JP4910924B2 - エチレン−酢酸ビニル共重合体組成物 - Google Patents
エチレン−酢酸ビニル共重合体組成物 Download PDFInfo
- Publication number
- JP4910924B2 JP4910924B2 JP2007191734A JP2007191734A JP4910924B2 JP 4910924 B2 JP4910924 B2 JP 4910924B2 JP 2007191734 A JP2007191734 A JP 2007191734A JP 2007191734 A JP2007191734 A JP 2007191734A JP 4910924 B2 JP4910924 B2 JP 4910924B2
- Authority
- JP
- Japan
- Prior art keywords
- vinyl acetate
- ethylene
- weight
- acetate copolymer
- epoxy
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Description
溶媒:テトラヒドロフラン
流速:1ml/min
温度:40℃
測定濃度:1mg/ml
注入量:100μl
カラム:東ソー製 TSKgel GMH HR−H 2本
数平均分子量が500未満の場合、エチレン−酢酸ビニル共重合体組成物表面がべたつくため好ましくなく、数平均分子量が50000以上の場合は、組成物の製造が困難となるため好ましくない。
JIS K6924−1に準拠。
JIS K6924−1に準拠。
HBr規定液による直接滴定によって求めた。具体的には、試薬として氷酢酸およびHBr0.1N氷酢酸規定液を用い、調製は、HBrガスを上記氷酢酸中に通し、評定は、乾燥純フタル酸水素カリで次式に従って行った。N=フタル酸水素カリの重量(g)/0.2042×滴定cc数とし、指示薬クリスタルバイオレットの0.1g/100ml−氷酢酸溶液を用いた。操作は、試料0.3〜0.5gを50mlの三角フラスコに秤量し、10mlのベンゼンまたはクロロホルムに溶解、0.1ml以下の指示薬を加え、マグネチックスターラーを用い、攪拌しながらHBr規定液で滴定、この際、HBrの蒸発を防ぐため、ビュレットの下部に付けたゴム栓で三角フラスコ上部を止めた。また、ビュレットの先端が溶液のすぐ上になるようにした。終点は青緑色を示す点とした。尚、計算は、次式にて行った。
(ニ)重量平均分子量、数平均分子量
ゲル浸透クロマトグラフィを用いて、以下に示す条件下で測定し、単分散ポリスチレンでユニバーサルな検量線を測定し、直鎖のポリエチレンの分子量として計算した数平均分子量、および重量平均分子量と数平均分子量の比(Mw/Mn)を求めた。
溶媒:テトラヒドロフラン
流速:1ml/min
温度:40℃
測定濃度:1mg/ml
注入量:100μl
カラム:東ソー製 TSKgel GMH HR−H 2本
(ホ)臭気
実施例および比較例により得られたペレットを500mlビンに100g入れ、40℃オーブンに30分放置した。その後、ビンを室温まで冷却し、パネラー10名による臭気評価を行った。
エチレン−酢酸ビニル共重合体(以下、EVAと記す。)として、MFRが9g/10分、酢酸ビニル含有量が10重量%であるEVA(東ソー(株)製 商品名ウルトラセン541、以下、EVAー1と記す。)100重量部に対し、エポキシ変性ジエン系重合体として、エポキシ化ポリブタジエンA((株)ADEKA製 商品名FC3000、Mn=5800、Mw/Mn=1.1、オキシラン酸素量=8.2%、以下、EPB−Aと記す場合がある)を0.008重量部になるよう配合し、単軸押出機(プラコー(株)製、押出機口径50mm)にて150℃の温度にて溶融混練しペレットを得た。臭気評価の比較用試料として、EVA−1を100重量部のみとしたペレットを同上の方法にて作成した。得られたペレットの臭気評価を実施し、エチレン−酢酸ビニル共重合体組成物の臭気が比較用試料EVA−1を100重量部のみとした試料に比べ少ないと評価したパネラー数は9名だった。
EVAとして、MFRが9g/10分、酢酸ビニル含有量が10重量%であるEVA−1が100重量部に対し、エポキシ変性ジエン系重合体として、EPB−Aを0.004重量部になるよう配合し、単軸押出機(プラコー(株)製、押出機口径50mm)にて150℃の温度にて溶融混練しペレットを得た。臭気評価の比較用試料として、EVA−1を100重量部のみとしたペレットを同上の方法にて作成した。得られたペレットの臭気評価を実施し、エチレン−酢酸ビニル共重合体組成物の臭気が比較用試料EVA−1を100重量部のみとした試料に比べ少ないと評価したパネラー数は7名だった。
実施例3
EVAとして、MFRが14g/10分、酢酸ビニル含有量が15重量%であるEVA(東ソー(株)製 商品名ウルトラセン625、以下、EVAー2と記す。)100重量部に対し、エポキシ変性ジエン系重合体として、EPB−Aを0.008重量部になるよう配合し、単軸押出機(プラコー(株)製、押出機口径50mm)にて150℃の温度にて溶融混練しペレットを得た。臭気評価の比較用試料として、EVA−2を100重量部のみとしたペレットを同上の方法にて作成した。得られたペレットの臭気評価を実施し、エチレン−酢酸ビニル共重合体組成物の臭気が比較用試料EVA−2を100重量部のみとした試料に比べ少ないと評価したパネラー数は10名だった。
実施例4
EVAとして、MFRが8g/10分、酢酸ビニル含有量が20重量%であるEVA(東ソー(株)製 商品名ウルトラセン637、以下、EVA−3と記す。)100重量部に対し、エポキシ変性ジエン系重合体として、EPB−Aを0.008重量部になるよう配合し、単軸押出機(プラコー(株)製、押出機口径50mm)にて150℃の温度にて溶融混練しペレットを得た。臭気評価の比較用試料として、EVA−2を100重量部のみとしたペレットを同上の方法にて作成した。得られたペレットの臭気評価を実施し、エチレン−酢酸ビニル共重合体組成物の臭気が比較用試料EVA−2を100重量部のみとした試料に比べ少ないと評価したパネラー数は8名だった。
EVAとして、EVAー1を100重量部に対し、エポキシ変性ジエン系重合体として、エポキシ化ポリブタジエンB(ダイセル化学工業(株)製 商品名エポリードPB3600、Mn=7300、Mw/Mn=16.4、オキシラン酸素量=8.5%、以下、EPB−Bと記す場合がある)を0.008重量部になるよう配合し、単軸押出機(プラコー(株)製、押出機口径50mm)にて150℃の温度にて溶融混練しペレットを得た。臭気評価の比較用試料として、EVA−1を100重量部のみとしたペレットを同上の方法にて作成した。得られたペレットの臭気評価を実施し、エチレン−酢酸ビニル共重合体組成物の臭気が比較用試料EVA−1を100重量部のみとした試料に比べ少ないと評価したパネラー数は7名だった。
Claims (1)
- 190℃、2160g荷重で測定したメルトマスフローレイトが0.5〜50g/10分、酢酸ビニル含有量が3〜50重量%であるエチレン−酢酸ビニル共重合体100重量部に対し、ゲルパーミエーションクロマトグラフィ(GPC)で測定した数平均分子量が500〜50000であるエポキシ変性ジエン系重合体が0.001重量部以上0.01重量部未満であるエチレン−酢酸ビニル共重合体組成物。