JP6839631B2 - 水性被覆材 - Google Patents
水性被覆材 Download PDFInfo
- Publication number
- JP6839631B2 JP6839631B2 JP2017160784A JP2017160784A JP6839631B2 JP 6839631 B2 JP6839631 B2 JP 6839631B2 JP 2017160784 A JP2017160784 A JP 2017160784A JP 2017160784 A JP2017160784 A JP 2017160784A JP 6839631 B2 JP6839631 B2 JP 6839631B2
- Authority
- JP
- Japan
- Prior art keywords
- component
- resin emulsion
- pigment
- coating material
- weight
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
1.顔料体積濃度が30〜70%である水性被覆材であって、
アクリル樹脂エマルション(A)、シリコーン樹脂エマルション(B)、及び顔料(C)を含み、
前記シリコーン樹脂エマルション(B)の平均粒子径は、前記アクリル樹脂エマルション(A)の平均粒子径よりも小さいことを特徴とする水性被覆材。
2.前記シリコーン樹脂エマルション(B)の平均粒子径は100nm以下であることを特徴とする1.記載の水性被覆材。
3.前記シリコーン樹脂エマルション(B)の混合比率は、前記アクリル樹脂エマルション(A)の固形分100重量部に対し1〜80重量部であることを特徴とする1.または2.に記載の水性被覆材。
表1に示す重量部にて、各原料を常法により混合・攪拌することによって、各水性被覆材を製造した。原料としては下記のものを使用した。
・樹脂2:アクリルスチレン樹脂エマルション(メチルメタクリレート・スチレン・n−ブチルアクリレート・2−エチルヘキシルアクリレート・アクリル酸の乳化重合体、全モノマー中の(メタ)アクリル酸アルキルエステルの構成比率:75重量%、平均粒子径:150nm、固形分:50重量%、ガラス転移温度:8℃、樹脂比重:1.0、媒体:水)
・樹脂3:シリコーン樹脂エマルション(オクタメチルシクロテトラシロキサン・アルコキシシラン化合物重合物の乳化分散体、樹脂中のシリコーン成分比率:100重量%、平均粒子径:50nm、固形分:30重量%、樹脂比重:1.0、媒体:水)
・樹脂4:シリコーン樹脂エマルション(ジメチルシロキサン化合物の乳化分散体、樹脂中のシリコーン成分比率:100重量%、平均粒子径:190nm、固形分:50重量%、樹脂比重:1.0、媒体:水)
・体質顔料1:粒状粉体(シリカ粉、平均粒子径4μm、比重2.6)
・体質顔料2:リン片状粉体(タルク、平均粒子径12μm、比重2.7)
・着色顔料1:酸化チタン(平均粒子径0.2μm、比重4.2)
・着色顔料2:弁柄(平均粒子径0.2μm、比重5.0)
・造膜助剤:エステル系造膜助剤
・分散剤:アニオン系分散剤
・増粘剤:セルロース系増粘剤、ウレタン系増粘剤
・消泡剤:鉱物油系消泡剤
(1)鏡面光沢度
ガラス板の片面に、すきま150μmのフィルムアプリケータを用いて被覆材を塗り、塗面を水平に置いて標準状態で48時間乾燥したときの鏡面光沢度(測定角度60度)を測定した。
ガラス板の片面に、すきま150μmのフィルムアプリケータを用いて被覆材を塗り、塗面を水平に置いて標準状態で14日間乾燥したものを試験体とした。この試験体の被膜表面を紙製ウエスで擦り、擦り傷による変色の程度を評価した。評価は、変色が認められなかったものを「a」、著しい変色が認められたものを「d」とする4段階(優:a>b>c>d:劣)で行った。
上記「耐変色性1」と同様の方法で試験体を作製した。この試験体の被膜表面に1分間連続して水を流した後、水による変色の程度を評価した。評価は、変色が認められなかったものを「a」、著しい変色が認められたものを「d」とする4段階(優:a>b>c>d:劣)で行った。
予め下塗材を塗装したスレート板に、被覆材を塗付け量0.3kg/m2にて刷毛塗りし、標準状態で14日間乾燥したものを試験体とした。この試験体を23℃の水中に7日間浸し、浸漬前後の被膜の色差(△E)を色彩色差計で測定した。評価は、色差0.3未満を「a」、色差0.3以上0.6未満を「b」、色差0.6以上1.0未満を「c」、色差1.0以上を「d」とする4段階(優:a>b>c>d:劣)で行った。
予め下塗材を塗装したアルミニウム板(上方から3分の1の長さのところで、内角度が135度になるように折り曲げたもの)に、被覆材を塗付け量0.3kg/m2にてスプレー塗りし、標準状態で14日間乾燥したものを試験体とした。この試験体について屋外暴露を実施し、垂直面における6ヶ月後の雨筋汚れによる変色の程度を評価した。評価は、変色が認められなかったものを「a」、著しい変色が認められたものを「d」とする4段階(優:a>b>c>d:劣)で行った。
試験結果を表1に示す。実施例1〜9では、各試験において良好な結果が得られた。
Claims (3)
- 顔料体積濃度が30〜70%である水性被覆材であって、
アクリル樹脂エマルション(A)、シリコーン樹脂エマルション(B)、及び顔料(C)を含み、
前記シリコーン樹脂エマルション(B)の平均粒子径は、前記アクリル樹脂エマルション(A)の平均粒子径よりも小さいことを特徴とする水性被覆材。 - 前記シリコーン樹脂エマルション(B)の平均粒子径は100nm以下であることを特徴とする請求項1記載の水性被覆材。
- 前記シリコーン樹脂エマルション(B)の混合比率は、前記アクリル樹脂エマルション(A)の固形分100重量部に対し1〜80重量部であることを特徴とする請求項1または2に記載の水性被覆材。