JP2020055168A - 包装材料及び包装製品 - Google Patents
包装材料及び包装製品 Download PDFInfo
- Publication number
- JP2020055168A JP2020055168A JP2018186131A JP2018186131A JP2020055168A JP 2020055168 A JP2020055168 A JP 2020055168A JP 2018186131 A JP2018186131 A JP 2018186131A JP 2018186131 A JP2018186131 A JP 2018186131A JP 2020055168 A JP2020055168 A JP 2020055168A
- Authority
- JP
- Japan
- Prior art keywords
- layer
- resin layer
- biomass
- thermoplastic resin
- derived
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
紙基材層14は、紙を含む層である。紙基材層14は、100g/m2以上700g/m2以下、好ましくは150g/m2以上600g/m2以下、より好ましくは200g/m2以上500g/m2以下の坪量を有する。紙基材層14としては、白板紙全般を対象とするが、特に安全性の観点から天然パルプを用いたアイボリー紙、ミルクカートン原紙、カップ原紙等の使用が好ましい。
印刷層12は、装飾、内容物の表示、賞味期間の表示、製造者、販売者などの表示、その他などの表示や美感の付与のために、印刷によって形成される層である。印刷層12は、例えば、絵、写真、文字、数字、図形、記号、模様などの所望の任意の絵柄を形成する絵柄層を含む。印刷層は、絵柄層の絵柄を際立たせるよう印刷により形成された地色層を更に含んでいてもよい。
着色剤としては、特に限定されず、従来公知の顔料や染料を用いることができる。
バインダー樹脂は、バイオマス由来成分を含む。例えば、バインダー樹脂は、ポリオールとイソシアネート化合物とヒドロキシ(メタ)アクリレートとの反応物であるウレタン(メタ)アクリレートを含み、ポリオール、イソシアネート化合物またはヒドロキシ(メタ)アクリレートの少なくともいずれかがバイオマス由来成分を含む。以下の説明において、バイオマス由来成分を含むウレタン(メタ)アクリレートのことを、バイオウレタン(メタ)アクリレートとも称する。
ポリエステルポリオールがバイオマス由来成分を含む場合、多官能アルコール及び多官能カルボン酸の少なくともいずれか一方がバイオマス由来成分を含む。バイオマス由来成分を含むポリエステルポリオールとして以下の例を挙げることができる。
・バイオマス由来の多官能アルコールとバイオマス由来の多官能カルボン酸との反応物
・化石燃料由来の多官能アルコールとバイオマス由来の多官能カルボン酸との反応物
・バイオマス由来の多官能アルコールと化石燃料由来の多官能カルボン酸との反応物
バイオマス由来のブチレングリコールは、植物原料からグリコールを製造し発酵することで得られたコハク酸を得て、これを水添することによって製造することができる。
バイオマス由来のエチレングリコールは、例えば、常法によって得られるバイオエタノールからエチレンを経て製造することができる。
ポリエーテルポリオールがバイオマス由来成分を含む場合、多官能アルコール及び多官能イソシアネートの少なくともいずれか一方がバイオマス由来成分を含む。バイオマス由来成分を含むポリエーテルポリオールとして以下の例を挙げることができる。
・バイオマス由来の多官能アルコールとバイオマス由来の多官能イソシアネートとの反応物
・化石燃料由来の多官能アルコールとバイオマス由来の多官能イソシアネートとの反応物
・バイオマス由来の多官能アルコールと化石燃料由来の多官能イソシアネートとの反応物
ポリカーボネートポリオールがバイオマス由来成分を含む場合、ポリカーボネートポリオールとしては、バイオマス由来成分を含む多官能アルコールと、化石燃料由来のカーボネートとの反応物を用いることができる。カーボネートとしては、例えば、ジメチルカーボネート、ジプロピルカーボネート、ジエチルカーボネート、ジエチレンカーボネート、ジブチルカーボネート、エチレンカーボネート、ジフェニルカーボネートなどが挙げられる。これらは単独或いは2種類以上を組み合わせて使用することができる。
次に、イソシアネート化合物について説明する。バイオマス由来成分を含むイソシアネート化合物としては、ポリエーテルポリオールにおいて説明したバイオマス由来の多官能イソシアネートを用いることができる。
次に、ヒドロキシ(メタ)アクリレートについて説明する。ヒドロキシ(メタ)アクリレートとしては、ヒドロキシエチル(メタ)アクリレート、ヒドロキシプロピル(メタ)アクリレート、ヒドロキシブチル(メタ)アクリレート、2−ヒドロキシ−3−フェノキシプロピル(メタ)アクリレート等の(メタ)アクリロイル基を一つ有するヒドロキシ(メタ)アクリレート;グリセリンジ(メタ)アクリレート、ペンタエリスリトールトリ(メタ)アクリレート、ジトリメチロールプロパントリ(メタ)アクリレート、ジペンタエリスリトールペンタ(メタ)アクリレート、ソルビトールペンタ(メタ)アクリレート等の(メタ)アクリロイル基を二つ以上有するヒドロキシ(メタ)アクリレート等が挙げられる。これらはそれぞれ単独で用いても良いし、2種類以上を併用しても良い。
Pbio(%)=PC14/105.5×100
表面保護層11は、印刷層12を保護する層である。表面保護層11は、印刷層12に接するように設けられていてもよい。表面保護層11は、固形分及び溶剤を含む塗料を塗布することによって形成される。塗料の固形分としては、印刷層12のバインダー樹脂と同様の材料を用いることができる。このため、表面保護層11の構成は、着色剤を含まない点以外は、印刷層12の構成と同様である。
内側熱可塑性樹脂層15は、従来公知の熱可塑性樹脂を用いて形成することができる。内側熱可塑性樹脂層15は、包装材料20の内側に位置している。包装材料20が、内側熱可塑性樹脂層を備えることで、耐熱性、耐圧性、耐水性、ヒートシール性、耐ピンホール性、耐突き刺し性、及びその他の物性を付与させることができる。
外側熱可塑性樹脂層13は、ポリエチレンを含む層である。外側熱可塑性樹脂層13は、印刷層12と紙基材層14との間に位置する。包装材料20が、外側熱可塑性樹脂層13を備えることで、紙基材層に防水性を付与したり、シール性を向上させたりすることができる。
中間熱可塑性樹脂層は、従来公知の熱可塑性樹脂を用いて形成することができる。包装材料20が、中間熱可塑性樹脂層を備えることで、各層間の密着性を付与させることができる。
バリア性樹脂層21は、酸素ガス及び水蒸気等の透過を阻止するガスバリア性や、可視光及び紫外線等の透過を阻止する遮光性を、付与乃至向上する層である。バリア性樹脂層21は、少なくとも1種のバリア性樹脂を含み、例えば、エチレン−ビニルアルコール共重合体(EVOH)、ポリビニルアルコール、ポリアクリロニトリル、ナイロン6、ナイロン6,6及びポリメタキシリレンアジパミド(MXD6)などのポリアミド、ポリエステル、ポリウレタン、並びに(メタ)アクリル樹脂などが挙げられ、これらの中でも、酸素ガス及び水蒸気等の透過を阻止するガスバリア性の観点から、EVOHが好ましい。
ポリオレフィン樹脂層23は、紙基材層14とその他の各層との間の接着性を高めるための層である。ポリオレフィン樹脂層23のポリオレフィンとしては、例えば、低密度ポリエチレン、直鎖状低密度ポリエチレン、中密度ポリエチレン、高密度ポリエチレン、ポリプロピレン、プロピレン−エチレン共重合体などが挙げられる。ポリオレフィン樹脂層23は、紙基材層14との接着性の観点から、ポリエチレン樹脂層であることが好ましい。
バリア層26は、酸素ガス及び水蒸気等の透過を阻止するガスバリア性や、可視光及び紫外線等の透過を阻止する遮光性を、付与乃至向上する層である。バリア層としては、金属箔又は蒸着フィルムであることが好ましい。
金属箔は、金属を圧延することによって得られた部材である。金属箔としては、従来公知の金属箔を用いることができる。酸素ガス及び水蒸気等の透過を阻止するガスバリア性や、可視光及び紫外線等の透過を阻止する遮光性の点からは、アルミニウム箔が好ましい。
蒸着フィルムは、基材と、基材に蒸着された蒸着膜と、を備える。蒸着膜は、基材よりも外面側に位置する。
本発明においては、プラスチックフィルム層28として各種プラスチックフィルムを用いてもよい。例えば、延伸ポリエチレンテレフタレートフィルム、延伸ナイロンフィルム、延伸ポリプロピレンフィルム、ナイロン6/メタキシリレンジアミンナイロン6共押共延伸フィルム又はポリプロピレン/ エチレン−ビニルアルコール共重合体共押共延伸フィルム等のいずれか、又はこれらの2以上のフィルムを積層した複合フィルムであってもよい。なお、プラスチックフィルムには、ポリビニルアルコールなどがコーティングされていてもよい。
アンカーコート層29は、プラスチックフィルム層28と内側熱可塑性樹脂層15との間の密着性を高めるための層である。アンカーコート層29を構成する材料としては、ポリエチレンイミンなどを用いることができる。これらの材料と溶剤とを含む塗料をプラスチックフィルム層28に塗布することにより、アンカーコート層29を形成することができる。
接着樹脂層は、任意の2層を接着する場合に設けられる層である。接着樹脂層は、従来公知の方法、例えば溶融押出しラミネート法やサンドラミネート法により形成することができる。接着樹脂層に使用できる熱可塑性樹脂としては、ポリエチレン系樹脂、ポリプロピレン系樹脂、又は環状ポリオレフィン系樹脂、又はこれら樹脂を主成分とする共重合樹脂、変性樹脂、又は、混合体(アロイでを含む)を用いることができる。ポリオレフィン系樹脂としては、例えば、低密度ポリエチレン(LDPE)、中密度ポリエチレン(MDPE)、高密度ポリエチレン(HDPE)、直鎖状(線状)低密度ポリエチレン(LLDPE)、ポリプロピレン(PP)、メタロセン触媒を利用して重合したエチレン−α・オレフィン共重合体、エチレン・ポリプロピレンのランダムもしくはブロック共重合体、エチレン−酢酸ビニル共重合体(EVA)、エチレン−アクリル酸共重合体(EAA)、エチレン・アクリル酸エチル共重合体(EEA)、エチレン−メタクリル酸共重合体(EMAA)、エチレン−メタクリル酸メチル共重合体(EMMA)、エチレン・マレイン酸共重合体、アイオノマー樹脂、また、層間の密着性を向上させるために、上記したポリオレフィン系樹脂を、アクリル酸、メタクリル酸、マレイン酸、無水マレイン酸、フマル酸、イタコン酸などの不飽和カルボン酸で変性した酸変性ポリオレフィン系樹脂などを用いることができる。また、ポリオレフィン樹脂に、不飽和カルボン酸、不飽和カルボン酸無水物、エステル単量体をグラフト重合、又は、共重合した樹脂などを用いることができる。これらの材料は、一種単独又は二種以上を組み合わせて使用することができる。環状ポリオレフィン系樹脂としては、例えば、エチレン−プロピレン共重合体、ポリメチルペンテン、ポリブテン、ポリノルボネンなどの環状ポリオレフィンなどを用いることができる。これらの樹脂は、単独又は複数を組み合せて使用できる。なお、上記したポリエチレン系樹脂としては、上述のバイオマス由来のエチレンをモノマー単位として用いたものを使用して、バイオマス度をさらに向上させることができる。
接着剤層は、任意の2層を接着する場合に設けられる層である。接着剤層は、バイオマス由来成分を含んでいてもよい。バイオマス由来成分を含む接着剤層においては、ポリオール又はイソシアネート化合物の少なくともいずれかがバイオマス由来成分を含む。
次に、包装材料20を構成する積層体の製造方法の一例について説明する。
包装材料20を用いることによって形成される包装製品の例について説明する。図12は、包装製品の例である液体用紙容器40を示す図である。液体用紙容器は、バリア性に優れることから、日本酒、焼酎、ワインなどのアルコール類、牛乳などの乳飲料、オレンジジュースやお茶などの清涼飲料などの食品、カーワックス、シャンプーや洗剤などの化学製品など液体全般の包装紙容器として好適に用いることができる。
紙基材層14として、320g/m2の坪量を有する液体容器原紙を準備した。続いて、溶融押出しラミネート法により紙基材層14上に外側熱可塑性樹脂層13を形成した。外側熱可塑性樹脂層13としては、化石燃料由来のポリエチレンを用いた。外側熱可塑性樹脂層13の厚さは17μmであった。
表/バイオ印/外熱17/紙/内熱(2)28
「/」は層と層の境界を表している。左端の層が、包装材料の外面を構成する層であり、右端の層が、包装材料の内面を構成する層である。
「表」は、表面保護層を意味する。「バイオ印」は、バイオマス由来の印刷層を意味する。「外熱」は、化石燃料由来の外熱を意味する。「紙」は、紙基材層を意味する。「内熱(2)」は、溶融押出しラミネート法により形成された化石燃料由来の内側熱可塑性樹脂層を意味する。数字は、層の厚み(単位はμm)を意味する。
印刷層12のバインダー樹脂のポリエステルポリオールとして、化石燃料由来の多官能アルコールとバイオマス由来成分を含む多官能カルボン酸との反応物を用いたこと以外は、実施例1Aの場合と同様にして、包装材料20を作製した。
印刷層12のバインダー樹脂として、化石燃料由来のポリエステルポリオールと、バイオマス由来成分を含むイソシアネート化合物と、化石燃料由来のヒドロキシ(メタ)アクリレートとの反応物であるバイオウレタン(メタ)アクリレートを用いたこと以外は、実施例1Aの場合と同様にして、包装材料20を作製した。
また、「印刷層のバインダー樹脂中のバイオマス由来成分」の欄において、「ポリオール」という記載は、印刷層のバインダー樹脂において用いられたポリオールがバイオマス由来成分を含むことを意味する。また、「イソシアネート化合物」という記載は、印刷層のバインダー樹脂において用いられたイソシアネート化合物がバイオマス由来成分を含むことを意味する。
また、「印刷層のポリオールのタイプ」の欄において、「エステル系」という記載は、印刷層のバインダー樹脂において用いられたポリオールがポリエステルポリオールであることを意味する。
また、「印刷層のポリオール中のバイオマス由来成分」の欄において、「多官能アルコール」という記載は、印刷層のバインダー樹脂のポリオールにおいて用いられた成分のうち少なくともポリエステルポリオールの多官能アルコールがバイオマス由来であることを意味する。同様に、「多官能カルボン酸」という記載は、印刷層のバインダー樹脂のポリオールにおいて用いられた成分のうち少なくともポリエステルポリオールの多官能カルボン酸がバイオマス由来であることを意味する。また、「−」という記載は、印刷層のバインダー樹脂のポリオールがバイオマス由来成分を含まないことを意味する。
印刷層12のバインダー樹脂のポリオールとしてポリエーテルポリオールを用いたこと以外は、実施例1Aの場合と同様にして、包装材料20を作製した。具体的には、ポリエーテルポリオールとして、バイオマス由来成分を含む多官能アルコールと化石燃料由来の多官能イソシアネートとの反応物を用いた。
印刷層12のバインダー樹脂のポリエーテルポリオールとして、化石燃料由来の多官能アルコールとバイオマス由来成分を含む多官能イソシアネートとの反応物を用いたこと以外は、実施例1Dの場合と同様にして、包装材料20を作製した。
印刷層12のバインダー樹脂として、化石燃料由来のポリエーテルポリオールと、バイオマス由来成分を含むイソシアネート化合物と、化石燃料由来のヒドロキシ(メタ)アクリレートとの反応物であるバイオウレタン(メタ)アクリレートを用いたこと以外は、実施例1Dの場合と同様にして、包装材料20を作製した。
印刷層12のバインダー樹脂のポリオールとしてポリカーボネートポリオールを用いたこと以外は、実施例1Aの場合と同様にして、包装材料20を作製した。具体的には、ポリカーボネートポリオールとして、バイオマス由来成分を含む多官能アルコールと化石燃料由来のカーボネートとの反応物を用いた。
印刷層12のバインダー樹脂として、化石燃料由来のポリカーボネートポリオールと、バイオマス由来成分を含むイソシアネート化合物と、化石燃料由来のヒドロキシ(メタ)アクリレートとの反応物であるバイオウレタン(メタ)アクリレートを用いたこと以外は、実施例1Gの場合と同様にして、包装材料20を作製した。
表面保護層11としてバイオマス由来成分を含むものを用いたこと以外は、実施例1Aの場合と同様にして、包装材料20を作製した。具体的には、表面保護層11のバインダー樹脂として、バイオマス由来成分を含むポリエステルポリオールと、化石燃料由来のイソシアネート化合物と、化石燃料由来のヒドロキシ(メタ)アクリレートとの反応物であるバイオウレタン(メタ)アクリレートを用いた。バイオマス由来成分を含むポリエステルポリオールとしては、バイオマス由来成分を含む多官能アルコールと化石燃料由来の多官能カルボン酸との反応物であるポリエステルポリオールを用いた。
バイオ表/バイオ印/外熱17/紙/内熱(2)28
「バイオ表」は、バイオマス由来の表面保護層を意味する。
表面保護層11のバインダー樹脂のポリエステルポリオールとして、化石燃料由来の多官能アルコールとバイオマス由来成分を含む多官能カルボン酸との反応物を用いたこと以外は、実施例1Iの場合と同様にして、包装材料20を作製した。
表面保護層11のバインダー樹脂として、化石燃料由来のポリエステルポリオールと、バイオマス由来成分を含むイソシアネート化合物と、化石燃料由来のヒドロキシ(メタ)アクリレートとの反応物であるバイオウレタン(メタ)アクリレートを用いたこと以外は、実施例1Iの場合と同様にして、包装材料20を作製した。
また、「表面保護層のバインダー樹脂中のバイオマス由来成分」の欄において、「ポリオール」という記載は、表面保護層のバインダー樹脂において用いられたポリオールがバイオマス由来成分を含むことを意味する。また、「イソシアネート化合物」という記載は、表面保護層のバインダー樹脂において用いられたイソシアネート化合物がバイオマス由来成分を含むことを意味する。
また、「表面保護層のポリオールのタイプ」の欄において、「エステル系」という記載は、表面保護層のバインダー樹脂において用いられたポリオールがポリエステルポリオールであることを意味する。
また、「表面保護層のポリオール中のバイオマス由来成分」の欄において、「多官能アルコール」という記載は、表面保護層のバインダー樹脂のポリオールにおいて用いられた成分のうち少なくともポリエステルポリオールの多官能アルコールがバイオマス由来であることを意味する。同様に、「多官能カルボン酸」という記載は、表面保護層のバインダー樹脂のポリオールにおいて用いられた成分のうち少なくともポリエステルポリオールの多官能カルボン酸がバイオマス由来であることを意味する。また、「−」という記載は、表面保護層のバインダー樹脂のポリオールがバイオマス由来成分を含まないことを意味する。
表面保護層11のバインダー樹脂のポリオールとしてポリエーテルポリオールを用いたこと以外は、実施例1Iの場合と同様にして、包装材料20を作製した。具体的には、ポリエーテルポリオールとして、バイオマス由来成分を含む多官能アルコールと化石燃料由来の多官能イソシアネートとの反応物を用いた。
表面保護層11のバインダー樹脂のポリエーテルポリオールとして、化石燃料由来の多官能アルコールとバイオマス由来成分を含む多官能イソシアネートとの反応物を用いたこと以外は、実施例1Lの場合と同様にして、包装材料20を作製した。
表面保護層11のバインダー樹脂として、化石燃料由来のポリエーテルポリオールと、バイオマス由来成分を含むイソシアネート化合物と、化石燃料由来のヒドロキシ(メタ)アクリレートとの反応物であるバイオウレタン(メタ)アクリレートを用いたこと以外は、実施例1Lの場合と同様にして、包装材料20を作製した。
表面保護層11のバインダー樹脂のポリオールとしてポリカーボネートポリオールを用いたこと以外は、実施例1Iの場合と同様にして、包装材料20を作製した。具体的には、ポリカーボネートポリオールとして、バイオマス由来成分を含む多官能アルコールと化石燃料由来のカーボネートとの反応物を用いた。
表面保護層11のバインダー樹脂として、化石燃料由来のポリカーボネートポリオールと、バイオマス由来成分を含むイソシアネート化合物と、化石燃料由来のヒドロキシ(メタ)アクリレートとの反応物であるバイオウレタン(メタ)アクリレートを用いたこと以外は、実施例1Oの場合と同様にして、包装材料20を作製した。
外側熱可塑性樹脂層13及び内側熱可塑性樹脂層15のポリエチレンとしてバイオマス由来成分を含むものを用いたこと以外は、実施例1Aの場合と同様にして、包装材料20を作製した。
表/バイオ印/バイオ外熱17/紙/バイオ内熱(2)28
「バイオ外熱」は、バイオマス由来成分を含む外側熱可塑性樹脂層を意味する。「バイオ内熱(2)」は、溶融押出しラミネート法により形成されたバイオマス由来の内側熱可塑性樹脂層を意味する。
実施例1Aの場合と同様にして、紙基材層14を準備し、紙基材層14上に外側熱可塑性樹脂層13を形成した。外側熱可塑性樹脂層13の厚さは20μmであった。続いて、溶融押出しラミネート法により紙基材層14上にバリア性樹脂層21、中間熱可塑性樹脂層22及び内側熱可塑性樹脂層15を形成した。バリア性樹脂層21としては、EVOHを用いた。バリア性樹脂層21の厚みは5μmであった。中間熱可塑性樹脂層22としては、化石燃料由来のポリエチレンを用いた。中間熱可塑性樹脂層22の厚みは5μmであった。内側熱可塑性樹脂層15としては、化石燃料由来のポリエチレンを用いた。内側熱可塑性樹脂層15の厚みは20μmであった。続いて、実施例1Aの場合と同様にして、外側熱可塑性樹脂層13上に印刷層12及び表面保護層11を形成した。このようにして、図2に示す層構成を有する包装材料20を作製した。
表/バイオ印/外熱20/紙/EVOH5/中熱5/内熱(2)20
「EVOH」は、EVOHを用いたバリア性樹脂層を意味する。「中熱」は、中間熱可塑性樹脂層を意味する。
バリア性樹脂層21としてポリメタキシリレンアジパミドを用いたこと以外は、実施例2と同様にして、包装材料20を作成した。バリア性樹脂層21の厚みは5μmであった。
表/バイオ印/外熱20/紙/MXD6 5/中熱5/内熱(2)20
「MXD6」は、ポリメタキシリレンアジパミドを用いたバリア性樹脂層を意味する。
バリア性樹脂層21としてナイロン6を用いたこと以外は、実施例2と同様にして、包装材料20を作成した。バリア性樹脂層21の厚みは5μmであった。
表/バイオ印/外熱20/紙/6NY5/中熱5/内熱(2)20
「6NY」は、ナイロン6を用いたバリア性樹脂層を意味する。
実施例1Aの場合と同様にして、紙基材層14を準備し、紙基材層14上に外側熱可塑性樹脂層13を形成した。外側熱可塑性樹脂層13の厚さは20μmであった。続いて、溶融押出しラミネート法により紙基材層14上にポリオレフィン樹脂層23、中間熱可塑性樹脂層22、バリア性樹脂層21、中間熱可塑性樹脂層24及び内側熱可塑性樹脂層15を形成した。ポリオレフィン樹脂層23としては、化石燃料由来のポリエチレンを用いた。ポリオレフィン樹脂層23の厚みは20μmであった。中間熱可塑性樹脂層22としては、化石燃料由来のポリエチレンを用いた。中間熱可塑性樹脂層22の厚みは5μmであった。バリア性樹脂層21としては、EVOHを用いた。バリア性樹脂層21の厚みは5μmであった。中間熱可塑性樹脂層24としては、化石燃料由来のポリエチレンを用いた。中間熱可塑性樹脂層24の厚みは5μmであった。内側熱可塑性樹脂層15としては、化石燃料由来のポリエチレンを用いた。内側熱可塑性樹脂層15の厚みは20μmであった。続いて、実施例1Aの場合と同様にして、外側熱可塑性樹脂層13上に印刷層12及び表面保護層11を形成した。このようにして、図3に示す層構成を有する包装材料20を作製した。
表/バイオ印/外熱20/紙/PE20/中熱5/EVOH5/中熱5/内熱(2)20
「PE」は、ポリエチレンを用いたポリオレフィン樹脂層を意味する。
バリア性樹脂層21としてポリメタキシリレンアジパミドを用いたこと以外は、実施例5と同様にして、包装材料20を作成した。バリア性樹脂層21の厚みは5μmであった。
表/バイオ印/外熱20/紙/PE20/中熱5/MXD6 5/中熱5/内熱(2)20
バリア性樹脂層21としてナイロン6を用いたこと以外は、実施例5と同様にして、包装材料20を作成した。バリア性樹脂層21の厚みは5μmであった。
表/バイオ印/外熱20/紙/PE20/中熱5/6NY5/中熱5/内熱(2)20
実施例1Aの場合と同様にして、紙基材層14を準備し、紙基材層14上に外側熱可塑性樹脂層13を形成した。外側熱可塑性樹脂層13の厚さは20μmであった。
表/バイオ印/外熱20/紙/接着樹脂20/AL箔7/接/PET12/AC/内熱(2)50
「AL箔」は、アルミニウム箔を意味する。「接」は、接着剤層を意味する。「PET」は、ポリエチレンテレフタレートを含むPETフィルムを意味する。「AC」は、アンカーコート層を意味する。
実施例1Aの場合と同様にして、紙基材層14を準備し、紙基材層14上に外側熱可塑性樹脂層13を形成した。外側熱可塑性樹脂層13の厚さは20μmであった。
表/バイオ印/外熱20/紙/接着樹脂20/AL箔7/接/PET12/AC/接着樹脂20/内熱(1)40
「内熱(1)」は、化石燃料由来の内側熱可塑性樹脂フィルムを意味する。
実施例1Aの場合と同様にして、紙基材層14を準備し、紙基材層14上に外側熱可塑性樹脂層13を形成した。外側熱可塑性樹脂層13の厚さは20μmであった。
表/バイオ印/外熱20/紙/接着樹脂20/AL箔7/接/PET12/接/内熱(1)60
実施例1Aの場合と同様にして、紙基材層14を準備し、紙基材層14上に外側熱可塑性樹脂層13を形成した。外側熱可塑性樹脂層13の厚さは20μmであった。
表/バイオ印/外熱20/紙/接着樹脂20/AL箔7/内熱(2)40
バリア層26としてポリエチレンテレフタレートフィルム上にアルミニウム蒸着膜を形成した蒸着フィルム(厚さ12μm)を用いたこと以外は、実施例11と同様にして、包装材料20を作成した。
表/バイオ印/外熱20/紙/接着樹脂20/VM-PET12/内熱(2)40
「VM-PET」は、蒸着フィルムを意味する。
実施例1Aの場合と同様にして、紙基材層14を準備し、紙基材層14上に外側熱可塑性樹脂層13を形成した。外側熱可塑性樹脂層13の厚さは20μmであった。
表/バイオ印/外熱20/紙/接着樹脂20/AL箔7/接着樹脂20/内熱(1)40
バリア層26としてポリエチレンテレフタレートフィルム上にアルミニウム蒸着膜を形成した蒸着フィルム(厚さ12μm)を用いたこと以外は、実施例13と同様にして、包装材料20を作成した。
表/バイオ印/外熱20/紙/接着樹脂20/VM-PET12/接着樹脂20/内熱(1)40
実施例1Aの場合と同様にして、紙基材層14を準備し、紙基材層14上に外側熱可塑性樹脂層13を形成した。外側熱可塑性樹脂層13の厚さは20μmであった。
表/バイオ印/外熱20/紙/接着樹脂20/AL箔7/接/内熱(1)60
バリア層26としてポリエチレンテレフタレートフィルム上にアルミニウム蒸着膜を形成した蒸着フィルム(厚さ12μm)を用いたこと以外は、実施例15と同様にして、包装材料20を作成した。
表/バイオ印/外熱20/紙/接着樹脂20/VM-PET12/接/内熱(1)60
実施例1Aの場合と同様にして、紙基材層14を準備し、紙基材層14上に外側熱可塑性樹脂層13を形成した。外側熱可塑性樹脂層13の厚さは20μmであった。
表/バイオ印/外熱20/紙/接着樹脂20/PET12/接/AL箔7/中熱20/内熱(2)40
実施例1Aの場合と同様にして、紙基材層14を準備し、紙基材層14上に外側熱可塑性樹脂層13を形成した。外側熱可塑性樹脂層13の厚さは20μmであった。
表/バイオ印/外熱20/紙/PE20/接着樹脂5/AL箔7/中熱5/内熱(2)30
バリア層26としてポリエチレンテレフタレートフィルム上にアルミニウム蒸着膜を形成した蒸着フィルム(厚さ12μm)を用いたこと以外は、実施例18と同様にして、包装材料20を作成した。
表/バイオ印/外熱20/紙/PE20/接着樹脂5/VM-PET12/中熱5/内熱(2)30
12 印刷層
13 外側熱可塑性樹脂層
14 紙基材層
15 内側熱可塑性樹脂層
20 包装材料
21 バリア性樹脂層
22 中間熱可塑性樹脂層
23 ポリオレフィン樹脂層
24 中間熱可塑性樹脂層
25 接着樹脂層
26 バリア層
27 接着剤層
28 プラスチックフィルム層
29 アンカーコート層
30 接着樹脂層
31 接着剤層
40 液体用紙容器
41 胴部
42 底部
43 上部
44 傾斜板
45 折込部
46 のりしろ
Claims (8)
- 少なくとも、表面保護層、印刷層、外側熱可塑性樹脂層、紙基材層、内側熱可塑性樹脂層が順に積層された包装材料であって、
前記外側熱可塑性樹脂層は、ポリエチレンを含み、
前記印刷層は、着色剤と、ポリオールとイソシアネート化合物とヒドロキシ(メタ)アクリレートとの反応物であるウレタン(メタ)アクリレートと、を含み、
前記ポリオール、前記イソシアネート化合物または前記ヒドロキシ(メタ)アクリレートの少なくともいずれかがバイオマス由来成分を含む、包装材料。 - 前記ポリオールがバイオマス由来成分を含む、請求項1に記載の包装材料。
- 前記イソシアネート化合物がバイオマス由来成分を含む、請求項1又は2に記載の包装材料。
- 前記表面保護層が、ポリオールとイソシアネート化合物とヒドロキシ(メタ)アクリレートとの反応物であるウレタン(メタ)アクリレートを含む、請求項1乃至3のいずれか一項に記載の包装材料。
- 前記表面保護層の前記ポリオール、前記イソシアネート化合物または前記ヒドロキシ(メタ)アクリレートの少なくともいずれかがバイオマス由来成分を含む、請求項4に記載の包装材料。
- 前記紙基材層と前記内側熱可塑性樹脂層との間にバリア層を更に備える、請求項1乃至5のいずれか一項に記載の包装材料。
- 前記バリア層が金属箔又は蒸着フィルムである、請求項6に記載の包装材料。
- 請求項1乃至7のいずれか一項に記載の包装材料を備える、包装製品。