JP2018020266A - 意匠塗膜の形成方法および意匠化粧板の製造方法 - Google Patents
意匠塗膜の形成方法および意匠化粧板の製造方法 Download PDFInfo
- Publication number
- JP2018020266A JP2018020266A JP2016151434A JP2016151434A JP2018020266A JP 2018020266 A JP2018020266 A JP 2018020266A JP 2016151434 A JP2016151434 A JP 2016151434A JP 2016151434 A JP2016151434 A JP 2016151434A JP 2018020266 A JP2018020266 A JP 2018020266A
- Authority
- JP
- Japan
- Prior art keywords
- coating film
- composition
- undercoat
- design
- topcoat
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
[1]
表面に凹凸を有する基材の凹凸面に下塗り塗料組成物を塗装し、次いで乾燥させて、下塗り乾燥塗膜を形成する、下塗り乾燥塗膜形成工程、
上記下塗り乾燥塗膜の上に、上塗り塗料組成物を塗装して、上塗り塗膜層を形成する、上塗り塗膜層形成工程、
上記塗装した上塗り塗料組成物の乾燥が終了する前に、上記上塗り塗膜層の表面の一部分、または上記上塗り塗膜層の表面の一部分および上記上塗り塗膜層の一部分を、略円筒状ローラーで掻き取る、掻き取り工程、および
上記掻き取り工程において下塗り乾燥塗膜上に残存した上塗り塗料組成物を乾燥させる、上塗り塗料組成物乾燥工程、
を包含する、意匠塗膜の形成方法であって、
上記略円筒状ローラーは、複数の溝を有し、
上記溝の幅は0.01〜3.0mmであり、隣接する溝と溝との間の距離が0.01〜10.0mmであり、
上記下塗り塗料組成物および上塗り塗料組成物は、それらの色調または色相のうち少なくとも1種が相違する、
意匠塗膜の形成方法。
[2]
上記略円筒状ローラーが有する複数の溝は、ローラーの略円周方向に沿って形成されている、意匠塗膜の形成方法。
[3]
上記溝は、深さが0.01〜3.0mmである、意匠塗膜の形成方法。
[4]
上記下塗り塗料組成物は、アニオン性水性樹脂分散体および顔料を含む、水性下塗り塗料組成物であり、
上記上塗り塗料組成物は、アニオン性水性樹脂分散体、沸点が100〜300℃である有機溶媒および顔料を含む、水性上塗り塗料組成物である、
意匠塗膜の形成方法。
[5]
上記上塗り塗膜層形成工程において基材の凹凸面に塗装される上塗り塗料組成物の量は、20〜200g/m2である、意匠塗膜の形成方法。
[6]
上記上塗り塗料組成物は、25℃における粘度が100〜2,000mPa・sである、意匠塗膜の形成方法。
[7]
表面に凹凸を有する基材の凹凸面に下塗り塗料組成物を塗装し、次いで乾燥させて、下塗り乾燥塗膜を形成する、下塗り乾燥塗膜形成工程、
上記下塗り乾燥塗膜の上に、上塗り塗料組成物を塗装して、上塗り塗膜層を形成する、上塗り塗膜層形成工程、
上記塗装した上塗り塗料組成物の乾燥が終了する前に、上記上塗り塗膜層の表面の一部分、または上記上塗り塗膜層の表面の一部分および上記上塗り塗膜層の一部分を、略円筒状ローラーで掻き取る、掻き取り工程、および
上記掻き取り工程において下塗り乾燥塗膜上に残存した上塗り塗料組成物を乾燥させる、上塗り塗料組成物乾燥工程、
を包含する、意匠化粧板の製造方法であって、
上記略円筒状ローラーは、複数の溝を有し、
上記溝の幅は0.01〜3.0mmであり、隣接する溝と溝との間の距離が0.01〜10.0mmであり、
上記下塗り塗料組成物および上塗り塗料組成物は、それらの色調または色相のうち少なくとも1種が相違する、
意匠化粧板の製造方法。
表面に凹凸を有する基材の凹凸面に下塗り塗料組成物を塗装し、次いで乾燥させて、下塗り乾燥塗膜を形成する、下塗り乾燥塗膜形成工程、
上記下塗り乾燥塗膜の上に、上塗り塗料組成物を塗装して、上塗り塗膜層を形成する、上塗り塗膜層形成工程、
上記塗装した上塗り塗料組成物の乾燥が終了する前に、上記上塗り塗膜層の表面の一部分、または上記上塗り塗膜層の表面の一部分および上記上塗り塗膜層の一部分を、略円筒状ローラーで掻き取る、掻き取り工程、および
上記掻き取り工程において下塗り乾燥塗膜上に残存した上塗り塗料組成物を乾燥させる、上塗り塗料組成物乾燥工程、
を包含する。ここで、上記略円筒状ローラーは複数の溝を有し、上記溝の幅は0.01〜3.0mmであり、隣接する溝と溝との間の距離が0.01〜10.0mmである。また、上記下塗り塗料組成物および上塗り塗料組成物は、それらの色調または色相のうち少なくとも1種が相違する。
本発明における下塗り塗料組成物として、アニオン性水性樹脂分散体および顔料を含む水性下塗り塗料組成物を用いるのが好ましい。アニオン性水性樹脂分散体は、塗膜形成樹脂成分である。アニオン性水性樹脂分散体として、例えば、アクリル樹脂エマルション、シリコーン含有アクリル樹脂エマルション、ウレタン樹脂エマルション、酢酸ビニル樹脂エマルション、フッ素樹脂エマルション、塩化ビニル樹脂エマルションなどを用いることができる。これらの樹脂は単独で用いてもよく、2種以上を併用してもよい。アニオン性水性樹脂分散体としては、アクリル樹脂エマルションまたはシリコーン含有アクリル樹脂エマルションを用いるのが好ましい。
(R1)nSi(OR2)4−n ・・・(1)
[式中、R1は、2個存在するときは同一または異なり、炭素数1〜8の1価の有機基を示す。R2は、同一または異なり、炭素数1〜5のアルキル基または炭素数1〜6のアシル基を示す。nは0〜2の整数である。]
で表される。
本発明における上塗り塗料組成物として、アニオン性水性樹脂分散体、沸点が100〜300℃である有機溶媒および顔料を含む、水性上塗り塗料組成物を用いるのが好ましい。上記水性上塗り塗料組成物に含まれるアニオン性水性樹脂分散体として、上記水性下塗り塗料組成物に含まれるアニオン性水性樹脂分散体を好適に用いることができる。
TI=ηN1/ηN2
ηN1:回転数6rpmにおける粘度
ηN2:回転数60rpmにおける粘度
本発明の意匠塗膜の形成方法は、下記工程を包含する:
表面に凹凸を有する基材の凹凸面に下塗り塗料組成物を塗装し、次いで乾燥させて、下塗り乾燥塗膜を形成する、下塗り乾燥塗膜形成工程、
上記下塗り乾燥塗膜の上に、上塗り塗料組成物を塗装して、上塗り塗膜層を形成する、上塗り塗膜層形成工程、
上記塗装した上塗り塗料組成物の乾燥が終了する前に、上記上塗り塗膜層の表面の一部分、または上記上塗り塗膜層の表面の一部分および上記上塗り塗膜層の一部分を、略円筒状ローラーで掻き取る、掻き取り工程、および
上記掻き取り工程において下塗り乾燥塗膜上に残存した上塗り塗料組成物を乾燥させる、上塗り塗料組成物乾燥工程。
下塗り乾燥塗膜形成工程は、表面に凹凸を有する基材の凹凸面に、下塗り塗料組成物を塗装し、次いで乾燥させて、下塗り乾燥塗膜を形成する工程である。
本発明の方法において用いられる基材として、例えば、サイディングおよびスレート材などが挙げられる。サイディングとして、例えば、窯業系サイディング(窯業建材)、金属系サイディングなどが挙げられる。窯業系サイディング(窯業建材)は、セメント、ケイ酸質原料、繊維質原料、混和材料などを用いて板状に成型し、乾燥(養生・硬化)させることによって製造される、JIS A 5422に規定された建材などである。金属系サイディングは、成型・エンボス加工された金属板と裏打材によって構成される、JIS A 6711に規定された建材などである。スレート材は、JIS A 5423によって規定される化粧スレートなどである。基材としてさらに、硬質木質セメント板、押出成型セメント板および軽量発泡コンクリートなどのセメント板を用いることもできる。
上塗り塗膜層形成工程は、上記下塗り乾燥塗膜の上に、上塗り塗料組成物を塗装して、上塗り塗膜層を形成する工程である。上塗り塗料組成物の塗装は、下塗り塗料組成物の塗装と同様にして行うことができる。
掻き取り工程は、上記で塗装した上塗り塗料組成物の乾燥が終了する前に、上記上塗り塗膜層の表面の一部分、または上記上塗り塗膜層の表面の一部分および上記上塗り塗膜層の一部分を、略円筒状ローラーで掻き取る工程である。
略円筒状ローラーの円周および軸方向長さは、基材の大きさなどに応じて適宜選択することができる。例えば、円周100〜1,000mm、軸方向長さ500mm〜1,500mmであってよい。
上塗り塗料組成物乾燥工程は、上記掻き取り工程において下塗り乾燥塗膜上に残存した上塗り塗料組成物を乾燥させる工程である。乾燥における温度および時間は、適宜選択することができる。例えば、室温〜150℃の温度条件下で、0.5〜60分間乾燥させることができる。
水性下塗り塗料組成物の製造
顔料分散剤としてBYK−190(ビックケミー社製)3部、白色塗料用の顔料として酸化チタン(TIPAQUE CR−95、石原産業社製)50部、沈降性硫酸バリウム(沈降性硫酸バリウム#100、堺化学社製)40部および脱イオン水20部からなる、白色分散ペーストに、アニオン性水性樹脂分散体としてVONCOAT SA−6360(アクリル樹脂エマルション、DIC社製、固形分濃度50%、粒子径150nm、酸価15mgKOH/g)を200部混合し、そしてリオファーストブラック593、リオファーストオーカーRD−230、リオファーストブラウンR−229(いずれも、トーヨーケム社製)でマンセル値4.9YR 5.5/4.7(オレンジ色)に着色した。さらに、ヒンダードアミン系光安定剤としてサノールLS292(チバスペシャルティケミカルズ社製)1部、造膜助剤としてテキサノール(イーストマンケミカルジャパン社製)10部および脱イオン水222.4部を混合した。最後に、NK2カップで30秒となるよう増粘剤としてプライマルASE−60(ダウケミカル社製)を添加して、PWC50質量%の水性下塗り塗料組成物を得た。なお、上記マンセル値は、(色相 明度/彩度)を表し、分光測色計CR−300(コニカミノルタ社製)を用いて測定した。
顔料分散剤としてBYK−190(ビックケミー社製)3部、白色塗料用の顔料として酸化チタン(TIPAQUE CR−95、石原産業社製)30部、沈降性硫酸バリウム(沈降性硫酸バリウム#100、堺化学社製)60部および脱イオン水20部からなる白色分散ペーストに、アニオン性水性樹脂分散体としてVONCOAT SA−6360(アクリル樹脂エマルション、DIC社製、固形分濃度50%、粒子径150nm、酸価15mgKOH/g)を200部混合し、そしてリオファーストブラック593、リオファーストオーカーRD−230、リオファーストブラウンR−229(いずれも、トーヨーケム社製)でマンセル値5.9YR 3.8/1.5(ブラウン色)に着色した。さらに、ヒンダードアミン系光安定剤としてサノールLS292(チバスペシャルティケミカルズ社製)1部、造膜助剤としてテキサノール(高沸点有機溶媒;イーストマンケミカルジャパン社製)10部および脱イオン水380部を混合した。最後に、NK2カップで15秒となるよう増粘剤としてプライマルASE−60(ダウケミカル社製)を添加して、PWC50質量%の水性上塗り塗料組成物を得た。
得られた塗料組成物を25℃にし、B型粘度計(VISCOMETER TVB−10;東機産業社製)を用いて、回転数60rpmでの粘度を測定した。なお、測定は、塗料組成物を撹拌した後に、10分間放置した後に行った。
「1)塗料組成物の粘度の測定」に記載の粘度測定方法を、回転数を6rpmの条件とした以外は同様の方法で粘度を測定した。チクソ係数(TI)を、下記式
TI=(回転数6rpmにおける粘度)/(回転数60rpmにおける粘度)
により算出した。
表面の凹凸を有する基材として、木目調窯業サイディング(凹凸の深さ:0.1〜6mm)を用いた。
上記で調製した水性下塗り塗料組成物を、基材の凹凸面に、エアスプレーガンを用いて、乾燥膜厚が50μmとなる量で塗装した。次いで、得られた塗膜を100℃で5分間乾燥させて、下塗り乾燥塗膜を得た。
次いで、得られた塗装物に対して、図1で概略説明される略円筒状ローラー(直径245mm、軸方向長さ600mm)を用いて、上塗り塗膜層の一部を掻き取り、上塗り塗料組成物の残存量を30g/m2とした。略円筒状ローラーの材質はEPTとした。また、略円筒状ローラーが有する溝の幅は0.2mmであり、溝の深さは0.1mmであり、隣接する溝と溝との間の距離は0.1mmであった。
実施例1で得られた意匠塗膜の上に、さらにクリヤー塗料組成物を塗装して、クリヤー塗膜を設けた。塗装に用いたクリヤー塗料組成物は、以下の通り調製した。水性クリヤー塗料組成物を用いたクリヤー塗膜の形成は、得られた意匠塗膜上に、乾燥膜厚50μmとなるようにスプレーにより塗装し、得られたクリヤー塗膜を100℃で10分間乾燥させることによって形成した。
アニオン性水性樹脂分散体としてVONCOAT SA−6360(アクリル樹脂エマルション、DIC社製、固形分濃度50.0%、粒子径150nm、酸価15mgKOH/g)を200部、造膜助剤としてテキサノール(イーストマンケミカルジャパン社製)10部、紫外線吸収剤としてチヌビン1130(BASF社製)2部、ヒンダードアミン系光安定剤としてサノールLS292(チバスペシャルティケミカルズ社製)2部および脱イオン水104部を混合し、さらに、NK2カップで30秒となるよう増粘剤としてプライマルASE−60(ダウケミカル社製)を添加して、水性クリヤー塗料組成物を得た。
掻き取りに用いた略円筒状ローラーとして、溝を有しない略円筒状ローラーを用いたこと以外は、実施例1と同様にして、意匠塗膜を得た。
3:表面に凹凸を有する基材、
5:上塗り塗膜層、
7:上塗り塗料組成物、
9:金属ローラー、
11:下塗り乾燥塗膜。
Claims (7)
- 表面に凹凸を有する基材の凹凸面に下塗り塗料組成物を塗装し、次いで乾燥させて、下塗り乾燥塗膜を形成する、下塗り乾燥塗膜形成工程、
前記下塗り乾燥塗膜の上に、上塗り塗料組成物を塗装して、上塗り塗膜層を形成する、上塗り塗膜層形成工程、
前記塗装した上塗り塗料組成物の乾燥が終了する前に、前記上塗り塗膜層の表面の一部分、または前記上塗り塗膜層の表面の一部分および前記上塗り塗膜層の一部分を、略円筒状ローラーで掻き取る、掻き取り工程、および
前記掻き取り工程において下塗り乾燥塗膜上に残存した上塗り塗料組成物を乾燥させる、上塗り塗料組成物乾燥工程、
を包含する、意匠塗膜の形成方法であって、
前記略円筒状ローラーは、複数の溝を有し、
前記溝の幅は0.01〜3.0mmであり、隣接する溝と溝との間の距離が0.01〜10.0mmであり、
前記下塗り塗料組成物および上塗り塗料組成物は、それらの色調または色相のうち少なくとも1種が相違する、
意匠塗膜の形成方法。 - 前記略円筒状ローラーが有する複数の溝は、ローラーの略円周方向に沿って形成されている、請求項1記載の意匠塗膜の形成方法。
- 前記溝は、深さが0.01〜3.0mmである、請求項1または2記載の意匠塗膜の形成方法。
- 前記下塗り塗料組成物は、アニオン性水性樹脂分散体および顔料を含む、水性下塗り塗料組成物であり、
前記上塗り塗料組成物は、アニオン性水性樹脂分散体、沸点が100〜300℃である有機溶媒および顔料を含む、水性上塗り塗料組成物である、
請求項1〜3いずれかに記載の意匠塗膜の形成方法。 - 前記上塗り塗膜層形成工程において基材の凹凸面に塗装される上塗り塗料組成物の量は、20〜200g/m2である、請求項1〜4いずれかに記載の意匠塗膜の形成方法。
- 前記上塗り塗料組成物は、25℃における粘度が100〜2,000mPa・sである、請求項1〜5いずれかに記載の意匠塗膜の形成方法。
- 表面に凹凸を有する基材の凹凸面に下塗り塗料組成物を塗装し、次いで乾燥させて、下塗り乾燥塗膜を形成する、下塗り乾燥塗膜形成工程、
前記下塗り乾燥塗膜の上に、上塗り塗料組成物を塗装して、上塗り塗膜層を形成する、上塗り塗膜層形成工程、
前記塗装した上塗り塗料組成物の乾燥が終了する前に、前記上塗り塗膜層の表面の一部分、または前記上塗り塗膜層の表面の一部分および前記上塗り塗膜層の一部分を、略円筒状ローラーで掻き取る、掻き取り工程、および
前記掻き取り工程において下塗り乾燥塗膜上に残存した上塗り塗料組成物を乾燥させる、上塗り塗料組成物乾燥工程、
を包含する、意匠化粧板の製造方法であって、
前記略円筒状ローラーは、複数の溝を有し、
前記溝の幅は0.01〜3.0mmであり、隣接する溝と溝との間の距離が0.01〜10.0mmであり、
前記下塗り塗料組成物および上塗り塗料組成物は、それらの色調または色相のうち少なくとも1種が相違する、
意匠化粧板の製造方法。