JP2019531203A - 1,1−二活性化ビニル化合物生成物を含有する複数層硬化性組成物および関連方法 - Google Patents
1,1−二活性化ビニル化合物生成物を含有する複数層硬化性組成物および関連方法 Download PDFInfo
- Publication number
- JP2019531203A JP2019531203A JP2019503710A JP2019503710A JP2019531203A JP 2019531203 A JP2019531203 A JP 2019531203A JP 2019503710 A JP2019503710 A JP 2019503710A JP 2019503710 A JP2019503710 A JP 2019503710A JP 2019531203 A JP2019531203 A JP 2019531203A
- Authority
- JP
- Japan
- Prior art keywords
- curable composition
- layer
- composition layer
- coating
- coating layer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
硬化性組成物は、色および/または他の視覚的効果、耐腐食性、接着性、密封性、耐摩耗性、耐化学薬品性等を提供するために、多種多様な基材に塗布することができる。例えば複数層コーティングは、しばしば、色および/または他の視覚的効果を提供するベースコート層、ならびにトップコート層を含み、このトップコート層は、時としてクリアコート層を含み、摩耗および引っ掻き傷防止層を提供する。自動車基材などの金属基材に塗布される複数層コーティングに関して、例えば、上を覆うベースコートおよびトップコートの下で、裸の金属基材に対してプライマー層および/または表面不活性化層が塗布されてもよい。一般に、複数層コーティングの各層は、例えば最終的な複数層コーティングを形成するために、異なる引火温度および/または焼付け温度などの様々な条件下で別個に脱水および/または硬化させられる。
複数層コーティングは、基材の少なくとも一部にわたって塗布された第1のコーティング層、および第1のコーティング層の少なくとも一部にわたって塗布された第2のコーティング層を含む。第1のコーティング層および第2のコーティング層は、共に、独立にポリマー樹脂を含む。第1のコーティング層および/または第2のコーティング層は、硬化した場合、1,1−二活性化ビニル化合物、もしくはその複数官能性形態、またはそれらの組合せの重合反応生成物を含む。
「硬化性組成物」は、本明細書で使用される場合、硬化変換に関与することができる1つまたは複数の構成成分を有する組成物を指す。この組成物は、化学的および/または物理的過程の結果として、ある期間にわたってその物理的特性が変化し得る。硬化性組成物は、室温もしくはより低い温度で硬化することができ、または硬化変換を開始および/もしくは加速するために、室温を超える温度などの高温もしくは他の条件(複数可)への曝露を必要とする場合がある。硬化性組成物が表面に塗布されると(および塗布中)、硬化反応が進行して、硬化した組成物を提供することができる。硬化した組成物は、ある期間にわたって粘着性がない表面を生じ、硬化し、次に完全に硬化する。組成物は、硬度がそれ以上増大しない場合に、完全に硬化したとみなされる。本開示によって提供される硬化性組成物は、単一層(しばしばモノコートと呼ばれる)もしくは複数層として基材の表面上に、および/またはプライマーなどの下層にわたって、任意の適切な方法によって直接的に塗布することができる。
(実施例1A)
金属基材上の1,1−二活性化ビニル化合物の重合生成物を含むコーティング層
1.基材パネルを水平位置にし、そのおよそ3インチ上部に綿ボールを保持し、その綿ボールを、塗布されたコーティング膜上に落下させる。
2.基材パネルのコーティング側を上に向けて5±2秒保持して、綿ボールをコーティング膜と接触させておく。
3.5±2秒後、基材パネルのコーティング側を下に反転する。
a.綿ボールが膜上に繊維を残さずに落下する場合、コーティングには粘着性がない。
b.綿ボールが落下しないか、または繊維を残す場合、コーティングに粘着性がなくなるまで、ステップ1〜3を適切な時間間隔(例えば、15分ごと)で反復する。
コーティング層は、鋼パネルに塗布した後、周囲条件下で15〜30分の間の時点において粘着性がない状態に達した。
(実施例1B)
金属基材上の1,1−二活性化ビニル化合物の重合生成物を含むコーティング層。
(実施例1C)
金属基材上の1,1−二活性化ビニル化合物の重合生成物を含むコーティング層。
(実施例2)
1,1−二活性化ビニル化合物の重合生成物を含む複数層コーティング系。
(実施例3)
1,1−二活性化ビニル化合物の重合生成物を含む複数層コーティング系。
(実施例4A)
1,1−二活性化ビニル化合物の重合生成物を含む複数層コーティング系。
(実施例4B)
比較用の複数層コーティング系。
(実施例5A)
1,1−二活性化ビニル化合物の重合生成物を含む複数層コーティング系
(実施例5B)
比較用の複数層コーティング系。
(実施例6)
1,1−二活性化ビニル化合物およびイオン性液体活性化剤、任意選択でポリチオール、および任意選択でエクステンダーを含む硬化性組成物。
本発明の態様
1.基材の少なくとも一部にわたって塗布された第1の硬化性組成物層、および
前記第1の硬化性組成物層の少なくとも一部にわたって塗布された第2の硬化性組成物層
を含む、複数層硬化性組成物であって、
前記第1の硬化性組成物層および前記第2の硬化性組成物層が、共に、独立にポリマー樹脂を含み、
前記第1の硬化性組成物層および/または前記第2の硬化性組成物層が、硬化した場合、1,1−二活性化ビニル化合物、もしくはその複数官能性形態、またはそれらの組合せの重合反応生成物を含む、
複数層硬化性組成物。
2.前記1,1−二活性化ビニル化合物が、メチレンジカルボニル化合物、ジハロビニル化合物、ジハロアルキル二置換ビニル化合物、もしくはシアノアクリレート化合物、もしくはそのいずれかの複数官能性形態、またはそれらのいずれかの組合せを含む、項1に記載の複数層硬化性組成物。
3.前記第1の硬化性組成物層および/または前記第2の硬化性組成物層が、硬化した場合、ジアルキルメチレンマロネート、ジアリールメチレンマロネート、ジアルキルメチレンマロネートの複数官能性形態、もしくはジアリールメチレンマロネートの複数官能性形態、またはそれらの任意の組合せの重合反応生成物を含む、項1または項2に記載の複数層硬化性組成物。
4.前記第1の硬化性組成物層および/または前記第2の硬化性組成物層が、硬化した場合、ジエチルメチレンマロネートおよびジエチルメチレンマロネートの複数官能性形態の重合反応生成物を含み、ジエチルメチレンマロネートの前記複数官能性形態が、ジエチルメチレンマロネートおよび少なくとも1つのポリオールのエステル交換付加物を含む、項3に記載の複数層硬化性組成物。
5.ジエチルメチレンマロネートおよび少なくとも1つのポリオールの前記エステル交換付加物が、ジエチルメチレンマロネートおよびジオールのエステル交換付加物を含む、項4に記載の複数層硬化性組成物。
6.前記ジオールが、1,5−ペンタンジオールおよび/または1,6−ヘキサンジオールを含む、項5に記載の複数層硬化性組成物。
7. (i)前記第1の硬化性組成物層が、前記第2のコーティング層が前記第1のコーティング層にわたって塗布された場合、前記第2のコーティング層における重合反応を活性化する活性化剤化合物を含み、あるいは、
(ii)前記第2の硬化性組成物層が、前記第2の硬化性組成物が前記第1の硬化性組成物層にわたって塗布されたら前記第1のコーティング層における重合反応を活性化する活性化剤化合物を含む、
項1から6のいずれか一項に記載の複数層硬化性組成物。
8.前記活性化剤化合物が、第三級アミン化合物を含む、項7に記載の複数層硬化性組成物。
9.前記活性化剤化合物が、2−(ジメチルアミノ)エタノールおよび/または1,4−ジアザビシクロ[2.2.2]オクタンを含む、項8に記載の複数層硬化性組成物。
10.前記活性化剤化合物が、イオン性液体を含む、項7に記載の複数層硬化性組成物。
11.前記第1の硬化性組成物層が、500℃未満の温度で加熱されると硬化する硬化性組成物を含み、前記第2の硬化性組成物層が、前記重合反応生成物を含む、項1から10のいずれか一項に記載の複数層硬化性組成物。
12.前記第1のコーティング層が、メラミン樹脂またはホルムアルデヒド縮合物を含まない、項1から11のいずれか一項に記載の複数層硬化性組成物。
13.前記第1の硬化性組成物層が、アクリル樹脂、ポリエステル樹脂、ポリウレタン樹脂、ポリ尿素樹脂、ポリエーテル樹脂、ポリチオエーテル樹脂、ポリカーボネート樹脂、ポリカルバメート樹脂、エポキシ樹脂、フェノール樹脂、もしくはアミノプラスト樹脂、またはそれらの任意の組合せを含む熱硬化性樹脂を含み、前記第2の硬化性組成物層が、前記重合反応生成物を含むクリアコート層を含む、項1から11のいずれか一項に記載の複数層コーティング。
14.前記第1の硬化性組成物層が、前記重合反応生成物を含み、前記第1の硬化性組成物層が、金属基材上に直接的に塗布される、項1から12のいずれか一項に記載の複数層コーティング。
15.前記第1の硬化性組成物層が、前記重合反応生成物を含み、前記第1の硬化性組成物層が、非金属基材上に直接的に塗布される、項1から12に記載の複数層硬化性組成物。
16.前記基材が、ポリマー性である、項1から15に記載の基材。
17.前記非金属基材が、自動車部品である、項1から16に記載の基材。
18.前記基材が、電着硬化性組成物層を含み、前記第1の硬化性組成物層が、前記電着コーティング層にわたって塗布される、項1から13のいずれか一項に記載の複数層コーティング。
19.前記1,1−二活性化ビニル化合物、もしくはその複数官能性形態、またはそれらの組合せの前記重合反応生成物を含む前記硬化性組成物層が、エクステンダーをさらに含む、項1から18のいずれか一項に記載の複数層硬化性組成物。
20.前記エクステンダーが、無水物含有ビニルポリマーを含む、項19に記載の複数層硬化性組成物。
21.前記無水物含有ビニルポリマーが、無水マレイン酸モノマー残基を含む、項20に記載の複数層硬化性組成物。
22.物品の表面にわたって堆積された項1から21のいずれか一項に記載の複数層硬化性組成物を含む、物品。
23.前記物品が、車両部品または自立構造体を含む、項22に記載の物品。
24.硬化性組成物基材のための方法であって、
基材の少なくとも一部にわたって第1の硬化性組成物層を塗布するステップと、
前記第1の硬化性組成物層の少なくとも一部にわたって第2の硬化性組成物層を塗布するステップと、
前記第1の硬化性組成物層および/または前記第2の硬化性組成物層を硬化させるステップとを含み、
前記第1の硬化性組成物層および前記第2の硬化性組成物層が、共に、独立にポリマー樹脂を含み、
前記第1の硬化性組成物層および/または前記第2の硬化性組成物層が、硬化した場合、1,1−二活性化ビニル化合物、もしくはその複数官能性形態、またはそれらの組合せの重合反応生成物を含む、
方法。
25.前記1,1−二活性化ビニル化合物が、メチレンジカルボニル化合物、ジハロビニル化合物、ジハロアルキル二置換ビニル化合物、もしくはシアノアクリレート化合物、もしくはそのいずれかの複数官能性形態、またはそれらのいずれかの組合せを含む、項24に記載の方法。
26.前記第1の硬化性組成物層および/または前記第2の硬化性組成物層を硬化させる前記ステップが、前記第1の硬化性組成物層および/または前記第2の硬化性組成物層の少なくとも一部にわたっておよび/またはその下に、活性化剤溶液をスプレーすることを含む、項24または項25に記載の方法。
27.前記活性化剤溶液が、第三級アミン化合物を含む、項26に記載の方法。
28.前記活性化剤溶液が、1,4−ジアザビシクロ[2.2.2]オクタンおよび/または2−(ジメチルアミノ)エタノールを含む、項27に記載の方法。
29. (i)前記第1の硬化性組成物層が、活性化剤化合物を含み、前記第2の硬化性組成物層を硬化させる前記ステップが、前記第2の硬化性組成物層における重合反応を、前記第1の硬化性組成物層中の前記活性化剤化合物で活性化することを含み、または
(ii)前記第2の硬化性組成物層が、活性化剤化合物を含み、前記第1の硬化性組成物層を硬化させる前記ステップが、前記第1の硬化性組成物層における重合反応を、前記第2の硬化性組成物層中の前記活性化剤化合物で活性化することを含む、
項24から28のいずれか一項に記載の方法。
30.前記活性化剤化合物が、第三級アミン化合物を含む、項29に記載の方法。
31.前記活性化剤化合物が、2−(ジメチルアミノ)エタノールおよび/または1,4−ジアザビシクロ[2.2.2]オクタンを含む、項30に記載の方法。
32.前記活性化剤化合物が、イオン性液体を含む、項29に記載の方法。
33.前記第1の硬化性組成物層および/または前記第2の硬化性組成物層の少なくとも1つが、硬化した場合、ジアルキルメチレンマロネート、ジアリールメチレンマロネート、ジアルキルメチレンマロネートの複数官能性形態、もしくはジアリールメチレンマロネートの複数官能性形態、またはそれらの組合せの重合反応生成物を含む、項24から32のいずれか一項に記載の方法。
34.前記第1の硬化性組成物層および/または前記第2の硬化性組成物層が、ジエチルメチレンマロネートおよびジエチルメチレンマロネートの複数官能性形態の重合反応生成物を含み、ジエチルメチレンマロネートの前記複数官能性形態が、ジエチルメチレンマロネートおよび少なくとも1つのポリオールのエステル交換付加物を含む、項33に記載の方法。
35.ジエチルメチレンマロネートおよび少なくとも1つのポリオールの前記エステル交換付加物が、ジエチルメチレンマロネートおよびジオールのエステル交換付加物を含む、項34に記載の方法。
36.前記第1の硬化性組成物層が、500℃未満の温度で加熱されると硬化する硬化性組成物を含み、前記第2の硬化性組成物層が、前記重合反応生成物を含む、項24から35のいずれか一項に記載の方法。
37.前記第1の硬化性組成物層が、メラミン樹脂またはホルムアルデヒド縮合物を含まない、項24から36のいずれか一項に記載の方法。
38.前記第1の硬化性組成物層が、硬化した場合、アクリル樹脂、ポリエステル樹脂、ポリウレタン樹脂、ポリ尿素樹脂、ポリエーテル樹脂、ポリチオエーテル樹脂、ポリカーボネート樹脂、ポリカルバメート樹脂、エポキシ樹脂、フェノール樹脂、もしくはアミノプラスト樹脂、またはそれらの任意の組合せを含む熱硬化性樹脂を含み、前記第2の硬化性組成物層が、硬化した場合、前記反応生成物を含むクリアコート層を含む、項24から37のいずれか一項に記載の方法。
39.前記第1の硬化性組成物層が、硬化した場合、前記重合反応生成物を含み、前記第1の硬化性組成物層が、金属基材上に直接的に塗布される、項24〜37のいずれか一項に記載の方法。
40.前記基材が、電着硬化性組成物層を含み、前記第1のコーティング層が、前記電着硬化性組成物層にわたって塗布される、項24〜38のいずれか一項に記載の方法。
41.前記1,1−二活性化ビニル化合物、もしくはその複数官能性形態、またはそれらの組合せの前記重合反応生成物を含む前記硬化性組成物層が、エクステンダーをさらに含む、項24〜40のいずれか一項に記載の方法。
42.前記エクステンダーが、無水物含有ビニルポリマーを含む、項41に記載の方法。
43.前記無水物含有ビニルポリマーが、無水マレイン酸モノマー残基を含む、項42に記載の方法。
Claims (43)
- 基材の少なくとも一部にわたって塗布された第1の硬化性組成物層、および
前記第1の硬化性組成物層の少なくとも一部にわたって塗布された第2の硬化性組成物層
を含む、複数層硬化性組成物であって、
前記第1の硬化性組成物層および前記第2の硬化性組成物層が、共に、独立にポリマー樹脂を含み、
前記第1の硬化性組成物層および/または前記第2の硬化性組成物層が、硬化した場合、1,1−二活性化ビニル化合物、もしくはその複数官能性形態、またはそれらの組合せの重合反応生成物を含む、
複数層硬化性組成物。 - 前記1,1−二活性化ビニル化合物が、メチレンジカルボニル化合物、ジハロビニル化合物、ジハロアルキル二置換ビニル化合物、もしくはシアノアクリレート化合物、もしくはそのいずれかの複数官能性形態、またはそれらのいずれかの組合せを含む、請求項1に記載の複数層硬化性組成物。
- 前記第1の硬化性組成物層および/または前記第2の硬化性組成物層が、硬化した場合、ジアルキルメチレンマロネート、ジアリールメチレンマロネート、ジアルキルメチレンマロネートの複数官能性形態、もしくはジアリールメチレンマロネートの複数官能性形態、またはそれらの任意の組合せの重合反応生成物を含む、請求項1に記載の複数層硬化性組成物。
- 前記第1の硬化性組成物層および/または前記第2の硬化性組成物層が、硬化した場合、ジエチルメチレンマロネートおよびジエチルメチレンマロネートの複数官能性形態の重合反応生成物を含み、ジエチルメチレンマロネートの前記複数官能性形態が、ジエチルメチレンマロネートおよび少なくとも1つのポリオールのエステル交換付加物を含む、請求項3に記載の複数層硬化性組成物。
- ジエチルメチレンマロネートおよび少なくとも1つのポリオールの前記エステル交換付加物が、ジエチルメチレンマロネートおよびジオールのエステル交換付加物を含む、請求項4に記載の複数層硬化性組成物。
- 前記ジオールが、1,5−ペンタンジオールおよび/または1,6−ヘキサンジオールを含む、請求項5に記載の複数層硬化性組成物。
- (i)前記第1の硬化性組成物層が、前記第2の硬化性組成物層が前記第1のコーティング層にわたって塗布された場合、前記第2の硬化性組成物層における重合反応を活性化する活性化剤化合物を含み、あるいは、
(ii)前記第2の硬化性組成物層が、前記第2の硬化性組成物層が前記第1の硬化性組成物層にわたって塗布されたら前記第1の硬化性組成物層における重合反応を活性化する活性化剤化合物を含む、
請求項1に記載の複数層硬化性組成物。 - 前記活性化剤化合物が、第三級アミン化合物を含む、請求項7に記載の複数層硬化性組成物。
- 前記活性化剤化合物が、2−(ジメチルアミノ)エタノールおよび/または1,4−ジアザビシクロ[2.2.2]オクタンを含む、請求項8に記載の複数層硬化性組成物。
- 前記活性化剤化合物が、イオン性液体を含む、請求項7に記載の複数層硬化性組成物。
- 前記第1の硬化性組成物層が、500℃未満の温度で加熱されると硬化する硬化性組成物を含み、前記第2の硬化性組成物層が、前記重合反応生成物を含む、請求項1に記載の複数層硬化性組成物。
- 前記第1の硬化性組成物層が、メラミン樹脂またはホルムアルデヒド縮合物を含まない、請求項11に記載の複数層硬化性組成物。
- 前記第1の硬化性組成物層が、アクリル樹脂、ポリエステル樹脂、ポリウレタン樹脂、ポリ尿素樹脂、ポリエーテル樹脂、ポリチオエーテル樹脂、ポリカーボネート樹脂、ポリカルバメート樹脂、エポキシ樹脂、フェノール樹脂、もしくはアミノプラスト樹脂、またはそれらの任意の組合せを含む熱硬化性樹脂を含み、前記第2の硬化性組成物層が、前記重合反応生成物を含むクリアコート層を含む、請求項1に記載の複数層硬化性組成物。
- 前記第1の硬化性組成物層が、前記重合反応生成物を含み、前記第1の硬化性組成物層が、金属基材上に直接的に塗布される、請求項1に記載の複数層硬化性組成物。
- 前記第1の硬化性組成物層が、前記重合反応生成物を含み、前記第1の硬化性組成物層が、非金属基材上に直接的に塗布される、請求項1に記載の複数層硬化性組成物。
- 前記基材が、ポリマー性である、請求項15に記載の基材。
- 前記非金属基材が、自動車部品である、請求項15に記載の基材。
- 前記基材が、電着硬化性組成物層を含み、前記第1の硬化性組成物層が、前記電着硬化性組成物層にわたって塗布される、請求項1に記載の複数層硬化性組成物。
- 前記1,1−二活性化ビニル化合物、もしくはその複数官能性形態、またはそれらの組合せの前記重合反応生成物を含む前記硬化性組成物層が、エクステンダーをさらに含む、請求項1に記載の複数層硬化性組成物。
- 前記エクステンダーが、無水物含有ビニルポリマーを含む、請求項19に記載の複数層硬化性組成物。
- 前記無水物含有ビニルポリマーが、無水マレイン酸モノマー残基を含む、請求項20に記載の複数層硬化性組成物。
- 物品の表面にわたって堆積された請求項1に記載の複数層硬化性組成物を含む、物品。
- 前記物品が、車両部品または自立構造体を含む、請求項22に記載の物品。
- 硬化性組成物基材のための方法であって、
基材の少なくとも一部にわたって第1の硬化性組成物層を塗布するステップと、
前記第1の硬化性組成物層の少なくとも一部にわたって第2の硬化性組成物層を塗布するステップと、
前記第1の硬化性組成物層および/または前記第2の硬化性組成物層を硬化させるステップとを含み、
前記第1の硬化性組成物層および前記第2のコーティング層が、共に、独立にポリマー樹脂を含み、
前記第1の硬化性組成物層および/または前記第2の硬化性組成物層が、硬化した場合、1,1−二活性化ビニル化合物、もしくはその複数官能性形態、またはそれらの組合せの重合反応生成物を含む、
方法。 - 前記1,1−二活性化ビニル化合物が、メチレンジカルボニル化合物、ジハロビニル化合物、ジハロアルキル二置換ビニル化合物、もしくはシアノアクリレート化合物、もしくはそのいずれかの複数官能性形態、またはそれらのいずれかの組合せを含む、請求項24に記載の方法。
- 前記第1の硬化性組成物層および/または前記第2の硬化性組成物層を硬化させる前記ステップが、前記第1の硬化性組成物層および/または前記第2の硬化性組成物層の少なくとも一部にわたっておよび/またはその下に、活性化剤溶液を塗布することを含む、請求項24に記載の方法。
- 前記活性化剤溶液が、第三級アミン化合物を含む、請求項26に記載の方法。
- 前記活性化剤溶液が、1,4−ジアザビシクロ[2.2.2]オクタンおよび/または2−(ジメチルアミノ)エタノールを含む、請求項27に記載の方法。
- (i)前記第1の硬化性組成物層が、活性化剤化合物を含み、前記第2の硬化性組成物層を硬化させる前記ステップが、前記第2の硬化性組成物層における重合反応を、前記第1の硬化性組成物層中の前記活性化剤化合物で活性化することを含み、または
(ii)前記第2の硬化性組成物層が、活性化剤化合物を含み、前記第1の硬化性組成物層を硬化させる前記ステップが、前記第1の硬化性組成物層における重合反応を、前記第2のコーティング層中の前記活性化剤化合物で活性化することを含む、
請求項24に記載の方法。 - 前記活性化剤化合物が、第三級アミン化合物を含む、請求項29に記載の方法。
- 前記活性化剤化合物が、2−(ジメチルアミノ)エタノールおよび/または1,4−ジアザビシクロ[2.2.2]オクタンを含む、請求項30に記載の方法。
- 前記活性化剤化合物が、イオン性液体を含む、請求項29に記載の方法。
- 前記第1の硬化性組成物層および/または前記第2の硬化性組成物層の少なくとも1つが、硬化した場合、ジアルキルメチレンマロネート、ジアリールメチレンマロネート、ジアルキルメチレンマロネートの複数官能性形態、もしくはジアリールメチレンマロネートの複数官能性形態、またはそれらの組合せの重合反応生成物を含む、請求項24に記載の方法。
- 前記第1の硬化性組成物層および/または前記第2の硬化性組成物層が、ジエチルメチレンマロネートおよびジエチルメチレンマロネートの複数官能性形態の重合反応生成物を含み、ジエチルメチレンマロネートの前記複数官能性形態が、ジエチルメチレンマロネートおよび少なくとも1つのポリオールのエステル交換付加物を含む、請求項33に記載の方法。
- ジエチルメチレンマロネートおよび少なくとも1つのポリオールの前記エステル交換付加物が、ジエチルメチレンマロネートおよびジオールのエステル交換付加物を含む、請求項34に記載の方法。
- 前記第1の硬化性組成物層が、500℃未満の温度で加熱されると硬化する硬化性組成物を含み、前記第2のコーティング層が、前記重合反応生成物を含む、請求項24に記載の方法。
- 前記第1の硬化性組成物層が、メラミン樹脂またはホルムアルデヒド縮合物を含まない、請求項36に記載の方法。
- 前記第1の硬化性組成物層が、硬化した場合、アクリル樹脂、ポリエステル樹脂、ポリウレタン樹脂、ポリ尿素樹脂、ポリエーテル樹脂、ポリチオエーテル樹脂、ポリカーボネート樹脂、ポリカルバメート樹脂、エポキシ樹脂、フェノール樹脂、もしくはアミノプラスト樹脂、またはそれらの任意の組合せを含む熱硬化性樹脂を含み、前記第2のコーティング層が、硬化した場合、前記重合反応生成物を含むクリアコート層を含む、請求項24に記載の方法。
- 前記第1の硬化性組成物層が、硬化した場合、前記重合反応生成物を含み、前記第1の硬化性組成物層が、金属基材上に直接的に塗布される、請求項24に記載の方法。
- 前記基材が、電着硬化性組成物層を含み、前記第1の硬化性組成物層が、前記電着硬化性組成物層にわたって塗布される、請求項24に記載の方法。
- 前記1,1−二活性化ビニル化合物、もしくはその複数官能性形態、またはそれらの組合せの前記重合反応生成物を含む前記硬化性組成物層が、エクステンダーをさらに含む、請求項24に記載の方法。
- 前記エクステンダーが、無水物含有ビニルポリマーを含む、請求項41に記載の方法。
- 前記無水物含有ビニルポリマーが、無水マレイン酸モノマー残基を含む、請求項42に記載の方法。