JP4801884B2 - レトルト食品用シームレス缶の水なし平版印刷インキ組成物 - Google Patents
レトルト食品用シームレス缶の水なし平版印刷インキ組成物 Download PDFInfo
- Publication number
- JP4801884B2 JP4801884B2 JP2004131939A JP2004131939A JP4801884B2 JP 4801884 B2 JP4801884 B2 JP 4801884B2 JP 2004131939 A JP2004131939 A JP 2004131939A JP 2004131939 A JP2004131939 A JP 2004131939A JP 4801884 B2 JP4801884 B2 JP 4801884B2
- Authority
- JP
- Japan
- Prior art keywords
- ink composition
- ink
- resin
- mass
- seamless
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Lifetime
Description
(B)脂肪族炭化水素系溶剤を主体とし、かつ実質的に芳香族炭化水素系溶剤を含まない有機溶剤
を含み、該アルキッド樹脂(A)における脂肪酸の数平均炭素数が10〜14であり、かつ固形分濃度が30〜70質量%であるレトルト食品用シームレス缶の水なし平版印刷インキ組成物に関する。
(1)アルキッド樹脂の製造
表1に示す多塩基酸、多価アルコールおよび脂肪酸を配合し、常法により酸価が3mgKOH/gになるまでエステル化反応を行い、液状のアルキッド樹脂(A−1〜A−4およびB−1)を製造した。
多塩基酸:
無水フタル酸
多価アルコール:
トリメチロールプロパン
ペンタエリスリトール
脂肪酸:
ヤシ油(数平均炭素数13.3)
デカン酸(数平均炭素数10)
亜麻仁油(数平均炭素数17.9)
バインダー樹脂として上記(1)で製造した液状のアルキッド樹脂(A−1〜A−4、B−1)および硬化剤入りバインダー樹脂(B−2)を用い、顔料としてフタロシアニンブルーを30部、および表2に示す有機溶剤を同表に示すように配合し、三本ロールにて練肉分散させて印刷インキ組成物を調製した。
B−2(硬化剤入りバインダー樹脂):
バインダー樹脂B−1の35部に硬化剤としてアルキル化メラミン樹脂(三井サイテックス(株)製のサイメル238)を10部配合した樹脂
顔料:
フタロシアニンブルー
溶剤B1:
脂肪族炭化水素系溶剤としてパラフィン類を23質量%、ナフテン類を77質量%含み、芳香族炭化水素系溶剤を不可避的に0.2質量%まで含む混合有機溶剤(日本石油(株)製のAF5)
溶剤B2:
脂肪族炭化水素系溶剤として1−ヘキサデセンを55質量%、1−オクタデセンを45質量%含み、芳香族炭化水素系溶剤を含まない(検出不能)混合有機溶剤(三菱化学(株)製のダイアレン168)
溶剤B3:
炭素数10〜14のアルキルベンゼンからなる混合有機溶剤(日本石油(株)製のアルケンL)
得られたインキ組成物について、つぎの試験を行った。結果を表2に示す。
インキ組成物を印刷適正試験機RIテスター(石川島産業機械(株)製)を使用して乾燥インキ被膜の厚さが2.5μmとなるように均一に試験用ゴムロールに写し、ついでアルミ2ピース缶(シームレス缶。肉厚50〜100μm、51mmφ)に40m/minの印刷速度で転写した。
A:インキの転写性およびインキ皮膜の表面平滑性が良好である。
B:若干インキの転写性およびインキ皮膜の表面平滑性がAより劣るが、全体として商品として使用可能である。
C:インキの転写性およびインキ皮膜の表面平滑性が不良であり、商品として使用できない。
インキ組成物を上記印刷適正試験機RIテスターを使用して乾燥インキ被膜の厚さが8.0μmとなるように均一に試験用ゴムロールに写し、ついで水なし平版印刷原版(東レ(株)製)に40m/minの印刷速度で連続10回転接触させた。
A:耐地汚れ性が良好で、非画線部への転移が認められない。
B:若干非画線部への転移が認められるが、全体として商品として使用可能である。
C:非画線部への転移が著しく、商品として使用できない。
乾燥インキ被膜の膜厚を2.0μmとしたほかは上記(3)と同様にして印刷し、かつ上塗り塗装した各シームレス缶をレトルト処理し、処理の前後において、つぎの特性を調べた。結果を表2に示す。
レトルト釜に脱イオン水5リットルを入れ、印刷された試験片に水蒸気が当たるようにセットする。水を130℃まで加熱し、その温度で30分間維持した後、室温まで放冷する。
JIS K5600−5−6に規定する碁盤目試験で評価する。
JIS K5600−5−4に規定するJIS−A硬度(鉛筆硬度)で評価する。
Claims (5)
- (A)1種または2種以上の脂肪酸を40〜60質量%含むアルキッド樹脂、および
(B)脂肪族炭化水素系溶剤を主体とし、かつ実質的に芳香族炭化水素系溶剤を含まない有機溶剤
を含み、該アルキッド樹脂(A)における脂肪酸の数平均炭素数が10〜14であり、かつアルキッド樹脂の固形分濃度が30〜70質量%であるレトルト食品用シームレス缶の水なし平版印刷インキ組成物。 - 前記脂肪族炭化水素系溶剤が、炭素数14〜18のα−オレフィンを70〜100質量%含む脂肪族炭化水素系溶剤である請求項1記載のインキ組成物。
- 前記アルキッド樹脂の酸価が30mgKOH/g以下であり、かつ水酸基価が120〜200mgKOH/gである請求項1または2記載のインキ組成物。
- 硬化剤を含まない請求項1〜3のいずれかに記載のインキ組成物。
- レトルト食品用シームレス缶の外周面に請求項1〜4のいずれかに記載のインキ組成物を水なし平版印刷した後、仕上げニスを塗装して焼付け硬化させるレトルト食品用シームレス缶の印刷方法。