JP2016184467A - セパレータ/中間層積層体、非水電解質二次電池用構造体、及び水性ラテックス - Google Patents
セパレータ/中間層積層体、非水電解質二次電池用構造体、及び水性ラテックス Download PDFInfo
- Publication number
- JP2016184467A JP2016184467A JP2015063047A JP2015063047A JP2016184467A JP 2016184467 A JP2016184467 A JP 2016184467A JP 2015063047 A JP2015063047 A JP 2015063047A JP 2015063047 A JP2015063047 A JP 2015063047A JP 2016184467 A JP2016184467 A JP 2016184467A
- Authority
- JP
- Japan
- Prior art keywords
- separator
- intermediate layer
- secondary battery
- electrolyte secondary
- negative electrode
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
前記中間層は、(A)不飽和二塩基酸に由来する構造単位及び/又は不飽和二塩基酸モノエステルに由来する構造単位とフッ化ビニリデン系単量体に由来する構造単位とを含む共重合体を含有する重合体粒子、並びに(B)無機粒子を含む。
前記重合体粒子の平均粒径が50nm以上700nm以下であることが好ましい。
前記重合体粒子が乳化重合により製造されるものであることが好ましい。
前記非水電解質二次電池用構造体は、前記正極と前記セパレータとの間、及び、前記負極と前記セパレータとの間の少なくとも一方に中間層を有し、
前記中間層は、(A)不飽和二塩基酸に由来する構造単位及び/又は不飽和二塩基酸モノエステルに由来する構造単位とフッ化ビニリデン系単量体に由来する構造単位とを含む共重合体を含有する重合体粒子、並びに(B)無機粒子を含む。
前記重合体粒子は、不飽和二塩基酸に由来する構造単位及び/又は不飽和二塩基酸モノエステルに由来する構造単位とフッ化ビニリデン系単量体に由来する構造単位とを含む共重合体を含有し、
正極、負極、及び前記正極と前記負極との間に積層されたセパレータを有する非水電解質二次電池用構造体において、前記正極と前記セパレータとの間、及び、前記負極と前記セパレータとの間の少なくとも一方に設けられる中間層の製造に用いられる。
本発明に係る水性ラテックスは、水中に分散した重合体粒子及び無機粒子を含むものであって、重合体粒子は、不飽和二塩基酸に由来する構造単位及び/又は不飽和二塩基酸モノエステルに由来する構造単位とフッ化ビニリデン系単量体に由来する構造単位とを含む共重合体を含有し、水性ラテックスは、正極、負極、及び前記正極と負極との間に積層されたセパレータを有する非水電解質二次電池用構造体において、正極とセパレータとの間、及び、負極とセパレータとの間の少なくとも一方に設けられる中間層の製造に用いられる。水性ラテックスにおいて、重合体粒子及び無機粒子の各々は、単独で用いてもよく、2種以上を組み合わせて用いてもよい。
重合体粒子は、不飽和二塩基酸に由来する構造単位及び/又は不飽和二塩基酸モノエステルに由来する構造単位とフッ化ビニリデン系単量体に由来する構造単位とを含む共重合体を含有するものである。共重合体は、不飽和二塩基酸に由来する構造単位及び/又は不飽和二塩基酸モノエステルに由来する構造単位が有するカルボニル基に起因する極性相互作用を示し、基材との接着力に優れる。よって、正極、負極、及び正極と負極との間に積層されたセパレータを有する非水電解質二次電池用構造体において、正極とセパレータとの間、及び、負極とセパレータとの間の少なくとも一方に設けられる中間層の製造に、共重合体を含有する重合体粒子を含む本発明に係る水性ラテックスを用いた場合、セパレータと中間層との接着強度、正極と中間層との接着強度、及び負極と中間層との接着強度が優れたものとなりやすい。重合体粒子において、共重合体は、単独で用いてもよく、2種以上を組み合わせて用いてもよい。
重合体粒子について、1740cm−1における赤外吸収スペクトルの吸光度A1740cm−1と3020cm−1における赤外吸収スペクトルの吸光度A3020cm−1との比A1740cm−1/A3020cm−1が0.10以上であることが好ましい。1740cm−1における吸収は、−CO−O−で表される基によるものであり、3020cm−1における吸収は−CH2−で表される基によるものである。共重合体において、−CO−O−で表される基は、不飽和二塩基酸に由来する構造単位及び/又は不飽和二塩基酸モノエステルに由来する構造単位に含まれ、−CH2−で表される基は、全構成単位に含まれることから、比A1740cm−1/A3020cm−1は、共重合体中の全構成単位のうち、不飽和二塩基酸に由来する構造単位及び不飽和二塩基酸モノエステルに由来する構造単位の合計の割合を反映している。
本発明に用いられる重合体粒子の平均粒径の上限は、700nm以下であることが好ましく、600nm以下であることがより好ましく、500nm以下であることが更により好ましい。上記上限が上記範囲内であると、本発明に係る水性ラテックスを用いて製造される中間層の厚みをコントロールしやすいため好ましい。
なお、上記平均粒径は、動的光散乱法により求められるキュムラント平均粒子径であり、ELSZ−2(大塚電子製)を用いて測定される。
無機粒子としては、非水電解質二次電池において、正極又は負極とセパレータとの間に樹脂膜(中間層)を設けた際に従来から用いられる無機フィラー等を制限なく用いることができる。無機粒子は、通常、熱的に安定な成分であり、中間層がこのような無機粒子を含有することにより、本発明に係るセパレータ/中間層積層体は、形状を維持しやすく、セパレータの加熱時の面積収縮率が小さくなるものと考えられる。
無機粒子の平均粒子径としては5nm〜2μmが好ましく、10nm〜1μmがより好ましい。
なお、水性ラテックスは、比重の高い成分である無機粒子を含むため、調製後速やかに粒子含有層の形成に用いること、又は事前に再分散することが好ましい。
本発明に係る水性ラテックスは、重合体粒子と無機粒子と水とからなるものであってもよいが、重合体粒子、無機粒子、及び水以外の成分(以下、他の成分とも記す。)を含むものであってもよい。
また、重合体粒子と無機粒子との質量比は、電極に対する密着性と耐熱収縮性の観点から、1:99〜99:1であることが好ましく、2:98〜70:30であることがより好ましく、5:95〜60:40であることが更に好ましい。
本発明に係る非水電解質二次電池用構造体は、正極、負極、及び正極及び負極との間に積層されたセパレータを有するものであって、非水電解質二次電池用構造体は、正極とセパレータとの間、及び、負極とセパレータとの間の少なくとも一方に中間層を有し、中間層は、(A)不飽和二塩基酸に由来する構造単位及び/又は不飽和二塩基酸モノエステルに由来する構造単位とフッ化ビニリデン系単量体に由来する構造単位とを含む共重合体を含有する重合体粒子、並びに(B)無機粒子を含む。
本発明に係る非水電解質二次電池用構造体が有する正極としては、正極反応の担い手となる正極活物質を有し、かつ、集電機能を有するものであれば特に限定されないものの、多くの場合、正極活物質を含む正極合剤層と、集電体として機能するとともに正極合剤層を保持する役割を果たす正極集電体とからなる。
正極集電体としては、リチウムイオン二次電池等の非水電解質二次電池の正極集電体として一般的に用いられているものが挙げられる。
本発明に係る非水電解質二次電池用構造体が有するセパレータは、特に限定されない。
本発明に用いられるセパレータは、非水電解質二次電池用構造体を構成するセパレータであり、該構造体から得られた非水電解質二次電池において、正極と負極とを電気的に絶縁し、電解液を保持する役割を果たすものである。本発明で用いられるセパレータとしては、特に限定されないものの、例えば、ポリオレフィン系高分子(例えば、ポリエチレン、ポリプロピレン等)、ポリエステル系高分子(例えば、ポリエチレンテレフタレート等)、ポリイミド系高分子(例えば、芳香族ポリアミド系高分子、ポリエーテルイミド等)、ポリエーテルスルホン、ポリスルホン、ポリエーテルケトン、ポリスチレン、ポリエチレンオキサイド、ポリカーボネート、ポリ塩化ビニル、ポリアクリロニトリル、ポリメチルメタクリレート、セラミックス等、及びこれらの少なくとも2種の混合物からなる単層又は多層の多孔膜;不織布;ガラス;紙等を挙げることができる。なお、前述のポリマーとしては、変性されたものを用いてもよい。
本発明に係る非水電解質二次電池用構造体が有する負極としては、負極反応の担い手となる負極活物質を有し、かつ、集電機能を有するものであれば特に限定されないものの、多くの場合、負極活物質を含む負極合剤層と、集電体として機能するとともに負極合剤層を保持する役割を果たす負極集電体とからなる。
本発明に係る非水電解質二次電池用構造体は、正極とセパレータとの間、及び、負極とセパレータとの間の少なくとも一方に、本発明に係る水性ラテックスを用いて製造される中間層を有する。
中間層は、主に重合体粒子及び無機粒子を原料として形成される。中間層についてSEM観察を行った際に、重合体粒子が粒子形状を保った状態で存在することが確認できることが好ましい。即ち、本発明に係る非水電解質二次電池用構造体では、中間層を構成する重合体粒子が溶融し一体化していることはないことが好ましい。中間層は、複数の重合体粒子が直接又は水溶性高分子を介して互いに接合されている構造を有することが好ましい。また、本発明に係る非水電解質二次電池用構造体の段階では、重合体粒子は、相互に接合又は水溶性高分子により接合されていなくてもよく、非水電解質二次電池用構造体から非水電解質二次電池を製造する際に注入される電解液によって、粒子表面が溶解又は膨潤することにより、重合体粒子が接合されてもよい。
(1)正極、セパレータ、及び負極から選択される少なくとも一種に、本発明に係る水性ラテックスを塗布し、水性ラテックスを乾燥することにより、中間層を形成する。
(2)本発明に係る水性ラテックスに、正極、セパレータ、及び負極から選択される少なくとも一種を浸漬し、これを水性ラテックスから取り出した後、水性ラテックスを乾燥することにより、中間層を形成する。
(3)本発明に係る水性ラテックスを基材に塗布し、水性ラテックスを乾燥した後、形成された塗膜を基材から剥離することにより、中間層を形成する。
(4)本発明に係る水性ラテックスに基材を浸漬し、基材を上記水性ラテックスから取り出した後、水性ラテックスを乾燥した後、形成された塗膜を基材から剥離することにより、中間層を形成する。
なお、本発明に係る水性ラテックスを、正極、セパレータ、負極、基材に塗布する場合には、少なくとも一面(即ち、片面又は両面)に塗布すればよい。
なお、基材から剥離することにより中間層を得る際の基材としては、ポリエチレンテレフタレート(PET)製の基材等を用いることができる。
本発明に係るセパレータ/中間層積層体は、非水電解質二次電池用のセパレータと、セパレータの少なくとも一方の主面に設けられた中間層とを有し、中間層は、(A)不飽和二塩基酸に由来する構造単位及び/又は不飽和二塩基酸モノエステルに由来する構造単位とフッ化ビニリデン系単量体に由来する構造単位とを含む共重合体を含有する重合体粒子、並びに(B)無機粒子を含む。セパレータ/中間層積層体において、セパレータと中間層とは直接接していてもよいし、セパレータと中間層との間に他の層が介在していてもよい。
本発明に係る非水電解質二次電池は、非水電解質二次電池用構造体から得られる。
非水電解質二次電池の電池構造としては、例えば、コイン型電池、ボタン型電池、円筒型電池、角型電池等の公知の電池構造が挙げられる。
非水電解質二次電池を構成する部材としては、非水電解質二次電池用構造体以外には、例えば、非水電解液、円筒缶、ラミネートパウチ等が挙げられる。
前記非水系溶媒として、電解質を構成するカチオン及びアニオンを輸送可能な非プロトン性の有機溶媒であって、かつ、実質的に二次電池の機能を損なわないものが挙げられる。そのような非水系溶媒として、リチウムイオン二次電池の非水電解液として通常用いられる有機溶媒が挙げられ、例えば、カーボネート類、ハロゲン化炭化水素、エーテル類、ケトン類、ニトリル類、ラクトン類、エステル類、オキソラン化合物等を用いることができる。中でも、プロピレンカーボネート、エチレンカーボネート、ジメチルカーボネート、ジエチルカーボネート、エチルメチルカーボネート、1,2−ジメトキシエタン、1,2−ジエトキシエタン、プロピオン酸メチル、プロピオン酸エチル、スクシノニトリル、1,3−プロパンスルトン、炭酸フルオロエチレン、炭酸ビニレン等が好ましい。
非水系溶媒は、1種単独で用いても2種以上を用いてもよい。
熱プレスを行う際の温度としては、常温〜160℃であることが好ましく、40〜120℃であることがより好ましい。熱プレスを行う際の圧力は、好ましくh0.01〜10MPa、より好ましくは0.1〜8MPaである。熱プレスを行う際、予熱時間は1秒〜1時間であることが好ましく、プレス時間は1秒から1時間であることが好ましい。
上記のような非水電解質二次電池は正極−中間層−セパレータ及び/又は負極−中間層−セパレータ間の密着に優れた電極を形成することができる。
コバルト酸リチウム(セルシードC5−H、日本化学工業製)、導電助剤(SuperP、TIMCAL製)、及びPVDF(ポリフッ化ビニリデン、KF#1100、クレハ製)を93:3:4の質量比でN−メチル−2−ピロリドンと混合して、固形分濃度69質量%のスラリーを作製した。115μmのスペーサーを用いてこのスラリーをアルミニウム箔にコートした後、120℃で3時間乾燥し、その後、プレスして、嵩密度3.6g/cm3、目付け量150g/m2の正極を得た。
BTR918(改質天然黒鉛、BTR製)、導電助剤(SuperP、TIMCAL製)、SBR(スチレンブタジエンゴムラテックス、BM−400、日本ゼオン製)、及びCMC(カルボキシメチルセルロース、セロゲン4H、第一工業製薬)を90:2:3:1の質量比で水と混合して、固形分濃度53質量%のスラリーを作製した。90μmのスペーサーを用いてこのスラリーを銅箔にコートした後、120℃で3時間乾燥し、その後、プレスして、嵩密度1.5g/cm3、目付け量56g/m2の負極を得た。
オートクレーブに280質量部の水をいれ、脱気後、0.5質量部のパーフルオロオクタン酸(PFOA)アンモニウム塩と0.05質量部の酢酸エチルとを入れ、次いで20質量部のフッ化ビニリデン(VDF)と5質量部のヘキサフルオロプロピレン(HFP)とを入れた。
過硫酸アンモニウムの添加量を0.5質量部から0.06質量部に変更し、マレイン酸モノメチルを添加しなかった以外は、実施例1と同様にして、VDF−HFP共重合体ラテックスを得た。樹脂濃度、平均粒径、及び吸光度比を実施例1と同様にして測定したところ、樹脂濃度は24.6質量%、平均粒径は195nm、吸光度比(A1740cm−1/A3020cm−1)は0.06であった。なお、IRスペクトルの測定結果を図1に示す。
マレイン酸モノメチルを用いてラテックスを得た実施例1では、吸光度比(A1740cm−1/A3020cm−1)が0.10以上であった。これに対し、マレイン酸モノメチルを用いずにラテックスを得た比較例1では、吸光度比(A1740cm−1/A3020cm−1)が0.10未満であった。
また、実施例1のコーティングセパレータの面積収縮率は、コーティング前のセパレータの面積収縮率よりも、はるかに小さかった。
更に、実施例1では、比較例1と比較して、正極とコーティングセパレータとの間の180°剥離強度、及び、コーティングセパレータと負極との間の180°剥離強度のいずれもが高く、特に、コーティングセパレータと負極との間の180°剥離強度の向上が著しかった。
Claims (6)
- 非水電解質二次電池用のセパレータと、前記セパレータの少なくとも一方の主面に設けられた中間層とを有し、
前記中間層は、(A)不飽和二塩基酸に由来する構造単位及び/又は不飽和二塩基酸モノエステルに由来する構造単位とフッ化ビニリデン系単量体に由来する構造単位とを含む共重合体を含有する重合体粒子、並びに(B)無機粒子を含むセパレータ/中間層積層体。 - 前記重合体粒子について、1740cm−1における赤外吸収スペクトルの吸光度A1740cm−1と3020cm−1における赤外吸収スペクトルの吸光度A3020cm−1との比A1740cm−1/A3020cm−1が0.10以上である請求項1に記載のセパレータ/中間層積層体。
- 前記重合体粒子の平均粒径が50nm以上700nm以下である請求項1又は2に記載のセパレータ/中間層積層体。
- 前記重合体粒子が乳化重合により製造されるものである請求項1〜3のいずれか1項に記載のセパレータ/中間層積層体。
- 正極、負極、及び前記正極及び前記負極との間に積層されたセパレータを有する非水電解質二次電池用構造体であって、
前記非水電解質二次電池用構造体は、前記正極と前記セパレータとの間、及び、前記負極と前記セパレータとの間の少なくとも一方に中間層を有し、
前記中間層は、(A)不飽和二塩基酸に由来する構造単位及び/又は不飽和二塩基酸モノエステルに由来する構造単位とフッ化ビニリデン系単量体に由来する構造単位とを含む共重合体を含有する重合体粒子、並びに(B)無機粒子を含む非水電解質二次電池用構造体。 - 水中に分散した重合体粒子及び無機粒子を含む水性ラテックスであって、
前記重合体粒子は、不飽和二塩基酸に由来する構造単位及び/又は不飽和二塩基酸モノエステルに由来する構造単位とフッ化ビニリデン系単量体に由来する構造単位とを含む共重合体を含有し、
正極、負極、及び前記正極と前記負極との間に積層されたセパレータを有する非水電解質二次電池用構造体において、前記正極と前記セパレータとの間、及び、前記負極と前記セパレータとの間の少なくとも一方に設けられる中間層の製造に用いられる水性ラテックス。