JP3185249B2 - セラミックグリーンブロックのカット方法 - Google Patents

セラミックグリーンブロックのカット方法

Info

Publication number
JP3185249B2
JP3185249B2 JP15362691A JP15362691A JP3185249B2 JP 3185249 B2 JP3185249 B2 JP 3185249B2 JP 15362691 A JP15362691 A JP 15362691A JP 15362691 A JP15362691 A JP 15362691A JP 3185249 B2 JP3185249 B2 JP 3185249B2
Authority
JP
Japan
Prior art keywords
ceramic green
cutting
green block
cut
dicing saw
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Lifetime
Application number
JP15362691A
Other languages
English (en)
Other versions
JPH054216A (ja
Inventor
紀之 久保寺
泰人 稲垣
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Murata Manufacturing Co Ltd
Original Assignee
Murata Manufacturing Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Murata Manufacturing Co Ltd filed Critical Murata Manufacturing Co Ltd
Priority to JP15362691A priority Critical patent/JP3185249B2/ja
Publication of JPH054216A publication Critical patent/JPH054216A/ja
Priority to US08/625,008 priority patent/US6526958B1/en
Priority to US09/348,713 priority patent/US6910473B1/en
Application granted granted Critical
Publication of JP3185249B2 publication Critical patent/JP3185249B2/ja
Anticipated expiration legal-status Critical
Expired - Lifetime legal-status Critical Current

Description

【発明の詳細な説明】
【０００１】
【産業上の利用分野】この発明は、セラミックグリーン
ブロックのカット方法に関するものである。
【０００２】
【従来の技術】焼成後のセラミックブロックからチップ
を切出す場合や、Ｓｉウエハをカットする場合、ダイシ
ングソーが用いられることが多い。ダイシングソーの特
徴として、カット時の寸法精度が高いことが挙げられ
る。しかし、ダイシングソーによれば、カットに際し
て、通常、高速の回転刃が適用されるため、軟らかい材
料や粘り着く材料のカットには、適していない。
【０００３】他方、セラミックグリーンブロックのカッ
トには、通常、ブレードによる押切りが適用されてい
る。これは、セラミックグリーンブロックは軟らかいた
め、ブレードによる押切りが可能であり、また、ダイシ
ングソー等に比べると、カットのスピードが速く、かつ
設備も安価であるため、所望のコストに見合うためであ
る。
【０００４】このようにセラミックグリーンブロックを
カットすることにより得られたチップは、たとえば、セ
ラミック電子部品を得るための要素として用いられてい
る。
【０００５】
【発明が解決しようとする課題】近年のように、電子部
品の小型化および高性能化が進むと、セラミックグリー
ンブロックからチップを切出すに当たって、より高いカ
ット精度が要求されるようになってきた。
【０００６】しかしながら、ブレードによる押切りで
は、そのカット原理からもわかるように、カット時のブ
ロックまたはチップの移動などが原因となり、高精度の
カットを得ることが難しい。また、ブレードによる押切
りによって、内部に金属膜または金属箔等の硬い部分を
持つセラミックグリーンブロックをカットすることは困
難である。
【０００７】他方、ダイシングソーによるカットは、精
度の面では満足できるが、セラミックグリーンブロック
のような軟らかいものに対しては、高速カットを適用す
ることができないため、このようなダイシングソーをカ
ット工程に適用するとその工程に要するコストが高くな
るという問題がある。
【０００８】それゆえに、この発明の目的は、ダイシン
グソーを適用しながら、ダイシングソーによるカットを
能率的に行なうことができる、セラミックグリーンブロ
ックのカット方法を提供しようとすることである。
【０００９】
【課題を解決するための手段】この発明は、上述した技
術的課題を解決するため、ダイシングソーでカットする
に当たって、セラミックグリーンブロックを熱処理して
その硬度を増してから、カットを実施することを特徴と
している。
【００１０】なお、この発明が適用されるセラミックグ
リーンブロックは、少なくともカットする部分がセラミ
ックグリーン体のみで構成される場合に限らず、金属ペ
ースト膜または金属箔等の異種の材料を含んでいてもよ
い。
【００１１】
【作用】この発明によれば、セラミックグリーンブロッ
クが熱処理されることにより、セラミックグリーンブロ
ックの硬度が増す。
【００１２】
【発明の効果】したがって、この発明によれば、セラミ
ックグリーンブロックに対しても、ダイシングソーによ
る高速カットを適用できるようになる。
【００１３】また、セラミックグリーンブロックをダイ
シングソーでカットするため、カット精度を高めること
ができるとともに、平滑な切断面を得ることができる。
【００１４】その結果、この発明を電子部品のためのチ
ップを得る目的で適用すれば、精度の高いチップの切出
しを行なえるため、電子部品チップの小型化や高性能化
に対応することができる。
【００１５】
【実施例】以下、この発明に従って実施した実験例につ
いて説明する。
【００１６】セラミック原料として、以下の配合比で調
合したものを用いた。 ＢａＴｉＯ3 固溶体仮焼原料 １００重量部 バインダ １０ 〃 可塑剤 ４ 〃 トルエン ５０ 〃 エタノール ５０ 〃 上述の調合で得られたスラリーを、ドクターブレード法
で、厚さ２０μｍ、幅１００ｍｍ、長さ１００ｍの寸法
にシート成形し、圧着機を用いて、次の３種類のセラミ
ックグリーンブロックを作製した。
【００１７】 ５０枚のシートを圧着して、５０ｍｍ
×５０ｍｍ×１ｍｍとしたセラミックグリーンブロック シートの片面にＮｉペーストを３μｍの厚みで塗布
したものを圧着し、５０ｍｍ×５０ｍｍ×１ｍｍとした
セラミックグリーンブロック シートと厚さ３μｍのＮｉ箔を交互に圧着し、５０
ｍｍ×５０ｍｍ×１ｍｍとしたセラミックグリーンブロ
ック これらのブロック〜を、ダイシングソーを用いて、
硬化処理なしで、カットした（送りスピード：５０ｍｍ
／秒）。得られた切断面の表面粗さを以下に示す。
【００１８】 Ｒａ＝０．２０〜０．３０μｍ Ｒａ＝０．２５〜０．３５μｍ Ｒａ＝０．５０〜１．００μｍ 他方、同じブロック〜を、次のように硬化させ、ダ
イシングソーを用いて、上記比較例と同じ送りスピード
でカットした。
【００１９】すなわち、ブロック〜に対して、１５
０℃で５時間の熱処理を行ない、可塑剤を解離させて硬
化させた後、それぞれ、カットした。その切断面の表面
粗さを以下に示す。
【００２０】 Ｒａ＝０．０５〜０．０８μｍ Ｒａ＝０．０５〜０．０８μｍ Ｒａ＝０．１０〜０．１５μｍ なお、硬化処理なしで、上述のような硬化処理を行なっ
た場合に得られた切断面の表面粗さと同等の切断面表面
粗さを得るには、ダイシングソーの送りスピードを２ｍ
ｍ／秒にまで落とす必要があった。したがって、これら
の実験例から、セラミックグリーンブロックを熱処理に
よって硬化処理することにより、ダイシングソーによる
カット時間を、１／２５に短縮できることがわかった。

Claims (1)

    (57)【特許請求の範囲】
  1. 【請求項１】 セラミックグリーンブロックを熱処理し
    てその硬度を増してから、ダイシングソーでカットす
    る、セラミックグリーンブロックのカット方法。
JP15362691A 1991-06-26 1991-06-26 セラミックグリーンブロックのカット方法 Expired - Lifetime JP3185249B2 (ja)