JP3909342B2 - スパッタリングターゲット並びに光情報記録媒体及びその製造方法 - Google Patents

スパッタリングターゲット並びに光情報記録媒体及びその製造方法 Download PDF

Info

Publication number
JP3909342B2
JP3909342B2 JP2006510380A JP2006510380A JP3909342B2 JP 3909342 B2 JP3909342 B2 JP 3909342B2 JP 2006510380 A JP2006510380 A JP 2006510380A JP 2006510380 A JP2006510380 A JP 2006510380A JP 3909342 B2 JP3909342 B2 JP 3909342B2
Authority
JP
Japan
Prior art keywords
recording medium
optical information
information recording
sputtering target
thin film
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
JP2006510380A
Other languages
English (en)
Other versions
JPWO2005083150A1 (ja
Inventor
英生 高見
政隆 矢作
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Nippon Mining Holdings Inc
Original Assignee
Nippon Mining and Metals Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Nippon Mining and Metals Co Ltd filed Critical Nippon Mining and Metals Co Ltd
Application granted granted Critical
Publication of JP3909342B2 publication Critical patent/JP3909342B2/ja
Publication of JPWO2005083150A1 publication Critical patent/JPWO2005083150A1/ja
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Description

技術分野
［０００１］本発明は、スパッタ膜の非晶質性が安定であり、記録層との密着性、機械特性に優れ、かつ透過率が高く、また非硫化物系で構成されているため、隣接する反射層、記録層の劣化が生じ難い光情報記録媒体用薄膜（特に保護膜としての使用）及びその製造方法並びにこれらに適用できるパッタリングターゲットに関する。
背景技術
［０００２］従来、主として相変化型の光情報記録媒体の保護層に一般的に使用されるZnS−SiO2は、光学特性、熱特性、記録層との密着性等において、優れた特性を有し、広く使用されている。
しかし、今日Blue-Rayに代表される書き換え型ＤＶＤは、さらに書き換え回数の増加、大容量化、高速記録化が強く求められている。
［０００３］光情報記録媒体の書き換え回数等が劣化する原因の一つとして、保護層ZnS−SiO2に挟まれるように配置された記録層材への、ZnS−SiO2からの硫黄成分の拡散が挙げられる。
また、大容量化、高遠記録化のため高反射率で高熱伝導特性を有する純AgまたはAg合金が反射層材に使用されるようになったが、このような反射層も保護層材であるZnS−SiO2と接するように配置されている。
したがって、この場合も同様に、ZnS−SiO2からの硫黄成分の拡散により、純AgまたはAg合金反射層材も腐食劣化して、光情報記録媒体の反射率等の特性劣化を引き起こす要因となっていた。
［０００４］これら硫黄成分の拡散防止対策として、反射層と保護層、記録層と保護層の間に、窒化物や炭化物を主成分とした中間層を設けた構成にすることも行なわれている。しかし、これは積層数の増加となり、スループット低下、コスト増加になるという問題を発生している。
上記のような問題を解決するため、保護層材に硫化物を含まない酸化物のみの材料へと置き換え、ZnS−SiO2と同等以上の光学特性、非晶質安定性を有する材料系を見出すことが急務となっていた。
［０００５］以上のようなことから、酸化物系保護層材、透明導電材あるいは光学薄膜が提案されている（特許文献１−３参照）。
しかし、特許文献１−３は、光学特性及び非晶質性が劣る領域を含む問題があった。
特許文献１：特開平０１−３１７１６７号公報
特許文献２：特開２０００−９０７４５号公報
特許文献３：特開２００３−１６６０５２号公報
発明の開示
発明が解決しようとする課題
［０００６］本発明は、膜の非晶質性が安定であり、記録層との密着性、機械特性に優れ、且つ透過率が高く、非硫化物系で構成することにより、隣接する反射層、記録層の劣化が生じ難い光情報記録媒体用薄膜（特に保護膜としての使用）及びその製造方法並びにこれらに適用できるパッタリングターゲットに関するものであり、これによって、光情報記録媒体の特性の向上を大幅に改善することを目的とする。
課題を解決するための手段
［０００７］上記の課題を解決するために、本発明者らは鋭意研究を行った結果、従来の保護層材ZnS−SiO2を、下記に提示する硫化物を含まない酸化物のみの材料へと置き換え、かつZnS−SiO2と同等の光学特性及び非晶質安定性を確保し、光情報記録媒体の特性改善が可能であるとの知見を得た。
［０００８］本発明はこの知見に基づき、１）HfO2及びY2O3の複合酸化物からなることを特徴とするスパッタリングターゲット、２）Y2O3の含有量が10〜95mol％、残部HfO2であることを特徴とする１記載のスパッタリングターゲット、３）さらに、ZrO2を10〜90mol％含有することを特徴とする１又は２記載のスパッタリングターゲットを提供する。
［０００９］また、本発明は、４）相対密度が90%以上であることを特徴とする１〜３のいずれかに記載のスパッタリングターゲット、５）上記１〜４のいずれかに記載のスパッタリングターゲットを使用して、少なくとも薄膜として光情報記録媒体構造の一部を形成することを特徴とする光情報記録媒体及びその製造方法、６）上記１〜５のいずれかに記載のスパッタリングターゲットを使用して、少なくとも薄膜として光情報記録媒体の構造の一部を形成し、且つ記録層又は反射層と隣接して配置されていることを特徴とする光情報記録媒体及びその製造方法を提供する。
発明の効果
［００１０］上記によって、従来の保護層材ZnS−SiO2を、硫化物を含まない酸化物のみの材料へと置き換えることによって、隣接する反射層、記録層等への硫黄による劣化を抑制すると共に、ZnS−SiO2と同等又はそれ以上の光学特性及び非晶質安定性を備え、記録層との密着性、機械特性に優れ、且つ透過率が高いという優れた特性を持つ光情報記録媒体用薄膜（特に保護膜としての使用）及びその製造方法並びにこれらに適用できるパッタリングターゲットを提供できる。
また、本材料系を使用することにより、光情報記録媒体の特性改善が可能となるという優れた効果を有する。
発明を実施するための最良の形態
［００１１］本発明のスパッタリングターゲットは、HfO2及びY2O3の複合酸化物からなる。特に、Y2O3の含有量は10〜95mol％とし、残部HfO2とする。Y2O3の含有量10mol％未満及びY2O3の含有量95mol％を超えると、非晶質性安定性に欠けるという問題があるからである。
さらに、ZrO2を10〜90mol％添加することができる。ZrO2は熱伝導率が高いという特性を持つ。この特性を活かして、ZrO2を付加的に添加する場合には、10〜90mol％添加するのが望ましい。ZrO210mol％未満では添加の効果がなく、またZrO290mol％を超えると非晶質性安定に欠けるという問題が生ずるので、添加する場合には、上記の範囲とするのが好ましい。
［００１２］この材料は、光学特性及び膜の非晶質性が安定しており、相変化型光記録媒体の保護層材に適している。成膜には、高周波スパッタリングを使用する。
本材料は、上記の通り非晶質性が安定し、透過率を向上させることが出来るため、書換え速度の速い相変化記録媒体や青色レーザー系の相変化記録媒体用保護層材に適する。
［００１３］また、本発明のスパッタリングターゲットは、相対密度が90％以上とすることが可能である。密度の向上は、スパッタ膜の均一性を高め、またスパッタリング時のパーティクルの発生を抑制できる効果を有する。
上記に述べるスパッタリングターゲットを使用して、少なくとも薄膜として光情報記録媒体構造の一部を形成する光情報記録媒体を提供することができる。さらに、上記スパッタリングターゲットを使用して、少なくとも薄膜として光情報記録媒体の構造の一部を形成し、且つ記録層又は反射層と隣接して配置されている光情報記録媒体を作製することができる。
［００１４］さらに、本発明のスパッタリングターゲットを使用して形成された薄膜は、光情報記録媒体の構造の一部を形成し、記録層又は反射層と隣接して配置されるが、上記の通り、ZnSを使用していないので、Ｓによる汚染がなく、保護層に挟まれるように配置された記録層材への硫黄成分の拡散がなくなり、これによる記録層の劣化がなくなるという著しい効果がある。
また、大容量化、高速記録化のため、高反射率で高熱伝導特性を有する純AgまたはAg合金が反射層材に便用されるようになったが、この隣接する反射層への硫黄成分の拡散も無くなり、同様に反射層材が腐食劣化して、光情報記録媒体の反射率等の特性劣化を引き起こす原因が一掃されるという優れた効果を有する。
［００１５］本発明のスパッタリングターゲットは、平均粒径が５μｍ以下である各構成元素の酸化物粉末を、常圧焼結又は高温加圧焼結することによって製造することができる。これによって、相対密度が90％以上を有するスパッタリングターゲットが得られる。この場合、焼結前に酸化ハフニウム及び酸化イットリウムを主成分とした酸化物粉末を、800〜1400℃で仮焼することが望ましい。この仮焼後、３μｍ以下に粉砕して焼結用の原料とする。
［００１６］さらに、本発明のスパッタリングターゲットを使用することにより、生産性が向上し、品質の優れた材料を得ることができ、光ディスク保護膜をもつ光記録媒体を低コストで安定して製造できるという著しい効果がある。
本発明のスパッタリングターゲットの密度向上は、空孔を減少させ結晶粒を微細化し、ターゲットのスパッタ面を均一かつ平滑にすることができるので、スパッタリング時のパーティクルやノジュールを低減させ、さらにターゲットライフも長くすることができるという著しい効果を有し、品質のばらつきが少なく量産性を向上させることができる。
実施例
［００１７］以下、実施例および比較例に基づいて説明する。なお、本実施例はあくまで一例であり、この例によって何ら制限されるものではない。すなわち、本発明は特許請求の範囲によってのみ制限されるものであり、本発明に含まれる実施例以外の種々の変形を包含するものである。
［００１８］（実施例１−６）
４Ｎ相当で５μｍ以下のY2O3粉及び３Ｎ相当で平均粒径５μｍ以下のZrO2粉及びHfO2粉を準備し、表１に示す組成となるように調合して、湿式混合し、乾燥後、1100℃で仮焼した。
さらに、この仮焼粉を平均粒径１μｍ相当まで湿式微粉砕した後、バインダーを添加してスプレードライヤーで造粒した。この造粒粉を冷間で加圧成形し、酸素雰囲気、1300〜1600℃で常圧焼結し、この焼結材を機械加工でターゲット形状に仕上げた。このターゲットの成分組成を表１に示す。
［００１９］［表１］
Figure 0003909342
［００２０］上記の仕上げ加工した６インチφサイズのターゲットを使用して、スパッタリングを行った。スパッタ条件は、ＲＦスパッタ、スパッタパワー1000Ｗ、Arガス圧0.5Paとし、目標膜厚1500Åで成膜した。
成膜サンプルの透過率（波長633nm）％、屈折率（波長633nm）、非晶質性（成膜サンプルのアニール処理（600℃×30min、Ar雰囲気）を施した、ＸＲＤ（Cu−Ｋα、40kV、30mA）による測定における２θ＝20−60°の範囲の未成膜ガラス基板に対する最大ピーク強度で表した）の測定した結果等を、まとめて表１に示す。
［００２１］以上の結果、実施例１−６のスパッタリングターゲットは、相対密度は90以上に達し、安定したＲＦスパッタができた。
また、スパッタ膜の透過率は、96〜98％（405μｍ）に達し、屈折率は1.9〜2.1であり、また特定の結晶ピークは見られず、安定した非晶質性（1.0〜1.1）を有していた。
さらに、本実施例のターゲットは、ZnSを使用していないので、硫黄の拡散・汚染による光情報記録媒体の特性劣化は生じない。また、後述する比較例に比べて、成膜サンプルの透過率、屈折率、非晶質の安定性が、いずれも良好な値を示した。
［００２２］（比較例１−６）
表１に示すように、本願発明の条件とは異なる原料粉の成分及び組成比の材料、特に比較例６においてはZnS原料粉を準備し、これを実施例と同様の条件で、ターゲットを作製し、かつこのターゲットを用いてスパッタ膜を形成した。
この結果を、同様に表１に示す。
［００２３］木発明の組成比から逸脱する比較例の成分・組成、例えば比較例１については、Ｙ酸化物が全く含有されていないため、また非晶質性が1.9と悪い結果となった。
比較例２は、同様にＹ酸化物量ないために、非晶質性が2.3と悪い結果となった。比較例３については、Ｙ酸化物単独であるために、同様に非晶質性が2.5と悪い結果となった。
比較例４については、Zr酸化物とＹ酸化物量との組合せで、Ｙ酸化物量の基準量よりも少なく、同様に非晶質性が2.1と悪い結果となった。
比較例５については、Hf酸化物とＹ酸化物量との組合せであるが、Ｙ酸化物量が基準量よりも少なく、同様に非晶質性が1.8と悪い結果となった。
また、特に比較例６は、ZnSが多く含有されており、透過率が80％と低く、また硫黄による汚染の危険のある材料であった。
産業上の利用可能性
［００２４］本発明のスパッタリングターゲットを使用して形成された薄膜は、光情報記録媒体の構造の一部を形成し、ZnSを使用していないので、記録層材への硫黄成分の拡散がなくなり、これによる記録層の劣化がなくなるという著しい効果がある。また、隣接する高反射率で高熱伝導特性を有する純AgまたはAg合金を反射層に用いた場合には、該反射層への硫黄成分の拡散も無くなり、反射層が腐食劣化して特性劣化を引き起こす原因が一掃されるという優れた効果を有する。
さらに、非晶質性が安定化するとともにターゲットに導電性が付与され、相対密度を90％以上の高密度化によって、安定したＲＦスパッタ成膜を可能とする。そして、スパッタの制御性を容易にし、スパッタリング効率を向上させることができるという著しい効果がある。さらにまた、成膜の際にスパッタ時に発生するパーティクル（発塵）やノジュールを低減し、品質のばらつきが少なく量産性を向上させることができ、光ディスク保護膜をもつ光記録媒体を低コストで安定して製造できるという著しい効果がある。

Claims (10)

  1. HfO2及びY2O3の複合酸化物からなることを特徴とする光情報記録媒体薄膜形成用スパッタリングターゲット。
  2. Y2O3の含有量が10〜95mol％、残部HfO2であることを特徴とする請求項１記載の光情報記録媒体薄膜形成用スパッタリングターゲット。
  3. さらに、ZrO2を10〜90mol％含有することを特徴とする請求項１又は２記載の光情報記録媒体薄膜形成用スパッタリングターゲット。
  4. 相対密度が90％以上であることを特徴とする請求項１〜３のいずれかに記載の光情報記録媒体薄膜形成用スパッタリングターゲット。
  5. 光情報記録媒体構造の少なくとも一部に、スパッタリングにより形成されたHfO2及びY2O3の複合酸化物からなる薄膜を備えていることを特徴とする光情報記録媒体。
  6. Y2O3の合有量が10〜95mol％、残部HfO2であることを特徴とする請求項５記載の光情報記録媒体。
  7. さらに、ZrO2を10〜90mol％含有することを特徴とする請求項５又は６記載の光情報記録媒体。
  8. 前記薄膜が記録層又は反射層と隣接して配置されていることを特徴とする請求項５〜７のいずれかに記載の光情報記録媒体。
  9. 請求項１〜４のいずれかに記載のターゲットを使用して、スパッタリングにより、光情報記録媒体構造の少なくとも一部に薄膜を形成することを特徴とする光情報記録媒体の製造方法。
  10. 前記薄膜を記録層又は反射層と隣接して形成することを特徴とする請求項９記載の光情報記録媒体の製造方法。
JP2006510380A 2004-02-27 2005-01-26 スパッタリングターゲット並びに光情報記録媒体及びその製造方法 Expired - Fee Related JP3909342B2 (ja)