JP2020122038A - ウレタン樹脂組成物、ウレタン樹脂組成物接着剤及び接着方法 - Google Patents
ウレタン樹脂組成物、ウレタン樹脂組成物接着剤及び接着方法 Download PDFInfo
- Publication number
- JP2020122038A JP2020122038A JP2019012749A JP2019012749A JP2020122038A JP 2020122038 A JP2020122038 A JP 2020122038A JP 2019012749 A JP2019012749 A JP 2019012749A JP 2019012749 A JP2019012749 A JP 2019012749A JP 2020122038 A JP2020122038 A JP 2020122038A
- Authority
- JP
- Japan
- Prior art keywords
- urethane resin
- resin composition
- compound
- mass
- adhesive layer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
以下の方法でウレタン樹脂組成物の製造を行った。
撹拌機、温度計、加熱装置、還流管を備えた容量2Lの四口セパラブルフラスコに、水酸基末端水添ポリイソプレン(商品名 EPOL、出光興産社製、数平均分子量2,500、水酸基含量0.9mol/kg、)を158g、ジフェニルメタン―4,4’―ジイソシアネート(以下、MDIと言う。商品名:ミリオネートMT、東ソー社製、イソシアネート基含量31.3%)を20.5g、ジラウリン酸ジオクチルスズ(キシダ化学社製)を0.111g、シクロヘキサノン(ゴードー社製)を1620g、それぞれ室温下で仕込んだ後、窒素ガスを吹き込むことでフラスコ内を窒素置換した。これらを80℃条件下で均一に撹拌しながら2時間反応させた後、グリシドール(商品名 エピオール OH、日油社製)を1.10g、80℃条件下で仕込んだ後、80℃条件下で均一に撹拌しながらさらに2時間反応させることでウレタン樹脂組成物を得た。得られたウレタン樹脂組成物について、以下の方法で数平均分子量、粘度およびエポキシ当量を測定した。
ゲル浸透クロマトグラフィー(GPC)により求めた。条件は以下の通りである。装置として高速GPC装置(東ソー社製HLC−8220)、カラムとしてG3000H−XL、G2500H−XL、G2000H−XLおよびG1000H−XL(いずれも東ソー社製)を記載の順に1本ずつ直列に接続したものを用い、移動相としてテトラヒドロフランを使用し、移動相速度を1.00mL/分とした。カラム温度は40℃とし、検出器は示差屈折率計で実施し、ポリスチレン換算分子量として分子量を求めた。サンプル溶液は濃度0.5%のTHF溶液を調製して用いた。数平均分子量は7,457であった。
JIS7117−2に準拠して、B型粘度計(芝浦システム社製ビスメトロンVS−A1)を用いて測定した。粘度は3mPa/s(25℃)であった。
JIS K7236に準拠して測定した。エポキシ当量は5,268g/eq.であった。
以下の方法でPP接着層用配合液の調製、試験片の作成および塗膜物性評価を行った。結果を表1に示す。
容量100mLのガラス瓶に、製造例1で得られたウレタン樹脂組成物、エポキシ樹脂硬化促進剤(商品名 サンエイドSI−110、三新化成社製)およびエポキシ樹脂硬化剤(ジシアンジアミド、東京化成工業社製)を表1に示す質量部で仕込んだ後、ミックスローターを用いて均一となるまで攪拌することでPP接着層用配合液を得た。
まず、PP接着層用配合組成物をポリプロプレン基材(日立化成社製コウベポリシートPP)にバーコーターを用いて塗布し、室温条件下で5分間静置した後、熱風乾燥器を用いて80℃で5分間乾燥させ、乾燥膜厚10μmの接着剤層を有するポリプロピレン試験片を得た。次に、接着層組成物として本発明のウレタン樹脂組成物とは異なるポリウレタン系樹脂(東ソー社製ニッポラン−5288、商品名)をポリエチレンテレフタレートフィルム(東洋紡製東洋紡エステルフィルムE5100)にバーコーターを用いて塗布し、室温条件下で5分間静置した後、熱風乾燥器を用いて80℃で5分間乾燥させ、乾燥膜厚10μmのポリウレタン系樹脂層を有するポリエチレンテレフタレートフィルム試験片を得た。そして、得られたそれぞれの試験片を接着剤層とポリウレタン系樹脂層が接する様に張り合わせた後、185℃で10分間加熱処理することで試験片を得た。
張り合わせて得た試験片について、JISK6854−2に準拠して180度剥離試験をおこない、接着強度を評価した。試験はオートコム型試験機(ティー・エス・イー社製UTPS−Acs(S))を用いて測定した。
製造例1で得られたウレタン樹脂組成物を用いて、実施例1と同様の方法で表1に示す組成のPP接着層用配合組成物を用いて試験片の作成および接着剤物性評価を行った。結果を表1に示す。
製造例1で得られたウレタン樹脂組成物を用いて、実施例1と同様の方法で表1に示す組成のPP接着層用配合組成物を用いて試験片の作成および接着剤物性評価を行った。結果を表1に示す。
実施例1に示す試験片の作成方法において、PP接着層用配合組成物の代わりにポリウレタン系樹脂(東ソー社製ニッポラン−5288、商品名)を用いた他は、実施例1と同様に評価を行った。結果を表1に示す。
Claims (15)
- 下記一般式(1):
で表される化合物(A)、
ポリイソシアネート化合物(B)、及び
一分子中に水酸基とエポキシ基をそれぞれ少なくとも1つ有する化合物(C)の反応生成物であって、該反応生成物の分子末端にエポキシ基を持つことを特徴とする、ウレタン樹脂組成物。 - 前記一般式(1)で表される化合物(A)が分子中の異なる炭素上に水酸基を有し、炭素数50〜400のポリオールポリオレフィンであることを特徴とする、請求項1に記載のウレタン樹脂組成物。
- 一分子中に水酸基とエポキシ基をそれぞれ少なくとも1つ有する化合物(C)がグリシドールであることを特徴とする、請求項1又は2に記載のウレタン樹脂組成物。
- 数平均分子量が3,000〜250,000であることを特徴とする、請求項1乃至3のいずれかに記載のウレタン樹脂組成物。
- 前記一般式(1)で表される化合物(A)、ポリイソシアネート化合物(B)、及び一分子中に水酸基とエポキシ基をそれぞれ少なくとも1つ有する化合物(C)の反応生成物における、前記一般式(1)で表される化合物(A)の含有量が30質量%〜99.9質量%であることを特徴とする、請求項1乃至4のいずれかに記載のウレタン樹脂組成物。
- 請求項1乃至5のいずれかに記載のウレタン樹脂組成物を含む接着剤組成物。
- 請求項6に記載の接着剤組成物から得られる接着剤層。
- 請求項7に記載の接着剤層を有する物品。
- 接着剤層と基材とを加熱して得られる請求項8に記載の物品。
- 基材がプラスティックである請求項8又は9に記載の物品。
- 基材がポリオレフィンである請求項8又は9に記載の物品。
- 請求項8乃至11のいずれかに記載の物品と他の基材とから得られる物品。
- 請求項8乃至11のいずれかに記載の物品と樹脂が塗布された基材とから得られる物品。
- 加熱処理することにより得られることを特徴とする、請求項8乃至13のいずれかに記載の物品の製造方法。
- 70℃以上で加熱処理することを特徴とする請求項14に記載の物品の製造方法。