JP2017007244A - 積層布帛および繊維製品 - Google Patents
積層布帛および繊維製品 Download PDFInfo
- Publication number
- JP2017007244A JP2017007244A JP2015126493A JP2015126493A JP2017007244A JP 2017007244 A JP2017007244 A JP 2017007244A JP 2015126493 A JP2015126493 A JP 2015126493A JP 2015126493 A JP2015126493 A JP 2015126493A JP 2017007244 A JP2017007244 A JP 2017007244A
- Authority
- JP
- Japan
- Prior art keywords
- spun yarn
- fabric
- laminated fabric
- laminated
- weight
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
【解決手段】布帛を積層してなる積層布帛において、1000〜1500μmの光の吸収率が70%以上である無機微粒子を含有するメタ系アラミド繊維Aを含む紡績糸aを、積層布帛を構成するいずれかの布帛に含ませ、かつ前記無機微粒子を含有しないメタ系アラミド繊維Bを含む紡績糸bを、積層布帛を構成するいずれかの布帛に含ませ、必要に応じて該積層布帛を用いて繊維製品を得る。
【選択図】なし
Description
しかしながら、カーボンブラックは赤外線の吸収効率が高いため、火炎を受けたり、熱源の近くにいるときに布帛の温度が高くなり火傷になりやすいという問題があった。
本発明において、メタ系アラミド繊維Aは1000〜1500μmの光の吸収率が70%以上である無機微粒子を含有する。かかる無機微粒子としては、カーボンブラックが好ましいが濃色の顔料でもよい。
かかる無機微粒子は耐久性の点でメタ系アラミド繊維Aを形成するポリマー中に含まれていることが好ましいが、繊維表面に付着していてもよい。
その際、無機微粒子の含有量は繊維重量対比1重量%以上(より好ましくは2〜9重量%)であることが好ましい。該含有量が1重量%未満では、十分な濃色性が得られないおそれがある。
紡績糸aは前記メタ系アラミド繊維Aを含む。かかる紡績糸aにおいて、メタ系アラミド繊維Aが紡績糸重量対比50〜99重量%含まれることが好ましい。その際、紡績糸aにパラ型アラミド繊維、導電性繊維、ポリエステル繊維などを含ませてもよい。
かかる導電性繊維としては、導電性繊維の導電部の導電体として、カーボンブラック、導電性酸化チタン、導電性ウィスカー、およびカーボンナノチューブの少なくとも一つを含む繊維が好ましい。
市販されている導電性繊維としては、帝人社製「メタリアン」(商品名)、ユニチカファイバー製「メガーナ」(商品名)、東レ社製「ルアナ」(商品名)、クラレ社製「クラカーボ」(商品名)などが例示される。
前記ポリエステル繊維において、繊維の表面積を大きくして優れた吸汗性などを得る上で、単繊維繊度5.0dtex以下(より好ましくは0.0001〜1.5dtex)であることが好ましい。
紡績糸bは前記メタ系アラミド繊維Bを含む。かかる紡績糸bにおいて、メタ系アラミド繊維Bが紡績糸重量対比50〜99重量%含まれることが好ましい。その際、紡績糸abには、前記のような、パラ型アラミド繊維、導電性繊維、ポリエステル繊維などを含ませてもよい。
すなわち、まず紡績糸を用意する。その際、紡績糸繊度(番手)は、耐糸切れ性や強度などの点で綿番手(Ecc)20〜60番手が好ましい。単糸数としては60本以上が好ましく、原綿単糸繊度としては3.0dtex以下(より好ましくは0.001〜3.0dtex)が好ましい。紡績糸の撚係数(下撚係数)としては3.6〜4.2(より好ましくは3.8〜4.0)の範囲が好ましい。該撚係数が大きい程、毛羽が収束し布帛の耐ピリング性が良くなる反面、紡績糸が剛直になり、伸度が低下して布帛の引裂き強力が低減したり、布帛が硬化するおそれがある。なお、撚係数は下記式により表される。
撚係数=撚数(回/吋)/紡績糸の綿番手(Ecc)1/2
紡績糸の紡績方法はリング紡績、MTS、MJS、MVSなどの革新紡績やリング紡績など通常の紡績方法でよい。撚り方向はZ方向またはS方向のいずれでもよい。
その際、合撚(上撚)の撚り方向は追撚方向である。例えば、紡績糸の撚り方向がZ撚りの場合、同じ方向のZ方向に撚りを行う。また、撚数は、好ましくは2000回/m以上、より好ましくは2100〜3000回/m、特に好ましくは2300〜2800回/mである。該撚数が2000回/m未満の場合、撚り止めセット、解撚した後、紡績糸の形態がコイル状にならないおそれがある。
布帛の構造としては、特に限定されるものではなく織物、編物、不織布いずれでもよい。なかでも、平織、綾織、2層の構造を有する2重織物などの織物が好適に例示される。なお、かかる布帛は常法により製編織することができる。
また、最内層の布帛に、前記紡績糸bが布帛重量に対して70重量%含まれることが好ましい。
(実施態様1)積層布帛が表地(最外層の布帛)および中地および裏地(最内層の布帛)で構成され、表地は前記紡績糸aのみで構成され、中地および裏地は前記紡績糸bのみで構成される。
(実施態様2)積層布帛が表地(最外層の布帛)および中地および裏地(最内層の布帛)で構成され、表地は前記紡績糸aおよび前記紡績糸bで構成され該表地において前記紡績糸aが外気側表面に露出し、前記紡績糸bが身体側裏面に露出し、中地および裏地は前記紡績糸bのみで構成される。
市販されている導電性繊維としては、帝人製「メタリアン」(商品名)、ユニチカファイバー製「メガーナ」(商品名)、東レ製「ルアナ」(商品名)、クラレ製「クラカーボ」(商品名)などが例示される。
また、積層布帛を構成するいずれかの布帛にさらに、ポリエステル繊維、ナイロン繊維、アクリル繊維、アクリレート系繊維、難燃レーヨン繊維、難燃ビニロン繊維などの繊維が含まれていてもよい。
本発明の積層布帛において、布帛を構成する繊維の繊維形態は特に限定されず、短繊維(紡績糸)でもよいし長繊維(マルチフィラメント)でもよい。
また、本発明の積層布帛において、吸汗剤、撥水剤、蓄熱剤、紫外線遮蔽あるいは制電剤、抗菌剤、消臭剤、防虫剤、防蚊剤、防蚊剤、蓄光剤、再帰反射剤等の機能を付与する他の各種加工を付加適用してもよい。
ここで、前記吸汗剤としては、ポリエチレングリコールジアクリレートまたはポリエチレングリコールジアクリレートの誘導体またはポリエチレンテレフタレート−ポリエチレングリコール共重合体または水溶性ポリウレタンが好ましい。
かくして得られた積層布帛において、1000〜1500μmの光の吸収率が70%以上である無機微粒子を含有するメタ系アラミド繊維Aを含む紡績糸aにより濃色性が得られる。また、前記無機微粒子を含有しないメタ系アラミド繊維Bを含む紡績糸bにより火傷しにくくなる。特に、最外層の布帛に前記紡績糸aが含まれ于、かつ最内層の布帛に前記紡績糸bが含まれていると、濃色性に優れかつ火傷しにくい積層布帛が得られやすくなる。
また、積層布帛において、ISO6942に規定する耐輻射熱試験において、センサー温度が24℃上昇するまでの時間RHTI24が10秒以上(より好ましくは12秒以上)であることが好ましい。10秒未満であると遮熱性が十分ではなく火傷がひどくなるおそれがある。
その際、前記紡績糸aを含む布帛を最も外気側に配し、かつ前記紡績糸bを含む布帛を最も肌側に配することが好ましい。
かかる繊維製品は、前記の積層布帛を用いているので、濃色性に優れかつ火傷しにくいという優れた特徴を有する。
(1)1000〜1500μmの光の吸収率
島津製作所製分光光度計MPC−3100で透過率、反射率を測定し、1000〜1500nmの範囲の近赤外線吸収率を算出した。
カーボンブラック(1000〜1500μmの光の吸収率90%以上)を6重量%含有する黒色の原着メタ型全芳香族ポリアミド繊維(MAB)、パラ型全芳香族ポリアミド繊維(PA)、導電性ナイロン繊維(NY)の各ステープルファイバー(いずれも繊維長は51mm)からなるMAB/PA/NY=93/5/2の質量比率で混紡した紡績糸40番手/双糸を経糸とし、カーボンブラックを含まない白色の原着メタ型全芳香族ポリアミド繊維(MAW)、パラ型全芳香族ポリアミド繊維(PA)、導電性ナイロン繊維(NY)の各ステープルファイバー(いずれも繊維長は51mm)からなるMAW/PA/NY=93/5/2の質量比率で混紡した紡績糸40番手/双糸を緯糸とし、織密度 経104本/25.4mm、緯52本/25.4mmで綾織物(2/1右綾;露出率が66.6%)を製織し、常法の加工条件で毛焼、精錬を実施した後、180℃で熱セットを実施し、目付け200g/m2(密度 経107本/25.4mm、緯54本/25.4mm)の綾織物Aを得た。
得られた最外層および最内層の織物は、JIS L1091 A−4法に規定する残炎が0.7秒、0.6秒であり、3層の積層体のISO6942に規定する耐輻射熱試験において、センサー温度が24℃上昇するまでの時間RHTI24が18.5秒であり、熱防護性に大変優れるものであった。また、外観は濃色であり汚れ等が目立たず良好であった。
カーボンブラック(実施例1と同じもの)を6重量%含有する黒色の原着メタ型全芳香族ポリアミド繊維(MAB)、パラ型全芳香族ポリアミド繊維(PA)、導電性ナイロン繊維(NY)の各ステープルファイバー(いずれも繊維長は51mm)からなるMAB/PA/NY=93/5/2の質量比率で混紡した紡績糸40番手/双糸を経糸および緯糸に使用し綾織物Aを得た以外は実施例1と同様に行った。
得られた最外層および最内層の織物は、JIS L1091 A−4法に規定する残炎が0.5秒、0.6秒であり、3層の積層体のISO6942に規定する耐輻射熱試験において、センサー温度が24℃上昇するまでの時間RHTI24が17.3秒であり、熱防護性に大変優れるものであった。また、外観は濃色であり汚れ等が目立たず良好であった。
カーボンブラック(実施例1と同じもの)を6重量%含有する黒色の原着メタ型全芳香族ポリアミド繊維(MAB)、パラ型全芳香族ポリアミド繊維(PA)、導電性ナイロン繊維(NY)の各ステープルファイバー(いずれも繊維長は51mm)からなるMAB/PA/NY=93/5/2の質量比率で混紡した紡績糸40番手/双糸を経糸および緯糸に使用し綾織物A、平織物ラミネート品B、綾織物Cを得た以外は実施例1と同様に行った。
得られた最外層および最内層の織物は、JIS L1091 A−4法に規定する残炎が0.6秒、0.4秒で良好であるものの、3層の積層体のISO6942に規定する耐輻射熱試験において、センサー温度が24℃上昇するまでの時間RHTI24が14.1秒であり、熱防護性に劣るものであった。また、外観は濃色であり汚れ等が目立たず良好であった。
カーボンブラックを含まない白色の原着メタ型全芳香族ポリアミド繊維(MAW)、パラ型全芳香族ポリアミド繊維(PA)、導電性ナイロン繊維(NY)の各ステープルファイバー(いずれも繊維長は51mm)からなるMAW/PA/NY=93/5/2の質量比率で混紡した紡績糸40番手/双糸を経糸および緯糸に使用し綾織物A、平織物ラミネート品B、綾織物Cを得た以外は実施例1と同様に行った。
得られた最外層および最内層の織物は、JIS L1091 A−4法に規定する残炎が0.5秒、0.4秒で良好であり、3層の積層体のISO6942に規定する耐輻射熱試験において、センサー温度が24℃上昇するまでの時間RHTI24が17.9秒で熱防護性に大変優れるものであったが、外観は淡色であり汚れ等が目立ち品位が良くないものであった。
Claims (13)
- 布帛を積層してなる積層布帛であって、
1000〜1500μmの光の吸収率が70%以上である無機微粒子を含有するメタ系アラミド繊維Aを含む紡績糸aが、積層布帛を構成するいずれかの布帛に含まれ、
かつ、前記無機微粒子を含有しないメタ系アラミド繊維Bを含む紡績糸bが、積層布帛を構成するいずれかの布帛に含まれることを特徴とする積層布帛。 - 前記紡績糸aと前記紡績糸bとが、積層布帛を構成する布帛であって互いに異なる布帛に含まれている、請求項1に記載の積層布帛。
- 前記無機微粒子がカーボンブラックである、請求項1に記載の積層布帛。
- 前記紡績糸aにおいて、メタ系アラミド繊維Aが紡績糸重量対比50〜99重量%含まれる、請求項1〜3のいずれかに記載の積層布帛。
- 前記紡績糸bにおいて、メタ系アラミド繊維Bが紡績糸重量対比50〜99重量%含まれる、請求項1〜4のいずれかに記載の積層布帛。
- 前記紡績糸aを含む布帛および前記紡績糸bを含む布帛が、積層布帛の最も外側に配されてなる、請求項1〜5のいずれかに記載の積層布帛。
- 前記紡績糸aを含む布帛がパラ系アラミド繊維を布帛重量対比3〜25重量%含む、請求項1〜6のいずれかに記載の積層布帛。
- 前記紡績糸aを含む布帛が導電性繊維を布帛重量対比1〜5重量%含む、請求項1〜7のいずれかに記載の積層布帛。
- 前記メタ系アラミド繊維Bが染色されている、請求項1〜8のいずれかに記載の積層布帛。
- 積層布帛を構成するいずれかの布帛において、JIS L1091 A−4法に規定する残炎時間が2秒以下である、請求項1〜9のいずれかに記載の積層布帛。
- 積層布帛において、ISO6942に規定する耐輻射熱試験において、センサー温度が24℃上昇するまでの時間RHTI24が10秒以上である、請求項1〜10のいずれかに記載の積層布帛。
- 積層布帛を構成するいずれかの布帛において、布帛の目付けが130〜300g/m2の範囲内である、請求項1〜11のいずれかに記載の積層布帛。
- 請求項1〜12のいずれかに記載された積層布帛を用いてなり、防護服、消防防火服、消防活動服、救助服、ワークウェア、警察制服、自衛隊衣服、および軍服からなる群より選択されるいずれかの繊維製品。