JP2021080403A - リキッド印刷インキ組成物、及び印刷物 - Google Patents
リキッド印刷インキ組成物、及び印刷物 Download PDFInfo
- Publication number
- JP2021080403A JP2021080403A JP2019210440A JP2019210440A JP2021080403A JP 2021080403 A JP2021080403 A JP 2021080403A JP 2019210440 A JP2019210440 A JP 2019210440A JP 2019210440 A JP2019210440 A JP 2019210440A JP 2021080403 A JP2021080403 A JP 2021080403A
- Authority
- JP
- Japan
- Prior art keywords
- pigment
- pigment red
- printing ink
- resin
- calcium carbonate
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
しかし、ベンゼン、トルエン、キシレン等の芳香族炭化水素やケトン溶剤を用いない事で樹脂溶解性や流動性が低下する傾向となる一方で、印刷スピードの高速化により、例えばグラビア印刷を例に挙げれば、版かぶりという印刷汚れを生じやすい状況となっている。版かぶりとは、グラビアシリンダーに供給された過剰なインキをドクターブレードに掻き取る際に、インキの流動性の悪さゆえ、ドクターブレードが押し上げられ、掻き切れなかったインキが汚れの原因となり発生する現象と考えられている。
また、流動性の低下により諧調再現性や重ね印刷適性にも影響を与える傾向となる。
これまで、樹脂組成による流動性や溶解性の向上による改善が試みられていたが、樹脂の選択や組成に制限が生じるのが現状である。
(1)炭酸カルシウムの平均粒子径が1μm〜16μmである
(2)炭酸カルシウムのBET比表面積が1.5m2/g〜5.0m2/gである
(3)前記BET比表面積÷平均粒子径が0.6〜3.0の範囲である
(1)炭酸カルシウムの平均粒子径が1μm〜16μmである
(2)炭酸カルシウムのBET比表面積が1.5m2/g〜5.0m2/gである
(3)前記BET比表面積÷平均粒子径が0.6〜3.0の範囲である
本発明のリキッド印刷インキ組成物は前記、表刷り印刷、裏刷り印刷、及び熱収縮シュリンクフィルム用途に幅広く対応する事ができるものである。
中でも、塩化ビニル/酢酸ビニル共重合体、ポリウレタン樹脂、硝化綿、ポリアミド樹脂、アクリル樹脂、及びポリエステル樹脂が好ましく、これらは単独で用いても良いし、複数組み合わせて使用してもよい。前記表刷り印刷、裏刷り印刷、及び熱収縮シュリンクフィルムのいずれの用途に使用するか、又基材となるフィルムの種類に応じてバインダー樹脂を適宜組み合わせて使用する事が好ましい。
塩化ビニル/酢酸ビニル共重合樹脂としては、塩化ビニルと酢酸ビニルが共重合したものであれば、特段限定されない。分子量としては重量平均分子量で5,000〜100,000のものが好ましく、10,000〜70,000が更に好ましい。塩化ビニル/酢酸ビニル共重合樹脂の固形分100質量%中、酢酸ビニルモノマー由来の構造は1〜30質量%が好ましく、塩化ビニルモノマー由来の構造は70〜95質量%であることが好ましい。この場合有機溶剤への溶解性が向上、更に基材への密着性、被膜物性、耐擦傷性等が良好となる。
また、有機溶剤への溶解性の観点からビニルアルコール構造由来の水酸基を含むものも好ましい。水酸基価としては20〜200mgKOH/gであることが好ましい。また、ガラス転移温度は50℃〜90℃であることが好ましい。
また塩化ビニル/酢酸ビニル共重合樹脂の添加量としては、インキ全量に対し0.15〜40質量%であることが好ましく、さらに好ましくは1.0〜35質量%である。
ウレタン樹脂としては、ポリオールとポリイソシアネートを反応させて得たポリウレタン樹脂であれば特に限定されない。ポリオールとしては例えば、ポリウレタン樹脂の製造に一般的に用いられる各種公知のポリオールを用いることができ、1種または2種以上を併用してもよい。例えば、エチレングリコール、1,2−プロパンジオール、1,3−プロパンジオール、2−メチル−1,3−プロパンジオール、2−エチル−2ブチル−1,3−プロパンジオール、1,3−ブタンジオール、1,4−ブタンジオール、ネオペンチルグリコール、ペンタンジオール、3−メチル−1,5ペンタンジオール、ヘキサンジオール、オクタンジオール、1,4−ブチンジオール、1,4―ブチレンジオール、ジエチレングリコール、トリエチレングリコール、ジプロピレングリコール、グリセリン、トリメチロールプロパン、トリメチロールエタン、1,2,6−ヘキサントリオール、1,2,4−ブタントリオール、ソルビトール、ペンタエスリトールなどの飽和または不飽和の低分子ポリオール類(1)、これらの低分子ポリオール類(1)と、セバシン酸、アジピン酸、フタル酸、イソフタル酸、テレフタル酸、マレイン酸、フマル酸、こはく酸、しゅう酸、マロン酸、グルタル酸、ピメリン酸、スペリン酸、アゼライン酸、トリメリット酸、ピロメリット酸などの多価カルボン酸あるいはこれらの無水物とを脱水縮合または重合させて得られるポリエステルポリオール類(2);環状エステル化合物、例えばポリカプロラクトン、ポリバレロラクトン、ポリ(β−メチル−γ−バレロラクトン)等のラクトン類、を開環重合して得られるポリエステルポリオール類(3);前記低分子ポリオール類(1)などと、例えばジメチルカーボネート、ジフェニルカーボネート、エチレンカーボネート、ホスゲン等との反応によって得られるポリカーボネートポリオール類(4);ポリブタジエングリコール類(5);ビスフェノールAに酸化エチレンまたは酸化プロピレンを付加して得られるグリコール類(6);1分子中に1個以上のヒドロキシエチル、アクリル酸ヒドロキシプロプル、アクリルヒドロキシブチル等、或いはこれらの対応するメタクリル酸誘導体等と、例えばアクリル酸、メタクリル酸又はそのエステルとを共重合することによって得られるアクリルポリオール(7)などが挙げられる。
また、反応停止を目的とした末端封鎖剤として、一価の活性水素化合物を用いることもできる。かかる化合物としてはたとえば、ジ−n−ブチルアミン等のジアルキルアミン類やエタノール、イソプロピルアルコール等のアルコール類があげられる。更に、特にポリウレタン樹脂中にカルボキシル基を導入したいときには、グリシン、L−アラニン等のアミノ酸を反応停止剤として用いることができる。これらの末端封鎖剤は単独で、または2種以上を混合して用いることができる。
また、ウレタン樹脂の添加量としては、インキ全量に対し0.15〜40質量%であることが好ましく、さらに好ましくは1.0〜35質量%である。
繊維素系樹脂としては、例えばセルロースアセテートプロピオネート、セルロースアセテートブチレートその他のセルロースエステル樹脂、ニトロセルロース(硝化綿ともいう)、ヒドロキシアルキルセルロース、およびカルボキシアルキルセルロース等が挙げられる。セルロースエステル樹脂はアルキル基を有することが好ましく、当該アルキル基は、例えば、メチル基、エチル基、プロピル基、イソプロピル基、ブチル基、イソブチル基、ペンチル基、ヘキシル基等が挙げられ、更にアルキル基が置換基を有していてもよい。 セルロース系樹脂としては、上記のうちセルロースアセテートプロピオネート、セルロースアセテートブチレート、およびニトロセルロースが好ましい。特に好ましくはニトロセルロースである。分子量としては重量平均分子量で5,000〜200,000のものが好ましく、10,000〜50,000が更に好ましい。また、ガラス転移温度が120℃〜180℃であるものが好ましい。ポリウレタン樹脂と併用すれば、耐ブロッキング性、耐擦傷性その他のインキ被膜物性が向上することが期待できる。
ニトロセルロース(硝化綿)は、天然セルロースと硝酸とを反応させて、天然セルロース中の無水グルコピラノース基の6員環中の3個の水酸基を、硝酸基に置換した硝酸エステルとして得られるものが好ましい。
ニトロセルロース(硝化綿)の添加量としては、インキ全量に対し0.15〜40質量%であることが好ましく、さらに好ましくは1.0〜35質量%である。
ポリアミド樹脂としては、例えば多塩基酸と多価アミンとを重縮合して得ることができる有機溶剤に可溶な熱可塑性ポリアミドである。特に、重合脂肪酸および/またはダイマー酸を含有する酸成分と、脂肪族および/または芳香族ポリアミンの反応物を含むポリアミド樹脂であることが好ましく、更には一級および二級モノアミンを一部含有するものが好ましい。
前記多塩基酸には、モノカルボン酸を併用することもできる。併用されるモノカルボン酸としては、酢酸、プロピオン酸、ラウリン酸、パルミチン酸、安息香酸、シクロヘキサンカルボン酸等が挙げられる。
ポリアミド樹脂の添加量としては、インキ全量に対し、0.15〜40質量%であることが好ましく、さらに好ましくは1.0〜35質量%である。
ポリエステル樹脂としては、多塩基酸成分と多価アルコール成分とをエステル化反応させたものであればよい。
多塩基酸成分としては、例えば、無水フタル酸、イソフタル酸、テレフタル酸、コハク酸、フマル酸、アジピン酸、アゼライン酸、セバシン酸、ダイマー酸、などの1種以上の二塩基酸及び、これらの酸の低級アルキルエステル化物が主として用いられ、必要に応じて、安息香酸、クロトン酸、p−t−ブチル安息香酸などの一塩基酸、無水トリメリット酸、メチルシクロヘキセントリカルボン酸、無水ピロメリット酸などの3価以上の多塩基酸などが併用される。
ポリエステル樹脂の添加量としては、インキ全量に対し、0.15〜40質量%であることが好ましく、さらに好ましくは1.0〜35質量%である。
ポリエステル樹脂の添加量としては、インキ全量に対し、0.15〜40質量%であることが好ましく、さらに好ましくは1.0〜35質量%である。
(1)炭酸カルシウムの平均粒子径が1μm〜16μmである
(2)炭酸カルシウムのBET比表面積が1.5m2/g〜5.0m2/gである
(3)前記BET比表面積÷平均粒子径が0.6〜3.0の範囲である
また、前記重質炭酸カルシウムの原料として石灰岩の他、大理石、鍾乳石、白亜(チョーク)、方解石、霰石、貝殻やサンゴの骨格、鶏卵の殻等の天然炭酸カルシウムを挙げる事ができ、中でも鶏卵の殻や貝殻は廃棄物でもあり環境保護の点で好ましい。
炭酸カルシウムの平均粒子径は、1μm〜16μmの範囲である事が好ましい。平均粒子径が1μm以上であれば、リキッド印刷インキが沈殿する事なくインキ安定性が保持される傾向となり、平均粒子径が16μm以下であれば、リキッド印刷インキとして重ね刷りした際の印刷適性を保持でき、印刷時に筋状の汚れの発生を抑制できる傾向となる。
炭酸カルシウムのBET比表面積が1.5m2/g〜5.0m2/gである事が好ましい。BET比表面積が1.5m2/g以上であれば、リキッド印刷インキが沈殿する事なくインキ安定性が保持され、耐版かぶり性が向上する傾向となる。BET比表面積が5.0m2/g以下であれば、リキッド印刷インキが沈殿する事なくインキ安定性が保持され、重ね刷りした際の印刷適性、及び諧調再現性が良好となる。尚、BET比表面積の値は、窒素及びISO 9277に従ったBET法に従うものである。
前記BET比表面積÷平均粒子径が0.6〜3.0の範囲である事が好ましい。
該炭酸カルシウムの非表面積対する平均粒子径サイズの比率を数値化するもので、
「BET比表面積÷平均粒子径が0.6〜3.0」の範囲であれば、リキッド印刷インキが沈殿する事なくインキ安定性が保持され、耐版かぶり性が向上する傾向となる。
加えて、軟包装向けラミネート適性、諧調再現性、重ね印刷適性をも兼備することが出来る。
ポーラス構造からなる多孔質を持ち合わせる代表的なものとして、卵殻粉末やホタテ殻粉末が挙げられその表面形状、及びその原材料が食品廃棄物で低コストである点からも特に好ましい。
前記卵殻粉末は、窒素及びISO 9277に従ったBET法で測定した場合、BET比表面積が1.5〜5.0m2/gの範囲にあるものが好ましく、これは卵殻粉末の主成分である炭酸カルシウムが多孔質体からなるポーラス構造であるためである。
卵殻粉末の平均粒子径が1μm〜16μmの範囲が好ましく、BET比表面積÷平均粒子径が0.6〜3.0の範囲が好ましい。
また、更に好ましくは平均粒子径が1μm〜10μmの範囲であり、BET比表面積が1.5〜10m2/gの範囲であり、BET比表面積÷平均粒子径が0.6〜3.0の範囲である。
また、卵殻粉末としては、市販の各種卵殻粉末や、これらを高温で焼成したものも用いることができる。また、白色の卵でない場合には、粉砕を行った後に、酸化型塩素系、酸化型酸素系、還元型などの漂白剤を用いて脱色することができる。
尚、製造工程において、焼成のホタテ粉末よりも未焼成のホタテ粉末の方がより好ましい。
尚、印刷時の作業衛生性と包装材料の有害性の両面から、トルエン、キシレン等の芳香族炭化水素系溶剤及び/又はケトン系溶剤を使用しない事がより好ましい。
本発明のリキッド印刷インキ組成物としては、着色剤を含まないインキの濃度調整用ニス及びオーバープリントニスとして使用することもできるし、着色剤を含む美粧性等を付与する目的でデザイン印刷等に用いる着色剤を含むインキとして使用することもできる。
着色剤としては顔料が好ましく、一般のインキ、塗料、及び記録剤などに使用されている無機顔料、有機顔料を挙げることができる。有機顔料としては、溶性アゾ系、不溶性アゾ系、アゾ系、フタロシアニン系、ハロゲン化フタロシアニン系、アントラキノン系、アンサンスロン系、ジアンスラキノニル系、アンスラピリミジン系、ペリレン系、ペリノン系、キナクリドン系、チオインジゴ系、ジオキサジン系、イソインドリノン系、キノフタロン系、アゾメチンアゾ系、フラバンスロン系、ジケトピロロピロール系、イソインドリン系、インダンスロン系、カーボンブラック系などの顔料が挙げられる。また、例えば、カーミン6B、レーキレッドC、パーマネントレッド2B、ジスアゾイエロー、ピラゾロンオレンジ、カーミンFB、クロモフタルイエロー、クロモフタルレッド、フタロシアニンブルー、フタロシアニングリーン、ジオキサジンバイオレット、キナクリドンマゼンタ、キナクリドンレッド、インダンスロンブルー、ピリミジンイエロー、チオインジゴボルドー、チオインジゴマゼンタ、ペリレンレッド、ペリノンオレンジ、イソインドリノンイエロー、アニリンブラック、ジケトピロロピロールレッド、昼光蛍光顔料等が挙げられる。また未酸性処理顔料、酸性処理顔料のいずれも使用することができる。以下に有機顔料として好ましいものの具体的な例を挙げる。
藍色顔料としてC.I.ピグメントブルー15、C.I.ピグメントブルー15:1、C.I.ピグメントブルー15:2、C.I.ピグメントブルー15:3、C.I.ピグメントブルー15:4、C.I.ピグメントブルー15:6、
緑色顔料としてC.I.ピグメントグリーン7、
赤色顔料としてC.I.ピグメントレッド57:1、C.I.ピグメントレッド48:1、C.I.ピグメントレッド48:2、C.I.ピグメントレッド48:3、C.I.ピグメントレッド146、C.I.ピグメントレッド242、C.I.ピグメントレッド185、C.I.ピグメントレッド122、C.I.ピグメントレッド178、C.I.ピグメントレッド149、C.I.ピグメントレッド144、C.I.ピグメントレッド166、
紫色顔料としてC.I.ピグメントバイオレット23、C.I.ピグメントバイオレット37、
黄色顔料としてC.I.ピグメントイエロー83、C.I.ピグメントイエロー14、C.I.ピグメントイエロー180、C.I.ピグメントイエロー139、
橙色顔料としてC.I.ピグメントオレンジ38、C.I.ピグメントオレンジ13、C.I.ピグメントオレンジ34、C.I.ピグメントオレンジ64、
等が挙げられ、これらの群から選ばれる少なくとも一種または二種以上を使用することが好ましい。
本発明のリキッド印刷インキ組成物は、バインダー樹脂、体質顔料、着色剤等を事前に連肉した後、追加すべきバインダー樹脂、その他各種添加剤などを有機溶剤中に溶解及び/又は分散することにより製造することができる。具体的には、体質顔料、及び着色剤をバインダー樹脂により有機溶剤に分散させた顔料分散体を製造し、得られた顔料分散体に、必要に応じて他の化合物などを配合することによりインキを製造することができる。
インキ中に気泡や予期せずに粗大粒子などが含まれる場合は、印刷物品質を低下させるため、濾過などにより取り除くことが好ましい。濾過器は従来公知のものを使用することができる。
インキの粘度は、使用される原材料の種類や量、バインダー樹脂、顔料、有機溶剤などを適宜選択することにより調整することができる。また、インキ中の顔料の粒度および粒度分布を調節することによりインキの粘度を調整することもできる。
本発明のリキッド印刷インキ組成物は、各種の基材と密着性に優れ、紙、合成紙、熱可塑性樹脂フィルム、プラスチック製品、鋼板等への印刷に使用することができるものであり、電子彫刻凹版等によるグラビア印刷版を用いたグラビア印刷用、又は樹脂版等によるフレキソ印刷版を用いたフレキソ印刷用のインキとして有用である一方で、版を使用せずインクジェットノズルからインキを吐出するインクジェット方式向けのインキを除くものである。
即ち、インクジェットインキの場合、ノズルから吐出したインク滴が、直接基材に密着し印刷物を形成するのに対し、本発明のリキッド印刷インキ組成物は、印刷インキを一旦印刷版又は印刷パターンに密着・転写した後、インキのみを再度基材に密着させ、必要に応じて乾燥させ印刷物とするものである。
本発明のリキッド印刷インキ組成物を用いてグラビア印刷方式やフレキソ印刷方式から形成される印刷インキの膜厚は、例えば10μm以下、好ましくは5μm以下である。
基材フィルムの印刷面には、コロナ放電処理がされていることが好ましく、アルミ、シリカ、アルミナ等が蒸着されていてもよい。
なお、本発明におけるGPC(ゲルパーミエーションクロマトグラフィー)による重量平均分子量、及び数平均分子量(ポリスチレン換算)の測定は東ソー(株)社製HLC−8420GPCシステムを用い以下の条件で行った。
分離カラム:東ソー(株)製TSKgel SuperHZを4本使用。カラム温度:40℃。移動層:和光純薬工業(株)製テトラヒドロフラン。流速:0.35ml/分。試料濃度:0.3質量%。試料注入量:10μL。
また、ガラス転移温度(Tg)の測定は、示差走査熱量計(株式会社TAインスツルメント製「DSC Q100」)を用い、窒素雰囲気下、冷却装置を用い温度範囲−80〜450℃、昇温温度10℃/分の条件で走査を行う事で行った。
また、炭酸カルシウムの平均粒子径は、日機装株式会社製ナノ粒子粒度分布測定器Nanotrac UPA EX−150を用いて測定した。
また、BET比表面積の値は、窒素及びISO 9277に従ったBET法に従うものである。
水酸基を有する塩化ビニル/酢酸ビニル共重合樹脂(樹脂モノマー組成が質量%で塩化ビニル/酢酸ビニル/ビニルアルコール=92/3/5、水酸基価(mgKOH)=64)を酢酸エチルで15%溶液とし、これを塩化ビニル/酢酸ビニル共重合樹脂溶液Evとした。
工業用硝化綿L1/8(ニトロセルロース、固形分70%、JIS K−6703により溶液濃度25.0%における粘度1.6〜2.9%品 Nobel社製)28.6部に、イソプロピルアルコール/酢酸エチル/酢酸ノルマルプロピル/メチルシクロヘキサン(質量比で25/25/13/10の比率)の混合液を71.4部加え、充分混合し固形分20%のニトロセルロース樹脂溶液Nを作製した。
攪拌機、温度計、環流冷却器および窒素ガス導入管を備えた4つ口フラスコに、ネオペンチルグリコールアジペートジオール84.5部(水酸基価:56.6mgKOH/g)とポリエチレングリコール15.5部(水酸基価:278mgKOH/g)およびイソホロンジイソシアネート27.55部を仕込み、窒素気流下に90℃で10時間反応させ、イソシアネート基含有率2.84重量%のウレタンプレポリマーを製造した後、これに酢酸エチル68.7部を加えてウレタンプレポリマーの均一溶液とした。次いで、イソホロンジアミン7.83部、ジ−n−ブチルアミン0.11部、酢酸エチル136.8部およびイソプロピルアルコール110.7部からなる混合物に、前記ウレタンプレポリマー溶液を添加し、45℃で5時間攪拌反応させて、ポリウレタン樹脂溶液Pu1を得た。
得られたポリウレタン樹脂溶液Pu1は、樹脂固形分濃度30質量%、樹脂固形分の重量平均分子量は54,000であった。
攪拌機、温度計、環流冷却器および窒素ガス導入管を備えた4つ口フラスコに、ネオペンチルグリコールアジペートジオール75部(水酸基価:224mgKOH/g)とポリエチレングリコール25部(水酸基価:278mgKOH/g)およびイソホロンジイソシアネート58.74部を仕込み、窒素気流下に90℃で10時間反応させ、イソシアネート基含有率2.80質量%のウレタンプレポリマーを製造した後、これに酢酸エチル85.5部を加えてウレタンプレポリマーの均一溶液とした。次いで、イソホロンジアミン9.66部、ジ−n−ブチルアミン0.11部、酢酸エチル170.1部およびイソプロピルアルコール137.6部からなる混合物に、前記ウレタンプレポリマー溶液を添加し、45℃で5時間攪拌反応させて、ポリウレタン樹脂溶液Pu2を得た。
得られたポリウレタン樹脂溶液Pu2は、樹脂固形分濃度30質量%、樹脂固形分の重量平均分子量は54,000であった。
攪拌機、温度計、環流冷却器および窒素ガス導入管を備えた4つ口フラスコに、ダイマー酸(ハリダイマー270S;ハリマ化成(株)製)100部、トール油脂肪酸(ハートールFA−1;ハリマ化成(株)製)1部、セバシン酸5部、エチレンジアミン10部、ヘキサメチレンジアミン5部、及びトリフェニルホスフィン0.24部を入れ、系内を窒素雰囲気とし、さらに、窒素気流下均一化の攪拌しながら200℃までゆっくりと昇温する。続いて攪拌しながら200℃にて5時間脱水縮合を行い、イソプロピルアルコール/工業用エタノール/メチルシクロヘキサン(質量比で20/20/60の比率)を添加することにより、固形分30%、軟化点123℃、アミン価2、酸価8、数平均分子量10,000のトール脂肪酸由来のダイマー酸変性ポリアミド樹脂溶液Paを得た。
固形アクリル樹脂(三菱ケミカル(株)製ダイヤナールBR−90)を酢酸エチルにて攪拌溶解して30%溶液とし、これをアクリル系樹脂溶液Acとした。
ニトロセルロース樹脂溶液N(固形分20%)25部、アルミナ処理された酸化チタン20部、炭酸カルシウム(a)として卵殻カルシウム(BET比表面積1.4、平均粒径1.83μm、BET比表面積/平均粒径=1.31)2部をペイントコンディショナーを用いて十分練肉した後、ウレタン樹脂Pu1としてバーノックERL−201(固形分質量30%、DIC(株)社製)20部、キレート溶液であるTC−401(固形分50%、マツモトファインケミカル社製)2部、可塑剤エポサイザーW−100EL(固形分100%、DIC(株)社製)1部、有機溶剤(D)として酢酸エチル8部、酢酸―n―プロピル7部、イソプロピルアルコール7部、n−プロピルアルコール3部、メチルシクロヘキサン5部を混合し十分混合し、表刷り用白色リキッド印刷インキを作製した。
実施例1の炭酸カルシウム(a)の卵殻カルシウム2部の代わりに、ホタテ殻粉末の炭酸カルシウム(b)(BET比表面積1.53、平均粒径4.39μm、BET比表面積/平均粒径=2.87)6部を添加しペイントコンディショナーを用いて十分練肉した後、有機溶剤(D)の酢酸エチル8部を6部へ変更した他は、実施例1と同様の手順にて表刷り用白色リキッド印刷インキを作製した。
実施例1の炭酸カルシウム(a)の卵殻カルシウム2部の代わりに、炭酸カルシウム(c)の卵殻カルシウム(BET比表面積8.0、平均粒径5.0μm、BET比表面積/平均粒径=0.63を4部添加しペイントコンディショナーを用いて十分練肉した後、有機溶剤(D)の各有機溶剤を表1に示す配合量へ微調整した他は、実施例1と同様の手順にて表刷り用白色リキッド印刷インキを作製した。
実施例1のニトロセルロース樹脂溶液N(固形分20%)25部の代わりに、ポリアミド樹脂溶液Pa(固形分30%)30部に変更し、アルミナ処理された酸化チタン20部を添加せずにペイントコンディショナーを用いて十分練肉した後、有機溶剤(D)の各有機溶剤を表1に示す配合量へ微調整した他は、実施例1と同様の手順にて表刷り用オーバープリントニス向けリキッド印刷インキを作製した。
塩化ビニル/酢酸ビニル共重合樹脂溶液Ev(固形分15%)20部、アルミナ処理していない酸化チタン35部、炭酸カルシウム(a)として卵殻カルシウム(BET比表面積1.4、平均粒径1.83μm、BET比表面積/平均粒径=1.31)2部をペイントコンディショナーを用いて十分練肉した後、ウレタン樹脂Pu2としてバーノックECL−341(固形分質量30%、DIC(株)社製)30部、付着付与剤であるスーパークロン360T(固形分50%、日本製紙(株)社製)1部、有機溶剤(D)として酢酸エチル8部、イソプロピルアルコール2部、n−プロピルアルコール2部を混合し十分混合し、裏刷り用白色リキッド印刷インキを作製した。
実施例5の卵殻カルシウム(BET比表面積1.4、平均粒径1.83μm、BET比表面積/平均粒径=1.31)2部の代わりにホタテ殻粉末の炭酸カルシウム(b)(BET比表面積1.53、平均粒径4.39μm、BET比表面積/平均粒径=2.87)6部を使用し有機溶剤(D)の酢酸エチル8部を4部へ変更した他は、実施例5と同様の手順にて裏刷り用白色リキッド印刷インキを作製した。
実施例5の卵殻カルシウム(a)(BET比表面積1.4、平均粒径1.83μm、BET比表面積/平均粒径=1.31)2部の代わりに卵殻カルシウム(c)(BET比表面積8.0、平均粒径5.0μm、BET比表面積/平均粒径=0.63を4部添加し、有機溶剤(D)の酢酸エチル8部を6部へ変更した他は、実施例5と同様の手順にて裏刷り用白色リキッド印刷インキを作製した。
表3に示す組成に従って、ニトロセルロース樹脂溶液N(固形分20%)25部、アルミナ処理された酸化チタン20部、炭酸カルシウム(a)として卵殻カルシウム(BET比表面積1.4、平均粒径1.83μm、BET比表面積/平均粒径=1.31)4部をペイントコンディショナーを用いて十分練肉した後、アクリル樹脂としてアクリディックWCL−1314(固形分質量30%、DIC(株)社製)25部、可塑剤エポサイザーW−100EL(固形分100%、DIC(株)社製)1部、有機溶剤(D)として酢酸エチル10部、イソプロピルアルコール11部、n−プロピルアルコール4部を混合し十分混合し、熱収縮シュリンクフィルム用白色リキッド印刷インキを作製した。
表3に示す組成に従って、実施例8と同様の手順にて、熱収縮シュリンクフィルム用白色リキッド印刷インキを作製した。
実施例3の炭酸カルシウム(c)の卵殻カルシウム4部の代わりに、炭酸カルシウム(d)ソフトン3200(BET比表面積0.7、平均粒径3.2μm、BET比表面積/平均粒径=4.57、白石カルシウム(株)社製)4部を添加し、実施例1、及び実施例3と同様の手順にて表刷り用白色リキッド印刷インキを作製した。
実施例3の炭酸カルシウム(c)の卵殻カルシウム4部の代わりに、炭酸カルシウム(e)ソフトン1000(BET比表面積2.2、平均粒径1.0μm、BET比表面積/平均粒径=0.45、白石カルシウム(株)社製)4部を添加し、実施例1、及び実施例3と同様の手順にて表刷り用白色リキッド印刷インキを作製した。
実施例3の炭酸カルシウム(c)の卵殻カルシウム4部の代わりに、炭酸カルシウム(f)BF−200(BET比表面積5.0、平均粒径0.4μm、BET比表面積/平均粒径=0.08、白石カルシウム(株)社製)4部を添加し、実施例1、及び実施例3と同様の手順にて表刷り用白色リキッド印刷インキを作製した。
実施例3の炭酸カルシウム(c)の卵殻カルシウム4部の代わりに、炭酸カルシウム(g)Brilliant1500(BET比表面積0.15、平均粒径12.0μm、BET比表面積/平均粒径=80.0、白石カルシウム(株)社製)4部を添加し、実施例1、及び実施例3と同様の手順にて表刷り用白色リキッド印刷インキを作製した。
実施例4の炭酸カルシウム(a)の卵殻カルシウム2部の代わりに、炭酸カルシウム(d)ソフトン3200(BET比表面積0.7、平均粒径3.2μm、BET比表面積/平均粒径=4.57、白石カルシウム(株)社製)4部を添加し、実施例1、及び実施例4と同様の手順にて表刷り用オーバープリントニス向けリキッド印刷インキを作製した。
表2に示す組成にて、実施例5〜6と同様の手順にて裏刷り用白色リキッド印刷インキを作製した。
表3に示す組成にて、実施例8〜10と同様の手順にて熱収縮シュリンクフィルム用白色リキッド印刷インキを作製した。
実施例、比較例で得られた白色リキッド印刷インキの粘度を酢酸エチルでザーンカップ#3(離合社製)で16秒(25℃)に調整し、版深度25μmを有するレーザーグラビア版を取り付けたMD型グラビア印刷機(富士機械株式会社製)を用いて、片面にコロナ放電処理を施した二軸延伸ポリプロピレンフィルム(フタムラ化学株式会社製 FOR 厚さ20μm)の処理面に印刷を行った。
耐版かぶり性試験は、グラビア版の円周600mmφで200m/minの印刷速度した際の、非印刷部の汚れ具合(耐版かぶり性)を目視評価した。
(評価基準)
5:印刷汚れが全く見られない。
4:印刷汚れが極僅かに確認できる。
3:印刷汚れ僅かに確認できるが実用範囲である。
2:印刷汚れが顕著に見られる。
1:印刷汚れが甚だしく見られる。
前記耐版カブリ性試験にて作製した表刷り印刷物のハイライト印刷部分(網点面積10%未満)におけるカスレの面積の割合と、非印刷部の汚れ具合を目視評価した。
(評価基準)
5:カスレが全くなく、非印刷部の汚れもない。
4:カスレが少し見られる 、若しくは非印刷部に汚れが少しみられる。
3:カスレが少し見られ 、且つ非印刷部に汚れが少し見られる。
2:カスレが見られ 、且つ非印刷部に汚れが見られる。
1:カスレが多く見られ、且つ非印刷部にも汚れが多く見られる。
実施例、比較例で得られた白色リキッド印刷インキの粘度を酢酸エチル/イソプロピアルコールの質量比率2/1の混合溶剤でザーンカップ#3(離合社製)を用いて16秒(25℃)に調整し、網点50%部を有するレーザーグラビア版を取り付けたMD型グラビア印刷機(富士機械株式会社製)を用いて、片面にコロナ放電処理を施した二軸延伸ポリプロピレンフィルム(フタムラ化学株式会社製 FOR 厚さ20μm)の処理面に印刷を行った。
諧調再現性の評価は、円周600mmφで200m/minのグラビア版で4000m印刷した際の、グラビア版の50%網点部分のセル開口部の面積と、印刷物の50%網点部分の面積を比較したドットゲインにより評価した。
グラビア印刷では網点が実際のセル開口部の面積よりも広がると、色調などの再現が悪くなるため、印刷物の網点はセル開口部の面積に近いものが望ましい。
(評価基準)
5:セル開口部の面積と比較し印刷物網点の面積が100%〜120%の範囲である。
4:セル開口部の面積と比較し印刷物網点の面積が121%〜130%の範囲である。
3:セル開口部の面積と比較し印刷物網点の面積が131%〜140%の範囲である。
2:セル開口部の面積と比較し印刷物網点の面積が141%〜160%の範囲である。
1:セル開口部の面積と比較し印刷物網点の面積が161%以上である。
前記耐版カブリ性試験にて作製した表刷り印刷物、及び裏刷り印刷物の印刷面に、ウレタン系のドライラミネート接着剤ディックドライLX−703VL/KR−90(DIC製)をドライラミネート機(DICエンジニアリング製)を使用して塗工し、接着剤塗工面に無延伸ポリプロピレンフィルム(以下、R−CPP:東レ合成フィルム社製 ZK−75 50μm)を積層させた。その後40℃で5日間エージングを施しラミネート物を得た。得られたラミネート物を15mm幅に切り出し、引っ張り速度300mm/分で90度の剥離試験を行った。
(評価基準)
5:ラミネート強度が5N/15mm以上である。
4:ラミネート強度が4N/15mm以上〜5N/15mm未満である。
3:ラミネート強度が3N/15mm以上〜4N/15mm未満である。
2:ラミネート強度が2N/15mm以上〜3N/15mm未満である 。
1:ラミネート強度が1N/15mm未満である。
実施例、比較例で得られた白色リキッド印刷インキを各々ガラス瓶に採取し、60℃で20日間保存を行ない、その後、離合社製ザーンカップ#4を用いて保存前と保存後の粘度変化を次の5段階にて評価した。
(評価基準)
5:粘度差が2秒未満で、粘度変化がほとんど無い。
4:粘度差が2秒以上5秒未満であり、粘度変化が僅かに見られる。
3:粘度差が5秒以上10秒未満であり、粘度変化がやや多い。
2:粘度差が10秒以上15秒未満であり、粘度変化が多い。
1:粘度差が15秒以上であり、粘度変化が非常に多い。
尚、評価項目の「−」印は未評価である事を示す。
Claims (9)
- バインダー樹脂(A)、体質顔料(B)、着色剤(C)、及び有機溶剤(D)を含有するリキッド印刷インキ組成物であって、前記体質顔料(B)が炭酸カルシウムであり、(1)〜(3)を満たすことを特徴とするリキッド印刷インキ組成物。
(1)炭酸カルシウムの平均粒子径が1μm〜16μmである
(2)炭酸カルシウムのBET比表面積が1.5m2/g〜5.0m2/gである
(3)前記BET比表面積÷平均粒子径が0.6〜3.0の範囲である
- 前記炭酸カルシウムがポーラス構造からなる多孔質である請求項1に記載のリキッド印刷インキ組成物。
- 前記炭酸カルシウムが卵殻粉末、及び/又はホタテ殻粉末である請求項1又は2の何れかに記載のリキッド印刷インキ組成物。
- 前記バインダー樹脂(A)が、塩化ビニル/酢酸ビニル共重合樹脂、ポリウレタン樹脂、繊維素系樹脂、ポリアミド樹脂、アクリル樹脂、及びポリエステル樹脂からなる群から選ばれる何れか1つである請求項1に記載のリキッド印刷インキ組成物。
- 前記有機溶剤(D)が、芳香族有機溶剤及び/又はケトン系溶剤を含有しない請求項1〜4の何れか1つに記載のリキッド印刷インキ組成物。
- 請求項1〜5の何れか1つに記載のリキッド印刷インキ組成物を含有する事を特徴とするフレキソインキ。
- 請求項1〜5の何れか1つに記載のリキッド印刷インキ組成物を含有する事を特徴とするグラビアインキ。
- 請求項6に記載のフレキソインキによってフレキソ印刷が施されている事を特徴とする印刷物。
- 請求項7に記載のグラビアインキによってグラビア印刷が施されている事を特徴とする印刷物。