JP2016074831A - 反応性ポリシロキサン化合物及びこれを含む塗料組成物 - Google Patents
反応性ポリシロキサン化合物及びこれを含む塗料組成物 Download PDFInfo
- Publication number
- JP2016074831A JP2016074831A JP2014206566A JP2014206566A JP2016074831A JP 2016074831 A JP2016074831 A JP 2016074831A JP 2014206566 A JP2014206566 A JP 2014206566A JP 2014206566 A JP2014206566 A JP 2014206566A JP 2016074831 A JP2016074831 A JP 2016074831A
- Authority
- JP
- Japan
- Prior art keywords
- group
- compound
- polysiloxane compound
- reactive polysiloxane
- reactive
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
【解決手段】下記一般式(1)で表される、ヒドロキシウレタン結合を介し、片末端に不飽和基を含有するポリシロキサン化合物である反応性ポリシロキサン化合物、特に、アミノ基を有するポリシロキサン化合物と、エチレン性不飽和基及び5員環環状カーボネート構造の両方を有する化合物とを反応させることにより得られる反応性ポリシロキサン化合物、及び、これを含む塗料組成物。
【選択図】なし
Description
[一般式(1)中、mは0〜300のいずれかの整数であり、X1は、水酸基とウレタン結合を有する下記式(2)〜(5)から選ばれるいずれかのヒドロキシウレタン結合であり、Zは、ないか、−CH2−O−、−O−、−O−(CH2)n−O−(但し、nは1〜10の整数)、−CO−O−、−CO−O−(CH2)n−O−(但し、nは1〜10の整数)から選ばれるいずれかである。また、R1及びR2は、それぞれCH3又はHであり、同一であっても異なっていてもよく、R3は、CH3又は式(6)の基であり、同一であっても異なっていてもよい。また、Y1は、構造中に、O、S又はNのいずれかの元素或いは環状構造を含んでいてもよい、炭素数1〜30の、アルキレン基又はアリーレン基又は繰り返し単位1〜300のポリエチレングリコール鎖である。Wは、炭素数1〜30のアルコキシ基、或いは、構造中に、O、S又はNのいずれかの元素或いは環状構造を含んでいてもよい、炭素数1〜30のアルキル基又はアリール基である。]
[式(3)中、R4は、H又はCH3である。]
[式(6)中、mは0〜300のいずれかの整数であり、Wは、炭素数1〜30のアルコキシ基、或いは、構造中に、O、S又はNのいずれかの元素或いは環状構造を含んでいてもよい、炭素数1〜30のアルキル基又はアリール基である。]
片末端にアミノ基を有するポリシロキサン化合物と、片末端にエチレン性不飽和基を有する、エチレン性不飽和基及び5員環環状カーボネート構造の両方を有する化合物とを反応させて得られた前記反応性ポリシロキサン化合物。
[一般式(7)及び(8)中の、R1、R2及びZは、前記一般式(1)中におけるこれらの記号と同義であり、一般式(7)中のR4は、H又はCH3である。]
[上記式中の、Y1、R3、W及びmは、前記一般式(1)中におけるこれらの記号と同義である。]
一般式(1)で示される本発明の反応性ポリシロキサン化合物を特徴づける、X1で示される化学構造、すなわち、前記一般式(2)〜(5)で示される化学構造は、いずれも水酸基とウレタン結合とを有するヒドロキシウレタン結合を有するが、該ヒドロキシウレタン結合は、下記に示したように、5員環環状カーボネート化合物とアミン化合物との付加反応により形成することができる。5員環環状カーボネート化合物とアミン化合物との反応においては、下記に示すように、5員環環状カーボネート基の開裂が2種類あるため、2種類の構造の生成物が得られることが知られている。また、この付加反応により得られる化学構造はウレタン結合であるが、水酸基を有した特異な構造を有したものであり、特に通常のウレタン結合と区別されヒドロキシウレタン結合(或いはヒドロキシウレタン構造)と呼ばれるものである。本明細書では、ヒドロキシウレタン結合と呼んでいる。
本発明の反応性ポリシロキサン化合物は、例えば、末端に1個のアミノ基を有するポリシロキサン化合物と、片末端にエチレン性不飽和基を有する、エチレン性不飽和基及び5員環環状カーボネート構造の両方を有する化合物とを反応させることによって容易に得られる。また、この際に使用される、エチレン性不飽和基と5員環環状カーボネート構造の両方を有する化合物としては、例えば、下記の一般式(7)又は(8)で示される化合物が挙げられ、いずれも本発明において好ましく使用できる。
本発明の反応性ポリシロキサン化合物の製造に使用される、片末端にアミノ基を有するポリシロキサン化合物としては、従来公知の化合物を特に制限なく使用可能であるが、勿論、本発明の目的に応じて新たに合成したものも用いることができる。特に、下記に示したような構造の、片末端に1個のアミノ基を有するポリシロキサン化合物を用いることが好ましい。市場から入手できるものとしては、例えば、官能基当量2500mg/molの片末端アミノ基変性シリコーンオイル(商品名:TSF−4701、モメンティブ・パフォーマンス・マテリアルズ・ジャパン製)、官能基当量3000mg/molの片末端アミノ基変性シリコーンオイル(商品名:TSF−4700、モメンティブ・パフォーマンス・マテリアルズ・ジャパン製)等が挙げられる。これらの化合物はいずれも、下記に示した構造を有する。なお、官能基当量は、官能基であるアミノ基1モルに結合している主骨格(ポリジメチルシロキサン)の質量を意味する。
上記したような片末端に1個のアミノ基を有するポリシロキサン化合物と、先述したような、エチレン性不飽和基及び5員環環状カーボネート構造の両方を有する化合物とを用い、5員環環状カーボネート構造(基)とアミノ基とを反応させることで、本発明の反応性ポリシロキサン化合物を得ることができる。上記反応は、例えば、溶剤の存在下或いは非存在下で、40〜200℃の温度で、4〜24時間反応を行うことで、本発明の一般式(1)で表される反応性ポリシロキサン化合物を得ることができる。
上記のようにして得られる本発明の反応性ポリシロキサン化合物は、分子内に、ポリシロキサンセグメントと、反応性のエチレン性不飽和基(不飽和結合)とを共に有する化合物であり、通常は、流動性を有する液状の物質である。このような構造を有するため、本発明の反応性ポリシロキサン化合物によれば、その構造中に存在する不飽和結合を分子間で、或いは、他の化合物と反応させることができる。また、その構造中に有する水酸基によって、他の材料との相溶性に優れるので、添加剤材料として有用である。特に、本発明の反応性ポリシロキサン化合物は、塗料組成物の材料として用いた場合に、各種の反応性モノマーとの相溶性に優れ、形成される塗膜或いは被膜は改質されて、優れた機能性を示すものとなる。
グリシジルメタクリレート(商品名:アクリエステルG、三菱レイヨン製、分子量142.1)100部と、触媒として臭化リチウム(和光純薬製)5.4部と、N−メチル−2−ピロリドン100部とを、撹拌装置及び大気開放口のある還流器を備えた反応容器内に仕込んだ。次いで、撹拌しながら二酸化炭素を連続して吹き込み、100℃にて10時間反応を行った。反応終了後の溶液に、水200部とトルエン200部を添加し、混合した。得られた混合液を分液ロートに移し、分離した水槽(下層)を除去し、その後、同様にして分液ロート中で水50部にて3回の洗浄を行うことにより、反応液から触媒を除去した。洗浄後のトルエン層(上層)から、ロータリーエバポレーターにてトルエンを蒸発留去し、淡黄色の液状物質を得た(収率93%)。
分子量約900の片末端水素ポリジメチルシロキサン(商品名:MCR−H07、gelest社製)90g、N,N−ビス(トリメチルシリル)アリルアミンを48.4g、白金1,3−ジビニルテトラメチルジシロキサン錯体(3%キシレン溶液)0.03gを仕込み、60℃まで昇温させ2時間の反応を行った。次いで、メタノールの60gを加え、還流条件下で6時間の反応を行った。反応終了後に、メタノール及び未反応のN,N−ビス(トリメチルシリル)アリルアミンを減圧留去し、透明なオイル状物質を得た。このオイル状物質の全アミン価(JIS−K7237)は、58mgKOH/gであった。このことから、この物質は下記構造式で表される片末端にアミノ基を有するポリシロキサン化合物と確認され、これをS−1と略称した。なお、上記の製造方法は、特許3666551に記載の方法を利用した。
合成例1で得たC−1を7.4部、官能基当量2500g/molの片末端アミノ基変性シリコーンオイル(商品名:TSF−4701、モメンティブ・パフォーマンス・マテリアルズ・ジャパン製)を100部、トルエンを46部、重合禁止剤としてp−メトキシフェノールを0.007部(和光純薬製)、撹拌装置及び大気開放口のある還流器を備えた反応容器内に仕込んだ。次いで、撹拌しながら60℃にて反応を行った。反応の進行はサンプリングした反応液のアミン濃度を中和滴定により確認し、アミン濃度が測定限界以下まで減少した時点で反応を終了した。反応時間は8時間であった。反応後の溶液のIR分析では、1800cm-1付近の環状カーボネートのカルボニル由来のピークは消失しており、1760cm-1付近にウレタン結合のカルボニルに由来する新しいピークが確認された。図2に、そのIRチャートを示した。反応の終了を確認した後に反応容器を減圧し、トルエンを完全に除去し、淡黄色透明な液状の化合物を得た。
合成例1で得たC−1を19.2部、合成例2で得たS−1を100部、トルエン51部、p−メトキシフェノールを0.019部使用した以外は、実施例1と同様の操作により淡黄色透明な液状化合物を得た。
得られた化合物の水酸基価(JIS K1557−1)は47.5mgKOH/gであり、GPC測定による重量平均分子量(ポリスチレン換算)は1100であった。以上のことから、得られた化合物は、ヒドロキシウレタン結合を介し、片末端に不飽和基を含有する、本発明で規定するポリシロキサン化合物であることが確認された。得られた化合物の化学構造中に、反応に使用したC−1由来の二酸化炭素成分が占める割合は、3.8%であった(化学構造式上の分子量からの計算値)。
実施例1で調製し、実施例1の塗料の作製に用いた本発明で規定するポリシロキサン化合物5部に代えて、官能基当量2300g/molのメタクリル変性反応性シリコーンオイル5部(商品名:X22−174BX、信越化学工業製)を用いた以外は実施例1と同様の配合組成により、本比較例の塗料を作製した。そして、作製した塗料を、実施例1と同様に100μmのポリエチレンテレフタレートフィルムに5μm厚になるように塗布し、紫外線を照射して硬化させ、評価用の試料を作製した。しかし、得られた試料の塗膜の表面状態は、不均一に成分が分離した状態であり、且つ、表面にベトつきがある状態で、形成された塗膜は、硬化が不十分であった。このように、その基本的特性である硬化が不十分と判断されたことから、耐溶剤性の評価以外の塗膜の評価は実施しなかった。
2−イソシアナトエチルメタクリレート(商品名:カレンズMOI、昭和電工製)を5.5部、水酸基価20mgKOH/gの反応性シリコーンオイル(商品名:X22−170BX、信越化学工業製)を100部、トルエンを100部、触媒として、ジブチルスズジラウレート(共同薬品株性)を0.05部、撹拌装置及び大気開放口のある還流器を備えた反応容器内に仕込んだ。そして、反応容器内を撹拌しながら、80℃にてIRを測定しながらイソシアネートがなくなるまで反応を実施した。反応時間は6時間であった。反応容器を減圧しトルエンを完全に除去して、本比較例の、淡黄色透明な液状の化合物を得た。この化合物は、シリコーン末端にウレタン結合を介してメタクリル基が導入された、反応性ポリシロキサン化合物である。
2−イソシアナトエチルメタクリレート(商品名:カレンズMOI、昭和電工製)を9.7部、水酸基価35mgKOH/gの両末端カルビノール変性反応性シリコーンオイル(商品名:KF−6002、信越化学工業製)を100部、トルエン100部、触媒としてジブチルスズジラウレート(共同薬品株性)を0.05部、使用して比較例2と同様に反応させ、本比較例のポリシロキサン化合物を得た。この化合物は、シリコーン両末端にウレタン結合を介してメタクリル基が導入された反応性ポリシロキサン化合物である。
上記の実施例及び比較例で得られた各塗膜の評価用の試料を用い、以下の項目について、下記の評価基準で評価した。表1に、評価結果をまとめて示した。
形成された各塗膜の溶剤に対する硬化状態を確認するため、メチルエチルケトン(MEK)及び酢酸エチル(EAc)の2種類の溶剤をそれぞれに用い、下記の条件下でラビング試験を行って評価した。試験は、荷重500g×10往復の条件で行い、ラビング試験後の塗膜表面を目視で評価し判定した。
<評価基準>
○:いずれの溶剤においても塗膜に変化は見られなかった。
×:塗膜の溶解や剥がれが確認された。
各塗膜表面の20℃における水の接触角を測定し、得られた測定値を用い、以下の基準で4段階に評価した。
<評価基準>
◎:105°以上
○:95°以上105°未満
△:85°以上95°未満
×:85°未満
各塗膜表面の20℃におけるn−ドデカンの接触角を測定し、得られた測定値を用い、以下の基準で3段階に評価した。
<評価基準>
○:20°以上
△:5°以上20°未満
×:5°未満
各塗膜に24mm幅のセロハンテープを貼り付けて、180°剥離における剥離強度を測定した。剥離強度が弱い物を離型性が良好であるとし、以下の基準により、3段階で評価した。
<評価基準>
○:剥離強度 5g未満
△:剥離強度 5g以上〜50g未満
×:剥離強度 50g以上
基材を含む硬化塗膜を3cm×3cmに切り取った物を評価試料とした。試料の中央部を、塗布面を上とし反対側に180度に折り目が付くまで折り曲げ、目視にて塗膜の状態を観察した。そして、以下の基準で、3段階に評価した。
<評価基準>
○:塗膜の割れや剥がれは確認できない。
△:塗膜は剥がれていないが折り曲げ部に亀裂が発生している。
×:塗膜の一部が剥がれ落ちた。
塗膜に黒マジック(マジックインキ No.500)で線を引き、5分間放置した後、乾いたティッシュペーパーにて拭き取りを行い、インクの残り具合を目視で観察し、下記の基準で、3段階に評価した。
<評価基準>
○:インクが完全に除去できる。
△:インクの大部分を除去できるが跡が残る。
×:インクが除去できない。
以下の基準により、塗膜を形成している成分の環境対応性を3段階で評価した。
<評価基準>
○:原材料の一部が二酸化炭素であり、且つ、有機錫触媒を使用していない。
△:原材料の一部が二酸化炭素であるか、有機錫触媒を使用していないか、のどちらかの条件を満たしている。
×:原材料に二酸化炭素を使用しておらず、有機錫触媒を使用している。
Claims (8)
- 下記一般式(1)で表される、ヒドロキシウレタン結合を介し、片末端にエチレン性不飽和基を有するポリシロキサン化合物であることを特徴とする反応性ポリシロキサン化合物。
[一般式(1)中、mは0〜300のいずれかの整数であり、X1は、水酸基とウレタン結合を有する下記式(2)〜(5)から選ばれるいずれかのヒドロキシウレタン結合であり、Zは、ないか、−CH2−O−、−O−、−O−(CH2)n−O−(但し、nは1〜10の整数)、−CO−O−、−CO−O−(CH2)n−O−(但し、nは1〜10の整数)から選ばれるいずれかである。また、R1及びR2は、それぞれCH3又はHであり、同一であっても異なっていてもよく、R3は、CH3又は式(6)の基であり、同一であっても異なっていてもよい。また、Y1は、構造中に、O、S又はNのいずれかの元素或いは環状構造を含んでいてもよい、炭素数1〜30の、アルキレン基又はアリーレン基又は繰り返し単位1〜300のポリエチレングリコール鎖である。Wは、炭素数1〜30のアルコキシ基、或いは、構造中に、O、S又はNのいずれかの元素或いは環状構造を含んでいてもよい、炭素数1〜30のアルキル基又はアリール基である。]
[式(2)中、R4は、H又はCH3である。]
[式(3)中、R4は、H又はCH3である。]
[式(6)中、mは0〜300のいずれかの整数であり、Wは、炭素数1〜30のアルコキシ基、或いは、構造中に、O、S又はNのいずれかの元素或いは環状構造を含んでいてもよい、炭素数1〜30の、アルキル基又はアリール基である。] - 片末端にアミノ基を有するポリシロキサン化合物と、片末端にエチレン性不飽和基を有する、エチレン性不飽和基及び5員環環状カーボネート構造の両方を有する化合物とを反応させて得られた請求項1に記載の反応性ポリシロキサン化合物。
- 前記エチレン性不飽和基及び5員環環状カーボネート構造の両方を有する化合物の、5員環環状カーボネート構造部が、エポキシ基と二酸化炭素から合成されたものである請求項2〜4のいずれか1項に記載の反応性ポリシロキサン化合物。
- 全質量のうちの0.1〜10質量%が、二酸化炭素由来の−O−CO−結合から構成されたものである請求項5に記載の反応性ポリシロキサン化合物。
- 水酸基価が5〜100mgKOH/gの範囲である請求項1〜6のいずれか1項に記載の反応性ポリシロキサン化合物。
- 塗膜或いは被膜の表面状態の改質剤として、請求項1〜7のいずれか1項に記載の反応性ポリシロキサン化合物を含有してなることを特徴とする塗料組成物。