JP2019059940A - 光学フィルム用粘着剤組成物、光学フィルム用粘着剤層、粘着剤層付光学フィルムおよび画像表示装置 - Google Patents
光学フィルム用粘着剤組成物、光学フィルム用粘着剤層、粘着剤層付光学フィルムおよび画像表示装置 Download PDFInfo
- Publication number
- JP2019059940A JP2019059940A JP2018214072A JP2018214072A JP2019059940A JP 2019059940 A JP2019059940 A JP 2019059940A JP 2018214072 A JP2018214072 A JP 2018214072A JP 2018214072 A JP2018214072 A JP 2018214072A JP 2019059940 A JP2019059940 A JP 2019059940A
- Authority
- JP
- Japan
- Prior art keywords
- sensitive adhesive
- meth
- pressure
- weight
- optical film
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
モノマー単位として、アルキル(メタ)アクリレート(a1)70重量%以上、
芳香環含有(メタ)アクリレート(a2)3〜25重量%、
アミド基含有モノマー(a3)0.1〜8重量%、
カルボキシル基含有モノマー(a4)0.01〜2重量%、および、
ヒドロキシル基含有モノマー(a5)0.01〜3重量%を含有し、
重量平均分子量(Mw)が100万〜250万であり、かつ、Mw/数平均分子量(Mn)が1.8以上10以下を満足する(メタ)アクリル系ポリマー(A)、並びに、架橋剤(B)を前記(メタ)アクリル系ポリマー(A)100重量部に対して、0.01〜3重量部を含有することを特徴とする光学フィルム用粘着剤組成物、に関する。
アルカリ金属塩のカチオン部を構成するアルカリ金属イオンとしては、リチウム、ナトリウム、カリウムの各イオンが挙げられる。これらアルカリ金属イオンのなかでもリチウムイオンが好ましい。
(1):(CnF2n+1SO2)2N− (但し、nは1〜10の整数)、
(2):CF2(CmF2mSO2)2N− (但し、mは1〜10の整数)、
(3):−O3S(CF2)lSO3 − (但し、lは1〜10の整数)、
(4):(CpF2p+1SO2)N−(CqF2q+1SO2)、(但し、p、qは1〜10の整数)、で表わされるもの等が用いられる。特に、フッ素原子を含むアニオン部は、イオン解離性の良いイオン化合物が得られることから好ましく用いられる。無機塩を構成するアニオン部としては、Cl−、Br−、I−、AlCl4 −、Al2Cl7 −、BF4 −、PF6 −、ClO4 −、NO3 −、AsF6 −、SbF6 −、NbF6 −、TaF6 −、(CN)2N−、等が用いられる。アニオン部としては、(CF3SO2)2N−、(C2F5SO2)2N−、等の前記一般式(1)で表わされる、(ペルフルオロアルキルスルホニル)イミドが好ましく、特に(CF3SO2)2N−、で表わされる(トリフルオロメタンスルホニル)イミドが好ましい。
本発明で用いられる有機カチオン−アニオン塩は、カチオン成分とアニオン成分とから構成されており、前記カチオン成分は有機物からなるものである。カチオン成分として、具体的には、ピリジニウムカチオン、ピペリジニウムカチオン、ピロリジニウムカチオン、ピロリン骨格を有するカチオン、ピロール骨格を有するカチオン、イミダゾリウムカチオン、テトラヒドロピリミジニウムカチオン、ジヒドロピリミジニウムカチオン、ピラゾリウムカチオン、ピラゾリニウムカチオン、テトラアルキルアンモニウムカチオン、トリアルキルスルホニウムカチオン、テトラアルキルホスホニウムカチオン等が挙げられる。
(1):(CnF2n+1SO2)2N− (但し、nは1〜10の整数)、
(2):CF2(CmF2mSO2)2N− (但し、mは1〜10の整数)、
(3):−O3S(CF2)lSO3 − (但し、lは1〜10の整数)、
(4):(CpF2p+1SO2)N−(CqF2q+1SO2)、(但し、p、qは1〜10の整数)、で表わされるもの等が用いられる。なかでも特に、フッ素原子を含むアニオン成分は、イオン解離性の良いイオン化合物が得られることから好ましく用いられる。
例えば、1−ブチルピリジニウムテトラフルオロボレート、1−ブチルピリジニウムヘキサフルオロホスフェート、1−ブチル−3−メチルピリジニウムテトラフルオロボレート、1−ブチル−3−メチルピリジニウムトリフルオロメタンスルホネート、1−ブチル−3−メチルピリジニウムビス(トリフルオロメタンスルホニル)イミド、1−ブチル−3−メチルピリジニウムビス(ペンタフルオロエタンスルホニル)イミド、1−へキシルピリジニウムテトラフルオロボレート、2−メチル−1−ピロリンテトラフルオロボレート、1−エチル−2−フェニルインドールテトラフルオロボレート、1,2−ジメチルインドールテトラフルオロボレート、1−エチルカルバゾールテトラフルオロボレート、1−エチル−3−メチルイミダゾリウムテトラフルオロボレート、1−エチル−3−メチルイミダゾリウムアセテート、1−エチル−3−メチルイミダゾリウムトリフルオロアセテート、1−エチル−3−メチルイミダゾリウムヘプタフルオロブチレート、1−エチル−3−メチルイミダゾリウムトリフルオロメタンスルホネート、1−エチル−3−メチルイミダゾリウムペルフルオロブタンスルホネート、1−エチル−3−メチルイミダゾリウムジシアナミド、1−エチル−3−メチルイミダゾリウムビス(トリフルオロメタンスルホニル)イミド、1−エチル−3−メチルイミダゾリウムビス(ペンタフルオロエタンスルホニル)イミド、1−エチル−3−メチルイミダゾリウムトリス(トリフルオロメタンスルホニル)メチド、1−ブチル−3−メチルイミダゾリウムテトラフルオロボレート、1−ブチル−3−メチルイミダゾリウムヘキサフルオロホスフェート、1−ブチル−3−メチルイミダゾリウムトリフルオロアセテート、1−ブチル−3−メチルイミダゾリウムヘプタフルオロブチレート、1−ブチル−3−メチルイミダゾリウムトリフルオロメタンスルホネート、1−ブチル−3−メチルイミダゾリウムペルフルオロブタンスルホネート、1−ブチル−3−メチルイミダゾリウムビス(トリフルオロメタンスルホニル)イミド、1−へキシル−3−メチルイミダゾリウムブロミド、1−へキシル−3−メチルイミダゾリウムクロライド、1−へキシル−3−メチルイミダゾリウムテトラフルオロボレート、1−へキシル−3−メチルイミダゾリウムヘキサフルオロホスフェート、1−へキシル−3−メチルイミダゾリウムトリフルオロメタンスルホネート、1−オクチル−3−メチルイミダゾリウムテトラフルオロボレート、1−オクチル−3−メチルイミダゾリウムヘキサフルオロホスフェート、1−へキシル−2,3−ジメチルイミダゾリウムテトラフルオロボレート、1,2−ジメチル−3−プロピルイミダゾリウムビス(トリフルオロメタンスルホニル)イミド、1−メチルピラゾリウムテトラフルオロボレート、3−メチルピラゾリウムテトラフルオロボレート、テトラヘキシルアンモニウムビス(トリフルオロメタンスルホニル)イミド、ジアリルジメチルアンモニウムテトラフルオロボレート、ジアリルジメチルアンモニウムトリフルオロメタンスルホネート、ジアリルジメチルアンモニウムビス(トリフルオロメタンスルホニル)イミド、ジアリルジメチルアンモニウムビス(ペンタフルオロエタンスルホニル)イミド、N,N―ジエチル―N―メチル―N−(2−メトキシエチル)アンモニウムテトラフルオロボレート、N,N―ジエチル―N―メチル―N−(2−メトキシエチル)アンモニウムトリフルオロメタンスルホネート、N,N―ジエチル―N―メチル―N−(2−メトキシエチル)アンモニウムビス(トリフルオロメタンスルホニル)イミド、N,N―ジエチル―N―メチル―N−(2−メトキシエチル)アンモニウムビス(ペンタフルオロエタンスルホニル)イミド、グリシジルトリメチルアンモニウムトリフルオロメタンスルホネート、グリシジルトリメチルアンモニウムビス(トリフルオロメタンスルホニル)イミド、グリシジルトリメチルアンモニウムビス(ペンタフルオロエタンスルホニル)イミド、1−ブチルピリジニウム(トリフルオロメタンスルホニル)トリフルオロアセトアミド、1−ブチル−3−メチルピリジニウム(トリフルオロメタンスルホニル)トリフルオロアセトアミド、1−エチル−3−メチルイミダゾリウム(トリフルオロメタンスルホニル)トリフルオロアセトアミド、N,N―ジエチル―N−メチル−N−(2−メトキシエチル)アンモニウム(トリフルオロメタンスルホニル)トリフルオロアセトアミド、ジアリルジメチルアンモニウム(トリフルオロメタンスルホニル)トリフルオロアセトアミド、グリシジルトリメチルアンモニウム(トリフルオロメタンスルホニル)トリフルオロアセトアミド、N,N−ジメチル−N−エチル−N−プロピルアンモニウムビス(トリフルオロメタンスルホニル)イミド、N,N−ジメチル−N−エチル−N−ブチルアンモニウムビス(トリフルオロメタンスルホニル)イミド、N,N−ジメチル−N−エチル−N−ペンチルアンモニウムビス(トリフルオロメタンスルホニル)イミド、N,N−ジメチル−N−エチル−N−へキシルアンモニウムビス(トリフルオロメタンスルホニル)イミド、N,N−ジメチル−N−エチル−N−ヘプチルアンモニウムビス(トリフルオロメタンスルホニル)イミド、N,N−ジメチル−N−エチル−N−ノニルアンモニウムビス(トリフルオロメタンスルホニル)イミド、N,N−ジメチル−N,N−ジプロピルアンモニウムビス(トリフルオロメタンスルホニル)イミド、N,N−ジメチル−N−プロピル−N−ブチルアンモニウムビス(トリフルオロメタンスルホニル)イミド、N,N−ジメチル−N−プロピル−N−ペンチルアンモニウムビス(トリフルオロメタンスルホニル)イミド、N,N−ジメチル−N−プロピル−N−ヘキシルアンモニウムビス(トリフルオロメタンスルホニル)イミド、N,N−ジメチル−N−プロピル−N−ヘプチルアンモニウムビス(トリフルオロメタンスルホニル)イミド、N,N−ジメチル−N−ブチル−N−ヘキシルアンモニウムビス(トリフルオロメタンスルホニル)イミド、N,N−ジメチル−N−ブチル−N−ヘプチルアンモニウムビス(トリフルオロメタンスルホニル)イミド、N,N−ジメチル−N−ペンチル−N−ヘキシルアンモニウムビス(トリフルオロメタンスルホニル)イミド、N,N−ジメチル−N,N−ジヘキシルアンモニウムビス(トリフルオロメタンスルホニル)イミド、トリメチルヘプチルアンモニウムビス(トリフルオロメタンスルホニル)イミド、N,N−ジエチル−N−メチル−N−プロピルアンモニウムビス(トリフルオロメタンスルホニル)イミド、N,N−ジエチル−N−メチル−N−ペンチルアンモニウムビス(トリフルオロメタンスルホニル)イミド、N,N−ジエチル−N−メチル−N−ヘプチルアンモニウムビス(トリフルオロメタンスルホニル)イミド、N,N−ジエチル−N−プロピル−N−ペンチルアンモニウムビス(トリフルオロメタンスルホニル)イミド、トリエチルプロピルアンモニウムビス(トリフルオロメタンスルホニル)イミド、トリエチルペンチルアンモニウムビス(トリフルオロメタンスルホニル)イミド、トリエチルヘプチルアンモニウムビス(トリフルオロメタンスルホニル)イミド、N,N−ジプロピル−N−メチル−N−エチルアンモニウムビス(トリフルオロメタンスルホニル)イミド、N,N−ジプロピル−N−メチル−N−ペンチルアンモニウムビス(トリフルオロメタンスルホニル)イミド、N,N−ジプロピル−N−ブチル−N−へキシルアンモニウムビス(トリフルオロメタンスルホニル)イミド、N,N−ジプロピル−N,N−ジヘキシルアンモニウムビス(トリフルオロメタンスルホニル)イミド、N,N−ジブチル−N−メチル−N−ペンチルアンモニウムビス(トリフルオロメタンスルホニル)イミド、N,N−ジブチル−N−メチル−N−ヘキシルアンモニウムビス(トリフルオロメタンスルホニル)イミド、トリオクチルメチルアンモニウムビス(トリフルオロメタンスルホニル)イミド、N−メチル−N−エチル−N−プロピル−N−ペンチルアンモニウムビス(トリフルオロメタンスルホニル)イミド、1−ブチル−3メチルピリジン−1−イウムトリフルオロメタンスルホナート等が挙げられる。これらの市販品として、例えば、「CIL−314」(日本カーリット社製)、「ILA2−1」(広栄化学社製)等が使用可能である。
また、例えば、テトラメチルアンモニウムビス(トリフルオロメタンスルホニル)イミド、トリメチルエチルアンモニウムビス(トリフルオロメタンスルホニル)イミド、トリメチルブチルアンモニウムビス(トリフルオロメタンスルホニル)イミド、トリメチルペンチルアンモニウムビス(トリフルオロメタンスルホニル)イミド、トリメチルヘプチルアンモニウムビス(トリフルオロメタンスルホニル)イミド、トリメチルオクチルアンモニウムビス(トリフルオロメタンスルホニル)イミド、テトラエチルアンモニウムビス(トリフルオロメタンスルホニル)イミド、トリエチルブチルアンモニウムビス(トリフルオロメタンスルホニル)イミド、テトラブチルアンモニウムビス(トリフルオロメタンスルホニル)イミド、テトラヘキシルアンモニウムビス(トリフルオロメタンスルホニル)イミド、等が挙げられる。
また、例えば、1−ジメチルピロリジニウムビス(トリフルオロメタンスルホニル)イミド、1−メチル−1−エチルピロリジニウムビス(トリフルオロメタンスルホニル)イミド、1−メチル−1−プロピルピロリジニウムビス(トリフルオロメタンスルホニル)イミド、1−メチル−1−ブチルピロリジニウムビス(トリフルオロメタンスルホニル)イミド、1−メチル−1−ペンチルピロリジニウムビス(トリフルオロメタンスルホニル)イミド、1−メチル−1−ヘキシルピロリジニウムビス(トリフルオロメタンスルホニル)イミド、1−メチル−1−へプチルピロリジニウムビス(トリフルオロメタンスルホニル)イミド、1−エチル−1−プロピルピロリジニウムビス(トリフルオロメタンスルホニル)イミド、1−エチル−1−ブチルピロリジニウムビス(トリフルオロメタンスルホニル)イミド、1−エチル−1−ペンチルピロリジニウムビス(トリフルオロメタンスルホニル)イミド、1−エチル−1−へキシルピロリジニウムビス(トリフルオロメタンスルホニル)イミド、1−エチル−1−へプチルピロリジニウムビス(トリフルオロメタンスルホニル)イミド、1,1−ジプロピルピロリジニウムビス(トリフルオロメタンスルホニル)イミド、1−プロピル−1−ブチルピロリジニウムビス(トリフルオロメタンスルホニル)イミド、1,1−ジブチルピロリジニウムビス(トリフルオロメタンスルホニル)イミド、1−プロピルピペリジニウムビス(トリフルオロメタンスルホニル)イミド、1−ペンチルピペリジニウムビス(トリフルオロメタンスルホニル)イミド、1,1−ジメチルピペリジニウムビス(トリフルオロメタンスルホニル)イミド、1−メチル−1−エチルピペリジニウムビス(トリフルオロメタンスルホニル)イミド、1−メチル−1―プロピルピペリジニウムビス(トリフルオロメタンスルホニル)イミド、1−メチル−1−ブチルピペリジニウムビス(トリフルオロメタンスルホニル)イミド、1−メチル−1−ペンチルピペリジニウムビス(トリフルオロメタンスルホニル)イミド、1−メチル−1−ヘキシルピペリジニウムビス(トリフルオロメタンスルホニル)イミド、1−メチル−1−へプチルピペリジニウムビス(トリフルオロメタンスルホニル)イミド、1−エチル−1−プロピルピペリジニウムビス(トリフルオロメタンスルホニル)イミド、1−エチル−1−ブチルピペリジニウムビス(トリフルオロメタンスルホニル)イミド、1−エチル−1−ペンチルピペリジニウムビス(トリフルオロメタンスルホニル)イミド、1−エチル−1−ヘキシルピペリジニウムビス(トリフルオロメタンスルホニル)イミド、1―エチル−1−ヘプチルピペリジニウムビス(トリフルオロメタンスルホニル)イミド、1,1−ジプロピルピペリジニウムビス(トリフルオロメタンスルホニル)イミド、1−プロピル−1−ブチルピペリジニウムビス(トリフルオロメタンスルホニル)イミド、1,1−ジブチルピペリジニウムビス(トリフルオロメタンスルホニル)イミド、1,1−ジメチルピロリジニウムビス(ペンタフルオロエタンスルホニル)イミド、1−メチル−1−エチルピロリジニウムビス(ペンタフルオロエタンスルホニル)イミド、1−メチル−1−プロピルピロリジニウムビス(ペンタフルオロエタンスルホニル)イミド、1−メチル−1―ブチルピロリジニウムビス(ペンタフルオロエタンスルホニル)イミド、1−メチル−1−ペンチルピロリジニウムビス(ペンタフルオロエタンスルホニル)イミド、1−メチル−1−ヘキシルピロリジニウムビス(ペンタフルオロエタンスルホニル)イミド、1−メチル−1―へプチルピロリジニウムビス(ペンタフルオロエタンスルホニル)イミド、1−エチル−1−プロピルピロリジニウムビス(ペンタフルオロエタンスルホニル)イミド、1−エチル−1−ブチルピロリジニウムビス(ペンタフルオロエタンスルホニル)イミド、1−エチル−1−ペンチルピロリジニウムビス(ペンタフルオロエタンスルホニル)イミド、1−エチル−1−ヘキシルピロリジニウムビス(ペンタフルオロエタンスルホニル)イミド、1−エチル−1−へプチルピロリジニウムビス(ペンタフルオロエタンスルホニル)イミド、1,1−ジプロピルピロリジニウムビス(ペンタフルオロエタンスルホニル)イミド、1―プロピル−1−ブチルピロリジニウムビス(ペンタフルオロエタンスルホニル)イミド、1,1−ジブチルピロリジニウムビス(ペンタフルオロエタンスルホニル)イミド、1−プロピルピペリジニウムビス(ペンタフルオロエタンスルホニル)イミド、1−ペンチルピペリジニウムビス(ペンタフルオロエタンスルホニル)イミド、1,1−ジメチルピペリジニウムビス(ペンタフルオロエタンスルホニル)イミド、1−メチル‐1−エチルピペリジニウムビス(ペンタフルオロエタンスルホニル)イミド、1−メチル−1−プロピルピペリジニウムビス(ペンタフルオロエタンスルホニル)イミド、1−メチル−1−ブチルピペリジニウムビス(ペンタフルオロエタンスルホニル)イミド、1−メチル−1−ペンチルピペリジニウムビス(ペンタフルオロエタンスルホニル)イミド、1−メチル−1−ヘキシルピペリジニウムビス(ペンタフルオロエタンスルホニル)イミド、1−メチル−1へプチルピペリジニウムビス(ペンタフルオロエタンスルホニル)イミド、1−エチル−1−プロピルピペリジニウムビス(ペンタフルオロエタンスルホニル)イミド、1−エチル−1−ヘプチルピペリジニウムビス(ペンタフルオロエタンスルホニル)イミド,1−エチル−1−ペンチルピペリジニウムビス(ペンタフルオロエタンスルホニル)イミド、1−エチル−1−ヘキシルピペリジニウムビス(ペンタフルオロエタンスルポニル)イミド、1−エチル−1−へプチルピペリジニウムビス(ペンタフルオロエタンスルホニル)イミド、1−プロピル−1−ブチルピペリジニウムビス(ペンタフルオロエタンスルホニル)イミド、1,1−ジプロピルピペリジニウムビス(ペンタフルオロエタンスルホニル)イミド、1,1―ジブチルピペリジニウムビス(ペンタフルオロエタンスルホニル)イミド等が挙げられる。
また、上記化合物のカチオン成分の代わりに、トリメチルスルホニウムカチオン、トリエチルスルホニウムカチオン、トリブチルスルホニウムカチオン、トリヘキシルスルホニウムカチオン、ジエチルメチルスルホニウムカチオン、ジブチルエチルスルホニウムカチオン、ジメチルデシルスルホニウムカチオン、テトラメチルホスホニウムカチオン、テトラエチルホスホニウムカチオン、テトラブチルホスホニウムカチオン、テトラヘキシルホスホニウムカチオンを用いた化合物等が挙げられる。
また、上記のビス(トリフルオロメタンスルホニル)イミドの代わりに、ビス(ペンタフルオロスルホニル)イミド、ビス(ヘプタフルオロプロパンスルホニル)イミド、ビス(ノナフルオロブタンスルホニル)イミド、トリフルオロメタンスルホニルノナフルオロブタンスルホニルイミド、ヘプタフルオロプロパンスルホニルトリフルオロメタンスルホニルイミド、ペンタフルオロエタンスルホニルノナフルオロブタンスルホニルイミド、シクロ−ヘキサフルオロプロパン−1,3−ビス(スルホニル)イミドアニオン等を用いた化合物等が挙げられる。
一般式(2):RaM3−aSi−X−Y−(AO)n−Z(式中、Rは、置換基を有していてもよい、炭素数1〜20の1価の有機基であり、Mは水酸基又は加水分解性基であり、aは0〜2の整数である。但し、Rが複数存在するとき複数のRは互いに同一であっても異なっていてもよく、Mが複数存在するとき複数のMは互いに同一であっても異なっていてもよい。AOは、直鎖または分岐鎖の炭素数1〜10のオキシアルキレン基を示し、nは1〜1700であり、オキシアルキレン基の平均付加モル数を示す。Xは、炭素数1〜20の直鎖または分岐鎖のアルキレン基を示す。Yは、エーテル結合、エステル結合、ウレタン結合、またはカーボネート結合を示す。
Zは、水素原子、1価の炭素数1〜10の炭化水素基、
一般式(2A):−Y1−X−SiRaM3−a(式中、R、M、Xは、前記と同じ。Y1は単結合、−CO−結合、−CONH−結合、または−COO−結合を示す。)、または、
一般式(2B):−Q{−(OA)n−Y−X−SiRaM3−a}m(式中、R、M、X、Yは、前記と同じ。OAは前記のAOに同じで、nは前記と同じ。Qは、2価以上の炭素数1〜10の炭化水素基であり、mは当該炭化水素基の価数と同じ。)で表される基である。)で表される化合物が挙げられる。
(メタ)アクリル系ポリマー(A)の重量平均分子量(Mw)は、GPC(ゲル・パーミエーション・クロマトグラフィー)により測定した。Mw/Mnについても、同様に測定した。
・分析装置:東ソー社製、HLC−8120GPC
・カラム:東ソー社製、G7000HXL+GMHXL+GMHXL
・カラムサイズ:各7.8mmφ×30cm 計90cm
・カラム温度:40℃
・流量:0.8mL/min
・注入量:100μL
・溶離液:テトラヒドロフラン
・検出器:示差屈折計(RI)
・標準試料:ポリスチレン
厚さ80μmのポリビニルアルコールフィルムを、速度比の異なるロール間において、30℃、0.3%濃度のヨウ素溶液中で1分間染色しながら、3倍まで延伸した。その後、60℃、4%濃度のホウ酸、10%濃度のヨウ化カリウムを含む水溶液中に0.5分間浸漬しながら総合延伸倍率が6倍まで延伸した。次いで、30℃、1.5%濃度のヨウ化カリウムを含む水溶液中に10秒間浸漬することで洗浄した後、50℃で4分間乾燥を行い、厚さ30μmの偏光子を得た。当該偏光子の両面に、けん化処理した厚さ80μmのトリアセチルセルロースフィルムをポリビニルアルコール系接着剤により貼り合せて偏光フィルムを作成した。
(アクリル系ポリマー(A1)の調製)
攪拌羽根、温度計、窒素ガス導入管、冷却器を備えた4つ口フラスコに、ブチルアクリレート74.8部、フェノキシエチルアクリレート23部、N−ビニル−2−ピロリドン1.5部、アクリル酸0.3部、4−ヒドロキシブチルアクリレート0.4部を含有するモノマー混合物を仕込んだ。さらに、前記モノマー混合物(固形分)100部に対して、重合開始剤として2,2’−アゾビスイソブチロニトリル0.1部を酢酸エチル100部と共に仕込み、緩やかに攪拌しながら窒素ガスを導入して窒素置換した後、フラスコ内の液温を55℃付近に保って8時間重合反応を行って、重量平均分子量(Mw)160万、Mw/Mn=3.7のアクリル系ポリマー(A1)の溶液を調製した。
製造例1で得られたアクリル系ポリマー(A1)の溶液の固形分100部に対して、イソシアネート架橋剤(三井化学社製のタケネートD160N,トリメチロールプロパンヘキサメチレンジイソシアネート)0.1部、ベンゾイルパーオキサイド(日本油脂社製のナイパーBMT)0.3部、およびγ−グリシドキシプロピルメトキシシラン(信越化学工業社製:KBM−403)0.2部を配合して、アクリル系粘着剤組成物の溶液を調製した。
次いで、上記アクリル系粘着剤組成物の溶液を、シリコーン系剥離剤で処理されたポリエチレンテレフタレートフィルム(セパレータフィルム:三菱化学ポリエステルフィルム(株)製,MRF38)の片面に、乾燥後の粘着剤層の厚さが23μmになるように塗布し、155℃で1分間乾燥を行い、セパレータフィルムの表面に粘着剤層を形成した。次いで、上記で作成した偏光フィルムに、セパレータフィルム上に形成した粘着剤層を転写して、粘着剤層付偏光フィルムを作製した。
実施例1において、表1に示すように、アクリル系ポリマー(A)の調製に用いたモノマーの種類、その使用割合を変え、また製造条件を制御して、表1に記載のポリマー性状(重量平均分子量,Mw/Mn)のアクリル系ポリマーの溶液を調製した。
粘着剤層付偏光フィルムを37インチサイズに切断したものをサンプルとした。当該サンプルを、厚さ0.7mmの無アルカリガラス(コーニング社製,EG−XG)にラミネーターを用いて貼着した。次いで、50℃、0.5MPaで15分間オートクレーブ処理して、上記サンプルを完全に無アクリルガラスに密着させた。かかる処理の施されたサンプルに、80℃、85℃、90℃(但し、90℃については、実施例3、23、25、28、29と比較例4、5についてのみ)の各雰囲気下で500時間処理を施した後(加熱試験)、また、60℃/90%RH、60℃/95%RHの各雰囲気下で500時間処理を施した後(加湿試験)、また、85℃と−40℃の環境を1サイクル1時間で300サイクル施した後(ヒートショック試験)、偏光板とガラスの間の外観を下記基準で目視にて評価した。
(評価基準)
◎:発泡、剥がれ等の外観上の変化が全くなし。
○:わずかながら端部に剥がれ、または発泡があるが、実用上問題なし。
△:端部に剥がれ、または発泡があるが、特別な用途でなければ、実用上問題なし。
×:端部に著しい剥がれあり、実用上問題あり。
前記<ガラスでの耐久性試験>において、被着体として用いた無アルカリガラスに結晶性ITOまたは非晶性ITO層を形成したものを、<ITOガラスでの耐久性試験>の被着体とした。前記のように、被着体を変えて、ITO層にサンプルを貼り合せたこと以外は、前記<ガラスでの耐久性試験>と同様の手順でITOガラスでの耐久性試験を実施した。ITO層はスパッタリングで形成した。ITOの組成は、結晶性ITOはSn比率10重量%、非晶性ITOはSn比率3重量%であり、サンプルの貼り合せ前に、それぞれ140℃×60分の加熱工程を実施した。なお、ITOのSn比率は、Sn原子の重量/(Sn原子の重量+In原子の重量)から算出した。
粘着剤層付偏光フィルムを8mm×8mmに切断したものをサンプルとした。当該サンプルを、フィルム表面にITO層が形成された導電性フィルム(商品名:エレクリスタ(P400L)、日東電工(株)製)を15mm×15mmに切断し、この導電性フィルム上の中央部に貼り合わせた後、50℃、5atmで15分間オートクレーブ処理したものを耐腐食性の測定サンプルとした。得られた測定用サンプルの抵抗値を後述の測定装置を用い測定し、これを「初期抵抗値」とした。
その後、測定用サンプルを60℃/90%RHの環境に、500時間投入した後に、抵抗値を測定したものを、「湿熱後の抵抗値」とした。なお、上記の抵抗値は、Accent Optical Technologies社製 HL5500PCを用いて測定を行った。上述のように測定した「初期抵抗値」及び「湿熱後の抵抗値」から、次式にて「抵抗値変化」を算出した。
粘着剤層付偏光フィルムを、縦420mm×横320mmのサイズに切り出したものをサンプルとして2枚用意した。このサンプルを、厚さ0.07mmの無アルカリガラス板の両面にクロスニコルになるようにラミネーターにて貼り合せた。次いで、50℃、5atmで15分間のオートクレーブ処理を行って二次サンプルとした(初期)。次いで、二次サンプルを、90℃の条件下で24時間の処理を行った(加熱後)。初期および加熱後の二次サンプルを、1万カンデラのバックライト上に置き、光漏れを下記の基準により、目視で評価した。
(評価基準)
◎:コーナームラの発生がなく、実用上問題ない。
○:コーナームラがわずかながら発生しているが、表示領域には表れていないので、実用上問題ない。
△:コーナームラが発生して表示領域にはわずかに表れているが、実用上問題ない。
×:コーナームラが発生して表示領域にはきつく表れており、実用上問題がある。
粘着剤層付偏光フィルムのセパレータフィルムを剥がした後、粘着剤表面の表面抵抗値(初期)を測定した。また、粘着剤層付偏光フィルムを60℃/95%RHの環境に500時間投入した後、40℃で1時間乾燥させてから、セパレータフィルムを剥がした後、粘着剤表面の表面抵抗値(湿熱後)を測定した。測定は、三菱化学アナリテック社製MCP−HT450を用いて行った。
粘着剤層付偏光フィルムを50mm×50mmのサイズに切断し、ガラスに貼り合せた。さらに、厚さ25μmのPETフィルム(ダイアホイルT100−25B,三菱樹脂社製)を50mm×50mmのサイズに切断し、偏光フィルムの上面に貼り合せて測定用サンプルとした。測定用サンプルを60℃/95%RHの環境に250時間投入した後、室温下に取り出して10分後のヘイズ値を測定した。ヘイズ値は、村上色彩技術研究所社製のヘイズメーターHM150を用いて測定した。
粘着剤層付偏光フィルムを、縦120mm×横25mmに裁断したものをサンプルとした。当該サンプルを、厚さ0.7mmの無アルカリガラス板(コーニング社製,EG−XG)に、ラミネーターを用いて貼り付け、次いで50℃、5atmで15分間オートクレーブ処理して完全に密着させた後、かかるサンプルの接着力を測定した。接着力は、かかるサンプルを引張り試験機(オートグラフSHIMAZU AG-1 1OKN)にて、剥離角度90°、剥離速度300mm/minで引き剥がす際の接着力(N/25mm、測定長80mm)を測定することにより求めた。測定は、1回/0.5sの間隔でサンプリングし、その平均値を測定値とした。
架橋剤(B)における、「イソシアネート系」の「D160N」は三井化学社製のタケネートD160N(トリメチロールプロパンのヘキサメチレンジイソシアネートのアダクト体)、「C/L」は日本ポリウレタン工業社製のコロネートL(トリメチロールプロパンのトリレンジイソシアネートのアダクト体)を、
「過酸化物系」はベンゾイルパーオキサイド(日本油脂社製,ナイパーBMT)を、
「シランカップリング剤(C)」は、
KBM403:信越化学工業(株)製のKBM403、
X−41−1056:信越化学工業(株)製のX−41−1056を、
「イオン性化合物(D)」は、
Li−TFSI:三菱マテリアル社製のビス(トリフルオロメタンスルホニル)イミドリチウム;
EMP−TFSI:三菱マテリアル社製の1−エチル−1−メチルピロリジニウム ビス(トリフルオロメタンスルホニル)イミド、を示す。
「ポリエーテル化合物(E)」は、カネカ社製のサイリルSAT10を示す。
Claims (18)
- モノマー単位として、アルキル(メタ)アクリレート(a1)70重量%以上、
芳香環含有(メタ)アクリレート(a2)3〜25重量%、
アミド基含有モノマー(a3)0.7〜8重量%(N-アルコキシアルキル(メタ)アクリルアミド系モノマーを除く)、
カルボキシル基含有モノマー(a4)0.01〜2重量%、および、
ヒドロキシル基含有モノマー(a5)0.01〜3重量%を含有し、
重量平均分子量(Mw)が100万〜250万であり、かつ、Mw/数平均分子量(Mn)が1.8以上10以下を満足する(メタ)アクリル系ポリマー(A)、並びに、架橋剤(B)を前記(メタ)アクリル系ポリマー(A)100重量部に対して、0.01〜3重量部を含有することを特徴とする光学フィルム用粘着剤組成物。 - 前記アミド基含有モノマー(a3)が、N−ビニル基含有ラクタム系モノマーであることを特徴とする請求項1に記載の光学フィルム用粘着剤組成物。
- 前記ヒドロキシル基含有モノマー(a5)が4−ヒドロキシブチル(メタ)アクリレートであることを特徴とする請求項1または2のいずれかに記載の光学フィルム用粘着剤組成物。
- 前記架橋剤(B)が、イソシアネート系架橋剤および過酸化物系架橋剤から選ばれるいずれか少なくとも1種を含有することを特徴とする請求項1〜3のいずれかに記載の光学フィルム用粘着剤組成物。
- 前記イソシアネート系架橋剤が脂肪族ポリイソシアネート系化合物を含有することを特徴とする請求項4記載の光学フィルム用粘着剤組成物。
- さらに、シランカップリング剤(C)を含有することを特徴とする請求項1〜5のいずれかに記載の光学フィルム用粘着剤組成物。
- 前記シランカップリング剤(C)が、1分子内に2つ以上のアルコキシシリル基を有することを特徴とする請求項6記載の光学フィルム用粘着剤組成物。
- 前記シランカップリング剤(C)が、分子内にエポキシ基を有することを特徴とする請求項6または7記載の光学フィルム用粘着剤組成物。
- 前記シランカップリング剤(C)は、前記(メタ)アクリル系ポリマー(A)100重量部に対して、0.001〜5重量部含有することを特徴とする請求項6〜8のいずれかに記載の光学フィルム用粘着剤組成物。
- さらに、イオン性化合物(D)を含有することを特徴とする請求項1〜9のいずれかに記載の光学フィルム用粘着剤組成物。
- 前記イオン性化合物(D)が、アルカリ金属塩及び/または有機カチオン−アニオン塩であることを特徴とする請求項10記載の光学フィルム用粘着剤組成物。
- 前記イオン性化合物(D)が、フルオロ基含有アニオンを含むことを特徴とする請求項11記載の光学フィルム用粘着剤組成物。
- 前記イオン性化合物(D)は、前記(メタ)アクリル系ポリマー(A)100重量部に対して、0.05〜10重量部含有することを特徴とする請求項10〜12のいずれかに記載の光学フィルム用粘着剤組成物。
- さらに、反応性シリル基を有するポリエーテル化合物(E)を含有することを特徴とする請求項1〜13のいずれかに記載の光学フィルム用粘着剤組成物。
- 前記反応性シリル基を有するポリエーテル化合物(E)は、前記(メタ)アクリル系ポリマー(A)100重量部に対して0.001〜10重量部含有することを特徴とする請求項14記載の光学フィルム用粘着剤組成物。
- 請求項1〜15のいずれかに記載の光学フィルム用粘着剤組成物により形成されることを特徴とする光学フィルム用粘着剤層。
- 光学フィルムの少なくとも片側に、請求項16に記載の光学フィルム用粘着剤層が形成されていることを特徴とする粘着剤層付光学フィルム。
- 請求項17に記載の粘着剤層付光学フィルムを少なくとも1つ用いたことを特徴とする画像表示装置。