JP4953891B2 - 黒色のポリプロピレン系樹脂予備発泡粒子 - Google Patents
黒色のポリプロピレン系樹脂予備発泡粒子 Download PDFInfo
- Publication number
- JP4953891B2 JP4953891B2 JP2007101339A JP2007101339A JP4953891B2 JP 4953891 B2 JP4953891 B2 JP 4953891B2 JP 2007101339 A JP2007101339 A JP 2007101339A JP 2007101339 A JP2007101339 A JP 2007101339A JP 4953891 B2 JP4953891 B2 JP 4953891B2
- Authority
- JP
- Japan
- Prior art keywords
- polypropylene resin
- weight
- parts
- particles
- resin
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
アルキルジエタノールアミド、アルキルジエタノールアミン、ヒドロキシアルキルエタノールアミン、脂肪酸モノグリセライド、脂肪酸ジグリセライドなどのノニオン系界面活性剤からなる帯電防止剤;
IRGANOX(登録商標)1010(チバ スペシャルティ ケミカルズ)、IRGANOX(登録商標)1076(チバ スペシャルティ ケミカルズ)、IRGANOX(登録商標)1330(チバ スペシャルティ ケミカルズ)、IRGANOX(登録商標)1425WL(チバ スペシャルティ ケミカルズ)、IRGANOX(登録商標)3114(チバ スペシャルティ ケミカルズ)等のヒンダードフェノール系酸化防止剤;
IRGAFOS(登録商標)168(チバ スペシャルティ ケミカルズ)、IRGAFOS(登録商標)P−EPQ(チバ スペシャルティ ケミカルズ)、IRGAFOS(登録商標)126(チバ スペシャルティ ケミカルズ)等のリン系加工安定剤;
ラクトン系加工安定剤;
ヒドロキシルアミン系加工安定剤;
IRGANOX(登録商標)MD1024(イルガノックス、チバ スペシャルティ ケミカルズ)等の金属不活性剤;
TINUVIN(チヌビン、登録商標)326(チバ スペシャルティ ケミカルズ)、TINUVIN(登録商標)327チバ スペシャルティ ケミカルズ)等のベンゾトリアゾール系紫外線吸収剤;
TINUVIN(チヌビン、登録商標)120(チバ スペシャルティ ケミカルズ登録商標)等のベンゾエート系光安定剤;
CHIMASSORB(登録商標)119(チバ スペシャルティ ケミカルズ)、CHIMASSORB(登録商標)944(チバ スペシャルティ ケミカルズ)、TINUVIN(登録商標)622(チバ スペシャルティ ケミカルズ)、TINUVIN(登録商標)770(チバ スペシャルティ ケミカルズ)等のヒンダードアミン系光安定剤;
ハロゲン系難燃剤および三酸化アンチモン等の難燃助剤;
非ハロゲン系難燃剤;
ハイドロタルサイト、ステアリン酸カルシウム等の酸中和剤;
IRGASTAB(登録商標)NA11(チバ スペシャルティ ケミカルズ)等の結晶核剤;
メラミン等のトリアジン系化合物、
などが例示される。
<予備発泡粒子における摩擦音防止効果>
予備発泡粒子200cm3を、30×30cmのガーゼに包んで口を縛った状態で平らな台の上に置き、オートグラフを用いて上から500mm/分の速度で圧縮し、そのときの音の発生をそばで聴取した。評価基準は下記による。
◎:全く摩擦音が発生しない
○:殆ど摩擦音が発生しないが、数回圧縮すると僅かに発生する。
×:大きな摩擦音が発生する。
<発泡成形体における摩擦音防止効果>
200×200×400mmの直方体状にカットしたポリプロピレン系樹脂発泡成形体を、0.05MPaの荷重の下、50mm/秒の速度で、水平なアクリル樹脂板上を、該ポリプロピレン系樹脂発泡体のスキン面(型内成形時に金型のキャビティ内面に接触していた面)を前記アクリル樹脂板に接触させた状態で移動させ、摩擦音の発生の有無を調べた。評価基準は下記による。
◎ :全く摩擦音が発生しない。
○ :殆ど摩擦音が発生しないが、数回移動させると僅かに発生する。
× :移動させた時に大きな摩擦音が発生する。
××:0.05MPaの荷重で圧縮するだけで、大きな摩擦音が発生する。
基材樹脂として、MI=8/10分、融点146℃のランダムポリプロピレン100重量部に対し、ポリエチレン系樹脂としてMI=2/10分、融点122℃で、コモノマーが4−メチルペンテンである直鎖状低密度ポリエチレンを25重量部、脂肪酸アミドとしてエルカ酸アミドを0.6重量部、平均粒子径60nmのカーボンブラックを5重量部、更にセル造核剤としてタルク0.3重量部用い、前記ランダムポリプロピレン、直鎖状低密度ポリエチレン、エルカ酸アミド、カーボンブラック及びタルクをドライブレンドした。このドライブレンドした混合物を、押出機内で溶融混練し、円形ダイよりストランド状に押出し、水冷後、カッターで切断し、一粒の重量が1.2mg/粒のポリプロピレン系樹脂粒子を得た。
ポリプロピレン100重量部に対するポリエチレン系樹脂の添加量を5重量部とした以外は、実施例1と同様の方法で予備発泡粒子と発泡成形体を得た。評価結果を表1に示す。表1に示すように、殆ど摩擦音が発生しないポリプロピレン系樹脂発泡粒子及びポリプロピレン系樹脂発泡成形体を得ることができた。
ポリプロピレン100重量部に対するエルカ酸アミドの添加量を0.3重量部とした以外は、実施例1と同様の方法で予備発泡粒子と発泡成形体を得た。得られた予備発泡粒子および発泡成形体についての評価結果を表1に示す。表1に示すように、殆ど摩擦音が発生しないポリプロピレン系樹脂発泡粒子及びポリプロピレン系樹脂発泡成形体を得ることができた。
脂肪酸アミドとして、エチレンビスステアリン酸アミドをポリプロピレン100重量部に対して0.6重量部添加したこと以外は、実施例1と同様の方法で予備発泡粒子と発泡成形体を得た。得られた予備発泡粒子および発泡成形体についての評価結果を表1に示す。表1に示すように、摩擦音が全く発生しないポリプロピレン系樹脂発泡粒子及びポリプロピレン系樹脂発泡成形体を得ることができた。
平均粒子径60nmのカーボンブラックの代わりに平均粒子径40nmのカーボンブラックを5重量部用いた以外は、実施例1と同様の方法で予備発泡粒子と発泡成形体を得た。評価結果を表1に示す。表1に示すように、殆ど摩擦音が発生しないポリプロピレン系樹脂発泡粒子及びポリプロピレン系樹脂発泡成形体を得ることができた。
平均粒子径60nmのカーボンブラックの添加量を10重量部とした以外は、実施例1と同様の方法で予備発泡粒子と発泡成形体を得た。評価結果を表1に示す。表1に示すように、殆ど摩擦音が発生しないポリプロピレン系樹脂発泡粒子及びポリプロピレン系樹脂発泡成形体を得ることができた。
平均粒子径60nmのカーボンブラックの代わりに、平均粒子径20nmのカーボンブラックを5重量部添加したこと以外は、実施例1と同様の方法で予備発泡粒子と発泡成形体を得た。得られた予備発泡粒子および発泡成形体についての評価結果を表1に示す。表1に示すように、得られたポリプロピレン系樹脂発泡粒子及びポリプロピレン系樹脂発泡成形体は、大きな摩擦音が発生した。このことから、ポリプロピレン系樹脂にポリエチレン系樹脂と脂肪酸アミドの両方を混合しても、平均粒子径が小さいカーボンブラックを用いた場合、摩擦音防止効果がないことがわかる。
ポリエチレン系樹脂を添加しなかったこと以外は、実施例1と同様の方法で予備発泡粒子と発泡成形体を得た。得られた予備発泡粒子および発泡成形体についての評価結果を表1に示す。表1に示すように、得られたポリプロピレン系樹脂発泡粒子及びポリプロピレン系樹脂発泡成形体は、大きな摩擦音が発生した。このことから、顔料として平均粒子径が40nm以上のカーボンブラックを用い、更に脂肪酸アミドを混合しても、ポリエチレン系樹脂を添加しない場合、摩擦音防止効果がないことがわかる。
エルカ酸アミドを添加しなかったこと以外は、実施例1と同様の方法で予備発泡粒子と発泡成形体を得た。得られた予備発泡粒子および発泡成形体についての評価結果を表1に示す。表1に示すように、得られたポリプロピレン系樹脂発泡粒子及びポリプロピレン系樹脂発泡成形体は、大きな摩擦音が発生した。このことから、顔料として平均粒子径が40nm以上のカーボンブラックを用い、更にポリエチレン系樹脂を混合しても、脂肪酸アミドを添加しない場合、摩擦音防止効果がないことがわかる。
Claims (3)
- ポリプロピレン系樹脂100重量部に対して、ポリエチレン系樹脂3重量部以上30重量部以下、脂肪酸アミド0.1重量部以上2重量部以下及び平均粒子径が40nm以上のカーボンブラック1重量部以上10重量部以下を含有するポリプロピレン系樹脂組成物からなるポリプロピレン系樹脂粒子、水、分散剤及び発泡剤を耐圧容器内に仕込み、所定の温度まで加熱し、加圧下で前記樹脂粒子に発泡剤を含浸したのち、前記耐圧容器内よりも低圧の雰囲気下に放出することによって得られることを特徴とする黒色のポリプロピレン系樹脂予備発泡粒子。
- 前記脂肪酸アミドとして、エルカ酸アミド、エチレンビスステアリン酸アミドから選ばれる1種以上を用いる請求項1記載のポリプロピレン系樹脂予備発泡粒子。
- 請求項1または2に記載のポリプロピレン系樹脂予備発泡粒子を金型内に充填し、加熱して得られるポリプロピレン系樹脂発泡成形体。