JP2019014680A - 歯科用ポルトランドセメント粉末 - Google Patents
歯科用ポルトランドセメント粉末 Download PDFInfo
- Publication number
- JP2019014680A JP2019014680A JP2017133538A JP2017133538A JP2019014680A JP 2019014680 A JP2019014680 A JP 2019014680A JP 2017133538 A JP2017133538 A JP 2017133538A JP 2017133538 A JP2017133538 A JP 2017133538A JP 2019014680 A JP2019014680 A JP 2019014680A
- Authority
- JP
- Japan
- Prior art keywords
- mass
- cement
- dental
- powder
- portland cement
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
従って、本発明の課題は、水と混練後初期からカルシウムの溶出量の多い歯科用セメントを提供することにある。
〔2〕(A)前記〔1〕記載の歯科用ポルトランドセメント粉末、及び(B)造影剤粉末を含有し、成分(A)90〜50質量部に対して(B)造影剤粉末10〜50質量部を含有する粉末状歯科用セメント組成物。
〔3〕(B)造影剤が、Zr、Ba、Bi、Sn、Ta及びZnから選ばれる金属の酸化物、硫酸塩並びに炭酸塩から選ばれる1種以上である〔2〕記載の粉末状歯科用セメント組成物。
SiO2の含有量は、23〜28質量%であり、24〜28質量%が好ましく、24〜27質量%がより好ましい。SiO2の含有量が23質量%未満ではC2S(2CaO・SiO2)が減少して長期のカルシウム溶出量が減少し、28質量%を超えるとセメントペーストの初期強度が低下してしまう。
Al2O3の含有量は、0.4〜2.2質量%であり、0.5〜2.1質量%が好ましく、0.5〜1.8質量%がより好ましく、0.5〜1.5質量%がさらに好ましい。Al2O3の含有量が0.4質量%未満では遊離石灰が残ってセメントに必要な鉱物が得られず、2.2質量%を超えると初期のカルシウム溶出量が不足する。
Fe2O3の含有量は、0〜0.2質量%であり、0〜0.18質量%が好ましい。Fe2O3は含有しなくてもよく、0.2質量%を超えるとセメントが黄白色になり審美性が低下してしまう。
SO3の含有量は、0〜5質量%であり、0〜4質量%が好ましく、0〜3質量%がより好ましい。SO3は含有しなくてもよく、5質量%を超えるとクリンカ量に対し過剰になり、硬化特性が低下する。
セメントクリンカと石膏は別々に粉砕した後混合してもよく、両者を混合して粉砕してもよい。
(B)造影剤粉末の粉末度(ブレーン比表面積)は、ポルトランドセメント粉末セメントとの混合性の観点から3000〜10000cm2/gが好ましく、3500〜9000cm2/gがより好ましく、4000〜8000cm2/gがさらに好ましい。
スルホン酸系混和剤としては、ナフタレンスルホン酸縮合物、リグニンスルホン酸縮合物、メラミンスルホン酸縮合物、アミノスルホン酸縮合物等が挙げられる。カルボン酸系混和剤としては、ポリカルボン酸系、オレフィンマレイン酸系等が挙げられる。セルロース系混和剤としては、メチルセルロース、ヒドロキシエチルセルロース、ヒドロキシプロピルセルロース等のアルキルセルロース、ヒドロキシアルキルセルロース等が挙げられる。
また、セメントクリンカ、石膏、造影剤と粉末状混和剤を粉砕しながら、混合する工程は、以下の方法のいずれでもよい。
(i)セメントクリンカ、石膏、造影剤、粉末状混和剤を粉砕しながら、混合する方法。
(ii)セメントクリンカ、石膏、造影剤、粉末状混和剤をそれぞれ別々に粉砕した粉末を、粉砕しながら混合する方法。
(iii)セメントクリンカと石膏を粉砕しながら混合したセメント組成物、造影剤、粉末状混和剤を粉砕しながら、混合する方法。
また、水/歯科用セメント比を36%で3分間混練したセメントペーストのフローは操作性の点から、8〜18cmとなるのが好ましい。JASS 15M103に準拠したパイプにより引抜きフローを測定できる。
(A)ポルトランドセメント粉末用原料
・二酸化けい素(石英型)(特級)
・炭酸カルシウム(特級)
・酸化アルミニウム(α型)(特級)
・酸化鉄(特級)
・焼石膏(1級)
(B)造影剤
・酸化ビスマス(特級)
・硫酸バリウム(特級)
・酸化ジルコニウム(特級)
ポルトランドセメント粉末用原料を調合・混合した後、ハンドプレス機でペレット化し、ペレットを箱型電気炉で1000℃で1時間、1500℃で1〜3時間焼成後、冷却して、セメントクリンカーを得た。
2で作製したセメントクリンカーに所定量の焼石膏を添加し5Lアルミナポットミルで粉砕し、ブレーン比表面積4000cm2/gのポルトランドセメント粉末を作製した。
ポルトランドセメント粉末の化学組成は、蛍光X線分析で測定した。
ポルトランドセメント粉末に造影剤と粉末型混和剤を所定量添加して、同ミルでブレーン比表面積5000cm2/gまで微粉砕し、歯科用セメントを作製した。
3で作製したポルトランドセメント粉末または歯科用セメントを150g計量し、これに純水54mlを注水し2分間練り混ぜてセメントペーストとした。これを注水から10分経過するまで静置した後に、吸引ろ過してセメントペーストに含まれる液体を得た。この液体を硝酸で希釈した後、誘導結合プラズマ(ICP)発光分光分析装置に供して、液体に含まれるカルシウムを定量した。
ポルトランドセメント粉末の化学組成とカルシウム溶出量を表1に示す。表1より、CaO、SiO2、Al2O3、Fe2O3、SO3及びSiO2/(Al2O3+Fe2O3)比のいずれかが本発明の範囲外の比較例1〜6は、カルシウム溶出量が2000ppm未満であり、十分なカルシウム溶出量を示さなかった。比較例5は、遊離石灰が20%以上残ったため、所望の鉱物を合成できなかった。そのため溶出試験は実施しなかった。比較例2は、太平洋セメント社製ホワイトセメントである。また、Fe2O3量が多い比較例7は、黄白色となり歯科用セメントとして好ましくなかった。これに対し、実施例1〜6は、カルシウム溶出量が多く、歯科用セメントとして有用である。
実施例1〜6と比較例1〜4、6のポルトランドセメント粉末と造影剤を用いて歯科用セメントを製造した。得られた歯科用セメントのカルシウム溶出量を表2に示す。
Claims (3)
- CaO 65〜72質量%、SiO2 23〜28質量%、Al2O3 0.4〜2.2質量%、Fe2O3 0〜0.2質量%、及びSO3 0〜5質量%を含有し、SiO2/(Al2O3+Fe2O3)質量比が10〜50である歯科用ポルトランドセメント粉末。
- (A)請求項1記載の歯科用ポルトランドセメント粉末、及び(B)造影剤粉末を含有し、成分(A)90〜50質量部に対して(B)造影剤粉末10〜50質量部を含有する粉末状歯科用セメント組成物。成分(A)90〜50質量部に対して
- (B)造影剤が、Zr、Ba、Bi、Sn、Ta及びZnから選ばれる金属の酸化物、硫酸塩並びに炭酸塩から選ばれる1種以上である請求項2記載の粉末状歯科用セメント組成物。