JP2020175936A - 吸収性透明蓋材 - Google Patents
吸収性透明蓋材 Download PDFInfo
- Publication number
- JP2020175936A JP2020175936A JP2019080514A JP2019080514A JP2020175936A JP 2020175936 A JP2020175936 A JP 2020175936A JP 2019080514 A JP2019080514 A JP 2019080514A JP 2019080514 A JP2019080514 A JP 2019080514A JP 2020175936 A JP2020175936 A JP 2020175936A
- Authority
- JP
- Japan
- Prior art keywords
- transparent
- layer
- less
- lid material
- absorbent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
〈態様1〉透明バリア性基材層、及び透明吸収層をこの順で具備している、吸収性透明蓋材。
〈態様2〉前記透明吸収層が、熱可塑性樹脂、及び吸湿剤を含有している透明吸湿層である、態様1に記載の吸収性透明蓋材。
〈態様3〉前記熱可塑性樹脂が、ポリオレフィン系樹脂である、態様2に記載の吸収性透明蓋材。
〈態様4〉前記吸湿剤が、ゼオライトである、態様2又は3に記載の吸収性透明蓋材。
〈態様5〉前記透明吸湿層の前記ゼオライトの平均粒子径D50が、300nm以下である、態様4に記載の吸収性透明蓋材。
〈態様6〉前記透明吸湿層が、HLB値が5以下のエステル化合物を更に含有している、態様2〜5のいずれか一項に記載の吸収性透明蓋材。
〈態様7〉前記透明吸収層の、前記透明バリア性基材層と反対側の面に、透明易剥離性層を更に有する、態様1〜6のいずれか一項に記載の吸収性透明蓋材。
〈態様8〉ブリスターパック用である、態様1〜7のいずれか一項に記載の吸収性透明蓋材。
〈態様9〉内容物、ブリスター容器、及び態様1〜8のいずれか一項に記載の吸収性透明蓋材を有し、
前記ブリスター容器が、ポケットを有しており、
前記吸収性透明蓋材が、ブリスター容器に接着され、それによって、前記ポケット内に内容物が密封されている、
内容物入りブリスターパック。
〈態様10〉態様1〜8のいずれか一項に記載の吸収性透明蓋材と、
ポケットを有するブリスター容器と
の組合せ。
図1に示すように、本発明の吸収性透明蓋材100は、透明バリア性基材層108、及び透明吸収層102をこの順で具備している。また、吸収性透明蓋材100は、透明吸収層102の片側又は両側に、透明スキン層106、106’を有していてよい。
透明バリア性基材層は、透明性及びバリア性を有する基材である。
透明バリア層としては、透明であり、かつ外部からの水分や有機ガス及び無機ガスが透明吸収層へと透過することを抑制することができる材料を用いることができる。かかる透明バリア層としては、例えばシリカ蒸着膜、アルミナ蒸着膜、若しくはシリカ・アルミナ二元蒸着膜等の無機物蒸着膜、又はポリ塩化ビニリデンコーティング膜、ポリクロロトリフルオロエチレンコーティング膜、若しくはポリフッ化ビニリデンコーティング膜等の有機物コーティング膜を用いることができる。また、上記のバリア性樹脂層を、透明バリア層として用いることもできる。
透明基材樹脂層としては、耐衝撃性、耐摩耗性等に優れた熱可塑性樹脂、例えば、ポリオレフィン系樹脂、ビニル系ポリマー、ポリエステル、ポリアミド等の熱可塑性樹脂を単独で、又は2種類以上組み合わせて複層で使用することができる。この樹脂層は、延伸フィルムであっても、無延伸フィルムであってもよい。また、この樹脂層は、透明バリア層の片面又は両面に存在していても良い。この樹脂層により、透明バリア層を保護することができる。
透明吸収層は、透明であり、かつ吸収剤を有する層である。この場合、吸湿剤は、熱可塑性樹脂中に分散していてよい。この熱可塑性樹脂としては、透明基材樹脂層に関して挙げた熱可塑性樹脂を用いることができ、中でもポリオレフィン系樹脂、特にポリエチレン系樹脂を用いることが、加工性等の観点から好ましい。
透明易剥離性層は、ブリスター容器に透明蓋材を接合させた後に、ブリスター容器から界面剥離させること、及び/又は透明易剥離性層を凝集破壊させることによって、透明蓋材の他の層をブリスター容器から分離させて開封することができる層を意味するものである。
(i)図2(a)に関して言及したように、透明易剥離性層からブリスター容器を界面剥離させることができるか、又は
(ii)図2(b)に関して言及したように、透明易剥離性層を凝集剥離させることができる。
透明スキン層は、透明スキン層用樹脂を含有しており、かつ透明吸収層の透明易剥離性層側の面に存在していることができる層である。透明スキン層は、透明吸収層の透明バリア性基材層側の面に更に存在していてもよい。また、透明スキン層は、透明吸収層に融着されていてもよい。
透明スキン層用樹脂としては、透明基材樹脂層に関して挙げた熱可塑性樹脂を、単独で又は混合させて用いることができ、中でもポリオレフィン系樹脂、特にポリエチレン系樹脂を用いることが、加工性等の観点から好ましい。透明吸収層の両側にスキン層が存在している場合、それぞれの透明スキン層を構成する透明スキン層用樹脂は、同一であっても異なっていてもよい。
吸収性透明蓋材は、随意の他の層を有していてもよい。他の層としては、例えば各層の間に存在する接着層が挙げられる。
図1に示すように、本発明の内容物入りブリスターパック400は、
内容物300、ブリスター容器200、及び吸収性透明蓋材100を有し、
ブリスター容器200が、ポケット202を有しており、
吸収性透明蓋材100が、ブリスター容器200に接着され、それによって、ポケット202内に内容物300が密封されている。
内容物は、ブリスター容器のポケット内に密封されている内容物である。かかる内容物としては、外気との接触によって劣化しうる物であれば限定されるものではなく、薬剤の他、食品、化粧品、衛生用品、医療機器、医療器具、電子部品等を挙げることができる。また、薬剤としては、医薬品製剤の他、洗浄剤、農薬、試薬等を含む。
ブリスター容器としては、ポケットを有するブリスター容器を用いることができる。
ブリスター容器用最内樹脂層は、ブリスター容器を作製したときに、内容物側に配置されることとなる層である。この層を介して、ブリスター容器を本発明のブリスターパック用蓋材と融着させることができる。最内樹脂層としては、例えば単層のブリスター容器用シートに関して挙げた樹脂を用いることができる。
ブリスター容器用基材層に用いられる樹脂としては、ブリスター容器用シートに適度なバリア性及び成形性を与える樹脂であれば特に制限されない。例えば、ポリオレフィン系樹脂、ポリ塩化ビニル、ポリ塩化ビニリデン、ポリプロピレン系樹脂、飽和ポリエステル、ポリアミド(例えば、ナイロン(登録商標)、ナイロン6、ナイロン6,6、ナイロンMXD6)、環状ポリオレフィン(COP、COC)、及びフッ素系樹脂(例えば、ポリクロロトリフルオロエチレン、ポリテトラフルオロエチレン)等、並びにこれらの混合物が挙げられる。これらは単層で用いても良いし、2層以上を積層して用いても良い。好ましくは、外部からの水分の浸入を防ぎ、防湿性に優れているものがよく、特にポリプロピレン系樹脂、ポリアミド及び飽和ポリエステルが挙げられる。
ブリスター容器用バリア層に用いられる材料としては、銅箔、アルミニウム箔等の金属箔層、環状オレフィンポリマー、エチレン−ビニルアルコール共重合体等のバリア性樹脂層、シリカ蒸着膜、アルミニウム蒸着膜、アルミナ蒸着膜、シリカ・アルミナ蒸着膜等の無機物蒸着膜、塩化ビニリデンコーティング膜、ポリクロロトリフルオロエチレンコーティング膜、ポリフッ化ビニリデンコーティング膜等の有機物コーティング膜、及びこれらの組合せを挙げることができる。
ブリスター容器用補強層は、ブリスター容器用シートの成形性を向上させるために用いられる。補強層に用いられる樹脂としては、例えば、高密度ポリエチレン、ポリ塩化ビニル、ポリプロピレン系樹脂、ポリエチレンテレフタレート、ポリアミド(例えば、ナイロン(登録商標)、ナイロン6、ナイロン6,6、ナイロンMXD6)等、並びにこれらの混合物が挙げられる。補強層の厚みは、例えば10μm以上、15μm以上、又は25μm以上であってよく、また60μm以下、又は50μm以下であってよい。
複層のブリスター容器用シートは、随意の他の層を有していてよい。他の層としては、例えば機能層、機能層上のスキン層、各層を接着させる接着層等が挙げられる。なお、吸収性透明蓋材の透明吸収層と、ブリスター容器用シートの機能層とは、同じものを用いても良いし、層の厚さや、吸収剤又は樹脂の種類又は含有量等が異なるものを用いてもよい。
本発明の組合せは、上記の透明蓋材と、ポケットを有するブリスター容器との組合せである。ブリスター容器としては、上記のブリスター容器を用いることができる。
〈実施例1〉
Tダイ法による共押出成形にて、透明スキン層、透明吸湿層、及び透明スキン層がこの順で配置されるようにして、2種3層の透明吸湿フィルムを作製した。透明スキン層としては、直鎖状低密度ポリエチレンを用い、吸湿層用樹脂組成物としては、エチレン−酢酸ビニル共重合体(EVA150、三井デュポン・ポリケミカル株式会社)48質量部、Na−A型ゼオライト(平均粒子径D50:50nm)32質量部、及びエステル化合物(HLB値3.0)5質量部を溶融混練して作製した樹脂組成物を用いた。各層の厚さは、透明スキン層10μm、透明吸湿層30μm、透明スキン層10μmとした。
PET(12μm)//アルミニウム箔(9μm)の層構成(ただし、「//」はドライラミネート接着剤を表す)を有する積層体のアルミニウム箔側に、アクリル変性ポリオレフィンを塗布して乾燥させることにより、透明易剥離性層を積層させて蓋材として用いたことを除き、実施例1と同様にして、比較例1の蓋材を作製した。
透明シリカ蒸着PETフィルム(GXフィルム、凸版印刷株式会社、厚さ12μm)にアクリル変性ポリオレフィンを塗布して乾燥させることにより、透明易剥離性層を積層させて蓋材として用いたことを除き、実施例1と同様にして比較例2の蓋材を作製した。
蓋材における吸湿層用樹脂組成物として、親水性ゼオライト(モレキュラーシーブ3A、ユニオン昭和株式会社)53質量部及びエチレン−メタクリル酸共重合体47質量部を溶融混練して作製した樹脂組成物を用いて、透明ではない吸湿フィルムを作製したことを除き、実施例1と同様にして、比較例3の蓋材を作製した。
〈剥離試験〉
作製した各蓋材の易剥離性層側を、ナイロン(25μm)//アルミニウム箔(40μm)//PVC(60μm)の層構成を有するブリスター容器用シートのPVC層側にヒートシールさせた。ヒートシール条件は、ブリスターパック用蓋材側の温度150℃、ブリスター容器用シート側の温度40℃、時間1.5秒、圧力0.2MPaとした。
〇:剥離強度が2N〜10Nであった。
×:剥離強度が2N〜10Nとならなかった。
ナイロン(25μm)//アルミニウム箔(40μm)//PVC(60μm)の層構成を有するブリスター容器用シートを、プレス機によりこのシートにポケットを形成して、ブリスター容器を作製した。
〇:内容物に付された文字が識別できた。
△:内容物に付された文字が識別できなかったものの、有無が確認できた。
×:内容物に付された文字が視認できなかった。
作製した各蓋材を100mm×100mmに切り出して吸湿試験用サンプルとし、このサンプルの質量を測定した。
○:吸湿量が1g/m2以上である。
×:吸湿量が1g/m2未満である。
〈製造例〉
熱可塑性樹脂、Na−A型ゼオライト(平均粒子径D50:50nm)、及びエステル化合物(HLB値3.0)を、表2及び表3に記載の配合でバンバリーミキサーを用いて160℃で10分間溶融混練して、各例の樹脂組成物を得た。
(メルトフローレート)
各例の樹脂組成物を測定可能なサイズにカットした。カットした樹脂組成物について、メルトインデクサ(株式会社テクノ・セブン)を用いて、温度190℃かつ荷重21.18Nの条件の下で、JIS K7210に準拠して、メルトフローレート(MFR)を測定した。
樹脂組成物を所定の重量にカットして、熱プレス成型によって100μmの厚みのフィルムを作製した。ここで、プレスの条件は、温度160℃、圧力40〜60MPa、2分間とした。このようにして得られたフィルムを、50mm四方にカットして、ヘイズ測定器(株式会社村上色彩研究所、HR−100)を用いて、JIS K7105に準拠してヘイズを測定した。なお吸湿後のヘイズについては、上記フィルムを23℃50%の環境下に静置し、吸湿後の重量変化が一定になるまで吸湿させ、その後上記と同じ方法で測定した。
各例の構成及び評価結果を表2及び表3に示す。
〈ブリスターパック用蓋材の作製〉
(参考例B1)
空冷方式インフレーションによる共押出成形にて、スキン層、機能層としての吸収層、及びスキン層がこの順で配置されるようにして、2種3層の吸収フィルムを作製した。スキン層としては、直鎖状低密度ポリエチレンを用い、吸収層用樹脂としては、親水性ゼオライト及びエチレン−メタクリル酸共重合体(EMAA)を溶融混練して作製した樹脂を用いた。各層の厚さは、スキン層10μm、吸収層30μm、スキン層10μmとした。
易剥離性層として、表4に示す構成の易剥離性層を用いたことを除き、参考例B1と同様にして、参考例B2〜B5及び参考比較例B1のブリスターパック用蓋材を作製した。
易剥離性層を積層させなかったことを除き、参考例B1と同様にして、参考比較例B2のブリスターパック用蓋材を作製した。
〈剥離試験〉
作製したブリスターパック用蓋材の易剥離性層又はスキン層側を、ナイロン(25μm)//アルミニウム箔(40μm)//PVC(60μm)の層構成を有するブリスター容器用シートのPVC層側にヒートシールさせた。ヒートシール条件は、ブリスターパック用蓋材側の温度150℃、ブリスター容器用シート側の温度40℃、時間3秒、圧力0.2MPaとした。
作製したブリスターパック用蓋材を100mm×100mmに切り出して吸湿試験用サンプルとし、このサンプルの質量を測定した。
○:吸湿量が1g/m2以上である。
×:吸湿量が1g/m2未満である。
102 透明吸収層
104 透明易剥離性層
104a 接合部
104b、104b’ 非接合部
106、106’ 透明スキン層
108 透明バリア性基材層
108a 透明バリア層
108b 透明基材樹脂層
144 破断部
200 ブリスター容器
202 ポケット
300 内容物
400 内容物入りブリスターパック
Claims (10)
- 透明バリア性基材層、及び透明吸収層をこの順で具備している、吸収性透明蓋材。
- 前記透明吸収層が、熱可塑性樹脂、及び吸湿剤を含有している透明吸湿層である、請求項1に記載の吸収性透明蓋材。
- 前記熱可塑性樹脂が、ポリオレフィン系樹脂である、請求項2に記載の吸収性透明蓋材。
- 前記吸湿剤が、ゼオライトである、請求項2又は3に記載の吸収性透明蓋材。
- 前記透明吸湿層の前記ゼオライトの平均粒子径D50が、300nm以下である、請求項4に記載の吸収性透明蓋材。
- 前記透明吸湿層が、HLB値が5以下のエステル化合物を更に含有している、請求項2〜5のいずれか一項に記載の吸収性透明蓋材。
- 前記透明吸収層の、前記透明バリア性基材層と反対側の面に、透明易剥離性層を更に有する、請求項1〜6のいずれか一項に記載の吸収性透明蓋材。
- ブリスターパック用である、請求項1〜7のいずれか一項に記載の吸収性透明蓋材。
- 内容物、ブリスター容器、及び請求項1〜8のいずれか一項に記載の吸収性透明蓋材を有し、
前記ブリスター容器が、ポケットを有しており、
前記吸収性透明蓋材が、ブリスター容器に接着され、それによって、前記ポケット内に内容物が密封されている、
内容物入りブリスターパック。 - 請求項1〜8のいずれか一項に記載の吸収性透明蓋材と、
ポケットを有するブリスター容器と
の組合せ。