JP4480138B2 - 薬包紙およびそれを使用して製袋した分包袋 - Google Patents
薬包紙およびそれを使用して製袋した分包袋 Download PDFInfo
- Publication number
- JP4480138B2 JP4480138B2 JP2004177103A JP2004177103A JP4480138B2 JP 4480138 B2 JP4480138 B2 JP 4480138B2 JP 2004177103 A JP2004177103 A JP 2004177103A JP 2004177103 A JP2004177103 A JP 2004177103A JP 4480138 B2 JP4480138 B2 JP 4480138B2
- Authority
- JP
- Japan
- Prior art keywords
- film
- medicine
- biaxially stretched
- resin
- plasma
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Description
而して、そのような特性を有する包装用材料としては、一般的に、セロハン、セロハンにポリ塩化ビニリデン系樹脂をコ−ティングしたフィルム、いわゆる、Kコ−トセロハン、あるいは、セロハンにエチレン−ビニルアルコ−ル共重合体をコ−ティングしたフィルム等の防湿セロハン等を主要基材とし、これに、印刷模様等を施した後、アルミニウム箔、ヒ−トシ−ル性樹脂層、その他等を積層した積層材が使用されている。
しかし、上記のようなセロハン、防湿セロハン等を主要基材とする積層材を使用して製袋した包装用容器は、優れた手切れ性(引き裂き性)を有するものの、印刷適性等に劣ると共に、極めて高価であり、更に、将来的に供給面での不安があるばかりではなく、近年、環境面から、包装用材料の廃棄処理適性が問われ、脱塩素、脱セロハン等の気運が高まり、その代替え材料が検討されているものである。
更に、内部に薬剤が収納された状態で連続し服用時に分離される複数の分包袋を製袋するための帯状の薬包紙であって、その原材がポリエチレンフタレ−トシ−ト又は二軸延伸ポリプロピレンシ−トを含む帯状の透明複合プラスチックシ−トであり、かつ、前記ポリエチレンフタレ−トシ−ト又は二軸延伸ポリプロピレンシ−トに、微細なキズが形成されていることを特徴とする薬包紙およびそれを使用して製袋した分包袋も提案されている(例えば、特許文献3参照。)。
また、上記の特許文献2に係る薬品包装用構成体においては、ポリエステルフィルムからなる基材の厚みを3μm以上6μm以下にすることにより、引き裂き強度を100g以上500g以下に調製し、その手切れ性(引き裂き性)を改良しているものではあるが、バリア−層を構成する素材として、アルミニウム箔を使用していることから、透明性に欠け、内容物の視認性等に劣るばかりではなく、使用後の廃棄物処理時に問題があり、例えば、再利用のためにアルミニウム箔と他の物質との分別回収が極めて困難であり、また、焼却処理すると、焼却炉でアルミニウム箔が燃えずに塊状の残滓物となり、焼却炉等を破壊する等の問題点があるものである。
更に、上記の特許文献3に係る薬包紙およびそれを使用して製袋した分包袋においては、バリア性を必要とする場合には、例えば、シリカ蒸着もしくはアルミ蒸着したポリエチレンフタレ−トシ−トフィルム等を使用するとしているが、上記のポリエチレンフタレ−トシ−ト又は二軸延伸ポリプロピレンシ−トに、全面に微細なキズが形成されていることから、それだけで十分なバリア性を到底に期待し得ないものであって、その要をなさないものであり、更に、全面に微細なキズが形成されているポリエチレンフタレ−トシ−ト又は二軸延伸ポリプロピレンシ−トに、シリカ蒸着もしくはアルミ蒸着等の蒸着層を形成すること自体が非常に難しく、仮に、シリカ蒸着もしくはアルミ蒸着等の蒸着層を形成し得たとしても、シリカ蒸着もしくはアルミ蒸着等の蒸着層にクラック等が発生し、バリア性が著しく劣化するという問題点があり、到底、その使用に耐えないものであることから好ましくないものである。
そこで本発明は、環境面、コスト面、ガスバリア性等を改良し、手切れ性(引き裂き性)、防湿性、酸素ガスバリア性、異物確認のための内容物視認性および金属探知機適性、印刷適性、製袋性、その他等の特性を有する薬包紙およびそれを使用して製袋した分包袋を提供することである。
しかも、本発明に係る薬包紙およびそれを使用して製袋した分包袋は、無機酸化物の薄膜からなるバリア層により、水蒸気、酸素ガス等に対するガスバリア性能を構成することから、極めて環境対応に適うものであると共に異物確認のための内容物視認性および金属探知機適性等を有するものである。
また、本発明に係る薬包紙およびそれを使用して製袋した分包袋は、それを構成する積層体を形成するポリエステル系樹脂フィルムとして、易引き裂き性に優れた2軸延伸ポリエチレンテレフタレ−トフィルムを使用することから、また、無機酸化物の薄膜からなるバリア層を有する2軸延伸ポリエステル系樹脂フィルムについて、その製袋時のヒ−トシ−ル部に相当する箇所に、貫通しない傷痕および/または貫通孔を形成し、而して、製袋時に、その貫通しない傷痕および/または貫通孔の部分を、ヒ−トシ−ル性樹脂層の面を対向させて重ね合わせ、次いで、その部分をヒ−トシ−ルして製袋し、分包袋を製造していることから、手切れ性(引き裂き性)、易開封性等に極めて優れているものである。 更に、本発明に係る薬包紙およびそれを使用して製袋した分包袋は、後述するように、それを構成する積層体を形成するポリエステル系樹脂フィルムの表面に、不活性ガスによるプラズマ処理面を形成したり、あるいは、帯電防止コ−ト層を設けたり、また、無機酸化物の薄膜からなるバリア層の面に、酸素ガスによるプラズマ処理面を設け、更にまた、ヒ−トシ−ル性樹脂層中に帯電防止剤を含有させる等の種々の加工処理を組み合わせて施すことから、積層体を構成する各層の密着性等を著しく向上させ、これにより、その印刷適性、製袋性、その他等の特性を著しく向上させ、環境面、コスト面、ガスバリア性等を著しく改良した薬包紙およびそれを使用して製袋した分包袋を製造し得るものである。
図1は、本発明に係る薬包紙についてその層構成の一例を示す概略的断面図であり、図2は、図1に示す本発明に係る薬包紙についてその構成の一例を示す概略的平面図であり、図3、図4および図5は、本発明に係る薬包紙を使用して製袋した分包袋についてその構成の一例を示す概略的平面図である。
なお、本発明に係る薬包紙Aは、図2に係る概略的平面図に示すように、上記の図1に示す本発明に係る薬包紙Aにおいて、無機酸化物の薄膜2からなるバリア層2aを有する2軸延伸ポリエステル系樹脂フィルム1であって、その製袋時のヒ−トシ−ル部に相当する箇所に、貫通しない傷痕および/または貫通孔5が形成されているものである。
而して、本発明においては、後述するように、上記の貫通しない傷痕および/または貫通孔の部分を、ヒ−トシ−ル性樹脂層の面を対向させて重ね合わせ、次いで、その部分をヒ−トシ−ルして製袋し、軟包装袋からなる分包袋を製造するものである。
而して、本発明においては、後述するように、上記の貫通しない傷痕および/または貫通孔の部分を、ヒ−トシ−ル性樹脂層の面を対向させて重ね合わせ、次いで、その部分をヒ−トシ−ルして製袋し、軟包装袋からなる分包袋を製造するものである。
なお、本発明においては、上記で製造した分包薬品包装体から薬品を飲む場合には、ヒ−トシ−ル部に設けてある貫通しない傷痕および/または貫通孔の部分を手に持って、その部分から引き裂くことにより、極めて容易に分包袋を開封して、内容物の薬品を飲むことができるものである。
例えば、本発明においては、図示しないが、充填包装する内容物の種類等によって、更に、他の素材等を任意に使用し、これを積層して、種々の形態からなる薬包紙、それを使用して製袋した分包袋等を設計して製造することができるものである。
また、例えば、図示しないが、本発明においては、無機酸化物の薄膜からなるバリア層については、無機酸化物の薄膜の1層からなる単層膜のみならず無機酸化物の薄膜の2層以上からなる多層膜等から構成することもできるものである。
更に、本発明において、上記のような本発明に係る薬包紙を積層する方法としては、図示しないが、例えば、アンカ−コ−ト剤によるアンカ−コ−ト剤層、ポリオレフィン系樹脂等を溶融押出した溶融押出樹脂層等を介して積層する溶融押出ラミネ−ト法、あるいは、例えば、ラミネ−ト用接着剤によるラミネ−ト用接着剤層等をを介して積層するドライラミネ−ト法、その他等により積層することができる。
また、本発明において、本発明に係る薬包紙を使用して製袋した分包袋等としては、上記に図示した例示の分包袋の形状に限定されるものでないことは言うまでもないことであり、その目的、用途等により、四方シ−ル型、自立性型、ガゼット型、角底型、ピロ−型、その他等の種々の形態からなる包装用袋を製造することができるものである。
本発明において、上記の2軸延伸ポリエステル系樹脂フィルムとしては、具体的には、例えば、ポリエチレンテレフタレ−ト樹脂、ポリブチレンテレフタレ−ト樹脂、ポリエチレン−2、6−ナフタレ−ト樹脂、ポリブチレン−2、6−ナフタレ−ト、ポリシクロヘキサンジメチレンテレフタレ−ト樹脂、その他等の各種のポリエステル系樹脂を使用することができる。
而して、本発明において、2軸延伸ポリエステル系樹脂フィルムとしては、特に、易引き裂き性を有する2軸延伸ポリエチレンテレフタレ−ト樹脂フィルム、または、2軸延伸ポリブチレンテレフタレ−ト樹脂フィルムを使用することが好ましいものである。
なお、本発明において、上記の2軸延伸ポリエステル系樹脂フィルムに代えて、例えば、2軸延伸ポリプロピレン系樹脂フィルム等でも、作業性、取り扱い性、その他等の問題を気にしなければ、十分に使用することができるものである。
本発明において、2軸延伸ポリエステル系樹脂フィルム膜厚としては、3〜50μm位、より好ましくは、5〜30μm位が望ましい。
而して、本発明において、不活性ガスによるプラズマ処理面について説明すると、かかるプラズマ処理面としては、気体をア−ク放電により電離させることにより生じるプラズマガスを利用して表面改質を行うプラズマ表面処理法等を利用してプラズマ処理面を形成することがてきる。
すなわち、本発明においては、窒素ガス、アルゴンガス、ヘリウムガス、その他等の不活性ガスをプラズマガスとして使用するプラズマ表面処理法でプラズマ処理を行うことによりプラズマ処理面を形成することができる。
なお、本発明において、プラズマガスとしては、上記の不活性ガスに、更に、酸素ガスを添加した混合ガスを使用することもできる。
また、本発明において、不活性ガスによるプラズマ処理面を形成する場合、2軸延伸ポリエステル系樹脂フィルムの一方の面に、後述する物理気相成長法による無機酸化物の薄膜からなるバリア層の面に、物理気相成長法による無機酸化物の薄膜からなるバリア層を形成する直前に、インラインでプラズマ処理を行うことにより、2軸延伸ポリエステル系樹脂フィルムの表面の水分、塵等を除去すると共にその表面の平滑化、活性化、その他等の表面処理を可能とすることから望ましいものである。
更に、本発明において、上記のプラズマ処理としては、プラズマ出力、プラズマガスの種類、プラズマガスの供給量、処理時間、その他等の条件を考慮してプラズマ放電処理をおこなうことが好ましいものである。
また、本発明において、プラズマを発生させる方法としては、例えば、直流グロ−放電、高周波放電、マイクロ波放電、その他等の装置を利用して行うことができる。
本発明においては、上記のような不活性ガスによるプラズマ処理面を介して、後述する物理気相成長法による無機酸化物の薄膜からなるバリア層を設けることにより、その両者を強固に密着させ、その密着性を著しく向上させ、その層間剥離等を防止し得ることができるものである。
なお、本発明において、不活性ガスによるプラズマ処理面について、その2乗平均粗さ、Ra、算術平均粗さ、Rms、最大高さ、Rmax等の表面粗さ、および、表面張力等については、例えば、表面粗さは、原子間力顕微鏡(AFM)を使用し、具体的には、デジタル インストルメエント(Digital Instrument)社製のナノスコ−プ(Nano Scope)IIIaを使用し、 無機酸化物の薄膜からなるバリア層を形成する際に、タッピングモ−ドで、無機酸化物の薄膜からなるバリア層を形成せずに、不活性ガスによるプラズマ放電処理してプラズマ処理面を形成したフィルムを使用し、その処理面を以下の条件で測定して、表面粗さを測定するものである。
(表面粗さの測定条件)
スキャンモ−ド(Scan Mode):タッピング(Tapping)AFM
スキャンサイズ(Scan Size):1μm
スキャンレイト(Scan Rate):1Hz
また、上記の表面張力は、例えば、協和界面科学株式会社製、機種名、接触角計FACE CA−Xを使用し、無機酸化物の薄膜からなるバリア層を形成せずに、不活性ガスによるプラズマ放電処理してプラズマ処理面を形成したフィルムを使用し、その処理面の表面張力を測定して、表面張力を測定した。
而して、かかる帯電防止コ−ト層としては、例えば、樹脂をビヒクルの主成分とし、これに帯電防止剤の1種ないそれ以上を添加し、更に、必要ならば、例えば、可塑剤、安定剤、酸化防止剤、光安定剤、紫外線吸収剤、硬化剤、架橋剤、滑剤、充填剤、着色剤、その他等の添加剤の1種ないし2種以上を任意に添加し、溶剤・希釈剤等で十分に混練して、樹脂組成物を調製し、次いで、該樹脂組成物を使用し、これを、上記の2軸延伸ポリエステル系樹脂フィルムの表面に、通常のコ−ティング法、あるいは、印刷法等を用いて、コ−ティングないし印刷して、帯電防止コ−ト層を形成することができる。
なお、本発明において、前述の2軸延伸ポリエステル系樹脂フィルムの製膜時に、フィルムの製膜原料であるポリエステル系樹脂のペレットに、上記のような帯電防止剤の1種ないしそれ以上を添加し、これを十分に混練し、次いで、その樹脂組成物を使用し、製膜化して、2軸延伸ポリエステル系樹脂フィルム中に帯電防止剤を混練り含有させて、2軸延伸ポリエステル系樹脂フィルムに帯電防止性を付与することもできる。
本発明において、具体的には、金属または金属の酸化物を原料とし、これを加熱して蒸気化し、前述の2軸延伸ポリエステル系樹脂フィルムの一方の面に蒸着する真空蒸着法、または、原料として金属または金属の酸化物を使用し、酸素を導入して酸化させて、2軸延伸ボリエステル系樹脂フィルムの一方の面に蒸着する酸化反応蒸着法、更に酸化反応をプラズマで助成するプラズマ助成式の酸化反応蒸着法等を用いて蒸着膜を形成することができる。
上記において、蒸着材料の加熱方式としては、例えば、抵抗加熱方式、高周波誘導加熱方式、エレクトロンビ−ム加熱方式(EB)等にて行うことができる。
図6に示すように、巻き取り式真空蒸着装置21の真空チャンバ−22の中で、巻き出しロ−ル23から、2軸延伸ポリエステル系樹脂フィルム1を繰り出し、次いで、該2軸延伸ポリエステル系樹脂フィルム1を、必要ならば、ガイドロ−ル24等を介して、冷却したコ−ティングドラム25に案内する。
あるいは、本発明においては、上記のように巻き出しロ−ル23から、2軸延伸ポリエステル系樹脂フィルム1を繰り出し、次いで、該2軸延伸ポリエステル系樹脂フィルム1を、必要ならば、ガイドロ−ル24等を介して、冷却したコ−ティングドラム25に案内する際に、その間に、例えば、マグネトロンスパッタリング装置35等を配設し、これを利用して、2軸延伸ポリエステル系樹脂フィルム1の一方の面に、不活性ガスによるプラズマ処理を施して、インラインでプラズマ処理面を形成することもできるものである。
而して、上記の冷却したコ−ティングドラム25上に案内された2軸延伸ポリエステル系樹脂フィルム1の面に、るつぼ26で、例えば、電子銃27にて電子線28を照射して、それにより熱せられた蒸着源29、例えば、金属アルミニウム、あるいは、酸化アルミニウム等を蒸発させ、更に、必要ならば、巻き取り式真空蒸着装置21の外に配置した酸素ガスボンベ30から酸素ガス供給パイプ31から酸素ガスを供給し、酸素ガス吹出口より酸素ガス等を噴出し、これを供給しながら、マスク32を介して、例えば、酸化アルミニウム等の無機酸化物の薄膜を成膜化し、次いで、上記において、酸化アルミニウム等の無機酸化物の薄膜を形成した2軸延伸ポリエステル系樹脂フィルム1を、必要ならば、ガイドロ−ル33等を介して送り出し、次いで、巻き取りロ−ル34に巻き取ることによって、その一方の面に無機酸化物の薄膜からなるバリア層を設けた2軸延伸ポリエステル系樹脂フィルム1を製造することができる。
なお、なお、図6中、符号35、35は、ブラズマ処理等を行うマグネトロンスパッタリング装置を表すものである。
而して、本発明においては、例えば、マグネトロンスパッタリング装置35、35等を配設し、これにより、例えば、2軸延伸ポリエステル系樹脂フィルム1の一方の面に、不活性ガスによるプラズマ処理を施してインラインでプラズマ処理面を形成し、そのプラズマ処理面を介して、2軸延伸ポリエステル系樹脂フィルムと酸化アルミニウム等の無機酸化物の薄膜からなるバリア層との密着性を向上させることができ、あるいは、蒸着後、更に、蒸着して製膜化した酸化アルミニウム等の無機酸化物の薄膜からなるバリア層の面に、酸素ガスによるプラズマ処理等を施してインラインで酸素ガスによるプラズマ処理面を形成し、後述するヒ−トシ−ル性樹脂との密着性を向上させることもできるものである。 また、本発明においては、上記のような巻き取り式真空蒸着装置を用いて、まず、第1層の無機酸化物の薄膜からなるバリア層を形成し、次いで、同様にして、該無機酸化物の薄膜からなるバリア層の上に、更に、無機酸化物の薄膜からなるバリア層を形成するか、あるいは、上記のような巻き取り式真空蒸着装置を用いて、これを2連に連接し、連続的に、無機酸化物の薄膜からなるバリア層を形成することにより、2層以上の多層膜からなる無機酸化物の薄膜を形成することができる。
而して、好ましいものとしては、ケイ素(Si)、アルミニウム(Al)等の金属の酸化物の蒸着膜を挙げることができる。
また、上記の金属の酸化物の蒸着膜は、ケイ素酸化物、アルミニウム酸化物、マグネシウム酸化物等のように金属酸化物として呼ぶことができ、その表記は、例えば、SiOX 、AlOX 、MgOX 等のようにMOX (ただし、式中、Mは、金属元素を表し、Xの値は、金属元素によってそれぞれ範囲がことなる。)で表される。
上記のXの値の範囲としては、ケイ素(Si)は、0〜2、アルミニウム(Al)は、0〜1.5、マグネシウム(Mg)は、0〜1、カルシウム(Ca)は、0〜1、カリウム(K)は、0〜0.5、スズ(Sn)は、0〜2、ナトリウム(Na)は、0〜0.5、ホウ素(B)は、0〜1、5、チタン(Ti)は、0〜2、鉛(Pb)は、0〜1、ジルコニウム(Zr)は0〜2、イットリウム(Y)は、0〜1.5の範囲の値をとることができる。
また、上記において、X=0の場合、完全な金属であり、透明ではなく全く使用することができない、また、Xの範囲の上限は、完全に酸化した値である。
本発明において、一般的に、ケイ素(Si)、アルミニウム(Al)以外は、使用される例に乏しく、ケイ素(Si)は、1.0〜2.0、アルミニウム(Al)は、0.5〜1.5の範囲の値のものを使用することができる。
本発明において、上記のような無機酸化物の薄膜からなるバリア層の膜厚としては、使用する金属、または、金属の酸化物の種類等によって異なるが、例えば、50〜2000Å位、好ましくは、100〜1000Å位の範囲内で任意に選択して形成することが望ましい。
また、本発明においては、無機酸化物の薄膜からなるバリア層としては、使用する金属または金属の酸化物としては、1種または2種以上の混合物で使用し、異種の材質で混合した無機酸化物の蒸着膜を構成することもできる。
而して、本発明において、酸素ガスによるプラズマ処理面としては、前述の不活性ガスによるプラズマ処理面と同様に形成することができる。
すなわち、本発明において、酸素ガスによるプラズマ処理面としては、気体をア−ク放電により電離させることにより生じるプラズマガスを利用して表面改質を行うプラズマ表面処理法等を利用して、酸素ガスによるプラズマ処理面を形成することがてきる。
而して、本発明において、プラズマガスとしては、酸素ガス、または、酸素ガスと窒素ガス、アルゴンガス、ヘリウムガス、その他等の不活性ガスとの混合ガス等を使用するプラズマ表面処理法でプラズマ処理を行うことにより、酸素ガスによるプラズマ処理面を形成することができる。
なお、本発明において、酸素ガスによるプラズマ処理面を形成する場合、2軸延伸ポリエステル系樹脂フィルムの一方の面に設けた不活性ガスによるプラズマ処理面に物理気相成長法による無機酸化物の薄膜からなるバリア層を形成した後、その直後に、該物理気相成長法による無機酸化物の薄膜からなるバリア層の面、インラインで酸素ガスによるプラズマ放電処理を行うことにより、酸素ガスによるプラズマ処理面を形成することができるものである。
更に、本発明において、上記のプラズマ処理としては、プラズマ出力、プラズマガスの種類、プラズマガスの供給量、処理時間、その他等の条件を考慮してプラズマ放電処理をおこなうことが好ましいものである。
また、本発明において、プラズマを発生させる方法としては、例えば、直流グロ−放電、高周波放電、マイクロ波放電、その他等の装置を利用して行うことができる。
而して、本発明においては、上記のような形成法において、適当な粒度分布を持った砥粒で形成した砥粒面からなる砥面をもった砥石ロ−ルないし板を圧着する方法で行うことが好ましく、具体的には、適当な粒度分布を持った砥粒で形成した砥粒面からなる砥面をもった砥石ロ−ルとその受けロ−ルとの間に、無機酸化物の薄膜からなるバリア層を有する2軸延伸ポリエステル系樹脂フィルムを挿入し、圧接して粗面加工を行うことにより、上記の無機酸化物の薄膜からなるバリア層を有する2軸延伸ポリエステル系樹脂フィルムに貫通しない傷痕および/または貫通孔を有する粗面を形成することができる。
本発明においては、上記のような粗面加工により、貫通しない傷痕からなる粗面、あるいは、貫通孔からなる粗面、更には、貫通しない傷痕からなる粗面と貫通孔からなる粗面とが混在している粗面、その他等の粗面を形成し、その易開封性の作用効果を奏するものである。
上記の樹脂のフィルムないしシ−トは、単層ないし多層で使用することができ、また、上記の樹脂のフィルムないしシ−トの厚さとしては、5μm〜300μm位、好ましくは、10μm〜110μm位が望ましい。
更に、本発明において、上記の樹脂のフィルムないしシ−トの厚さとしては、本発明に係る薬包紙を使用し、分包袋の製袋時において、本発明に係る薬包紙を構成する無機酸化物の薄膜からなるバリア層に、擦り傷、あるいは、クラック等を発生するすることを防止するために、更に、手切れ性、引き裂き性等の易開封性等を考慮すると、その膜厚を厚くもなく、また、薄くもなくすることが好ましく、具体的には、10μm〜60μm位、望ましくは、15μm〜50μm位であることが好ましいものである。
而して、本発明においては、上記のような樹脂のフィルムないしシ−トの中でも、特に、厚さ20μm〜40μm位のポリエチレンフィルムあるいは無延伸ポリプロピレンフィルムないしシ−トを使用することが好ましいものである。
上記において、一般的な添加剤としては、例えば、滑剤、架橋剤、酸化防止剤、紫外線吸収剤、光安定剤、充填剤、補強剤、帯電防止剤、顔料、その他等を使用することができ、更には、改質用樹脂等も使用することがてきる。
本発明においては、その他、例えば、通常の包装材料を製造するときに使用する積層法、例えば、ウエットラミネ−ション法、無溶剤ラミネ−ション法、共押出ラミネ−ション法、インフレ−ション法、その他の方法等で行うことができる。
而して、本発明においては、上記の積層を行う際に、必要ならば、例えば、その積層する基材の表面に、コロナ放電処理、オゾン処理、フレ−ム処理、プラズマ処理等の前処理を任意に施すことができる。
更に、本発明において、溶融押出ラミネ−ト法における溶融押出樹脂としては、例えば、低密度ポリエチレン、中密度ポリエチレン、高密度ポリエチレン、直鎖状(線状)低密度ポリエチレン、メタロセン系触媒を使用して重合したエチレンーα・オレフイン共重合体、ポリプロピレン、エチレンー酢酸ビニル共重合体、アイオノマー樹脂、エチレンーアクリル酸エチル共重合体、エチレンーアクリル酸共重合体、エチレンーメタクリル酸共重合体、エチレンープロピレン共重合体、メチルペンテンポリマー、ポリエチレン、ポリプロピレン等のポリオレフイン系樹脂をアクリル酸、メタクリル酸、無水マレイン酸、フマール酸、その他等の不飽和カルポン酸で変性した酸変性ポリオレフイン系樹脂、その他等を使用することができる。
上記の接着剤の組成系は、水性型、溶液型、エマルジョン型、分散型等のいずれの組成物形態でもよく、また、その性状は、フィルム・シート状、粉末状、固形状等のいずれの形態でもよく、更に、接着機構については、化学反応型、溶剤揮発型、熱溶融型、熱圧型等のいずれの形態でもよいものである。
而して、本発明においては、積層する両者の一方の面に、上記のラミネート用接着剤を、例えば、ロールコート法、グラビアロールコート法、キスコート法、その他等のコート法、あるいは、印刷法等によって施し、次いで、溶剤等を乾燥させてラミネート用接着剤層を形成すことができ、そのコーティングないし印刷量としては、0.1〜10g/m2 (乾燥状態)位が望ましい。
而して、上記のようなアンカ−コ−ト剤、あるいは、ラミネ−ト用接着剤を使用して形成してなるアンカ−コ−ト剤層、あるいは、ラミネ−ト用接着剤層は、柔らかく、柔軟性に富み、かつ、屈曲性に富む薄膜を形成することができ、その引っ張り伸長度を向上させ、無機酸化物の薄膜からなるバリア層に対し柔軟性、屈曲性等を有する被膜として作用し、例えば、ラミネ−ト加工、印刷加工、あるいは、製袋加工等の後加工時における無機酸化物の薄膜の後加工適性を向上させ、後加工時における無機酸化物の薄膜へのクラック等の発生等を防止するものである。
ちなみに、本発明において、上記のようなアンカ−コ−ト剤によるアンカ−コ−ト剤層および/またはラミネ−ト用接着剤によるラミネ−ト用接着剤層は、JIS規格K7113に基づいて、100〜300%の範囲からなる引っ張り伸度を有するものである。
而して、本発明においては、上記のようなアンカ−コ−ト剤によるアンカ−コ−ト剤層および/またはラミネ−ト用接着剤によるラミネ−ト用接着剤層の引っ張り伸度、その他により、無機酸化物の薄膜からなるバリア層とヒ−トシ−ル性樹脂層との密接着性を向上させ、これにより、無機酸化物の薄膜へのクラック等の発生を防止し、そのラミネ−ト強度等を高めるものである。
上記において、引っ張り伸度が、100%未満であると、薬包紙としての柔軟性がなくなり、無機酸化物の薄膜へのクラック等が発生し易くなることから好ましくなく、また、引っ張り伸度が、300%を越えると、アンカ−コ−ト剤、あるいは、ラミネ−ト用接着剤等としての接着性の強度が十分でなく、要求されるラミネ−ト強度が発現されにくくなることから好ましくないものである。
その他、例えば、合成紙等も使用することができる。
本発明において、上記のフィルムないしシ−トは、未延伸、一軸ないし二軸方向に延伸されたもの等のいずれのものでも使用することができる。
また、その厚さは、任意であるが、数μmから300μm位の範囲から選択して使用することができる。
更に、本発明においては、フィルムないしシ−トとしては、押し出し成膜、インフレ−ション成膜、コ−ティング膜等のいずれの性状の膜でもよい。
これらの材料は、一種ないしそれ以上を組み合わせて使用することができる。
また、上記のフィルムないしシ−トの厚さとしては、任意であるが、通常、5μmないし300μm位、更には、10μmないし100μm位が望ましい。
上記の印刷模様層としては、通常のインキビヒクルの1種ないし2種以上を主成分とし、これに、必要ならば、可塑剤、安定剤、酸化防止剤、光安定剤、紫外線吸収剤、硬化剤、架橋剤、滑剤、帯電防止剤、充填剤、その他等の添加剤の1種ないし2種以上を任意に添加し、更に、染料・顔料等の着色剤を添加し、溶媒、希釈剤等で充分に混練してインキ組成物を調整し、次いで、該インキ組成物を使用し、例えば、グラビア印刷、オフセット印刷、凸版印刷、スクリ−ン印刷、転写印刷、フレキソ印刷、その他等の印刷方式を使用し、上記の基材フィルムの片面に、文字、図形、記号、模様、その他等からなる所望の印刷模様を印刷して、本発明にかかる印刷模様層を形成することができるものである。
更に、本発明においては、本発明に係る薬包紙を使用し、連続的に、あにいは、バッチ式に製袋することができる。
その他、分包袋としては、例えば、自立性分包袋(スタンディングパウチ)等も可能である。
上記において、ヒ−トシ−ルの方法としては、例えば、バ−シ−ル、回転ロ−ルシ−ル、ベルトシ−ル、インパルスシ−ル、高周波シ−ル、超音波シ−ル等の公知の方法で行うことができる。
而して、上記の分包薬品包装体は、本発明に係る薬包紙を構成する積層体が、3g/m2 ・day以下の透湿度を有し、防湿性を著しく改良すると共に酸素ガスバリア性等にも優れ、更に、手切れ性(引き裂き性)、印刷適性、製袋性、その他等の特性を有することから、環境面、コスト面、ガスバリア性等を著しく改良した薬包紙およびそれを使用して製袋した分包袋を提供することができるものである。
次に、上記の本発明について実施例を挙げて更に具体的に説明する。
(蒸着条件)
蒸着チヤンバー内の真空度;2×10-4mbar
巻き取りチヤンバー内の真空度;2×10-2mbar
電子ビーム電力;25kw
フィルムの搬送速度;600m/min
(2).他方、粒度#60〜120の粒度分布を有するダイヤモンド粉をエポキシ樹脂をバインダ−として、直径5インチ、巾8mmの金属の外周面に塗布し、次いで、エポキシ樹脂を硬化させて、砥石ロ−ルを製造した。
次いで、上記で製造した砥石ロ−ルを使用し、これと受けロ−ルとの間に、上記で膜厚20nmの酸化アルミニウムの蒸着膜を形成した厚さ12μmの二軸延伸ポリエチレンテレフタレ−トフィルムを、その二軸延伸ポリエチレンテレフタレ−トフィルムの面が、砥石ロ−ルの面に対向するようにして通して圧接し、これにより粗面化加工処理を施し、上記の二軸延伸ポリエチレンテレフタレ−トフィルムに貫通しない多数の傷痕と貫通孔とが混在した易カット性部分を形成した。
(3).次に、上記の(1)で易カット性部分を形成した二軸延伸ポリエチレンテレフタレ−トフィルムの酸化アルミニウムの蒸着膜の面に、2液硬化型のポリウレタン系ラミネ−ト用接着剤をグラビアロ−ルコ−ト法を用いて厚さ4.0g/m2 (乾燥状態)にコ−ティングしてラミネ−ト用接着剤層を形成し、次いで、該ラミネ−ト用接着剤層の面に、厚さ20μmの低密度ポリエチレンフィルムをドライラミネ−トして積層して、本発明に係る薬包紙を製造した。
(4).次に、上記で製造した薬包紙を使用し、その低密度ポリエチレンフィルムの面を内面になるようにして対向させ、かつ、二軸延伸ポリエチレンテレフタレ−トフィルムに貫通しない多数の傷痕と貫通孔とが混在した易カット性部分を相互に対向するように重ね合わせ、しかる後、その重なり合った易カット性部分をヒ−トシ−ルし、更に、底部に相当する外周端部の部分の端部もヒ−トシ−ルしてシ−ル部を形成し、その上方に開口部を有する三方シ−ル型の軟包装用袋からなる分包袋を製造した。
次いで、上記で製造した三方シ−ル型の軟包装用袋からなる分包袋内に、その開口部から粉末状の医薬を充填包装し、しかる後、その開口部をヒ−トシ−ルし、上方シ−ル部を形成して分包薬品包装体を製造した。
上記で製造した分包薬品包装体は、防湿性を著しく改良すると共に酸素ガスバリア性等にも優れ、更に、手切れ性(引き裂き性)、製袋性、その他等の特性を有し、環境面、コスト面、ガスバリア性等を著しく改良することができた。
(蒸着条件)
蒸着チヤンバー内の真空度;2×10-4mbar
巻き取りチヤンバー内の真空度;2×10-2mbar
電子ビーム電力;25kw
フィルムの搬送速度;600m/min
(2).他方、粒度#60〜120の粒度分布を有するダイヤモンド粉をエポキシ樹脂をバインダ−として、直径5インチ、巾8mmの金属の外周面に塗布し、次いで、エポキシ樹脂を硬化させて、砥石ロ−ルを製造した。
次いで、上記で製造した砥石ロ−ルを使用し、これと受けロ−ルとの間に、上記で膜厚20nmの酸化アルミニウムの蒸着膜を形成した厚さ12μmの二軸延伸ポリエチレンテレフタレ−トフィルムを、その二軸延伸ポリエチレンテレフタレ−トフィルムの面が、砥石ロ−ルの面に対向するようにして通して圧接し、これにより粗面化加工処理を施し、上記の二軸延伸ポリエチレンテレフタレ−トフィルムに貫通しない多数の傷痕と貫通孔とが混在した易カット性部分を形成した。
(3).次に、上記の(1)で易カット性部分を形成した二軸延伸ポリエチレンテレフタレ−トフィルムの酸化アルミニウムの蒸着膜の面に、2液硬化型のポリウレタン系ラミネ−ト用接着剤をグラビアロ−ルコ−ト法を用いて厚さ4.0g/m2 (乾燥状態)にコ−ティングしてラミネ−ト用接着剤層を形成し、次いで、該ラミネ−ト用接着剤層の面に、厚さ20μmの低密度ポリエチレンフィルムをドライラミネ−トして積層して、本発明に係る薬包紙を製造した。
(4).次に、上記で製造した薬包紙を使用し、その低密度ポリエチレンフィルムの面を内面となるように対向させ、かつ、二軸延伸ポリエチレンテレフタレ−トフィルムに貫通しない多数の傷痕と貫通孔とが混在した易カット性部分を相互に対向するように重ね合わせ、しかる後、その重なり合った易カット性部分をヒ−トシ−ルし、更に、底部に相当する外周端部の部分の端部もヒ−トシ−ルしてシ−ル部を形成し、その上方に開口部を有する三方シ−ル型の軟包装用袋からなる分包袋を製造した。
次いで、上記で製造した三方シ−ル型の軟包装用袋からなる分包袋内に、その開口部から粉末状の医薬を充填包装し、しかる後、その開口部をヒ−トシ−ルして上方シ−ル部を形成して分包薬品包装体を製造した。
上記で製造した分包薬品包装体は、防湿性を著しく改良すると共に酸素ガスバリア性等にも優れ、更に、手切れ性(引き裂き性)、製袋性、その他等の特性を有し、環境面、コスト面、ガスバリア性等を著しく改良することができた。
(蒸着条件)
蒸着チヤンバー内の真空度;2×10-4mbar
巻き取りチヤンバー内の真空度;2×10-2mbar
電子ビーム電力;25kw
フィルムの搬送速度;600m/min
(2).他方、粒度#60〜120の粒度分布を有するダイヤモンド粉をエポキシ樹脂をバインダ−として、直径5インチ、巾8mmの金属の外周面に塗布し、次いで、エポキシ樹脂を硬化させて、砥石ロ−ルを製造した。
次いで、上記で製造した砥石ロ−ルを使用し、これと受けロ−ルとの間に、上記で膜厚20nmの酸化アルミニウムの蒸着膜を形成した厚さ12μmの二軸延伸ポリエチレンテレフタレ−トフィルムを、その二軸延伸ポリエチレンテレフタレ−トフィルムの面が、砥石ロ−ルの面に対向するようにして通して圧接し、これにより粗面化加工処理を施し、上記の二軸延伸ポリエチレンテレフタレ−トフィルムに貫通しない多数の傷痕と貫通孔とが混在した易カット性部分を形成した。
(3).次に、上記の(1)で易カット性部分を形成した二軸延伸ポリエチレンテレフタレ−トフィルムの酸化アルミニウムの蒸着膜の面に、2液硬化型のポリウレタン系ラミネ−ト用接着剤をグラビアロ−ルコ−ト法を用いて厚さ4.0g/m2 (乾燥状態)にコ−ティングしてラミネ−ト用接着剤層を形成し、次いで、該ラミネ−ト用接着剤層の面に、厚さ20μmの低密度ポリエチレンフィルムをドライラミネ−トして積層して、本発明に係る薬包紙を製造した。
(4).次に、上記で製造した薬包紙を使用し、その低密度ポリエチレンフィルムの面を内面となるように対向させ、かつ、二軸延伸ポリエチレンテレフタレ−トフィルムに貫通しない多数の傷痕と貫通孔とが混在した易カット性部分を相互に対向するように重ね合わせ、しかる後、その重なり合った易カット性部分をヒ−トシ−ルし、更に、底部に相当する外周端部の部分の端部もヒ−トシ−ルしてシ−ル部を形成し、その上方に開口部を有する三方シ−ル型の軟包装用袋からなる分包袋を製造した。
次いで、上記で製造した三方シ−ル型の軟包装用袋からなる分包袋内に、その開口部から粉末状の医薬を充填包装し、しかる後、その開口部をヒ−トシ−ルして上方シ−ル部を形成して分包薬品包装体を製造した。
上記で製造した分包薬品包装体は、防湿性を著しく改良すると共に酸素ガスバリア性等にも優れ、更に、手切れ性(引き裂き性)、製袋性、その他等の特性を有し、環境面、コスト面、ガスバリア性等を著しく改良することができた。
(蒸着条件)
蒸着チヤンバー内の真空度;2×10-4mbar
巻き取りチヤンバー内の真空度;2×10-2mbar
電子ビーム電力;25kw
フィルムの搬送速度;600m/min
しかる後、更に、もう一機のマグネトロンスパッタリング装置を使用し、酸素ガス1000sccmを導入して、出力5kWでプラズマ処理を行って、上記の酸化アルミニウムの蒸着膜の面に、酸素ガスによるプラズマ処理面を形成して巻き取った。
(2).他方、粒度#60〜120の粒度分布を有するダイヤモンド粉をエポキシ樹脂をバインダ−として、直径5インチ、巾8mmの金属の外周面に塗布し、次いで、エポキシ樹脂を硬化させて、砥石ロ−ルを製造した。
次いで、上記で製造した砥石ロ−ルを使用し、これと受けロ−ルとの間に、上記で膜厚20nmの酸化アルミニウムの蒸着膜を形成した厚さ12μmの二軸延伸ポリエチレンテレフタレ−トフィルムを、その二軸延伸ポリエチレンテレフタレ−トフィルムの面が、砥石ロ−ルの面に対向するようにして通して圧接し、これにより粗面化加工処理を施し、上記の二軸延伸ポリエチレンテレフタレ−トフィルムに貫通しない多数の傷痕と貫通孔とが混在した易カット性部分を形成した。
(3).次に、上記の(1)で易カット性部分を形成した二軸延伸ポリエチレンテレフタレ−トフィルムの酸化アルミニウムの蒸着膜の酸素ガスによるプラズマ処理面の面に、2液硬化型のポリウレタン系ラミネ−ト用接着剤をグラビアロ−ルコ−ト法を用いて厚さ4.0g/m2 (乾燥状態)にコ−ティングしてラミネ−ト用接着剤層を形成し、次いで、該ラミネ−ト用接着剤層の面に、厚さ20μmの低密度ポリエチレンフィルムをドライラミネ−トして積層して、本発明に係る薬包紙を製造した。
(4).次に、上記で製造した薬包紙を使用し、その低密度ポリエチレンフィルムの面を内面となるように対向させ、かつ、二軸延伸ポリエチレンテレフタレ−トフィルムに貫通しない多数の傷痕と貫通孔とが混在した易カット性部分を相互に対向するように重ね合わせ、しかる後、その重なり合った易カット性部分をヒ−トシ−ルし、更に、底部に相当する外周端部の部分の端部もヒ−トシ−ルしてシ−ル部を形成し、その上方に開口部を有する三方シ−ル型の軟包装用袋からなる分包袋を製造した。
次いで、上記で製造した三方シ−ル型の軟包装用袋からなる分包袋内に、その開口部から粉末状の医薬を充填包装し、しかる後、その開口部をヒ−トシ−ルして上方シ−ル部を形成して分包薬品包装体を製造した。
上記で製造した分包薬品包装体は、防湿性を著しく改良すると共に酸素ガスバリア性等にも優れ、更に、手切れ性(引き裂き性)、製袋性、その他等の特性を有し、環境面、コスト面、ガスバリア性等を著しく改良することができた。
(蒸着条件)
蒸着チヤンバー内の真空度;2×10-4mbar
巻き取りチヤンバー内の真空度;2×10-2mbar
電子ビーム電力;25kw
フィルムの搬送速度;600m/min
しかる後、更に、もう一機のマグネトロンスパッタリング装置を使用し、酸素ガス1000sccmを導入して、出力5kWでプラズマ処理を行って、上記の酸化アルミニウムの蒸着膜の面に、酸素ガスによるプラズマ処理面を形成して巻き取った。
(2).次に、上記の(1)で形成した酸素ガスによるプラズマ処理面の面に、2液硬化型のポリウレタン系ラミネ−ト用接着剤をグラビアロ−ルコ−ト法を用いて厚さ4.0g/m2 (乾燥状態)にコ−ティングしてラミネ−ト用接着剤層を形成し、次いで、該ラミネ−ト用接着剤層の面に、厚さ20μmの低密度ポリエチレンフィルムをドライラミネ−トして積層して、本発明に係る積層体を製造した。
(3).他方、粒度#60〜120の粒度分布を有するダイヤモンド粉をエポキシ樹脂をバインダ−として、直径5インチ、巾8mmの金属の外周面に塗布し、次いで、エポキシ樹脂を硬化させて、砥石ロ−ルを製造した。
次いで、上記で製造した砥石ロ−ルを使用し、これと受けロ−ルとの間に、上記で製造した積層体を、それを構成する二軸延伸ポリエチレンテレフタレ−トフィルムの面が、砥石ロ−ルの面に対向するようにして通して圧接し、これにより粗面化加工処理を施し、上記の積層体を構成する二軸延伸ポリエチレンテレフタレ−トフィルムに貫通しない多数の傷痕と貫通孔とが混在した易カット性部分を形成して、本発明に係る薬包紙を製造した。 (4).次に、上記で製造した薬包紙を使用し、その低密度ポリエチレンフィルムの面を内面となるように対向させ、かつ、積層体を構成する二軸延伸ポリエチレンテレフタレ−トフィルムに貫通しない多数の傷痕と貫通孔とが混在した易カット性部分を相互に対向するように重ね合わせ、しかる後、その重なり合った易カット性部分をヒ−トシ−ルし、更に、底部に相当する外周端部の部分の端部もヒ−トシ−ルしてシ−ル部を形成し、その上方に開口部を有する三方シ−ル型の軟包装用袋からなる分包袋を製造した。
次いで、上記で製造した三方シ−ル型の軟包装用袋からなる分包袋内に、その開口部から粉末状の医薬を充填包装し、しかる後、その開口部をヒ−トシ−ルして上方シ−ル部を形成して分包薬品包装体を製造した。
上記で製造した分包薬品包装体は、防湿性を著しく改良すると共に酸素ガスバリア性等にも優れ、更に、手切れ性(引き裂き性)、製袋性、その他等の特性を有し、環境面、コスト面、ガスバリア性等を著しく改良することができた。
(蒸着条件)
蒸着チヤンバー内の真空度;2×10-4mbar
巻き取りチヤンバー内の真空度;2×10-2mbar
電子ビーム電力;25kw
フィルムの搬送速度;600m/min
しかる後、更に、もう一機のマグネトロンスパッタリング装置を使用し、酸素ガス1000sccmを導入して、出力5kWでプラズマ処理を行って、上記の酸化アルミニウムの蒸着膜の面に、酸素ガスによるプラズマ処理面を形成して巻き取った。
(2).他方、粒度#60〜120の粒度分布を有するダイヤモンド粉をエポキシ樹脂をバインダ−として、直径5インチ、巾8mmの金属の外周面に塗布し、次いで、エポキシ樹脂を硬化させて、砥石ロ−ルを製造した。
次いで、上記で製造した砥石ロ−ルを使用し、これと受けロ−ルとの間に、上記で膜厚20nmの酸化アルミニウムの蒸着膜を形成した厚さ12μmの二軸延伸ポリエチレンテレフタレ−トフィルムを、その二軸延伸ポリエチレンテレフタレ−トフィルムの面が、砥石ロ−ルの面に対向するようにして通して圧接し、これにより粗面化加工処理を施し、上記の二軸延伸ポリエチレンテレフタレ−トフィルムに貫通しない多数の傷痕と貫通孔とが混在した易カット性部分を形成した。
(3).次に、上記の(1)で易カット性部分を形成した二軸延伸ポリエチレンテレフタレ−トフィルムの酸化アルミニウムの蒸着膜の酸素ガスによるプラズマ処理面の面に、2液硬化型のポリウレタン系ラミネ−ト用接着剤をグラビアロ−ルコ−ト法を用いて厚さ4.0g/m2 (乾燥状態)にコ−ティングしてラミネ−ト用接着剤層を形成し、次いで、該ラミネ−ト用接着剤層の面に、帯電防止剤を含有する厚さ20μmの低密度ポリエチレンフィルムをドライラミネ−トして積層して、本発明に係る薬包紙を製造した。
(4).次に、上記で製造した薬包紙を使用し、その低密度ポリエチレンフィルムの面を内面となるように対向させ、かつ、二軸延伸ポリエチレンテレフタレ−トフィルムに貫通しない多数の傷痕と貫通孔とが混在した易カット性部分を相互に対向するように重ね合わせ、しかる後、その重なり合った易カット性部分をヒ−トシ−ルし、更に、底部に相当する外周端部の部分の端部もヒ−トシ−ルしてシ−ル部を形成し、その上方に開口部を有する三方シ−ル型の軟包装用袋からなる分包袋を製造した。
次いで、上記で製造した三方シ−ル型の軟包装用袋からなる分包袋内に、その開口部から粉末状の医薬を充填包装し、しかる後、その開口部をヒ−トシ−ルして上方シ−ル部を形成して分包薬品包装体を製造した。
上記で製造した分包薬品包装体は、防湿性を著しく改良すると共に酸素ガスバリア性等にも優れ、更に、手切れ性(引き裂き性)、製袋性、その他等の特性を有し、環境面、コスト面、ガスバリア性等を著しく改良することができた。
上記の実施例1において、基材フィルムとして、厚さ12μmの二軸延伸ポリエチレンテレフタレ−トフィルムを使用する代わりに、厚さ26μmの防湿セロハンを使用し、その他は、上記の実施例1と同様にして、同様に、薬包紙、分包袋、分包薬品包装体を製造した。
上記の実施例1において、基材フィルムとして、厚さ12μmの二軸延伸ポリエチレンテレフタレ−トフィルムを使用する代わりに、厚さ26μmのKコ−トセロハンを使用し、その他は、上記の実施例1と同様にして、同様に、薬包紙、分包袋、分包薬品包装体を製造した。
次に、上記の実施例1〜6、および、比較例1〜2において製造した薬包紙、および、それを使用して製袋した分包袋、分包薬品包装体等について、第1および第2の水蒸気透過度、引き裂き性、および、手切れ性等を測定した。
(1).第1の水蒸気透過度の測定
これは、薬包紙について、温度40℃、湿度100%RHの条件で、米国、モコン(MOCON)社製の測定機〔機種名、パ−マトラン(PERMATRAN3/31)〕を使用し、薬包紙を構成する基材フィルム側を水蒸気に向けてセッティングして測定した。
(2).第2の水蒸気透過度の測定
これは、分包袋について、その分包袋内に塩化カルシウム包装体を作成し、更に、その包装体を40℃、湿度90%の恒温恒湿器に入れ、重量増加量を経時で測定して、評価した。
(3).引き裂き性の測定
これは、薬包紙を使用し、そのヒ−トシ−ル性樹脂層の面を内面となるように対向させ、かつ、薬包紙を構成する基材フィルムに貫通しない多数の傷痕と貫通孔とが混在した易カット性部分を相互に対向するように重ね合わせ、しかる後、その重なり合った易カット性部分をヒ−トシ−ルし、シ−ル巾10mmからなるヒ−トシ−ル部を形成し、更に、そのヒ−トシ−ル部に、長さ5mmの切込み部を設け、而して、該切込み部より上下に引き裂いて、引き裂き強度測定機、テンシロンを使用し、その引き裂き強度を測定し、数値化して、易引き裂き性を評価した。
(4).手切れ性の測定
これは、上記と同様に、薬包紙を使用し、そのヒ−トシ−ル性樹脂層の面を内面となるように対向させ、かつ、薬包紙を構成する基材フィルムに貫通しない多数の傷痕と貫通孔とが混在した易カット性部分を相互に対向するように重ね合わせ、しかる後、その重なり合った易カット性部分をヒ−トシ−ルし、シ−ル巾10mmからなるヒ−トシ−ル部を形成し、更に、そのヒ−トシ−ル部分を手に持って引き裂いて、触感による手切れ性を確認して評価した。
上記の測定結果について、下記の表1に示す。
┌────┬────────┬───────────────┐ │ │ 薬包紙 │ 薬包紙・分包袋 │ │ ├────────┼───────┬───────┤ │ │ 水蒸気透過度 │ 引き裂き性 │ 手切れ性 │ ├────┼────────┼───────┼───────┤ │実施例1│ 1.2 │ 201 │ ○ │ ├────┼────────┼───────┼───────┤ │実施例2│ 1.5 │ 113 │ ◎ │ ├────┼────────┼───────┼───────┤ │実施例3│ 1.9 │ 240 │ ◎ │ ├────┼────────┼───────┼───────┤ │実施例4│ 1.3 │ 180 │ ◎ │ ├────┼────────┼───────┼───────┤ │実施例5│ 1.2 │ 176 │ ○ │ ├────┼────────┼───────┼───────┤ │実施例6│ 1.5 │ 120 │ ◎ │ ├────┼────────┼───────┼───────┤ │比較例1│ 88.6 │ 91 │ ◎ │ ├────┼────────┼───────┼───────┤ │比較例2│ 10.4 │ 87 │ ◎ │ └────┴────────┴───────┴───────┘
┌────┬───────────────────────────────┐ │ │ 分包袋:塩化カルシウム増加量 │ │ ├───────┬───────┬───────┬───────┤ │ │ 3日後 │ 7日後 │ 14日後 │ 28日後 │ ├────┼───────┼───────┼───────┼───────┤ │実施例1│ 0.096 │ 0.245 │ 0.501 │ 1.120 │ ├────┼───────┼───────┼───────┼───────┤ │実施例2│ 0.123 │ 0.315 │ 0.644 │ 1.344 │ ├────┼───────┼───────┼───────┼───────┤ │実施例3│ 0.150 │ 0.371 │ 0.770 │ 1.624 │ ├────┼───────┼───────┼───────┼───────┤ │実施例4│ 0.095 │ 0.222 │ 0.483 │ 1.050 │ ├────┼───────┼───────┼───────┼───────┤ │実施例5│ 0.105 │ 0.238 │ 0.511 │ 1.210 │ ├────┼───────┼───────┼───────┼───────┤ │実施例6│ 0.130 │ 0.332 │ 0.662 │ 1.350 │ ├────┼───────┼───────┼───────┼───────┤ │比較例1│ 7.81 │18.97 │40.32 │81.24 │ ├────┼───────┼───────┼───────┼───────┤ │比較例2│ 0.87 │ 2.17 │ 4.93 │ 9.85 │ └────┴───────┴───────┴───────┴───────┘ 上記の表1において、水蒸気透過度の単位は、[g/m2 /day・40℃・100%RH]であり、塩化カルシウム増加量の単位は、[g]であり、引き裂き性の単位は、[gf]である。
また、上記の表1において、手切れ性の欄中、◎は、極めて良好、○は、良好、×は、不良を表す。
これに対し、比較例1〜2にかかるものは、水蒸気透過度、引き裂き性等において劣るものであった。
B 分包袋
C 分包薬品包装体
1 2軸延伸ポリエステル系樹脂フィルム
2 無機酸化物の薄膜 2a バリア層
3 ヒ−トシ−ル性樹脂層
4 積層体
5 貫通しない傷痕および/または貫通孔
11、13 ヒ−トシ−ル部
12 錠剤あるいは粉末状の薬品
Claims (6)
- 易引き裂き性2軸延伸ポリエステル系樹脂フィルムの一方の面に、不活性ガスによるプラズマ処理面を施すことにより、プラズマ放電処理後のプラズマ処理面の表面粗さは、2乗平均粗さ、Raで1nm以上1.5nm以下であり、また、算術平均粗さ、Rmsで1nm以上1.5nm以下であり、更に、最大高さ、Rmaxで10nm以上15nm以下であり、かつ、表面張力が60dyne/cm以上からなるプラズマ処理面を形成し、
次いで、上記の易引き裂き性2軸延伸ポリエステル系樹脂フィルムの一方の面に、上記のプラズマ処理面を介して、無機酸化物の薄膜からなるバリア層を設け、
更に、上記のバリア層の面に、ヒ−トシ−ル性樹脂層を設けた積層体からなり、
更に、上記の積層体が、該積層体を構成する、無機酸化物の薄膜からなるバリア層を有する2軸延伸ポリエステル系樹脂フィルムが、製袋時のヒ−トシ−ル部に相当する箇所に、貫通しない傷痕および/または貫通孔を有し、
かつ、積層体が、3g/m2 ・day以下の透湿度を有することを特徴とする薬包紙。 - 易引き裂き性2軸延伸ポリエステル系樹脂フィルムが、易引き裂き性2軸延伸ポリエチレンテレフタレ−トフィルムまたは易引き裂き性2軸延伸ポリブチレンテレフタレ−トフィルムからなることを特徴とする上記の請求項1に記載する薬包紙。
- 易引き裂き性2軸延伸ポリエステル系樹脂フィルムが、帯電防止コ−ト層を有することを特徴とする上記の請求項1〜2のいずれか1項に記載する薬包紙。
- 無機酸化物の薄膜からなるバリア層が、物理気相成長法による酸化アルミニウムの蒸着膜からなることを特徴とする上記の請求項1〜3のいずれか1項に記載する薬包紙。
- 無機酸化物の薄膜からなるバリア層が、その他方の面に、酸素ガスによるプラズマ処理面を有することを特徴とする上記の請求項1〜4のいずれか1項に記載する薬包紙。
- ヒ−トシ−ル性樹脂層が、帯電防止剤を含有することを特徴とする上記の請求項1〜5のいずれか1項に記載する薬包紙。