JP4508602B2 - 鉄を主成分とする合金の化学研磨剤及びこれを用いた鉄を主成分とする合金の表面処理方法 - Google Patents
鉄を主成分とする合金の化学研磨剤及びこれを用いた鉄を主成分とする合金の表面処理方法 Download PDFInfo
- Publication number
- JP4508602B2 JP4508602B2 JP2003366499A JP2003366499A JP4508602B2 JP 4508602 B2 JP4508602 B2 JP 4508602B2 JP 2003366499 A JP2003366499 A JP 2003366499A JP 2003366499 A JP2003366499 A JP 2003366499A JP 4508602 B2 JP4508602 B2 JP 4508602B2
- Authority
- JP
- Japan
- Prior art keywords
- iron
- acid
- based alloy
- alloy
- aqueous solution
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Description
以下、本発明について詳細に説明する。
フェライト・マルテンサイト系ステンレス(Fe合金鋼400番台)及びオーステナイト系ステンレス(Fe合金鋼300番台)の2種の鉄を主成分とする合金を選択し、それぞれを、直径3.95mm、長さ17.8mm、内径1.2mmのパイプ形状に加工したものをテストピースとして用いた。
なお、このテストピースには、いずれも切断加工時に内径の切り口に0.05〜0.1mm程度の微小バリが発生しており、又、面粗さは異なる5点間の平均でRa0.41〜0.43、Ry2.96〜3.66であった。
ところで、アルミサッシ用のアルミニウム板を用い、このアルミニウム板をプレス加工によってその表面やエッジ部に発生する微細な凸部又はバリを発生させたものを実施例1及び実施例2の化学研磨剤(25℃)に浸漬したところ、実施例1及び実施例2共に、浸漬後1〜2分後には、その表面が硝酸によって酸化され、白色化(水酸化アルミニウムの皮膜が生成)し、むしろ光沢が失われ、商品価値が著しく低下することが確認された。
Claims (7)
- 鉄を主成分とする合金の表面を処理するための酸性水溶液であって、
この酸性水溶液は、少なくともリン酸、硝酸及び硫酸を含み、当該酸性水溶液全体におけるリン酸の濃度が20〜90重量%、硝酸の濃度が0.5〜9.9重量%、硫酸の濃度が1〜9.9重量%であり、
更に、酸性水溶液中には、合金を浸漬した際に合金表面に重金属を析出させ、いわゆるガルバニ電池を起こすことができる、温度25℃における標準電極電位が−0.15以上の、重金属イオン及び/又は金属酸化物が配合されてなることを特徴とする鉄を主成分とする合金の化学研磨剤(銀、ニッケル、コバルト、マンガン、錫、アンチモン、鉛、亜鉛、マグネシウムの群より選ばれた金属の重クロム酸塩又は重クロム酸アンモニウム塩が共存しているものを除く。)。 - 請求項1に記載の鉄を主成分とする合金の化学研磨剤において、前記重金属イオンが、錫イオン、鉛イオン又は銅イオンから選ばれた少なくとも1種以上である鉄を主成分とする合金の化学研磨剤。
- 請求項1又は2に記載の鉄を主成分とする合金の化学研磨剤において、前記酸性水溶液中で重金属イオンを発生する化合物がアンモニウム塩又はフッ化物である鉄を主成分とする合金の化学研磨剤。
- 請求項1ないし3のいずれか1項に記載の鉄を主成分とする合金の化学研磨剤において、更に塩酸が酸性水溶液全体に対して0.1〜9.9重量%配合されてなり、且つ硫酸と塩酸の和が10重量%未満である鉄を主成分とする合金の化学研磨剤。
- 請求項1ないし4のいずれか1項に記載の鉄を主成分とする合金の化学研磨剤において、更に有機酸が酸性水溶液全体に対して0.01〜20.0重量%配合されてなる鉄を主成分とする合金の化学研磨剤。
- 請求項1ないし5のいずれか1項に記載の鉄を主成分とする合金の化学研磨剤において、更に抑制剤、界面活性剤及び溶解促進剤から選ばれた少なくとも1種以上が加えられてなる鉄を主成分とする合金の化学研磨剤。
- 請求項1ないし6のいずれか1項に記載の化学研磨剤を用いて、鉄を主成分とする合金の表面に存在する不動態化膜を除去するとともに、鉄を主成分とする合金に対する機械加工時やプレス加工時などに当該鉄を主成分とする合金の表面やエッジ部に発生する微細な凸部又はバリ或いは表面の不純物を除去することを特徴とする鉄を主成分とする合金の表面処理方法。