JP5142055B2 - 透明不燃性シートからなる防煙垂壁 - Google Patents
透明不燃性シートからなる防煙垂壁 Download PDFInfo
- Publication number
- JP5142055B2 JP5142055B2 JP2010260764A JP2010260764A JP5142055B2 JP 5142055 B2 JP5142055 B2 JP 5142055B2 JP 2010260764 A JP2010260764 A JP 2010260764A JP 2010260764 A JP2010260764 A JP 2010260764A JP 5142055 B2 JP5142055 B2 JP 5142055B2
- Authority
- JP
- Japan
- Prior art keywords
- glass fiber
- fiber fabric
- film
- transparent
- glass
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Lifetime
Description
なお、後述の建築基準法の評価法に基づく発熱性試験において、変形、熔融、亀裂などの損傷を抑え、不燃性をさらに向上させ、不燃性の認定に合格する水準にするために、本発明の透明不燃性シートは、ガラス繊維織物20が30〜70重量%であり、一対の硬化樹脂層32、34が70〜30重量%であることが好ましい。
Td:拡散透過率(%)
Tt:全光線透過率(%)
実施例1〜3は、同一のガラス繊維織物及び同一の熱硬化性樹脂を用い、熱硬化性樹脂の量を変化させた。
実施例1〜3と、同一のガラス繊維織物を用い、エポキシ樹脂を含浸させ、次いで硬化させた。
実施例1〜3と同様の方法及び同様のビニルエステル樹脂により、透明不燃性シートを得た。ただし、実施例4は、ガラス繊維織物の種類及びビニルエステルの量が実施例1〜3と異なる。
実施例5
輻射電気ヒ−タ−から実施例1〜4の何れか又は比較例1で得られた透明不燃性シートの表面に50kW/m2の輻射熱を照射し、加熱開始後20分間の総発熱量を測定した。また、加熱開始後20分間の間に、200kW/m2を超えた発熱時間を測定した。
全光線透過率は、JIS K 7105の「プラスチックの光学的特性試験方法」(Testing Methods forOptical Properties of plastics)、「5.5 光線透過率及び全光線反射率」に従った。具体的には、積分球式測定装置を用いて全光線透過量を測定し、全光線透過率を求めた。
透明不燃性シートのヘーズの測定方法は、JIS K 7105の「プラスチックの光学的特性試験方法」(Testing Methods for Optical Properties of Plastics)、「6.4ヘーズ」に従った。具体的には、積分球式測定装置を用いて拡散透過率及び全光線透過率を測定し、その比によって表した。
JIS規格L1096「一般織物試験方法」曲げ反発性A法(ガーレ法)に準じて測定した。
目視でガラス繊維織物が認められるか否かで判定した。
遮煙スクリーンは、例えば、エレベーターのドアの外側の上部に、丸めた状態で収納されている。そして、火災等の非常時に、遮煙スクリーンがエレベーターのドアの前に降下し、エレベーター中に煙が侵入するのを防止ないし低減する。
20 ガラス繊維織物
22 経糸
24 緯糸
28 間隔
32 硬化樹脂層
34 硬化樹脂層
42 第1フィルム
44、44a、44b、47 48 未硬化の樹脂組成物
46 第2フィルム
50 床
52 天井
54 壁
58 防煙垂壁
59 遮煙スクリーン
59a 格納箱
60 ガラス繊維織物ロール
62 ガラス繊維
70 第1フィルムロール
72 第1フィルム
74 未硬化樹脂組成物
76、78 樹脂溜り
80 第2フィルムロール
82 第2フィルム
88 ドクターブレード
90、92、94、96 ローラー
98 加熱硬化ゾーン
100 透明不燃性シート
Claims (4)
- 建築物の天井に垂下して取り付けられた、透明不燃性シートからなる防煙垂壁であって、前記透明不燃性シートが、
少なくとも1枚のガラス繊維織物と、
前記ガラス繊維織物を挟む一対の硬化樹脂層と、
を含む透明不燃性シートであって、
前記ガラス繊維織物が30〜70重量%であり、前記一対の硬化樹脂層が70〜30重量%であり、
前記透明不燃性シート1m2当たり、前記一対の硬化樹脂層の重量が15〜500gの範囲であり、
前記ガラス繊維織物中のガラス繊維を構成するガラス組成物と前記一対の硬化樹脂層を構成する樹脂組成物との屈折率の差が0.02以下であり、
前記ガラス繊維織物中のガラス繊維を構成するガラス組成物と前記一対の硬化樹脂層を構成する樹脂組成物とのアッベ数の差が30以下であり、
全光線透過率が80%以上であり、かつ、ヘーズが20%以下であり、
輻射電気ヒーターから透明不燃性シートの表面に50kW/m2の輻射熱を照射する発熱性試験において、加熱開始後20分間の総発熱量が8MJ/m2以下であり、且つ加熱開始後20分間、最高発熱速度が10秒以上継続して200kW/m2を超えない、
透明不燃性シートである、防煙垂壁。 - 前記ガラス繊維織物中の隣接する経糸の間の隙間が0.5mm以下であり、又は、前記ガラス繊維織物中の隣接する緯糸の間の隙間が0.5mm以下である請求項1に記載の防煙垂壁。
- 前記1枚のガラス繊維織物の重量が、20〜150g/m2である請求項1または2に記載の防煙垂壁。
- 前記ガラス繊維織物中のガラス繊維の番手が、5tex〜70texである請求項1〜3のいずれかに記載の防煙垂壁。