JP2015529725A - アクリル−シリコーン系ハイブリッドエマルジョン粘着剤組成物及びその製造方法 - Google Patents
アクリル−シリコーン系ハイブリッドエマルジョン粘着剤組成物及びその製造方法 Download PDFInfo
- Publication number
- JP2015529725A JP2015529725A JP2015528413A JP2015528413A JP2015529725A JP 2015529725 A JP2015529725 A JP 2015529725A JP 2015528413 A JP2015528413 A JP 2015528413A JP 2015528413 A JP2015528413 A JP 2015528413A JP 2015529725 A JP2015529725 A JP 2015529725A
- Authority
- JP
- Japan
- Prior art keywords
- acrylic
- adhesive composition
- sensitive adhesive
- acrylate
- group
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
Claims (23)
- 反応型シリコーン樹脂からなるシード(seed)とアクリル系単量体混合物とが乳化重合されたアクリル系エマルジョン樹脂を含むことを特徴とする、アクリル−シリコーン系ハイブリッドエマルジョン粘着剤組成物。
- 前記反応型シリコーン樹脂は、官能基を有するポリアルキルシロキサンを含むことを特徴とする、請求項1に記載のアクリル−シリコーン系ハイブリッドエマルジョン粘着剤組成物。
- 前記反応型シリコーン樹脂は、官能基を有するポリジメチルシロキサンを含むことを特徴とする、請求項1に記載のアクリル−シリコーン系ハイブリッドエマルジョン粘着剤組成物。
- 前記官能基は、ヘキセニル基及び/又はビニル基であることを特徴とする、請求項2又は3に記載のアクリル−シリコーン系ハイブリッドエマルジョン粘着剤組成物。
- 前記シードは、アクリル系単量体混合物100重量部に対して5〜20重量部含まれることを特徴とする、請求項1に記載のアクリル−シリコーン系ハイブリッドエマルジョン粘着剤組成物。
- 前記反応型シリコーン樹脂は、分子量が500,000以下であることを特徴とする、請求項1に記載のアクリル−シリコーン系ハイブリッドエマルジョン粘着剤組成物。
- 前記アクリル系単量体混合物は、i)炭素数1〜14のアルキル基を有する(メタ)アクリル酸エステル単量体、ii)アリルエステル、ビニルエステル、不飽和アセテート及び不飽和ニトリルからなる群から選択される1種以上の単量体、iii)不飽和カルボン酸及び水酸基含有不飽和単量体からなる群から選択される1種以上の単量体、及びiv)架橋剤を含むことを特徴とする、請求項1に記載のアクリル−シリコーン系ハイブリッドエマルジョン粘着剤組成物。
- 前記アクリル系単量体混合物は、アクリル系単量体混合物の全重量を基準として、i)炭素数1〜14のアルキル基を有する(メタ)アクリル酸エステル単量体60〜90重量%、ii)アリルエステル、ビニルエステル、不飽和アセテート及び不飽和ニトリルからなる群から選択される1種以上の単量体5〜35重量%、iii)不飽和カルボン酸及び水酸基含有不飽和単量体からなる群から選択される1種以上の単量体0.5〜5重量%、及びiv)架橋剤0.1〜3重量%を含むことを特徴とする、請求項7に記載のアクリル−シリコーン系ハイブリッドエマルジョン粘着剤組成物。
- 前記アクリル系単量体混合物には、エポキシ基含有不飽和単量体がさらに含まれていることを特徴とする、請求項7に記載のアクリル−シリコーン系ハイブリッドエマルジョン粘着剤組成物。
- 前記エポキシ基含有不飽和単量体は、アクリル系単量体混合物の全重量を基準として0.1〜3重量%含まれることを特徴とする、請求項9に記載のアクリル−シリコーン系ハイブリッドエマルジョン粘着剤組成物。
- 前記エポキシ基含有不飽和単量体は、グリシジル(メタ)アクリレートまたはアリルグリシジルエーテルであることを特徴とする、請求項9に記載のアクリル−シリコーン系ハイブリッドエマルジョン粘着剤組成物。
- 前記i)の単量体は、メチル(メタ)アクリレート、エチル(メタ)アクリレート、プロピル(メタ)アクリレート、イソプロピル(メタ)アクリレート、ブチル(メタ)アクリレート、イソブチルアクリレート、t−ブチルメタクリレート、ペンチルメタクリレート、ヘキシルメタクリレート、ヘプチルアクリレート、イソオクチルアクリレート、オクチルメタクリレート、2−エチルヘキシル(メタ)アクリレート、イソデシルアクリレート、デシルメタクリレート、ドデシルメタクリレート、イソボルニルメタクリレート、及びラウリル(メタ)アクリレートからなる群から選択される1つ以上であることを特徴とする、請求項7に記載のアクリル−シリコーン系ハイブリッドエマルジョン粘着剤組成物。
- 前記i)の単量体は、(メタ)アクリル酸エステル単量体の全重量を基準として、2−エチルヘキシルアクリレート20〜40重量%及びブチルアクリレート60〜80重量%の混合物からなることを特徴とする、請求項7に記載のアクリル−シリコーン系ハイブリッドエマルジョン粘着剤組成物。
- 前記ii)の単量体は、酢酸ビニル、ブタン酸ビニル、プロピオン酸ビニル、ラウリン酸ビニル、ビニルピロリドン、アクリロニトリル及びメタクリロニトリルからなる群から選択される1つ以上であることを特徴とする、請求項7に記載のアクリル−シリコーン系ハイブリッドエマルジョン粘着剤組成物。
- 前記iii)の単量体は、アクリル酸、イタコン酸、無水マレイン酸、フマル酸、クロトン酸、メタクリル酸、エチルメタクリレート、ヒドロキシメチル(メタ)アクリレート、ヒドロキシエチル(メタ)アクリレート、ヒドロキシプロピル(メタ)アクリレート、ヒドロキシブチル(メタ)アクリレート、ヒドロキシヘキシル(メタ)アクリレート、ヒドロキシオクチル(メタ)アクリレート、ヒドロキシラウリル(メタ)アクリレート及びヒドロキシプロピレングリコール(メタ)アクリレートからなる群から選択される1つ以上であることを特徴とする、請求項7に記載のアクリル−シリコーン系ハイブリッドエマルジョン粘着剤組成物。
- 前記iv)の架橋剤は、5〜15個のアルキレンオキシド基を含み、アクリレート基またはビニル基を有する化合物であることを特徴とする、請求項7に記載のアクリル−シリコーン系ハイブリッドエマルジョン粘着剤組成物。
- 前記架橋剤は、ポリエチレングリコールジアクリレート及びポリプロピレングリコールジアクリレートからなる群から選択される1種以上であることを特徴とする、請求項16に記載のアクリル−シリコーン系ハイブリッドエマルジョン粘着剤組成物。
- 前記アクリル−シリコーン系ハイブリッドエマルジョン粘着剤組成物の固形分は55〜65%であることを特徴とする、請求項1に記載のアクリル−シリコーン系ハイブリッドエマルジョン粘着剤組成物。
- アクリル−シリコーン系ハイブリッドエマルジョン粘着剤組成物の粘度は500〜2000cpsであることを特徴とする、請求項1に記載のアクリル−シリコーン系ハイブリッドエマルジョン粘着剤組成物。
- 請求項1に記載のアクリル−シリコーン系ハイブリッドエマルジョン粘着剤組成物の製造方法であって、
(A)反応型シリコーン樹脂からなるシード(seed)を含む乳化液を製造する過程と、
(B)アクリル系単量体混合物の全重量を基準として、i)炭素数1〜14のアルキル基を有する(メタ)アクリル酸エステル単量体60〜90重量%、ii)アリルエステル、ビニルエステル、不飽和アセテート及び不飽和ニトリルからなる群から選択される1種以上の単量体5〜35重量%、iii)不飽和カルボン酸及び水酸基含有不飽和単量体からなる群から選択される1種以上の単量体0.5〜5重量%、及びiv)架橋剤0.1〜3重量%を含むアクリル系単量体混合物を含むプレエマルジョン溶液を製造する過程と、
(C)前記過程(A)の乳化液に開始剤及び過程(B)のプレエマルジョン溶液を添加し、重合して、アクリル系エマルジョン樹脂を製造する過程とを含むことを特徴とする、アクリル−シリコーン系ハイブリッドエマルジョン粘着剤組成物の製造方法。 - 前記開始剤は、アンモニウム又はアルカリ金属の過硫酸塩、過酸化水素、パーオキサイド、及びハイドロパーオキサイドからなる群から選択される1つ以上であることを特徴とする、請求項20に記載のアクリル−シリコーン系ハイブリッドエマルジョン粘着剤組成物の製造方法。
- アクリル−シリコーン系ハイブリッドエマルジョン粘着剤組成物は、硬化型感圧粘着剤組成物であることを特徴とする、請求項1に記載のアクリル−シリコーン系ハイブリッドエマルジョン粘着剤組成物。
- 請求項1に記載のアクリル−シリコーン系ハイブリッドエマルジョン粘着剤組成物を粘着用フィルム又はシート上に適用して粘着剤層を形成する、粘着シート。