JP2022543090A - プラスター処理コンパウンド - Google Patents
プラスター処理コンパウンド Download PDFInfo
- Publication number
- JP2022543090A JP2022543090A JP2022506598A JP2022506598A JP2022543090A JP 2022543090 A JP2022543090 A JP 2022543090A JP 2022506598 A JP2022506598 A JP 2022506598A JP 2022506598 A JP2022506598 A JP 2022506598A JP 2022543090 A JP2022543090 A JP 2022543090A
- Authority
- JP
- Japan
- Prior art keywords
- weight
- plaster
- solution
- aqueous
- compound
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
プラスター処理用コンパウンド、特に、水ガラスを含有する防水プラスター処理用コンパウンドであって、20~69重量%のケイ酸カリウム水溶液と、20~59.9重量%のケイ酸リチウム水溶液と、10~20重量%のオクチルトリエトキシシランと、0.1~1重量%の水ガラス安定剤とを含有する。
Description
本発明はプラスターの処理のためのコンパウンド、特に、水ガラスを含有する防水プラスター処理を強化するためのコンパウンドに関する。
現行の技術から、プラスターの表面特性を改善するための広範囲の手段が知られており、その組成はプラスターの組成、特にその結合材の種類に関連している。
アクリル系プラスターは合成樹脂結合材を含有し、これにより、プラスターは、硬く、強靭で、撥水性である。それらの主な欠点は、ほこり付着に対する抵抗が低いことに加えて、熱安定性が低く、抗真菌効果が弱く、特に蒸気透過性が低いことである。
ケイ酸塩プラスターの結合材はカリウム水ガラスから作られており、そのため、これらは優れた蒸気透過性を有し、あらゆる種類の断熱システムに使用することができる。これらの欠点には、可撓性および撥水性が低いことが含まれる。
これらの現代のプラスターに加えて、石灰プラスターは、古い建築物および歴史的な建築物に使用されている。それらの問題は、物理的(水分変化、機械的影響)および生物学的(植物の根、微生物の影響)であり得る漸進的分解であるが、石灰モルタルおよびプラスターの主要な硬化生成物としての炭酸カルシウムの分解からなる特に化学的分解である。
プラスターの強化は、水ガラスを塗装することによっても行うことができる。水ガラスを使用する公知の溶液の欠点は、それらが使用された後、プラスターの表面層がしばしば硬化し基材から分離することである。
チェコ特許文献CZ PV 1988ー8934から、アクリレートおよびスチレンアクリレート、メチルシロキサンおよびシロキシドならびに水ガラスを10重量%までをベースとするファサード塗料が知られている。充填剤は石灰石および顔料である。この塗料は、その有機塩基のために十分な蒸気透過性を有さない。塗料は水をはじくが、古いプラスターの補修処理には適していない。
さらなるチェコ特許文献CZ PV 1991ー1916から、石灰石、カリウム水ガラス、コロイド状二酸化ケイ素、シリコーン、シロキサンおよび顔料をベースとするプラスター用塗料が知られている。この塗料は、良好な蒸気透過性を有しておらず、また、古いプラスターの補修処理には適していない。
チェコ特許文献CZ 279049から、5~15重量%のシリカと、5~15重量%の50%のスチレンアクリレート分散物と、20~30重量%の石灰石、ドロマイト、マグネサイトまたはそれらの混合物と、10~20重量%のケイ酸アルミニウム、アルカリ金属、アルカリ性土壌およびマグネシウムと、0.1~15重量%の有機白色および着色顔料と、0.2~1重量%のシランまたはポリオルガノシロキサンに基づく疎水化添加剤とを含有するカリウム水ガラスからなる塗料物質が知られている。この塗料の欠点は、それがプラスター上に硬い層を形成し、これがプラスターの破壊を引き起こし得ることである。
上記の現在の技術から、公知の現在の技術の主な欠点は、公知のプラスター表面処理物質がしばしばプラスター表面の破壊を引き起こすことであることは明らかである。
本発明の目的は、プラスターの長期表面特性を安定化し改善するプラスター処理コンパウンドを提供することである。
上記の欠点は大幅に取りのぞかれ、本発明の目的はプラスター処理コンパウンド、特に、水ガラスを含有する防水プラスター処理の強化用のコンパウンドによって達成され、本発明によれば、それが、20~69重量%のケイ酸カリウム水溶液と、20~59.9重量%のケイ酸リチウム水溶液と、10~20重量%のオクチルトリエトキシシラン溶液と、0.1~1重量%の水ガラス安定剤とからなることを特徴とする。このコンパウンドの利点は、分解に対する高い耐性である。このコンパウンドは優れた抗真菌効果も有し、環境にやさしく、健康に害がなく、UV放射をよく反射するが、有機毒性物質を放出しない。疎水化効果を改善するために、シラン濃度が30重量%までのオクチルトリエトキシシランのコンパウンドに溶液を添加する。利点は、コンパウンドの蒸気透過性、抗真菌効果および熱安定性の低下がないことである。
プラスター処理コンパウンドはさらに、0.1~1重量%のコロイド状銀水溶液を含有し、最も有利には100ppmの濃度を有する。その利点は、コロイド状銀の溶液を含有することであり、これは真菌、ウイルスおよび細菌の防除を有意に改善する。
ケイ酸カリウム水溶液が酸化カリウムに対するシリカのモル質量比が1.67~1.73の範囲であり、密度が1650~1670kg/m3の範囲であることが有利である。この組成物の利点は、コーティングのプラスターへの優れた接着性と、コンパウンドのプラスターとの化学結合の最適化である。
さらに有利には、ケイ酸リチウム水溶液は、その酸化リチウムに対するシリカのモル質量比が3.8~4.1の範囲であり、密度が1100~1300kg/m3の範囲である。このコンパウンドの利点は、優れた撥水性である。さらなる利点は、このコンパウンドが粘度を低下させ、アルカリ度を低下させることであり、これは、このコンパウンドがプラスター表面へのより深く、より有効な浸透を達成することを助ける。リチウム水ガラスは撥水性であり、その一方で、プラスターの表面を覆い、水の連続的な侵入からプラスター表面を保護し、プラスター中に生じる孔を満たし、それによってプラスター中の水および塩の輸送を妨げる。
水ガラス安定剤が親水性アルコキシアルキルーアンモニウム塩であることが有利である。
本発明によるプラスター処理コンパウンドの主な利点は、それが深さにおいてプラスターの表面を同時に安定化し、その特性を有意に改善することである。硬化後、プラスターの表面は古典的なガラスに似ているが、強く、硬く、耐摩耗性であり、水に加えて、塩溶液、油およびディーゼル油にも耐性がある。別の利点は、コンパウンドが、プラスターと接触している金属元素に対して耐食効果を有することである。プラスターの表面は蒸気透過性であり、プラスター中に残留するか、またはメーソンリーまたは地面から上昇することによってプラスターに入り得る水蒸気の放出を確実にする。さらに、プラスターの摩耗が著しく排除される。プラスターは滑らかで、光沢があり、洗浄可能な表面を有する。このコンパウンドは環境保護的であり、健康にも害がない。
実施例1
防水プラスター処理の強化用コンパウンドは、67重量%のケイ酸カリウム水溶液と、21重量%のケイ酸リチウム水溶液と、11重量%のオクチルトリエトキシシラン溶液と、0.1重量%の水ガラス安定剤と、0.9重量%の濃度が100ppmであるコロイド状銀水溶液とを含有する。
ケイ酸カリウム水溶液は、酸化カリウムに対するシリカのモル質量比が1.7であり、密度が1660kg/m3の範囲内である。
ケイ酸リチウム水溶液は、酸化リチウムに対するシリカのモル質量比が4.03であり、密度が1209kg/m3である。
水ガラス安定剤は、N,N,N’,N’ーテトラキス(2ーヒドロキシプロピル)エチレンジアミンの98%水溶液の形態の親水性アルコキシアルキルーアンモニウム塩である。
実施例2
防水プラスター処理の強化用コンパウンドは、69重量%のケイ酸カリウム水溶液と、20重量%のケイ酸リチウム水溶液と、10重量%のオクチルトリエトキシシラン溶液と、1重量%の水ガラス安定剤とを含有する。
ケイ酸カリウム水溶液は、酸化カリウムに対するシリカのモル質量比が1.67であり、密度が1650kg/m3の範囲内である。
ケイ酸リチウム水溶液は、酸化リチウムに対するシリカのモル質量比が3.8であり、密度が1100kg/m3である。
水ガラス安定剤は、N,N,N’,N’ーテトラキス(2ーヒドロキシプロピル)エチレンジアミンの98%水溶液の形態の親水性アルコキシアルキルーアンモニウム塩である。
実施例3
防水プラスター処理の強化用コンパウンドは、68重量%のケイ酸カリウム水溶液と、20重量%のケイ酸リチウム水溶液と、10重量%のオクチルトリエトキシシラン溶液と、1重量%の水ガラス安定剤と、1重量%の濃度が100ppmであるコロイド状銀水溶液とを含有する。
ケイ酸カリウム水溶液は、酸化カリウムに対するシリカのモル質量比が1.73であり、密度が1670kg/m3の範囲内である。
ケイ酸リチウム水溶液は、酸化リチウムに対するシリカのモル質量比が4.1であり、密度が1300kg/m3である。
水ガラス安定剤は、N,N,N’,N’ーテトラキス(2ーヒドロキシプロピル)エチレンジアミンの98%水溶液の形態の親水性アルコキシアルキルーアンモニウム塩である。
実施例4
防水プラスター処理の強化用コンパウンドは、69重量%のケイ酸カリウム水溶液と、20重量%のケイ酸リチウム水溶液と、10重量%のオクチルトリエトキシシラン溶液と、1重量%の水ガラス安定剤とを含有する。
ケイ酸カリウム水溶液は、酸化カリウムに対するシリカのモル質量比が1.69であり、密度が1655kg/m3の範囲内である。
ケイ酸リチウム水溶液は、酸化リチウムに対するシリカのモル質量比が4.05であり、密度が1250kg/m3である。
水ガラス安定剤は、N,N,N’,N’ーテトラキス(2ーヒドロキシプロピル)エチレンジアミンの98%水溶液の形態の親水性アルコキシアルキルーアンモニウム塩である。
実施例5
防水プラスター処理の強化用コンパウンドは、20重量%のケイ酸カリウム水溶液と、59.8重量%のケイ酸リチウム水溶液と、20重量%のオクチルトリエトキシシラン溶液と、0.1重量%の水ガラス安定剤と、0.1重量%の濃度が100ppmであるコロイド状銀水溶液とを含有する。
ケイ酸カリウム水溶液は、酸化カリウムに対するシリカのモル質量比が1.69であり、密度が1660kg/m3の範囲内である。
ケイ酸リチウム水溶液は、酸化リチウムに対するシリカのモル質量比が4.01であり、密度が1150kg/m3である。
水ガラス安定剤は、N,N,N’,N’ーテトラキス(2ーヒドロキシプロピル)エチレンジアミンの98%水溶液の形態の親水性アルコキシアルキルーアンモニウム塩である。
実施例6
防水プラスター処理の強化用コンパウンドは、20重量%のケイ酸カリウム水溶液と、59.9重量%のケイ酸リチウム水溶液と、20重量%のオクチルトリエトキシシラン溶液と、0.1重量%の水ガラス安定剤とを含有する。
ケイ酸カリウム水溶液は、酸化カリウムに対するシリカのモル質量比が1.68であり、密度が1662kg/m3の範囲内である。
ケイ酸リチウム水溶液は、酸化リチウムに対するシリカのモル質量比が4.03であり、密度が1211kg/m3である。
水ガラス安定剤は、N,N,N’,N’ーテトラキス(2ーヒドロキシプロピル)エチレンジアミンの98%水溶液の形態の親水性アルコキシアルキルーアンモニウム塩である。
本発明によるプラスター処理コンパウンドは、プラスターの表面処理、特に古いプラスターの改修、および湿った壁上のプラスターの改修に使用することができる。
Claims (8)
- プラスター処理コンパウンド、特に、水ガラスを含有する防水プラスター処理の強化用コンパウンドであって、20~69重量%のケイ酸カリウム水溶液と、20~59.9重量%のケイ酸リチウム水溶液と、10~20重量%のオクチルトリエトキシシラン溶液と、0.1~1重量%の水ガラス安定剤とを含有することを特徴とするプラスター処理コンパウンド。
- さらに0.1~1重量%のコロイド状銀水溶液を含むことを特徴とする請求項1に記載のプラスター処理コンパウンド。
- 前記コロイド状銀水溶液の濃度が100ppmであることを特徴とする請求項2に記載のプラスター処理用コンパウンド。
- 前記ケイ酸カリウム水溶液が、酸化カリウムに対するシリカのモル質量比が1.67~1.73の範囲であることを特徴とする、請求項1から3のいずれか1項に記載のプラスター処理コンパウンド。
- 前記ケイ酸カリウム水溶液の密度が1650~1670kg/m3の範囲内であることを特徴とする、請求項1から4のいずれか1項に記載のプラスター処理コンパウンド。
- 前記ケイ酸リチウム水溶液が、リチウム酸化物に対するシリカのモル質量比が3.8~4.1の範囲内であることを特徴とする、請求項1から5のいずれか1項に記載のプラスター処理コンパウンド。
- 前記ケイ酸リチウム水溶液の密度が1100~1300kg/m3の範囲内であることを特徴とする、請求項1から6のいずれか1項に記載のプラスター処理コンパウンド。
- 前記水ガラス安定剤が親水性アルコキシアルキルアンモニウム塩であることを特徴とする、請求項1から7のいずれか1項に記載のプラスター処理コンパウンド。