なった。次に、塗膜を爪でかきとり、容易に塗膜が剥離するか否かを試験した。
塗膜の剥離がないか僅かに見られる場合を○、塗膜が容易に剥離する場合を×と評価した。
実施例1〜9及び比較例1〜4の原料組成及びその性能などをまとめて表1及び2に示す。
本発明に係るこの上に更に上塗り塗装を行なうための一液型熱硬化性組成物を鋼板接合構造体(筐体)に使用した場合の例として自動販売機外箱の製造について、図面を参照して説明する。
自動販売機製造の概略は、はじめに自動販売機外箱のうち扉部分を除いた鋼板接合構造体を組み立て、続いて扉部分を組み立て、それぞれ別々に塗装し、その後、内箱、自動販売機としての各種内装機器を取りつけ、扉を取りつけて完成する。自動販売機外箱のうち扉部分を除いた鋼板接合構造体の組み立てについて以下に詳しく説明するが、扉部分も同様に組み立てられる。
扉2部分を除いた自動販売機外箱(鋼板接合構造体−筐体)1は複数の亜鉛鋼板を組み合わせることによって構成され、図1は自動販売機の斜視図、図2は図1の自動販売機外箱(鋼板接合構造体−筐体)の分解斜視図、図3は(実施例1のこの上に更に上塗り塗装を行なうための一液型熱硬化性組成物を塗布する)図2の自動販売機外箱の各部材の接合部を示す部分図である。
自動販売機外箱の組み立ては、はじめに亜鉛鋼板をプレス加工により打ち抜き、曲げ等の板金加工により製作したものを各部の組み立て用部材として使用した。まず、側板部材3に背板部材4を組み合わせ、治具により固定し(図示せず)、スポット溶接により亜鉛鋼板間を溶着し接合した。この場合、スポット溶接は20〜100mm間隔を基本に接合が行われる。次に、側板部材3と背板部材4の接合体に天板部材5を同様に固定し、スポット溶接により亜鉛鋼板間を溶着し接合した。以下、天板補強板部材(図示せず)、外箱底部部材6、側面補強板部材(図示せず)、基台部材7を同様に固定し、スポット溶接により亜鉛鋼板間を溶着し接合して自動販売機外箱を組み立てた。
続いて、予め実施例1において調製したこの上に更に上塗り塗装をするための一液型熱硬化性組成物の入ったカートリッジ容器(ノズル付き円筒容器)のノズルを内径が5〜10mmにカットした。次に、カートリッジ容器が装填された被覆材打設用カートリッジガンを鋼板接合部8に対して30〜60度の角度に保持して、カットしたノズル先端を鋼板接合部8等に接触させ鋼板接合部8等に沿って手前に引きながら、カートリッジから前記一液型熱硬化性組成物を押し出し、前記一液型熱硬化性組成物がビード状(断面形状が高さ約5mm幅約10mmのカマボコ様)に形成されるように鋼板接合部8に塗布して被覆した。続いて、ビード状の被覆部をヘラ押さえして平らにし、厚みを約2mmにした。
続いて、自動販売機外箱(鋼板接合構造体−筐体)の全外表面にアクリル樹脂系塗料を用いて下塗り工程と上塗り工程の2回塗装し、それぞれ150〜170℃の温度、15〜20分間で焼き付け処理を行ない、自動販売機外箱(鋼板接合構造体−筐体)を製作した。
〔鋼板接合構造体の被覆、塗装の評価〕
扉部分を除いた自動販売機外箱(鋼板接合構造体−筐体)外面接合部に対して、前記一液型熱硬化性組成物を被覆し2回の焼付塗装を実施した後の目視による評価は、膨れ、キレツはなく良好な外観であった。指蝕により上塗り塗料の軟化の有無を調べたところ、軟化することなく良好な塗膜を形成していた。また、被覆部の一部にカッターで切れ込みを入れ指で摘み180°に折り返して引き剥がそうとしたが、引き剥がすことはできず良好な接着性を示した。また、鋼板接合部を被覆する際の作業性についても、前記一液型熱硬化性組成物は良好であった。
2 扉
3 側板部材
4 背板部材
5 天板部材
6 外箱底部部材
7 基台部材
8 鋼板接合部
Claims (8)
- イソシアネート基含有ウレタンプレポリマー(A)と、オキサゾリジン環を有する化合物(B)と、硬化促進剤(C)と、ポリウレア化合物を少なくとも含有する揺変性付与剤(D)とを含有する、この上に更に上塗り塗装を行うための一液型熱硬化性組成物であって、
硬化促進剤(C)が、オキサゾリジン環の加水分解を促進する開環触媒と、オキサゾリジン環の加水分解の結果生成する活性水素基とイソシアネート基との反応促進触媒とからなり、かつ、
イソシアネート基含有ウレタンプレポリマー(A)100質量部に対して、オキサゾリジン環を有する化合物(B)の使用量が5〜25質量部の割合であり、硬化促進剤(C)の使用量については、前記開環触媒が0.1〜2.0質量部の割合であり、前記反応促進触媒が0.005〜0.04質量部の割合であり、ポリウレア化合物を少なくとも含有する揺変性付与剤(D)の使用量が5〜110質量部の割合であること、
を特徴とする前記のこの上に更に上塗り塗装を行うための一液型熱硬化性組成物。 - 前記イソシアネート基含有ウレタンプレポリマー(A)が、アルコール成分とイソシアネート成分とを活性水素(基)に対してイソシアネート基過剰の条件で反応させて得られるものであり、かつ、該アルコール成分が、ポリオキシアルキレン系ポリオール又は該ポリオキシアルキレン系ポリオールと分子内にエチレン性不飽和結合を有する水酸基含有化合物との混合物である、請求項1に記載のこの上に更に上塗り塗装を行うための一液型熱硬化性組成物。
- 前記ポリオキシアルキレン系ポリオールが、総不飽和度0.04meq/g以下かつ数平均分子量3,000〜10,000のポリオキシアルキレン系ポリオールであり、かつ、前記の分子内にエチレン性不飽和結合を有する水酸基含有化合物が、平均分子量1,000以下の分子内にエチレン性不飽和結合を有する水酸基含有化合物である、請求項2に記載のこの上に更に上塗り塗装を行うための一液型熱硬化性組成物。
- 前記のオキサゾリジン環を有する化合物(B)が、ウレタン結合及びオキサゾリジン環を有する化合物である、請求項1〜3のいずれか一項に記載のこの上に更に上塗り塗装を行うための一液型熱硬化性組成物。
- 前記硬化促進剤(C)が、鉄(III)アセチルアセトネートとp-トルエンスルホニルイソシアネートとからなる、請求項1〜4のいずれか一項に記載のこの上に更に上塗り塗装を行うための一液型熱硬化性組成物。
- 前記ポリウレア化合物が、ポリイソシアネートとモノアミンとの反応生成物である、請求項1〜5のいずれか一項に記載のこの上に更に上塗り塗装を行うための一液型熱硬化性組成物。
- 更に、耐候安定剤、充填剤、接着性付与剤、保存安定性改良剤、可塑剤、着色剤及び溶剤からなる群から選ばれる1種又は2種以上の添加剤を含有する、請求項1〜6のいずれか一項に記載のこの上に更に上塗り塗装を行うための一液型熱硬化性組成物。
- 請求項1〜7のいずれか一項に記載のこの上に更に上塗り塗装を行うための一液型熱硬化性組成物からなる被覆材を鋼板接合構造体の少なくとも鋼板接合部に塗布し、次いで該鋼板接合部を含む鋼板接合構造体の表面に塗料を塗装し、前記被覆材と前記塗料とを同時に焼き付け硬化させること、を特徴とする鋼板接合構造体の被覆、塗装方法。