JP2017508870A5 - - Google Patents
Download PDFInfo
- Publication number
- JP2017508870A5 JP2017508870A5 JP2016540674A JP2016540674A JP2017508870A5 JP 2017508870 A5 JP2017508870 A5 JP 2017508870A5 JP 2016540674 A JP2016540674 A JP 2016540674A JP 2016540674 A JP2016540674 A JP 2016540674A JP 2017508870 A5 JP2017508870 A5 JP 2017508870A5
- Authority
- JP
- Japan
- Prior art keywords
- coating material
- containing particles
- coating
- average
- particles
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Links
- 239000011248 coating agent Substances 0.000 claims 31
- 238000000576 coating method Methods 0.000 claims 31
- 239000011651 chromium Substances 0.000 claims 29
- 239000000463 material Substances 0.000 claims 27
- 239000002245 particle Substances 0.000 claims 14
- 239000007789 gas Substances 0.000 claims 6
- 238000000034 method Methods 0.000 claims 5
- IJGRMHOSHXDMSA-UHFFFAOYSA-N nitrogen Chemical compound N#N IJGRMHOSHXDMSA-UHFFFAOYSA-N 0.000 claims 4
- 239000011362 coarse particle Substances 0.000 claims 3
- 239000000203 mixture Substances 0.000 claims 3
- 239000003973 paint Substances 0.000 claims 3
- 239000000843 powder Substances 0.000 claims 3
- 238000004438 BET method Methods 0.000 claims 2
- 238000004519 manufacturing process Methods 0.000 claims 2
- 229910052757 nitrogen Inorganic materials 0.000 claims 2
- 239000011148 porous material Substances 0.000 claims 2
- 239000007921 spray Substances 0.000 claims 2
- 239000004215 Carbon black (E152) Substances 0.000 claims 1
- VQWFNAGFNGABOH-UHFFFAOYSA-K Chromium(III) hydroxide Chemical compound [OH-].[OH-].[OH-].[Cr+3] VQWFNAGFNGABOH-UHFFFAOYSA-K 0.000 claims 1
- 239000000853 adhesive Substances 0.000 claims 1
- 230000001070 adhesive Effects 0.000 claims 1
- 239000000956 alloy Substances 0.000 claims 1
- 229910045601 alloy Inorganic materials 0.000 claims 1
- REDXJYDRNCIFBQ-UHFFFAOYSA-N aluminium(3+) Chemical class [Al+3] REDXJYDRNCIFBQ-UHFFFAOYSA-N 0.000 claims 1
- OKTJSMMVPCPJKN-UHFFFAOYSA-N carbon Chemical compound [C] OKTJSMMVPCPJKN-UHFFFAOYSA-N 0.000 claims 1
- 229910052799 carbon Inorganic materials 0.000 claims 1
- 229910000423 chromium oxide Inorganic materials 0.000 claims 1
- 150000001875 compounds Chemical class 0.000 claims 1
- 239000000470 constituent Substances 0.000 claims 1
- 238000010285 flame spraying Methods 0.000 claims 1
- 239000008187 granular material Substances 0.000 claims 1
- 150000002430 hydrocarbons Chemical class 0.000 claims 1
- 238000003703 image analysis method Methods 0.000 claims 1
- 238000007561 laser diffraction method Methods 0.000 claims 1
- 239000000314 lubricant Substances 0.000 claims 1
- 229910052751 metal Inorganic materials 0.000 claims 1
- 239000002184 metal Substances 0.000 claims 1
- XXGJRAFLOAKNCC-UHFFFAOYSA-N methane;molecular hydrogen Chemical compound C.[H][H] XXGJRAFLOAKNCC-UHFFFAOYSA-N 0.000 claims 1
- 239000007787 solid Substances 0.000 claims 1
- 239000000758 substrate Substances 0.000 claims 1
- WGLPBDUCMAPZCE-UHFFFAOYSA-N trioxochromium Chemical compound O=[Cr](=O)=O WGLPBDUCMAPZCE-UHFFFAOYSA-N 0.000 claims 1
- 238000011144 upstream manufacturing Methods 0.000 claims 1
Claims (28)
- Ｃｒ含有粒子を形成するＣｒ含有量９５質量％超のＣｒ豊富な領域を含有する塗装材料であって、Ｃｒ含有粒子の少なくとも一部が集塊又は凝集塊の形態で存在することを特徴とする塗装材料。
- Ｃｒ含有粒子を形成するＣｒ含有量９５質量％超のＣｒ豊富な領域を含有する塗装材料であって、Ｃｒ含有粒子の少なくとも一部が細孔を有することを特徴とする塗装材料。
- Ｃｒ含有粒子を形成するＣｒ含有量９５質量％超のＣｒ豊富な領域を含有する塗装材料であって、Ｃｒ豊富な領域が４ＧＰａ以下の平均ナノハードネスＨＩＴ ０．００５／５／１／５を有することを特徴とする塗装材料。
- Ｃｒ含有粒子を形成するＣｒ含有量９５質量％超のＣｒ豊富な領域を含有する塗装材料であって、Ｃｒ含有粒子が、ＢＥＴ法で測定して、０．０５ｍ２／ｇを超える平均表面積を有することを特徴とする塗装材料。
- Ｃｒ豊富な領域が４ＧＰａ以下の平均ナノハードネスＨＩＴ ０．００５／５／１／５を有することを特徴とする請求項１、２又は４に記載の塗装材料。
- Ｃｒ含有粒子の少なくとも一部が細孔を有することを特徴とする請求項１、３又は４に記載の塗装材料。
- Ｃｒ含有粒子の少なくとも一部が凝結塊又は凝集塊の形態で存在することを特徴とする請求項２、３又は４に記載の塗装材料。
- Ｃｒ含有粒子が、ＢＥＴ法で測定して、０．０５ｍ２／ｇを超える平均表面積を有することを特徴とする請求項１、２又は３に記載の塗装材料。
- 粉末又は顆粒の形態で存在することを特徴とする請求項１〜８のいずれか１項に記載の塗装材料。
- Ｃｒ含有粒子の少なくとも一部が、定量的画像解析法による測定で、１０体積％を超える平均空隙率を有することを特徴とする請求項１〜９のいずれか１項に記載の塗装材料。
- Ｃｒ含有粒子の表面に、少なくとも一部の領域において、Ｃｒよりも低い降伏強度を有する材料が塗布されていることを特徴とする請求項１〜１０のいずれか１項に記載の塗装材料。
- Ｃｒ含有粒子が、レーザー回折法で測定して、５μｍ＜ｄ５０＜１５０μｍを満たす平均粒径／顆粒径ｄ５０を有することを特徴とする請求項１〜１１のいずれか１項に記載の塗装材料。
- 硬質材料及び潤滑剤からなる群から選ばれる少なくとも１つの成分を含有することを特徴とする請求項１〜１２のいずれか１項に記載の塗装材料。
- 塗装材料が少なくとも１つの他の金属を含有するか粉末混合物の構成成分であることを特徴とする請求項１〜１３のいずれか１項に記載の塗装材料。
- 前記粉末混合物がＭＣｒＡｌＹ合金の組成を有することを特徴とする請求項１４に記載の塗装材料。
- Ｃｒ含有量が５０質量％を超えることを特徴とする請求項１〜１４のいずれか１項に記載の塗装材料。
- 請求項１〜１６のいずれか１項に記載の塗装材料を用いる塗料の製造方法。
- 塗装材料の製造が、酸化クロム及び水酸化クロムからなる群から選ばれる少なくとも１つの化合物を、所望により固体炭素源を添加して、水素又は炭化水素の少なくとも一時的な作用下に、還元する工程を含む請求項１７に記載の方法。
- 塗料が熱スプレー法により製造されることを特徴とする請求項１７又は１８に記載の方法。
- 塗料がコールドガススプレー法により製造されることを特徴とする請求項１７〜１９のいずれか１項に記載の方法。
- 少なくとも下記の工程を含有することを特徴とする請求項２０に記載の方法：
・１０〜１００バールの圧力及び室温〜１，４００℃までの温度を有するプロセスガスを準備する工程；
・プロセスガスをコンヴァージェント−ダイヴァージェントノズル中で加速する工程；
・塗装材料を、コンヴァージェント−ダイヴァージェントノズルの上流で、中で又は下流で、プロセスガス中に注入する工程；
・塗装材料の衝撃時に、基材上に接着性の塗膜を形成する工程。 - 前記プロセスガスが窒素又は窒素豊富なガスであることを特徴とする請求項２１に記載の方法。
- 前記塗膜が高速フレーム溶射法により製造されることを特徴とする請求項１７〜１９のいずれか１項に記載の方法。
- 請求項２０〜２３のいずれか１項に記載の方法によって得られる、５０質量％を超えるＣｒ含有量、２０μｍを超える平均膜厚及び少なくとも部分的に変形されたＣｒ含有粗粒を含有する微細構造を有する塗膜。
- 変形されたＣｒ含有粗粒がコールド変形されたものであることを特徴とする請求項２４に記載の塗膜。
- 粗粒の少なくとも一部が層表面に平行な方向に伸張されていることを特徴とする請求項２４又は２５に記載の塗膜。
- 粗粒が１．３を超える平均アスペクト比を有することを特徴とする請求項２６に記載の塗膜。
- 変形されたＣｒ含有粗粒が４ＧＰａを超える平均ナノハードネスＨＩＴ ０．００５／５／１／５を有することを特徴とする請求項２４〜２７のいずれか１項に記載の方法。