JP3339154B2 - 難燃性組成物及び電線、ケーブル - Google Patents
難燃性組成物及び電線、ケーブルInfo
- Publication number
- JP3339154B2 JP3339154B2 JP34144093A JP34144093A JP3339154B2 JP 3339154 B2 JP3339154 B2 JP 3339154B2 JP 34144093 A JP34144093 A JP 34144093A JP 34144093 A JP34144093 A JP 34144093A JP 3339154 B2 JP3339154 B2 JP 3339154B2
- Authority
- JP
- Japan
- Prior art keywords
- surface treatment
- retardant composition
- flame
- magnesium hydroxide
- cable
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Lifetime
Description
【０００１】
【産業上の利用分野】本発明は燃焼時にハロゲン化水素
ガスを発生せず、かつ吸湿性を抑えた難燃性組成物、及
び該難燃性組成物の被覆層を具えた電線、ケーブルに関
するものである。
ガスを発生せず、かつ吸湿性を抑えた難燃性組成物、及
び該難燃性組成物の被覆層を具えた電線、ケーブルに関
するものである。
【０００２】
【従来の技術】電線、ケーブルの燃焼時の発煙、毒性、
腐食等の二次災害を防止する目的から、例えば特開平1-
141929号公報に示されるように、被覆材に難燃性を付与
する難燃剤の一つとして、水酸化マグネシウムが使用さ
れている。
腐食等の二次災害を防止する目的から、例えば特開平1-
141929号公報に示されるように、被覆材に難燃性を付与
する難燃剤の一つとして、水酸化マグネシウムが使用さ
れている。
【０００３】
【発明が解決しようとする課題】従来から使用されてい
る水酸化マグネシウムは、海水中のマグネシウムを原料
とするものである。これを難燃剤として使用した難燃性
組成物は、高湿度空気中に放置すると水分を吸湿し、電
線、ケーブルに被覆する際、押出機内で吸湿した水分が
発泡し、外観不良になるという問題があった。
る水酸化マグネシウムは、海水中のマグネシウムを原料
とするものである。これを難燃剤として使用した難燃性
組成物は、高湿度空気中に放置すると水分を吸湿し、電
線、ケーブルに被覆する際、押出機内で吸湿した水分が
発泡し、外観不良になるという問題があった。
【０００４】
【課題を解決するための手段】本発明は上述の問題点を
解消し、吸湿性を抑えた難燃性組成物及びそれを用いた
電線、ケーブルを提供するもので、その特徴は、水酸化
マグネシウムを主成分とする天然鉱物を粉砕し、脂肪
酸、脂肪酸金属塩、シランカップリング剤、チタネート
カップリング剤より選ばれた少なくとも１種類を主成分
とする表面処理剤を、上記天然鉱物に対して0.5〜5重量
％添加して表面処理（ただし湿式表面処理を除く）を施
してプラスチック又はゴムに添加し難燃性を付与すると
ともに吸湿性を抑えた難燃性組成物及び該難燃性組成物
の被覆層を具えている電線、ケーブルにある。
解消し、吸湿性を抑えた難燃性組成物及びそれを用いた
電線、ケーブルを提供するもので、その特徴は、水酸化
マグネシウムを主成分とする天然鉱物を粉砕し、脂肪
酸、脂肪酸金属塩、シランカップリング剤、チタネート
カップリング剤より選ばれた少なくとも１種類を主成分
とする表面処理剤を、上記天然鉱物に対して0.5〜5重量
％添加して表面処理（ただし湿式表面処理を除く）を施
してプラスチック又はゴムに添加し難燃性を付与すると
ともに吸湿性を抑えた難燃性組成物及び該難燃性組成物
の被覆層を具えている電線、ケーブルにある。
【０００５】
【作用】上述の問題を解決するため、種々の水酸化マグ
ネシウムを用いて検討を行ったところ、水酸化マグネシ
ウムを主成分とする天然鉱物を原料とした水酸化マグネ
シウムが吸湿性を抑えるのにすぐれていることを見出し
た。このメカニズムに関しては不明であるが、結晶構造
等が従来品と異なっているためではないかと思われる。
なお、表面処理剤の添加量を 0.5〜５重量％と規定した
のは、 0.5重量％未満では表面処理の効果を示さず、５
重量％を越えるとコスト面で好ましくないからである。
ネシウムを用いて検討を行ったところ、水酸化マグネシ
ウムを主成分とする天然鉱物を原料とした水酸化マグネ
シウムが吸湿性を抑えるのにすぐれていることを見出し
た。このメカニズムに関しては不明であるが、結晶構造
等が従来品と異なっているためではないかと思われる。
なお、表面処理剤の添加量を 0.5〜５重量％と規定した
のは、 0.5重量％未満では表面処理の効果を示さず、５
重量％を越えるとコスト面で好ましくないからである。
【０００６】
【実施例】表１に示す各種材料を６インチオープンロー
ルで15分混練した後、ペレタイザーにて約３mm×３mm×
３mmのペレットに加工し、吸湿性を評価した。結果は表
１の通りである。
ルで15分混練した後、ペレタイザーにて約３mm×３mm×
３mmのペレットに加工し、吸湿性を評価した。結果は表
１の通りである。
【０００７】表面処理の方法は次のように行った。 （１）スーパーミキサー内で水酸化マグネシウムを攪拌
する。 （２）水酸化マグネシウムを攪拌しながら、表面処理剤
を約５分間にわたって徐々に投入する。 （３）表面処理剤を全量投入した後、さらに約20分間攪
拌する。
する。 （２）水酸化マグネシウムを攪拌しながら、表面処理剤
を約５分間にわたって徐々に投入する。 （３）表面処理剤を全量投入した後、さらに約20分間攪
拌する。
【０００８】用いたプラスチック材及び水酸化マグネシ
ウム表面処理剤の銘柄等は次の通りである。 ＥＥＡ：日本ユニカーＷＮ−１７０ 水酸化マグネシウム Ａ：従来（海水法）の水酸化マグネシウム 例、協和化学キスマ５ Ｂ：従来（海水法）の水酸化マグネシウム 例、協和化学キスマ５Ｂ Ｃ：天然鉱物（ブルーサイト）を原料としてシランカッ
プリング剤で表面処理した水酸化マグネシウム 例、神島化学マグシーズＮ−１ シランカップリング剤＝信越化学 添加量 0.1重量％ Ｄ：同上をシランカップリング剤で表面処理した水酸化
マグネシウム 例、シランカップリング剤＝信越化学 添加量＝ 0.5重
量％ Ｅ：同上を脂肪酸で表面処理した水酸化マグネシウム 脂肪酸＝ステアリン酸 添加量＝ 0.5重量％ Ｆ：同上を脂肪酸金属塩で表面処理した水酸化マグネシ
ウム 例、脂肪酸金属塩＝ステアリン酸亜鉛 添加量＝ 0.5重量％
ウム表面処理剤の銘柄等は次の通りである。 ＥＥＡ：日本ユニカーＷＮ−１７０ 水酸化マグネシウム Ａ：従来（海水法）の水酸化マグネシウム 例、協和化学キスマ５ Ｂ：従来（海水法）の水酸化マグネシウム 例、協和化学キスマ５Ｂ Ｃ：天然鉱物（ブルーサイト）を原料としてシランカッ
プリング剤で表面処理した水酸化マグネシウム 例、神島化学マグシーズＮ−１ シランカップリング剤＝信越化学 添加量 0.1重量％ Ｄ：同上をシランカップリング剤で表面処理した水酸化
マグネシウム 例、シランカップリング剤＝信越化学 添加量＝ 0.5重
量％ Ｅ：同上を脂肪酸で表面処理した水酸化マグネシウム 脂肪酸＝ステアリン酸 添加量＝ 0.5重量％ Ｆ：同上を脂肪酸金属塩で表面処理した水酸化マグネシ
ウム 例、脂肪酸金属塩＝ステアリン酸亜鉛 添加量＝ 0.5重量％
【０００９】
【表１】
【００１０】吸湿量の測定は以下のようにして行った。
ペレット 100ｇを上述の試料より採取し、湿度70％のデ
シケータ中に放置し、各時間毎の水分量を測定した。水
分量はカールフィッシャー水分計にて測定した。比較例
１，２に示す従来の水酸化マグネシウムを使用したもの
は、１日後でも水分量が約300ppmと多く、30日後では約
1400ppmまで増加した。比較例は天然鉱物を用い表面処
理を施した例であるが、表面処理剤の量が少ないため、
比較例１，２と同様の傾向を示した。これに対して、実
施例１〜３は１日後の水分量が約100ppm前後と少なく、
30日後でも 350〜400ppm程度までしか水分量が増えてお
らず、吸湿性が少ないことが確認できた。
ペレット 100ｇを上述の試料より採取し、湿度70％のデ
シケータ中に放置し、各時間毎の水分量を測定した。水
分量はカールフィッシャー水分計にて測定した。比較例
１，２に示す従来の水酸化マグネシウムを使用したもの
は、１日後でも水分量が約300ppmと多く、30日後では約
1400ppmまで増加した。比較例は天然鉱物を用い表面処
理を施した例であるが、表面処理剤の量が少ないため、
比較例１，２と同様の傾向を示した。これに対して、実
施例１〜３は１日後の水分量が約100ppm前後と少なく、
30日後でも 350〜400ppm程度までしか水分量が増えてお
らず、吸湿性が少ないことが確認できた。
【００１１】以上は材料としてＥＥＡを使用した場合を
示したが、エチレンプロピレンゴム、アクリルゴム、超
低密度ポリエチレン、直鎖状低密度ポリエチレン、エチ
レンビニルアセテート、エチレンメタアクリレート、エ
チレンメチルメタアクリレート等のゴム、プラスチック
材料においても、又これらの混合物に対しても同様の効
果が認められ、天然鉱物を原料とした水酸化マグネシウ
ムが吸湿性が少ないことが確認された。
示したが、エチレンプロピレンゴム、アクリルゴム、超
低密度ポリエチレン、直鎖状低密度ポリエチレン、エチ
レンビニルアセテート、エチレンメタアクリレート、エ
チレンメチルメタアクリレート等のゴム、プラスチック
材料においても、又これらの混合物に対しても同様の効
果が認められ、天然鉱物を原料とした水酸化マグネシウ
ムが吸湿性が少ないことが確認された。
【００１２】
【発明の効果】以上説明したように、本発明の難燃性組
成物によれば、吸湿性が少なく、電線、ケーブルの製造
時に特に乾燥工程を必要としないで、外観良好な電線、
ケーブルを作成することができる。
成物によれば、吸湿性が少なく、電線、ケーブルの製造
時に特に乾燥工程を必要としないで、外観良好な電線、
ケーブルを作成することができる。
Claims (2)
- 【請求項１】 水酸化マグネシウムを主成分とする天然
鉱物を粉砕し、脂肪酸、脂肪酸金属塩、シランカップリ
ング剤、チタネートカップリング剤より選ばれた少なく
とも１種類を主成分とする表面処理剤を、上記天然鉱物
に対して0.5〜5重量％添加して表面処理（ただし湿式表
面処理を除く）を施してプラスチック又はゴムに添加し
難燃性を付与するとともに吸湿性を抑えたことを特徴と
する難燃性組成物。 - 【請求項２】 請求項１記載の難燃性組成物の被覆層を
具えていることを特徴とする電線、ケーブル。