JP2015221903A - アクリルフィルムおよびその製造方法 - Google Patents
アクリルフィルムおよびその製造方法 Download PDFInfo
- Publication number
- JP2015221903A JP2015221903A JP2015134891A JP2015134891A JP2015221903A JP 2015221903 A JP2015221903 A JP 2015221903A JP 2015134891 A JP2015134891 A JP 2015134891A JP 2015134891 A JP2015134891 A JP 2015134891A JP 2015221903 A JP2015221903 A JP 2015221903A
- Authority
- JP
- Japan
- Prior art keywords
- film
- acrylic
- acrylic film
- liquid crystal
- additive
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
これら耐熱アクリル系樹脂を押出し機により溶融押出しフィルムに成形する場合、前記耐熱アクリル系樹脂の熱分解物に起因する異物によって、アクリルフィルムを組み込んだ液晶表示装置の画像が悪化するという問題が生じてきている。これは、近年の液晶表示装置の大型化に伴い、従来見落とされがちであったアクリルフィルムの欠陥が問題になってきたことに起因する問題である。この熱分解に起因する異物を抑制するという課題に対し、アクリル樹脂の溶融粘度やスクリューを規定した製膜法が開示されている(特許文献4)。このように、近年の液晶表示装置の大型化によって、従来では見落とされがちであったアクリルフィルムのわずかな欠陥が問題となってきているのが現状である。
一方、前記横ダンは、特に厚み60μm以下の薄手製膜をする場合や幅1.5m以上の広幅製膜する場合により顕著に発生し、さらに10m/分以上のスピードで連続製膜する場合に明らかに顕在化するものであることも判明した。
以上の検討から、近年の液晶表示装置の大画面化に伴い、前記横ダンが画面の中に入る頻度が増加したためアクリルフィルムの欠陥に由来する液晶表示装置の画面のにじみが発生することとなったことが判明した。また、大型液晶表示装置に用いることを目的としてアクリルフィルムを大型化したり生産性を高めたりする際に、特に前記画像のにじみが問題となることが判明した。
[2] 前記添加剤が、安定剤、紫外線吸収剤、可塑剤およびマット剤からなる群より選ばれる少なくとも一種であることを特徴とする[1]に記載のアクリルフィルム。
[3] 前記添加剤が安定剤または紫外線吸収剤であることを特徴とする[1]または[2]に記載のアクリルフィルム。
[4] 前記アクリルフィルムが、ラクトン環単位、無水マレイン酸単位、グルタル酸無水物単位の少なくとも1種の単位を含み、厚みが20μm〜85μmであることを特徴とする[1]〜[3]のいずれか一項に記載のアクリルフィルム。
[5] 前記アクリルフィルムの幅が1.5m〜4.0mであることを特徴とする[1]〜[4]のいずれか一項に記載のアクリルフィルム。
[6] アクリル樹脂のペレットを押出し機に投入して溶融させてメルトを得る工程と、
前記ダイからメルトを押出す工程と、
前記ダイから押出されたメルトを固化して製膜する工程と、を含むアクリルフィルムの製造方法において、
前記アクリル樹脂のペレットを押出し機に投入して溶融させてメルトを得る工程において、前記ペレットとともに直径30μm〜1mmのアクリル樹脂粉体を前記押出機に投入し、かつ、前記アクリル樹脂粉体の添加量が、前記ペレットに対して0.01質量%〜10質量%であることを特徴とするアクリルフィルムの製造方法。
[7] 製膜速度が10m/分〜70m/分であることを特徴とする[6]に記載のアクリルフィルムの製造方法。
[8] 前記ダイから押出されたメルトを固化して製膜する工程において、キャストロール上にメルトを流延し、前記キャストロールより1〜30℃低い温度に設定されたタッチロールをメルトを流延した前記キャストロールに0.1MP〜10MPの圧力で押圧することを特徴とする請求項[6]または[7]に記載のアクリルフィルムの製造方法。
[9] 前記ペレットを押出し機に投入して溶融させてメルトを得る工程において、添加剤含有量が異なる複数種のペレットを押出し機に投入して溶融する工程を含み、かつ、前記複数種のペレットのうち最も添加剤含有量が少ないペレットと最も添加剤含有量が多いペレットの間の添加剤含有量の比が1.1〜10倍であることを特徴とする[6]〜[8]のいずれか一項に記載のアクリルフィルムの製造方法。
[10] 製膜後のフィルムを少なくとも一方向に1.1倍〜3.5倍の倍率で延伸する工程を含むことを特徴とする[6]〜[9]のいずれか一項に記載のアクリルフィルムの製造方法。
[11] [6]〜[10]のいずれか一項に記載の製造方法で製造したことを特徴とする[1]〜[5]のいずれか一項に記載のアクリルフィルム。
[12] [1]〜[5]および[11]のいずれか一項に記載のアクリルフィルムを用いた偏光板。
[13] [1]〜[5]および[11]のいずれか一項に記載のアクリルフィルムを用いた光学補償フィルム。
[14] [1]〜[5]および[11]のいずれか一項に記載のアクリルフィルムを用いた反射防止フィルム。
[15] [1]〜[5]および[11]のいずれか一項に記載のアクリルフィルムを用いた液晶表示装置。
以下に記載する構成要件の説明は、本発明の代表的な実施態様に基づいてなされることがあるが、本発明はそのような実施態様に限定されるものではない。なお、本明細書において「〜」を用いて表される数値範囲は、「〜」の前後に記載される数値を下限値および上限値として含む範囲を意味する。
また、本明細書中において、特に特定しない場合は “アクリルフィルム”はメタクリル系フィルムおよびアクリル系フィルムを表す。一方、“(メタ)アクリレート”はアクリレートおよびメタクリレートを表し、“(メタ)アクリル”はアクリルおよびメタクリルを表す。
本発明のアクリル樹脂とは、主成分として、(メタ)アクリル酸または(メタ)アクリル酸の誘導体を重合して得られる樹脂およびその誘導体を含有する樹脂であり、本発明の効果を損なわない限り特に限定されずに公知の(メタ)アクリル酸系熱可塑性樹脂を用いることができる。前記(メタ)アクリル酸の誘導体としては、メタクリル酸エステルやアクリル酸エステルを挙げることができる。前記メタクリル酸エステルとしては、メタクリル酸シクロヘキシル、メタクリル酸t−ブチルシクロヘキシル、メタクリル酸メチル等をあげることができる。前記アクリル酸エステルとしては、アクリル酸メチル、アクリル酸エチル、アクリル酸ブチル、アクリル酸イソプロピル、アクリル酸2−エチルヘキシル等を挙げることができる。
その他の(メタ)アクリル酸の誘導体であるアクリル樹脂として、例えば、下記一般式(1)で表される構造のものを挙げることができる。
本発明のアクリル樹脂に共重合可能なアクリル樹脂以外の単量体としては、スチレン及びo−メチルスチレン,p−メチルスチレン,2,4−ジメチルスチレン,o−エチルスチレン,p−エチルスチレン,p−tert−ブチルスチレン等の核アルキル置換スチレン、α−メチルスチレン,α−メチル−p−メチルスチレン等のα−アルキル置換スチレン等の芳香族ビニル化合物類、アクリロニトリル、メタクリルニトリル等のシアン化ビニル類、N−フェニルマレイミド、N−シクロヘキシルマレイミド等のマレイミド類、ラクトン環単位、グルタル酸無水物単位、無水マレイン酸等の不飽和カルボン酸無水物類、マレイン酸等の不飽和酸類、グルタルイミド単位等が挙げられる。
ラクトン環構造が重合体の分子鎖中(重合体の主骨格中は主鎖中ともいう)に形成されることにより、共重合体であるアクリル樹脂に高い耐熱性が付与され、かつ、Tgも高くなるため好ましい。また、耐熱性向上およびフィルム製造時の泡やシルバーストリーク抑制の観点から、ラクトン環構造を導く環化縮合反応の反応率は十分に高いことが好ましい。
前記R11〜R13の炭素数は1〜10であることが好ましく、1〜5であることがより好ましい。
無水マレイン酸構造が重合体の分子鎖中(重合体の主骨格中)に形成されることにより、共重合体であるアクリル樹脂に高い耐熱性が付与され、かつ、Tgも高くなるため好ましい。
前記R21およびR22の炭素数は1〜10であることが好ましく、1〜5であることがより好ましい。
グルタル酸無水物構造が重合体の分子鎖中(重合体の主骨格中)に形成されることにより、共重合体であるアクリル樹脂に高い耐熱性が付与され、かつ、Tgも高くなるため好ましい。
また、前記アクリル系樹脂は、耐熱性を損なわない範囲で共重合可能なその他の単量体成分を共重合した単位を有していても良い。共重合可能なその他の単量体成分としては、具体的にはスチレン、α−メチルスチレン、o−メチルスチレン、p−メチルスチレン、o−エチルスチレン、p−エチルスチレンおよびp−t−ブチルスチレンなどの芳香族ビニル系単量体、アクリロニトリル、メタクリロニトリル、エタクリロニトリルなどのシアン化ビニル系単量体、アリルグリシジルエーテル、スチレン−p−グリシジルエーテル、p−グリシジルスチレン、無水イタコン酸、N−メチルマレイミド、N−エチルマレイミド、N−シクロヘキシルマレイミド、N−フェニルマレイミド、アクリルアミド、メタクリルアミド、N−メチルアクリルアミド、ブトキシメチルアクリルアミド、N−プロピルメタクリルアミド、アクリル酸アミノエチル、アクリル酸プロピルアミノエチル、メタクリル酸ジメチルアミノエチル、メタクリル酸エチルアミノプロピル、メタクリル酸フェニルアミノエチル、メタクリル酸シクロヘキシルアミノエチル、N−ビニルジエチルアミン、N−アセチルビニルアミン、アリルアミン、メタアリルアミン、N−メチルアリルアミン、p−アミノスチレン、2−イソプロペニル−オキサゾリン、2−ビニル−オキサゾリン、2−アクロイル−オキサゾリン、2−スチリル−オキサゾリン、アクリロニトリル等のニトリル系単量体、酢酸ビニル等のビニルエステル類、グルタルイミド単位等が挙げられる。
本発明のアクリルフィルムは少なくとも一種の添加剤を含むことを特徴とする。また、前記添加剤のフィルム面内における添加剤濃度分布が0.01%〜3%であることを特徴とする。
以下各添加剤を詳細に説明する。
本発明において、フィルム構成材料中に、安定剤の少なくとも一種を前記アクリル樹脂の加熱溶融前または加熱溶融時に添加することが好ましい。これらは、フィルム構成材料の酸化防止、分解して発生した酸の捕捉、光または熱によるラジカル種基因の分解反応を抑制または禁止する等、解明出来ていない分解反応を含めて、着色や分子量低下に代表される変質や材料の分解による揮発成分の生成を抑制するために有用である。その時、製膜するための溶融温度においても安定化剤自身が分解せずに機能することが求められる。これらの安定化剤は次に挙げられる効果に用いるがこれらに限定されるものではない。
本発明において、フィルム構成材料の熱溶融時における安定化のために用いる化合物として有用なヒンダードフェノール系安定剤は既知の化合物であり、例えば、米国特許第4,839,405号明細書の第12〜14欄に記載されているものなどの、2,6−ジアルキルフェノール誘導体化合物が含まれる。中でも、特に分子量500以上のフェノール系安定剤を添加することが好ましい態様である。好ましいフェノール系安定剤としては、ヒンダードフェノール系安定剤が挙げられる。これらの素材は、市販品として容易に入手可能であり、下記のメーカーから販売されている。チバ・スペシャルティ・ケミカルズ社から、Irganox 1076、Irganox 1010、Irganox 3113、Irganox 245、Irganox 1135、Irganox 1330、Irganox 259、Irganox 565、Irganox 1035、Irganox 1098、Irganox 1425WL、として入手することができる。また、旭電化工業株式会社から、アデカスタブ AO−50、アデカスタブ AO−60、アデカスタブ AO−20、アデカスタブ AO−70、アデカスタブ AO−80として入手できる。さらに、住友化学株式会社から、スミライザーBP−76、スミライザーBP−101、スミライザーGA−80、として入手できる。また、シプロ化成株式会社からシーノックス326M、シーノックス336B、としても入手することが可能である。
上記の亜リン酸系安定剤としては、特開2004−182979号公報の[0023]〜[0039]に記載の化合物をより好ましく用いることができる。亜リン酸エステル系安定剤の具体例としては、特開昭51−70316号公報、特開平10−306175号公報、特開昭57−78431号公報、特開昭54−157159号公報、特開昭55−13765号公報に記載の化合物を挙げることができる。さらに、その他の安定剤としては、発明協会公開技報(公技番号2001−1745、2001年3月15日発行、発明協会)17頁〜22頁に詳細に記載されている素材を好ましく用いることができる。
安定剤としてさらに使用されるチオエーテル系安定剤について記述する。本発明においてアクリル樹脂に添加することができるチオエーテル系安定剤も分子量500以上が好ましく、公知の任意のチオエーテル系安定剤を用いることができる。これらは、住友化学株式会社からスミライザーTPL、同TPM、同TPS、同TDPとして市販されている。旭電化工業株式会社から、アデカスタブAO−412Sとしても入手可能である。
上記スズ系安定剤としては、公知の任意のスズ系安定剤を用いることができる。好ましいスズ系安定剤の具体例としては、オクチル錫マレエートポリマー、モノステアリル錫トリス(イソオクチルチオグリコレート)、ジブチル錫ジラウレートが挙げられる。
アクリル樹脂は高温下では酸によっても分解が促進されるため、本発明のアクリルフィルムにおいては酸捕捉剤を含有することが好ましい。
なお酸捕捉剤は酸掃去剤、酸捕獲剤、酸キャッチャー等と称されることもあるが、本発明においてはこれらの呼称による差異なく用いることができる。
光安定剤としては、ヒンダードアミン光安定剤(HALS)化合物などが挙げられ、これは既知の化合物であり、例えば、米国特許第4,619,956号明細書の第5〜11欄および米国特許第4,839,405号明細書の第3〜5欄に記載されているように、2,2,6,6−テトラアルキルピペリジン化合物、またはそれらの酸付加塩もしくはそれらと金属化合物との錯体が含まれる。これらは、旭電化からアデカスタブLA−57、同LA−52、同LA−67、同LA−62、同LA−77として、またチバ・スペシャリティーケミカルズ社からTINUVIN 765、同144として市販されている。
本発明のアクリル樹脂には、1種または2種以上の紫外線吸収剤を含有させることが好ましい。前記紫外線吸収剤としては、特に制限はないが、液晶の劣化防止の観点から、波長380nm以下の紫外線の吸収能に優れ、かつ、液晶表示性の観点から、波長400nm以上の可視光の吸収が少ないものが好ましい。例えば、オキシベンゾフェノン系化合物、ベンゾトリアゾール系化合物、サリチル酸エステル系化合物、ベンゾフェノン系化合物、シアノアクリレート系化合物、ニッケル錯塩系化合物などが好ましい例として挙げられる。特に好ましい紫外線吸収剤は、ベンゾトリアゾール系化合物やベンゾフェノン系化合物である。中でも、ベンゾトリアゾール系化合物は、アクリル樹脂に対する不要な着色が少ないことからもっとも好ましい。これら好ましい紫外線吸収剤は、特開昭60−235852号、特開平3−199201号、同5−1907073号、同5−194789号、同5−271471号、同6−107854号、同6−118233号、同6−148430号、同7−11056号、同7−11055号、同7−11056号、同8−29619号、同8−239509号、特開2000−204173号の各公報に記載がある。前記紫外線吸収剤の添加量は、調製する溶融物(メルト)の0.01〜2質量%であることが好ましく、0.01〜1.5質量%であることがさらに好ましい。
紫外線吸収性モノマーから誘導されるポリマー中の紫外線吸収性モノマーの含有量が1〜70質量%であることが好ましく、より好ましくは、5〜60質量%である。
本発明のアクリルフィルムに可塑剤として知られる化合物を添加することは、機械的性質向上、柔軟性を付与、耐吸水性付与、水分透過率低減等のフィルムの改質観点において好ましい。また本発明で行う溶融流延法においては、用いる可塑剤の添加によりフィルム構成材料の溶融温度を低下させる目的、または同じ加熱温度においてアクリル樹脂よりも可塑剤を含むフィルム構成材料の粘度が低下出来る目的を含んでいる。
具体的には、リン酸シクロアルキルエステル、リン酸アリールエステルが挙げられる。これらの置換基は、同一でもあっても異なっていてもよく、さらに置換されていても良い。またアルキル基、シクロアルキル基、アリール基のミックスでも良く、また置換基同志が共有結合で結合していても良い。 またエチレンビス(ジメチルホスフェート)、ブチレンビス(ジエチルホスフェート)等のアルキレンビス(ジアルキルホスフェート)、エチレンビス(ジフェニルホスフェート)、プロピレンビス(ジナフチルホスフェート)等のアルキレンビス(ジアリールホスフェート)、フェニレンビス(ジブチルホスフェート)、ビフェニレンビス(ジオクチルホスフェート)等のアリーレンビス(ジアルキルホスフェート)、フェニレンビス(ジフェニルホスフェート)、ナフチレンビス(ジトルイルホスフェート)等のアリーレンビス(ジアリールホスフェート)等のリン酸エステルが挙げられる。これらの置換基は、同一でもあっても異なっていてもよく、さらに置換されていても良い。またアルキル基、シクロアルキル基、アリール基のミックスでも良く、また置換基同志が共有結合で結合していても良い。
本発明では、アクリル樹脂にマット剤(以下、微粒子ともいう)を混合してもよい。前記マット剤としては、無機化合物の微粒子や有機化合物の微粒子が挙げられ、いずれでもよい。本発明におけるアクリル樹脂に含まれる微粒子の平均一次粒子サイズは、ヘイズを低く抑えるという観点から5nm〜3μmであることが好ましく、5nm〜2.5μmであることがより好ましく、10nm〜2.0μmであることがさらに好ましい。ここで、微粒子の平均一次粒子サイズは、アクリル樹脂フィルムを透過型電子顕微鏡(倍率50万〜100万倍)で観察し、粒子100個の一次粒子サイズの平均値を求めることにより決定する。微粒子の添加量は、アクリル樹脂に対して0.005〜1.0質量%であることが好ましく、より好ましくは0.01〜0.8質量%であり、さらに好ましくは0.02〜0.4質量%である。
その他の添加剤として、赤外線吸収剤、レターデーション調整剤を添加してもよく、これらの種類は特に制限されない。その他の添加剤の添加量は0〜1000ppmであることが好ましく、 0.1〜5質量%であることが好ましく、0.2〜3質量%であることが特に好ましい。
本発明のアクリルフィルムは少なくとも一種の添加剤を含むことを特徴とする。また、前記添加剤のフィルム面内における添加剤濃度分布が0.01%〜3%であることを特徴とする。
本発明のアクリルフィルムは、従来技術と異なり、アクリル樹脂に添加する添加剤の濃度分布を与えてあり、この添加剤の濃度分布によってアクリル樹脂とキャストロールとの密着性または粘着性を弱まることでキャストロールへの全面としての粘着を抑制し、横ダンを解消したものである。すなわち、このようにフィルム面内に添加剤濃度に差を与えてムラをあえて生じさせることにより、フィルム局部ごとの物性(例えばフィルム塑性、粘性由来のクリープ性等)の差を生じさせることができる。その結果、アクリル樹脂とキャストロールとの全面密着性および/または前面粘着性を弱めることで、製膜後のアクリルフィルムのキャストロールからの剥離性を向上させ、横ダンを解消することができる。
前記添加剤濃度分布は0.01%〜3%であり、0.05%〜2.5%であることが好ましく、0.1%〜2.0%であることがより好ましい。フィルム面内の添加剤の濃度分布が0.01%以上であれば、十分なムラが生じるためフィルム物性が均一でなくなり、アクリルフィルムがキャストロールとの全面密着性が弱くなるため、製膜時の横ダンが生じしにくくなる。一方、添加剤の濃度分布が3%以下であれば、フィルムの物性のバラツキが大きくなりすぎず好ましい。特に、フィルム面内のレターデーション(Re)、厚み方向のレターデーション(Rth)などの光学特性に悪影響を与えることがない程度のフィルムの物性のバラツキであるため、このようなアクリルフィルムを液晶表示装置に用いた際に、画像ムラの発生を抑制することができ、好ましい。
(レターデーション)
本発明のアクリルフィルムの面内方向の複屈折(Re)は0.1nm〜10nmが好ましく、より好ましくは0.1nm〜8nm、さらに好ましくは0.2nm〜6nmである。Reの遅相軸はどこを向いていてもかまわないが、より好ましいのが幅方向を向いているものである。
測定されるフィルムが、1軸または2軸の屈折率楕円体で表されるものである場合には、以下の方法によりRthが算出される。
Rthは、前記Reを、面内の遅相軸(KOBRA 21ADH、またはWRにより判断される)を傾斜軸(回転軸)として(遅相軸がない場合には、フィルム面内の任意の方向を回転軸とする)のフィルム法線方向に対して法線方向から片側50度まで10度ステップで各々その傾斜した方向から波長λnmの光を入射させて全部で6点測定し、その測定されたレターデーション値と平均屈折率の仮定値および入力された膜厚値を基にKOBRA 21ADHまたはWRが算出する。
上記において、法線方向から面内の遅相軸を回転軸として、ある傾斜角度にレターデーションの値がゼロとなる方向をもつフィルムの場合には、その傾斜角度より大きい傾斜角度でのレターデーション値はその符号を負に変更した後、KOBRA 21ADH、またはWRが算出する。
なお、遅相軸を傾斜軸(回転軸)として(遅相軸がない場合には、フィルム面内の任意の方向を回転軸とする)、任意の傾斜した2方向からレターデーション値を測定し、その値と平均屈折率の仮定値、および入力された膜厚値を基に、以下の式(A)および式(B)よりRthを算出することもできる。
また、式(A)におけるnxは、面内における遅相軸方向の屈折率を表し、nyは面内においてnxに直交する方向の屈折率を表し、nzはnxおよびnyに直交する方向の屈折率を表す。
測定されるフィルムが、1軸や2軸の屈折率楕円体で表現できないもの、いわゆる光学軸(optic axis)がないフィルムの場合には、以下の方法により、Rthは算出される。
Rthは、前記Reを、面内の遅相軸(KOBRA 21ADH、またはWRにより判断される)を傾斜軸(回転軸)として、フィルム法線方向に対して−50度から+50度まで10度ステップで各々その傾斜した方向から波長λnmの光を入射させて11点測定し、その測定されたレターデーション値と平均屈折率の仮定値および入力された膜厚値を基にKOBRA 21ADHまたはWRが算出する。
本発明のアクリルフィルムのReの波長分散は0.001nm〜1.5nmであることが好ましく、より好ましくは0.0004nm〜1nm、さらに好ましくは0.007nm〜0.8nmである。
本発明のアクリルフィルムのRthの波長分散は0.1nm〜4nmであることが好ましく、より好ましくは0.2nm〜3nm、さらに好ましくは0.3nm〜2.5nmである。ここでいう波長分散とは630nmで測定したReおよびRthと、450nmで測定したReおよびRthの差の絶対値を指す。
本発明のアクリルフィルムにおける1μm〜10mmの異物は3個/m2以下であることが好ましく、2個/m2以下であることがより好ましく、1個/m2以下であることが特に好ましい。このようなアクリルフィルム中に存在する微小な異物が偏光板での像の歪の原因となる。本発明のアクリルフィルムはさらに偏光板に組み込んだ際の像の歪も解消でき、また、画像のにじみも解消できる。好ましい。
より詳しくは、異物が発生しなければ、異物の屈折率、波長分散が周囲の正常部と同程度となり、これが原因で液晶表示板に使用した時に像の歪みが発生することがないため好ましい。このような歪みの解消は、液晶表示装置の解像力が高くなり、必要性が高くなっている。
本発明のアクリルフィルムの製膜後(未延伸)の厚みは20μm〜85μmが好ましく、より好ましくは20μm〜65μm、さらに好ましくは30μm〜60μmである。本発明のアクリルフィルムは、フィルム面内に前記添加剤濃度分布を有しているため、厚みが20μm〜85μmの薄いアクリルフィルムを製膜しても、横ダンを抑制することができる。
厚みむらは長手方向、幅方向いずれも0%〜3%が好ましく、より好ましくは0%〜2%、さらに好ましくは0%〜1%である。
本発明のアクリルフィルムの製膜幅は1.5m〜4mであることが好ましく、1.7m〜3.5mであることがより好ましく、2.0m〜3mであることが特に好ましい。通常の製膜幅は1m以下であり、本発明のアクリルフィルムは、フィルム面内に前記添加剤濃度分布を有しているため、フィルム製膜幅が1.5m〜4mである広幅のアクリルフィルムを製膜しても、横ダンを抑制することができる。また、4m以下であれば十分なフィルムの生産性であり、また、製造設備の経済上も好ましい。
本発明のアクリルフィルムは以下のような方法で製造することができる。また、本発明の製造方法によれば、アクリルフィルムの横ダンを抑制することができ、該フィルムを偏光板に用いて液晶表示装置に組み込んだ際の画像のにじみを抑制することができる。
以下において、本発明のアクリルフィルムの製造方法を詳細に説明する。
本発明のアクリルフィルムは溶液製膜法を用いて製造しても、溶融製膜法を用いて製造しても良いが、溶融製膜法により製造されることが好ましい。溶融製膜法では、あらかじめ樹脂や添加剤を混合してペレット化した後、混練押出し機に投入し溶融して溶融樹脂(以下、メルトともいう)を得て、メルトをダイから押出し、これをキャスティングドラム上で冷却固化し製膜する。
本発明で好ましく使用される溶融製膜法では、溶液製膜法と異なり、製膜直前のダイから押出されたメルトを濾過に掛けることが一般的に好ましくないことが知られている。溶融製膜法では、メルト化したアクリル樹脂が濾過機内に滞留している間にも熱分解が進行してしまうため、濾過器内で熱分解物由来の異物が発生する。すなわち、濾過により却って異物が増加し易い傾向があり、濾過にかけることは好ましくない。したがって、1μm〜10mmの異物を3個/m2を超えてアクリルフィルムに発生させないようにするためには、フィルム製造時に異物の原因となる異物の核を根本的に発生させないような方法でアクリルフィルムを製造することが必要である。
前記アクリル樹脂と前記添加物とは、溶融製膜に先立ち混合してペレット(アクリル樹脂ペレットともいう)化するのが好ましい。
ペレットは、前記アクリル樹脂と前記添加物を乾燥して含水率を0.1%以下にした混合物を得て、その後前記混合物を押出機に導入して150℃〜300℃で溶融し、溶融した混合物をヌードル状に押出し、空気中あるいは水中で固化し裁断することで得られる。また、押出機による溶融後、溶融した前記混合物を水中に口金より直接押出ながらカットする、アンダーウオーターカット法等によりペレット化を行ってもかまわない。
前記押出機としては、単軸スクリュー押出機、非かみ合い型異方向回転二軸スクリュー押出機、かみ合い型異方向回転二軸スクリュー押出機、かみ合い型同方向回転二軸スクリュー押出機などを用いることができる。前記押出機の回転数は10rpm〜1000rpmが好ましく、より好ましくは20rpm〜700rpmである。前記押出機内における押出滞留時間は10秒以上10分以内が好ましく、より好ましくは20秒間〜5分以内である。
ペレットの大きさは10mm3〜1000mm2であることが好ましく、より好ましくは30mm3〜500mm3である。
本発明のアクリルフィルムの製造方法では、押出機のホッパー内に、前記アクリル樹脂ペレットに加えて、直径30μm〜1mmのアクリル樹脂の粉体を、前記ペレットに対して0.01質量%〜10質量%添加する。押出機内ペレットとアクリル樹脂粉体の添加により、ペレットとアクリル樹脂粉体のサイズが異なることに起因する、アクリル樹脂間に溶融速度の差が生じる。これにより、添加剤の混合度合にバラツキを与えることができ、本発明のアクリルフィルムの添加剤濃度分布を達成することができ、横ダンを抑制することができる。
溶融製膜に先立ちペレット中の水分を減少させることが好ましい。好ましい乾燥温度は40〜200℃であり、より好ましくは60〜150℃であり、さらに好ましくは80℃〜130℃である。乾燥後のペレット中の含水率は0.5質量%以下であることが好ましく、0.1質量%以下であることがさらに好ましい。乾燥は空気中で行っても良く、窒素中で行っても良く、真空中で行っても良い。
乾燥後のペレットは前記押出機の供給口を介してシリンダー内に供給され、混練および溶融される。シリンダー内は供給口側から順に、供給部、圧縮部、計量部とで構成される。押出機のスクリュー圧縮比は1.5〜4.5が好ましい。シリンダー内径に対するシリンダー長さの比(L/D)は20〜70が好ましい。シリンダー内径は30mm〜150mmが好ましい。さらに残存酸素による溶融樹脂の酸化を防止するため、押出機内を不活性(窒素等)気流中、あるいはベント付き押出し機を用い真空排気しながら実施するのも好ましい。
樹脂中の異物濾過のためブレーカープレート式の濾過やリーフ型ディスクフィルターを組み込んだ濾過装置を設けることが好ましい。
濾過はさらに精度高く異物濾過をするために、ギアポンプ通過後にいわゆるリーフ型ディスクフィルターを組み込んだ濾過装置を設けることが好ましい。濾過は、濾過部を1カ所設けて行うことができ、また複数カ所設けて行う多段濾過でもよい。フィルター濾材の濾過精度は高い方が好ましいが、濾材の耐圧や濾材の目詰まりによる濾圧上昇から、濾過精度は15μmm〜3μmmが好ましくさらに好ましくは10μmm〜3μmmである。特に最終的に異物濾過を行うリーフ型ディスクフィルター装置を使用する場合では品質の上で濾過精度の高い濾材を使用することが好ましく、耐圧、フィルターライフの適性を確保するために装填枚数にて調整することが可能である。濾材の種類は、高温高圧下で使用される点から鉄鋼材料を用いることが好ましく、鉄鋼材料の中でも特にステンレス鋼,スチールなどを用いることが好ましく、腐食の点から特にステンレス鋼を用いることが望ましい。濾材の構成としては、線材を編んだものの他に、例えば金属長繊維あるいは金属粉末を焼結し形成する焼結濾材が使用でき、濾過精度,フィルターライフの点から焼結濾材が好ましい。
吐出量の変動を減少させ厚み精度を向上させるために、押出機出機とダイの間にギアポンプを設けることが好ましい。これによりダイ内の樹脂圧力変動巾を±1%以内にできる。
ギアポンプによる定量供給性能を向上させるために、スクリューの回転数を変化させて、ギアポンプ前の圧力を一定に制御する方法も用いることができる。
ダイ端部でのメルトの滞留を抑制するために、スタチックミキサーを押出し機からダイの間のメルト配管に設置することが好ましい。
前記スタチックミキサーは押出し機からダイの間のメルト配管のどこに設置しても良いが、溶融濾過器とダイの間に設置するのがより好ましく、さらに好ましくはダイの入口直前である。
前記スタチックミキサーは4枚〜50枚のエレメントを有することが好ましく、より好ましくは5枚〜40枚、さらに好ましくは6枚〜30枚である。配管の中央部に比べ配管壁近傍はメルトの流速が遅く滞留時間が長くなり熱分解物由来の異物が発生しやすい。これに対しスタチックミキサーを用いることで配管内のメルトの撹拌が促され、配管壁のメルトの滞留が抑制されるためである。
前記スタチックミキサーは、長方形の板を30°から360°、より好ましくは60°から240°、さらに好ましくは80°から200°ねじったものを、メルト配管に沿って前記枚数の範囲で装着させることが好ましい。このように構成されたスタチックミキサーをメルトが通ることで、メルトは回転させられ配管内での撹拌が促される。このようなスタチックミキサーの1枚あたりの長さは特に限定されないが、メルト配管の直径の0.5倍〜10倍が好ましく、より好ましくは0.8倍〜6倍、さらに好ましくは1.0倍〜3倍である。
前記スタチックミキサーの材質は特に限定されないが、ステンレススチールを用いるのが好ましく、この上にハードクロムやタングステンカーバイドなどのメッキを施すことがより好ましい。
前記の如く構成された押出機によって溶融され、必要に応じ濾過機、ギアポンプを経由して溶融樹脂がダイに連続的に送られる。ダイはTダイ、フィッシュテールダイ、ハンガーコートダイの何れのタイプでも構わない。
ダイは5〜50mm間隔で厚み調整可能であることが好ましい。また下流のフィルム厚み、厚み偏差を計算し、その結果をダイの厚み調整にフィードバックさせる自動厚み調整ダイも有効である。
単層製膜装置以外にも、多層製膜装置を用いて製造も可能である。
このようにして、樹脂が供給口から押出機に入ってからダイから出るまでの滞留時間は3分〜40分が好ましく、さらに好ましくは4分〜30分である。
ダイよりシート上に押し出された溶融樹脂(メルト)をキャストロール(以下、チルロールともいう)上で冷却固化し、フィルムを得る。
この時、ダイとキャストロールの間を遮蔽し風の影響を抑制することが好ましい。
メルトがキャストロールに接触する際、静電印加法、エアナイフ法、エアーチャンバー法、バキュームノズル法、タッチロール法等を用いてもよく、用いなくてもよい。このような中でもタッチロール法が均一に密着させることができる観点から好ましい。このような密着向上法はメルトの全面に実施してもよく、一部に実施してもよい。
本発明においてチルロールとは、ダイから押し出されたメルトが最初に接触するキャストロールのことをいい、タッチロールとは、タッチロールはキャストロール(チルロール)と対向して設置され、タッチロールとキャストロールの間にダイから押出したメルトを通し、成型しながら冷却固化させるもののことをいう。本発明の製造方法では、タッチロール法を用いることが、アクリルフィルム両面に均一に微圧をかけて、アクリルフィルムとキャストロールへの片面の密着力を弱める観点から好ましい。なお、以下においてキャストロールという場合は、前記チルロールと、複数キャストロールが存在する場合の2番目以降のキャストロールとを含む。
本発明において、タッチ圧とは、タッチロールを押し付けている力をフィルムとタッチロールの接触面積で割った値である。タッチ圧は0.1MPa〜10MPaであることが好ましく、0.3MPa〜7MPaであることがより好ましい。タッチ圧が0.1MPa以上であれば、タッチロールの有する微圧着により、メルトとキャストロールへの片面の密着力を弱める効果が十分発揮されるため好ましく、タッチ圧が10MPa以下であれば、タッチ圧が強すぎることに起因するアクリルフィルムの横ダンが抑制できるため好ましい。なお、従来一般的に用いられているタッチロールの面圧は30MPa程度である。
このような弱いタッチ圧を実現するには、タッチロールは通常の剛性の高いものではなく、弾性を有するものが好ましい。このためには、ロールの外筒厚みを通常のロールよりも薄くすることが必要であり、外筒の肉厚Zは、0.05mm〜7.0mmが好ましく、より好ましくは0.2mm〜5.0mm、さらに好ましくは0.3mm〜3.5mmである。
前記タッチロールおよびキャストロールの材質は金属であることが好ましく、より好ましくはステンレスである。また、タッチロールおよびキャストロールの表面に金属メッキを行ったタッチロールおよびキャストロールも好ましい。タッチロールおよびキャストロールの表面が金属であればタッチロールおよびキャストロールのRaを100nm以下にすることが容易となるため好ましい。
このように、多連式キャストロールの温度分布の設定により、製膜するアクリルフィルムを徐冷することにより、パッキング密度の向上を促進することができる。そのため、得られるアクリルフィルムの湿度膨張係数、熱膨張係数およびRaを本発明の範囲に制御しやすくすることができる。また、得られるアクリルフィルムの両面の物性をより均一化することや、アクリルフィルム内の残存ひずみを解消しやすくすることもできるため、本発明の偏光板の保護フィルムとして前記アクリルフィルムを使用した場合に、湿度および熱に対する寸法安定性を向上させることができる。
ダイから押出されたメルトをキャストロール上で固化する際、用いるタッチロールの温度は、アクリル樹脂のTgを基準としてTg−30℃〜Tg+10℃であることが好ましく、Tg−20℃〜Tg+5℃であることがより好ましく、Tg−10℃〜Tgであることが特に好ましい。例えば、本発明で用いることが好ましいアクリル樹脂の場合は、タッチロールの温度は60℃〜160℃とすることが好ましく、70℃〜150℃とすることがより好ましく、80℃〜140℃とすることが特に好ましいが、これらは本発明を限定するものではない。
キャストロールの温度は、アクリル樹脂のTgを基準としてTg−100℃〜Tg+15℃であることが好ましく、Tg−80℃〜Tg+5℃であることがより好ましく、Tg−60℃〜Tgであることが特に好ましい。例えば、本発明で用いることが好ましいアクリル樹脂の場合は、キャストロールの温度は40℃〜160℃とすることが好ましく、50℃〜150℃とすることがより好ましく、80℃〜140℃ととすることが特に好ましいが、これらは本発明を限定するものではない。
このような温度制御はこれらのロール内部に温調した液体、気体を通すことで達成できる。このように内部に温調機構を有するものがより好ましい。前記温調機構としては、例えば、タッチロールを金属シャフトの上に設置してその間に熱媒(流体)を通した態様が挙げられ、外筒と金属シャフトの上に間に弾性体層を設けて外筒の間に熱媒(流体)を満たした態様が挙げられる。これらの態様において前記熱媒の温度を調整することで、タッチロールなどの温度を調整できる。
ダイから押出されたメルトをキャストロール上で固化する際、前記範囲の温度のタッチロールを用い、前記範囲のタッチ圧で挟み込んで製膜することにより、タッチロールとキャストロール(チルロール)の間でメルトとキャストロール(チルロール)への片面の密着力が弱まり、横ダンが発生し難くなる。
本発明のアクリルフィルムの製造方法では、製膜速度(ライン速度)が10m/分〜70m/分にすることが好ましく、より好ましくは15m/分〜60m/分、さらに好ましくは20m/分〜50m/分である。製膜速度を10m/分〜70m/分にすることで、スクリューの回転数が高まり、ペレットと粉体との攪拌時間が異なり、ペレット間の混練に不均一を与え、添加剤の濃度分布のバラツキが本発明の範囲に満たすことができる。製膜速度が10m/分以上であれば混練不均一性を十分発生させることができ好ましく、70m/分以下であればペレットが充分溶融されて融解状態が良好となる。
また製膜速度を上記のようにすることによりダイ内の滞留時間を抑制でき、異物の数を低減できる。本発明の製膜速度を未満ではダイ内の滞留時間が増加し好ましくなく、製膜速度が本発明の範囲を超えると、ダイ内でのメルトの流れが乱れフィルム内の均一性が低下し偏光板にした時に像の歪が発生し好ましくない。
通常のアクリルの溶融製膜は10m/未満の速度で行われるが、上記のような高速で製膜することでさらに、ダイリップでのズリの効果をより強く発現することもできる。製膜速度が10m/分〜70m/分であればこのようなズリの効果を高め、ReおよびRthを調整することができ好ましい。
このようにして延製膜した後、両端をトリミングすることも好ましい。トリミングで切り落とした部分は破砕し、再度原料として使用してもよい。
また片端あるいは両端に厚みだし加工(ナーリング処理)を行うことも好ましい。厚みだし加工による凹凸の高さは1μm〜50μmが好ましく、より好ましくは3μm〜20μmである。厚みだし加工は両面に凸になるようにしても、片面に凸になるようにしても構わない。厚みだし加工の幅は1mm〜50mmが好ましく、より好ましくは3mm〜30mmである。押出し加工は室温〜300℃で実施できる。
この後、キャスティングドラムから剥ぎ取り、ニップロールを経た後巻き取る。巻き取り速度は10m/分〜100m/分が好ましく、より好ましくは15m/分〜80m/分、さらに好ましくは20m/分〜70m/分である。
好ましい巻き取り張力は2kg/m幅〜50kg/幅、より好ましくは5kg/m幅〜30kg/幅である。
巻き取る前に片面或いは両面にラミフィルムを付けることも好ましい。ラミフィルムの厚みは5μm〜100μmが好ましく、10μm〜50μmがより好ましい。材質はポリエチレン、ポリエステル、ポリプロピレン等、特に限定されない。
溶融製膜した熱可塑性フィルムは縦延伸(以下、MD延伸ともいう)、横延伸(以下、MD延伸ともいう)を行うのが好ましく、さらに緩和収縮処理を組み合わせても良い。
延伸倍率={(延伸後の長さ)−(延伸前の長さ)}/(延伸前の長さ)
縦延伸は2対のニップロールを設置し、この間を加熱しながら出口側のニップロールの周速を入口側のニップロールの周速より速くすることで達成できる。この際、ニップロール間の間隔(L)と延伸前のフィルム幅(W)を変えることで厚み方向のレターデーションの発現性を変えることができる。L/Wが2を超え50以下(長スパン延伸)ではRthを小さくでき、L/Wが0.01〜0.3(短スパン延伸)ではRthを大きくできる。本発明では長スパン延伸、短スパン延伸、これらの間の領域(中間延伸=L/Wが0.3を超え2以下)どれを使用しても良いが、配向角を小さくできる長スパン延伸、短スパン延伸が好ましい。さらに高Rthを狙う場合は短スパン延伸、低Rthを狙う場合は長スパン延伸と区別して使用することがより好ましい。
これらの縦延伸の好ましい延伸温度は(Tg−10℃)〜(Tg+50)℃であり、より好ましくは(Tg−5℃)〜(Tg+40)℃であり、さらに好ましくは(Tg)〜(Tg+30)℃である。縦延伸の好ましい延伸倍率は前記延伸倍率の好ましい範囲と同様である。
横延伸はテンターを用い実施できる。即ちフィルムの幅方向の両端部をクリップで把持し、横方向に拡幅することで延伸する。この時、テンター内に所望の温度の風を送ることで延伸温度を制御できる。延伸温度は、Tg−10℃〜Tg+60℃が好ましく、Tg−5℃〜Tg+45℃がより好ましく、Tg〜Tg+30℃がさらに好ましい。縦延伸の好ましい延伸倍率は前記延伸倍率の好ましい範囲と同様である。
このようなMD延伸やTD延伸の前に予熱、延伸の後に後熱処理を行うことで延伸後のRe,Rth分布を小さくし、ボーイングに伴う配向角のばらつきを小さくできる。予熱、後熱処理はどちらか一方であっても良いが、両方行うのがより好ましい。これらの予熱、後熱処理はクリップで把持して行うのが好ましく、即ち延伸と連続して行うのが好ましい。
後熱処理は延伸温度より1℃〜50℃、より好ましく2℃〜40℃、さらに好ましくは3℃〜30℃低くすることが好ましい。さらに好ましくは延伸温度以下でかつTg以下にするのが好ましい。好ましい予熱時間は1秒〜10分であり、より好ましくは5秒〜4分、さらに好ましくは10秒〜2分である。熱固定の際、テンターの幅はほぼ一定に保つことが好ましい。ここで「ほぼ」とは延伸終了後のテンター幅の0%(延伸後のテンター幅と同じ幅)〜−10%(延伸後のテンター幅より10%縮める=縮幅)を指す。延伸幅以上に拡幅すると、フィルム中に残留歪が発生しやすく好ましくない。
予熱は延伸温度±50℃、より好ましくは延伸温度±35℃、さらに好ましくは延伸温度±20℃である。後熱処理後のボーイングが進行方向に凸の場合は延伸温度より下げるのが好ましく、進行方向に凹の場合は延伸温度より高くするのが好ましい。好ましい予熱時間は1秒〜10分であり、より好ましくは5秒〜4分、さらに好ましくは10秒〜2分である。予熱の際、テンターの幅はほぼ一定に保つことが好ましい。ここで「ほぼ」とは未延伸フィルムの幅の±10%を指す。
このように熱固定温度<延伸温度<予熱温度であることがより好ましい。
本発明のアクリルフィルムの製造方法では、前記延伸温度、前記延伸倍率、前記延伸速度条件下でMD方向延伸工程およびTD方向延伸工程による二軸延伸を行うことが好ましい。また、本発明のアクリルフィルムの製造方法における二軸延伸は、同時二軸延伸であっても、逐次二軸延伸であってもよい。
本発明のアクリルフィルムの製造方法では、MD方向の延伸倍率/TD方向の延伸倍率の比が0.95〜1.15であることが好ましく、0.97〜1.10であることがより好ましく、0.99〜1.02であることが特に好ましい。MD方向の延伸倍率/TD方向の延伸倍率の比が0.95〜で1.15であれば、Re、Rthが本発明の範囲内に制御できるため好ましい。
このようなMD延伸やTD延伸によりRe、Rthの幅方向、長手方向のばらつき、配向角のMD(長手方向)あるいはTD(幅方向)からのずれを小さくできる。
前記縦延伸や横延伸の後に緩和処理を行うのが好ましい。緩和処理はTg±40℃、より好ましくはTg±30℃、さらに好ましくはTg±20℃で、低張力(0.1〜10kg/m、より好ましくは0.2〜5kg/m、さらに好ましくは0.3〜3kg/m)で0.1分〜30分、より好ましくは0.3分〜15分、さらに好ましくは0.5分〜8分熱処理するのが好ましい。これにより延伸により発現した複屈折(レターデーション)を変化させずに、熱収縮を抑制できる。
前記アクリルフィルムに、発明協会公開技報(公技番号2001−1745、2001年3月15日発行、発明協会)にて32頁〜45頁に詳細に記載されている機能性層を組み合わせることも好ましい。中でも好ましいのが、偏光層の付与により得られる本発明の偏光板、光学異方性層の付与により得られる光学補償フィルム、反射防止層の付与により得られる反射防止フィルムである。また、これらの加工したフィルムを本発明の液晶表示装置に用いることも好ましい。
本発明のアクリルフィルムに、少なくとも偏光子(以下、偏光膜ともいう)を積層することで、本発明の偏光板を得ることができる。以下において、本発明の偏光板を説明する。
本発明の偏光板のアクリルフィルムには、本発明のアクリルフィルムが用いられる。また、前記アクリルフィルムには表面処理をしておくこともできる。表面処理方法としては、例えば、コロナ放電処理、表面易接着層の塗布処理、表面ケン化処理、プラズマ処理、グロー放電処理、火炎処理、オゾン処理、UVオゾン処理、紫外線処理等の方法が挙げられる。
本発明の偏光板のセルロースアシレートフィルムには、公知の偏光板用のセルロースアシレートフィルムが用いられる。例えば、公知のトリアセチルセルロース(TAC)フィルム(例えば、富士フィルム(株)製フジタックT−60)などを好ましく用いることができる。また、前記ルロースアシレートフィルムには表面処理をしておくこともできる。表面処理方法としては、例えば、けん化処理などが挙げられる。
前記偏光子としては、例えば、ポリビニルアルコールフィルムを沃素溶液中に浸漬して延伸したもの等を用いることができる。
本発明の偏光板は、最外層の少なくとも一方として粘着剤層を有していても良い(このような偏光板を粘着型偏光板と称することがある)。特に好ましい形態として、前記アクリルフィルムの偏光子が接着されていない側に、他の光学フィルムや液晶セル等の他部材と接着するための粘着剤層を設けることができる。
本発明の偏光板の製造方法を説明する。
本発明の偏光板は、接着剤を用いて前記偏光子の少なくとも片面に本発明のアクリルフィルムの片面(表面処理をしてある場合は表面処理面)を貼り合わせることで製造できる。また、セルロースアシレートフィルム、偏光子および本発明のアクリルフィルムの順に貼り合わせる場合は、本発明の偏光板は偏光子の両面に接着剤を用いて偏光子とその他のフィルムを張り合わせることで製造できる。本発明の偏光板の製造方法においては、本発明のアクリルフィルムが偏光子と直接貼合されていることが好ましい。
本発明のアクリルフィルムに光学異方性層を付与することで、本発明の光学補償フィルムを得ることができる。以下において、本発明の光学補償フィルムを説明する。
光学異方性層は、液晶表示装置の黒表示における液晶セル中の液晶性化合物を補償するように設計することが好ましい。黒表示における液晶セル中の液晶性化合物の配向状態は、液晶表示装置のモードにより異なる。この液晶セル中の液晶性化合物の配向状態に関しては、IDW’00、FMC7−2のP411〜414等に記載されている。
光学異方性層は、支持体上に直接液晶性化合物から形成するか、もしくは配向膜を介して液晶性化合物から形成する。配向膜は、10μm以下の膜厚を有することが好ましい。
光学異方性層に用いる液晶性化合物には、棒状液晶性化合物およびディスコティック液晶性化合物が含まれる。棒状液晶性化合物およびディスコティック液晶性化合物は、高分子液晶でも低分子液晶でもよく、さらに、低分子液晶が架橋され液晶性を示さなくなったものも含まれる。光学異方性層は、液晶性化合物および必要に応じて重合性開始剤や任意の成分を含む塗布液を、配向膜の上に塗布することで形成できる。本発明の配向膜として好ましい例は、特開平8−338913号公報に記載されている。
棒状液晶性化合物としては、アゾメチン類、アゾキシ類、シアノビフェニル類、シアノフェニルエステル類、安息香酸エステル類、シクロヘキサンカルボン酸フェニルエステル類、シアノフェニルシクロヘキサン類、シアノ置換フェニルピリミジン類、アルコキシ置換フェニルピリミジン類、フェニルジオキサン類、トラン類およびアルケニルシクロヘキシルベンゾニトリル類が好ましく用いられる。
なお、棒状液晶性化合物には、金属錯体も含まれる。また、棒状液晶性化合物を繰り返し単位中に含む液晶ポリマーも、棒状液晶性化合物として用いることができる。すなわち、棒状液晶性化合物は、(液晶)ポリマーと結合していてもよい。
棒状液晶性化合物については、例えば、季刊化学総説第22巻液晶の化学(1994)日本化学会編の第4章、第7章および第11章、および液晶デバイスハンドブック日本学術振興会第142委員会編の第3章に記載のものを採用できる。
棒状液晶性化合物の複屈折率は、0.001〜0.7の範囲にあることが好ましい。
ディスコティック液晶性化合物には、C.Destradeらの研究報告(Mol.Cryst.71巻、111頁(1981年))に記載されているベンゼン誘導体、C.Destradeらの研究報告(Mol.Cryst.122巻、141頁(1985年)、Physics lett,A,78巻、82頁(1990))に記載されているトルキセン誘導体、B.Kohneらの研究報告(Angew.Chem.96巻、70頁(1984年))に記載されたシクロヘキサン誘導体およびJ.M.Lehnらの研究報告(J.C.S.,Chem.Commun.,1794頁(1985年))、J.Zhangらの研究報告(J.Am.Chem.Soc.116巻、2655頁(1994年))に記載されているアザクラウン系やフェニルアセチレン系マクロサイクルが含まれる。
D(−LQ)r
(一般式(5)中、Dは円盤状コアであり、Lは二価の連結基であり、Qは重合性基であり、rは4〜12の整数である。)
L1:−AL−CO−O−AL−、
L2:−AL−CO−O−AL−O−、
L3:−AL−CO−O−AL−O−AL−、
L4:−AL−CO−O−AL−O−CO−、
L5:−CO−AR−O−AL−、
L6:−CO−AR−O−AL−O−、
L7:−CO−AR−O−AL−O−CO−、
L8:−CO−NH−AL−、
L9:−NH−AL−O−、
L10:−NH−AL−O−CO−、
L12:−O−AL−O−、
L13:−O−AL−O−CO−、
L14:−O−AL−O−CO−NH−AL−、
L15:−O−AL−S−AL−、
L16:−O−CO−AL−AR−O−AL−O−CO−、
L17:−O−CO−AR−O−AL−CO−、
L18:−O−CO−AR−O−AL−O−CO−、
L19:−O−CO−AR−O−AL−O−AL−O−CO−、
L20:−O−CO−AR−O−AL−O−AL−O−AL−O−CO−、
L21:−S−AL−、
L22:−S−AL−O−、
L23:−S−AL−O−CO−、
L24:−S−AL−S−AL−、
L25:−S−AR−AL−。
ディスコティック液晶性化合物と共に使用する添加剤の例としては、可塑剤、界面活性剤、重合性モノマーおよびポリマーなどを挙げることができる。長軸の配向方向の変化の程度も、上記と同様に、液晶性分子と添加剤との選択により調整できる。
ディスコティック液晶性化合物のディスコティックネマティック液晶相−固相転移温度は、70〜300℃が好ましく、70〜170℃がさらに好ましい。
配向させた液晶性分子を、配向状態を維持して固定することができる。固定化は、重合反応により実施することが好ましい。重合反応には、熱重合開始剤を用いる熱重合反応と光重合開始剤を用いる光重合反応とが含まれる。光重合反応が好ましい。
光重合開始剤の例には、α−カルボニル化合物(米国特許2367661号、同2367670号の各公報記載)、アシロインエーテル(米国特許2448828号公報記載)、α−炭化水素置換芳香族アシロイン化合物(米国特許2722512号公報記載)、多核キノン化合物(米国特許3046127号、同2951758号の各公報記載)、トリアリールイミダゾールダイマーとp−アミノフェニルケトンとの組み合わせ(米国特許3549367号公報記載)、アクリジンおよびフェナジン化合物(特開昭60−105667号、米国特許4239850号の各公報記載)およびオキサジアゾール化合物(米国特許4212970号公報記載)が含まれる。
液晶性分子の重合のための光照射は、紫外線を用いることが好ましい。
照射エネルギーは、20mJ/cm2〜50J/cm2の範囲にあることが好ましく、20mJ/cm2〜5000mJ/cm2の範囲にあることがより好ましく、100mJ/cm2〜800mJ/cm2の範囲にあることがさらに好ましい。また、光重合反応を促進するため、加熱条件下で光照射を実施してもよい。
保護層を、光学異方性層の上に設けてもよい。
フッ素系化合物としては、従来公知の化合物が挙げられるが、具体的には、例えば特開2001−330725号公報明細書中の段落番号[0028]〜[0056]に記載のフッ素系化合物等が挙げられる。
塗布液の調製に使用する溶媒としては、有機溶媒が好ましく用いられる。有機溶媒の例には、アミド(例、N,N−ジメチルホルムアミド)、スルホキシド(例、ジメチルスルホキシド)、ヘテロ環化合物(例、ピリジン)、炭化水素(例、ベンゼン、ヘキサン)、アルキルハライド(例、クロロホルム、ジクロロメタン、テトラクロロエタン)、エステル(例、酢酸メチル、酢酸ブチル)、ケトン(例、アセトン、メチルエチルケトン)、エーテル(例、テトラヒドロフラン、1,2−ジメトキシエタン)が含まれる。アルキルハライドおよびケトンが好ましい。2種類以上の有機溶媒を併用してもよい。
均一性の高い光学補償フィルムを作製する場合には、前記塗布液の表面張力が25mN/m以下であることが好ましく、22mN/m以下であることがさらに好ましい。
塗布液の塗布は、公知の方法(例、押し出しコーティング法、ダイレクトグラビアコーティング法、リバースグラビアコーティング法、ダイコーティング法)により実施できる。
長尺フィルムをラビング処理する場合は、フィルムを搬送装置により一定張力の状態で1〜100m/minの速度で搬送することが好ましい。ラビングロールは、任意のラビング角度設定のためフィルム進行方向に対し水平方向に回転自在とされることが好ましい。0〜60度の範囲で適切なラビング角度を選択することが好ましい。液晶表示装置に使用する場合は、40〜50度が好ましい。45度が特に好ましい。
本発明のアクリルフィルムの上に反射防止層を付与することで、本発明の反射防止フィルムが得られる。反射防止膜は、一般に、防汚性層でもある低屈折率層と、および低屈折率層より高い屈折率を有する少なくとも一層の層(本明細書中における、高屈折率層、および中屈折率層)とを(透明)支持体上に設けて成る。
一方、生産性が高い反射防止膜として、無機粒子をマトリックスに分散されてなる薄膜を積層塗布してなる反射防止膜が各種提案されている。
上述したような塗布による反射防止フィルムに最上層表面が微細な凹凸の形状を有する防眩性を付与した反射防止層から成る反射防止フィルムも挙げられる。
本発明のアクリルフィルムは前記いずれの方式にも適用できるが、特に好ましいのが塗布による方式(塗布型)である。
(透明)支持体上に少なくとも中屈折率層、高屈折率層、低屈折率層(最外層)の順序の層構成から成る反射防止膜は、以下の関係を満足する屈折率を有する様に設計される。
高屈折率層の屈折率>中屈折率層の屈折率>透明支持体の屈折率>低屈折率層の屈折率
また、透明支持体と中屈折率層との間に、ハードコート層を設けてもよい。さらには、中屈折率ハードコート層、高屈折率層および低屈折率層からなってもよい。
例えば、特開平8−122504号公報、同8−110401号公報、同10−300902号公報、特開2002−243906号公報、特開2000−111706号公報等が挙げられる。
反射防止膜の高い屈折率を有する層は、平均粒子サイズ100nm以下の高屈折率の無機化合物超微粒子およびマトリックスバインダーを少なくとも含有する硬化性膜から成る。
高屈折率の無機化合物微粒子としては、屈折率1.65以上の無機化合物が挙げられ、好ましくは屈折率1.9以上のものが挙げられる。例えば、Ti、Zn、Sb、Sn、Zr、Ce、Ta、La、In等の酸化物、これらの金属原子を含む複合酸化物等が挙げられる。
このような超微粒子とするには、粒子表面が表面処理剤で処理されること(例えば、シランカップリング剤等:特開平11−295503号公報、同11−153703号公報、特開2000−9908号公報、アニオン性化合物或は有機金属カップリング剤:特開2001−310432号公報等)、高屈折率粒子をコアとしたコアシェル構造とすること(特開2001−166104等)、特定の分散剤併用(例、特開平11−153703号公報、特許番号US6210858B1、特開2002−2776069号公報等)等挙げられる。
マトリックスを形成する材料としては、従来公知の熱可塑性樹脂、硬化性樹脂皮膜等が挙げられる。
さらに、ラジカル重合性および/またはカチオン重合性の重合性基を少なくとも2個以上含有の多官能性化合物含有組成物、加水分解性基を含有の有機金属化合物およびその部分縮合体組成物から選ばれる少なくとも1種の組成物が好ましい。例えば、特開2000−47004号公報、同2001−315242号公報、同2001−31871号公報、同2001−296401号公報等に記載の化合物が挙げられる。
また、金属アルコキドの加水分解縮合物から得られるコロイド状金属酸化物と金属アルコキシド組成物から得られる硬化性膜も好ましい。例えば、特開2001−293818号公報等に記載されている。
高屈折率層の屈折率は、−般に1.70〜2.20である。高屈折率層の厚さは、5nm〜10μmであることが好ましく、10nm〜1μmであることがさらに好ましい。
中屈折率層の屈折率は、低屈折率層の屈折率と高屈折率層の屈折率との間の値となるように調整する。中屈折率層の屈折率は、1.50〜1.70であることが好ましい。
低屈折率層は、高屈折率層の上に順次積層して成る。低屈折率層の屈折率は1.20〜1.55である。好ましくは1.30〜1.50である。
耐擦傷性、防汚性を有する最外層として構築することが好ましい。耐擦傷性を大きく向上させる手段として表面への滑り性付与が有効で、従来公知のシリコーンの導入、フッ素の導入等から成る薄膜層の手段を適用できる。
含フッ素化合物の屈折率は1.35〜1.50であることが好ましい。より好ましくは1.36〜1.47である。また、含フッ素化合物はフッ素原子を35〜80質量%の範囲で含む架橋性若しくは重合性の官能基を含む化合物が好ましい。
例えば、特開平9−222503号公報明細書段落番号[0018]〜[0026]、同11−38202号公報明細書段落番号[0019]〜[0030]、特開2001−40284号公報明細書段落番号[0027]〜[0028]、特開2000−284102号公報等に記載の化合物が挙げられる。
シリコーン化合物としてはポリシロキサン構造を有する化合物であり、高分子鎖中に硬化性官能基あるいは重合性官能基を含有して、膜中で橋かけ構造を有するものが好ましい。例えば、反応性シリコーン(例、サイラプレーン(チッソ(株)製等)、両末端にシラノール基含有のポリシロキサン(特開平11−258403号公報等)等が挙げられる。
また、シランカップリング剤等の有機金属化合物と特定のフッ素含有炭化水素基含有のシランカップリング剤とを触媒共存下に縮合反応で硬化するゾルゲル硬化膜も好ましい。
低屈折率層が最外層の下層に位置する場合、低屈折率層は気相法(真空蒸着法、スパッタリング法、イオンプレーティング法、プラズマCVD法等)により形成されてもよい。安価に製造できる点で、塗布法が好ましい。
低屈折率層の膜厚は、30〜200nmであることが好ましく、50〜150nmであることがさらに好ましく、60〜120nmであることが最も好ましい。
ハードコート層は、反射防止フィルムに物理強度を付与するために、透明支持体の表面に設ける。特に、透明支持体と前記高屈折率層の間に設けることが好ましい。
ハードコート層は、光および/または熱の硬化性化合物の架橋反応、または、重合反応により形成されることが好ましい。
前記硬化性官能基としては、光重合性官能基が好ましく、また、加水分解性官能基含有の有機金属化合物は有機アルコキシシリル化合物が好ましい。
これらの化合物の具体例としては、高屈折率層で例示したと同様のものが挙げられる。
ハードコート層の具体的な構成組成物としては、例えば、特開2002−144913号公報、同2000−9908号公報、国際公開第00/46617号パンフレット等記載のものが挙げられる。
高屈折率層はハードコート層を兼ねることができる。このような場合、高屈折率層で記載した手法を用いて微粒子を微細に分散してハードコート層に含有させて形成することが好ましい。
ハードコート層の膜厚は用途により適切に設計することができる。ハードコート層の膜厚は、0.2〜10μmであることが好ましく、より好ましくは0.5〜7μmである。
ハードコート層の強度は、JIS K5400に従う鉛筆硬度試験で、H以上であることが好ましく、2H以上であることがさらに好ましく、3H以上であることが最も好ましい。また、JIS K5400に従うテーバー試験で、試験前後の試験片の摩耗量が少ないほど好ましい。
前方散乱層は、液晶表示装置に適用した場合の、上下左右方向に視角を傾斜させたときの視野角改良効果を付与するために設ける。前記ハードコート層中に屈折率の異なる微粒子を分散することで、ハードコート機能と兼ねることもできる。
例えば、前方散乱係数を特定化した特開平11−38208号公報、透明樹脂と微粒子の相対屈折率を特定範囲とした特開2000−199809号公報、ヘイズ値を40%以上と規定した特開2002−107512号公報等が挙げられる。
前記の層以外に、プライマー層、帯電防止層、下塗り層や保護層等を設けてもよい。
反射防止フィルムの各層は、ディップコート法、エアーナイフコート法、カーテンコート法、ローラーコート法、ワイヤーバーコート法、グラビアコート、マイクログラビア法やエクストルージョンコート法(米国特許2681294号明細書)により、塗布により形成することができる。
本発明の光学補償フィルムおよび偏光板は、種々のモードの液晶表示装置に用いることができ、本発明の液晶表示装置を得られる。以下、本発明の液晶表示装置について、各液晶モードにおける光学異方性層の好ましい形態とあわせて説明する。
本発明のアクリルフィルムは、IPSモードの液晶セルを有するIPS型液晶表示装置の光学補償シートの支持体、または偏光板の保護膜としても特に有利に用いられる。これらのモードは黒表示時に液晶材料が略平行に配向する態様であり、電圧無印加状態で液晶分子を基板面に対して平行配向させて、黒表示する。これらの態様において本発明のアクリルフィルムを用いた偏光板は視野角拡大、コントラストの良化に寄与する。
IPS液晶表示装置は、例えば特開2003−15160号、特開2003−75850号、特開2003−295171号、特開2004−12730号、特開2004−12731号、特開2005−106967号、特開2005−134914号、特開2005−241923号、特開2005−284304号、特開2006−189758号、特開2006−194918号、特開2006−220680号、特開2007−140353号、特開2007−178904号、特開2007−293290号、特開2007−328350号、特開2008−3251号、特開2008−39806号、特開2008−40291号、特開2008−65196号、特開2008−76849号、特開2008−96815号各公報などに記載のものも使用できる。
TNモードの液晶セルは、カラーTFT液晶表示装置として最も多く利用されており、多数の文献に記載がある。
TNモードの黒表示における液晶セル中の配向状態は、セル中央部で棒状液晶性分子が立ち上がり、セルの基板近傍では棒状液晶性化合物が寝た配向状態にある。
また、セル中央部分の棒状液晶性化合物に対しては、ホモジニアス配向(長軸が寝ている水平配向)の棒状液晶性化合物もしくは(透明)支持体で補償し、セルの基板近傍の棒状液晶性化合物に対しては、ハイブリット配向のディスコティック液晶性化合物で補償することもできる。
ホモジニアス配向の液晶性化合物は、液晶性化合物の長軸の平均配向方向と偏光膜の面との角度が5度未満の状態で配向している。
ハイブリット配向の液晶性化合物は、液晶性化合物の長軸の平均配向方向と偏光膜の面との角度が15度以上であることが好ましく、15度〜85度であることがさらに好ましい。
ホメオトロピック配向(水平配向)しているディスコティック液晶性化合物層およびホモジニアス配向(水平配向)している棒状液晶性化合物層に関しては、特開平12−304931号および同12−304932号の各公報に記載されている。ハイブリット配向しているディスコティック液晶性化合物層に関しては、特開平8−50206号公報に記載がある。
OCBモードの液晶セルは、棒状液晶性化合物を液晶セルの上部と下部とで実質的に逆の方向に(対称的に)配向させるベンド配向モードの液晶セルである。ベンド配向モードの液晶セルを用いた液晶表示装置は、米国特許4583825号、同5410422号の各公報に開示されている。棒状液晶性化合物が液晶セルの上部と下部とで対称的に配向しているため、ベンド配向モードの液晶セルは、自己光学補償機能を有する。そのため、この液晶モードは、OCB(Optically Compensatory Bend)液晶モードと呼ばれる。
OCBモードの液晶セルもTNモード同様、黒表示においては、液晶セル中の配向状態は、セル中央部で棒状液晶性化合物が立ち上がり、セルの基板近傍では棒状液晶性化合物が寝た配向状態にある。
VAモードの液晶セルでは、電圧無印加時に棒状液晶性化合物が実質的に垂直に配向している。
VAモードの液晶セルには、(1)棒状液晶性化合物を電圧無印加時に実質的に垂直に配向させ、電圧印加時に実質的に水平に配向させる狭義のVAモードの液晶セル(特開平2−176625号公報記載)に加えて、(2)視野角拡大のため、VAモードをマルチドメイン化した(MVAモードの)液晶セル(SID97、Digest of tech. Papers(予稿集)28(1997)845記載)、(3)棒状液晶性化合物を電圧無印加時に実質的に垂直配向させ、電圧印加時にねじれマルチドメイン配向させるモード(n−ASMモード)の液晶セル(日本液晶討論会の予稿集58〜59(1998)記載)および(4)SURVAIVALモードの液晶セル(LCDインターナショナル98で発表)が含まれる。
ECBモードおよびSTNモードの液晶表示装置に対しては、上記と同様の考え方で光学的に補償することができる。
以下に本発明で使用した測定法について記載する。
製膜フィルムの両端を10cmずつスリットした後、全幅にわたり等間隔で10点サンプリングした。また、製膜方向に1mの間隔で計3箇所に、横方向に同様に10点サンプリングした。サンプリングは、MD(製膜方向)×TD(幅方向)が10cm×10cmの正方形となるように切り出すことにより行った。
得られたサンプルフィルム中に含まれる安定剤、可塑剤、紫外線吸収剤の含有量は、各添加剤を内標として、下記のガスクロマトグラフィー法により測定した。無機微粒子マット剤の含有量はコールターカウンター法により求めた。サンプルフィルムの添加剤濃度のうち、求めた添加剤濃度が最大であったサンプルフィルムの添加剤濃度と、求めた添加剤濃度が最小であったサンプルフィルムの添加剤濃度との間の濃度差を、全サンプルフィルムの添加剤濃度の平均値で割り、百分率で表示したものを添加剤濃度分布とした。
各サンプルフィルム0.25gをそれぞれクロロホルム20mlに溶解し、ガスクロマトグラフィーを用い、対応添加剤を内標として定量評価できる。ガスクロマトグラフィーによる測定条件は下記の通りである。
使用機種:GC−15A((株)島津製作所製)
カラム:シリコンOV、2%、1.6m、3φ、260℃
キャリアガス:窒素50ml/min
注入量:2μl
検出器:FID、水素0.6kg/cm2、空気0.5kg/cm2、気化室:280℃
各サンプルフィルムをアセトン、メチレンクロライド溶媒に溶解し、無機マット剤の含有量をコールターカウンター(株式会社セイシン企業製PITA−1)により測定し、測定された粒子数をフィルム固形分に換算した。
目開きの差が10μmである2種の目開きのふるいを用意し、ふるいの目開きの平均値をアクリル樹脂粉体のサイズとした。
製膜状態(但しタッチロール、チルロールは25℃とする)に富士フイルム(株)製超低圧用プレスケール(LLW)を全幅にわたり通過させた。このようにして発色したプレスケールを富士フィルム(株)製圧力測定システム(専用濃度計(FPD−305E)、専用圧力換算機(FPD−306E))を用いて、全幅にわたり圧力を測定し、この平均値をタッチ圧とした。
製膜したフィルムを全幅でスクリーンの前10cmに平行に設置し、フィルム中央部から1m離れた所にスライド投影機(例えばキャビン工業(株)製CoLor CabinIII)を置き、投影した。フィルムを送り出しながら搬送方向に10m目視評価し、スクリーンに映った幅方向のスジ状模様の本数を数えた。横ダンは0〜15本/mであることが好ましく、0〜5本/mであることがより好ましく、0〜3本/mであることが特に好ましい。
製膜したアクリルフィルムを含有する偏光板をIPS型液晶表示装置(26型IPS液晶テレビモニター(26C3500)、東芝(株)製)に組み込まれていた偏光板の代わりに組み込んだ。全面1mmピッチの格子模様を表示し、格子が正方形からずれて見える個数を目視で計測し、格子が歪んで見える点の数を5倍のルーペを用いて画面全面にわたって調べ、これを画面中の全格子数で割り百分率で表したものを「画像のにじみ」とした。画像のにじみは0〜10%であることが好ましく、0〜5%であることがより好ましく、0〜3%であることが特に好ましい。
添加剤(安定剤、紫外線吸収剤、可塑剤など)の熱揮散性は、TG−TDA(差動系示差熱天秤)(理学電械(株)製、TG8120)を用い、100ml/min窒素雰囲気中に、10℃/minの速度で240℃まで昇温し、240℃に1時間した前後の添加剤の質量減少量を測定し、これを熱揮散性の指標とした。
(アクリル樹脂の調製)
ラクトン環単位を含む下記アクリル樹脂LA−1の調製を行った。
特開2008−9378号公報[0222]〜[0224]の製造例1に従い、メタクリル酸メチル7500g、2−(ヒドロキシメチル)アクリル酸メチル2500gから、ラクトン化率98%、Tg=134℃のアクリル樹脂LA−1を得た。
ラクトン環単位を含む下記アクリル樹脂LA−2の調製を行った。
特開2008−58768号公報[0105]〜[0106]の製造例2に従い、メタクリル酸メチル=8000g、2−(ヒドロキシメチル)アクリル酸メチル2000gから、ラクトン化率97%、Tg=130℃のアクリル樹脂LA−2を得た。
無水マレイン酸単位を含む下記アクリル酸樹脂MA−2の調製を行った。
特開2007−113109号公報の[0049]記載の「耐熱アクリル樹脂」に従い、無水マレイン酸10モル%、スチレン16モル%、メタクリル酸メチル74モル%から、Tg=112s℃のアクリル樹脂MA−2を得た。
グルタル酸無水物単位を含む下記アクリル酸樹脂GU−1およびGU−2の調製を行った。
特開2006−241263号公報の[0130]〜[0135]に従い、グルタル酸無水物単位32重量%、メタクリル酸メチル単位65重量%、メタクリル酸単位3重量%から、Tg=138℃のアクリル樹脂GU−1を得た。
特開2008−50550号公報実施例8に記載の樹脂を[0093]〜[0109]に従い合成し、スチレン−メタクリル酸共重合体60質量部とメタクリル酸メチル−アクリル酸メチル共重合体40質量部とを含むアクリル樹脂ST−1を調製した。
(アクリルフィルムの製膜)
調製した前記アクリル樹脂LA−1を90℃の真空乾燥機で乾燥して含水率を0.03%以下とした後、安定剤イルガノックス1010(チバガイギ(株)製、240℃加熱1時間前後の揮散量1.2%)1.0重量%を添加し、230℃において窒素気流中下、ベント付2軸混練押出し機を用い、水中に押出しストランド状にした後、裁断し直径3mm長さ5mmのペレットを得た。
このペレットを90℃の真空乾燥機で乾燥し含水率を0.03%以下とした。一方、前記アクリル樹脂A−1をターボ工業社製(ターボミルT−400型)の粉砕機によって粉砕し、安定剤イルガノックス1010を0.1重量%を添加し、ふるいにかけることにより直径100μmのアクリル樹脂粉体を得た。前記ペレットに加え、前記アクリル樹脂粉体0.01質量%を、1軸混練押出し機のホッパー(供給部)内に投入し、供給部220℃、圧縮部230℃、計量部240℃で混練し押出した。このとき押し出し機とダイの間に300メッシュのスクリーンフィルター、ギアポンプ、濾過精度7μmのリーフディスクフィルターをこの順に配置し、これらをメルト配管で連結した。さらにスタチックミキサーはダイ直前のメルト配管内に設置した。これをハンガーコートダイから押出した。
この後、3連のキャストロール上にメルト(溶融樹脂)を押出した。この時、最上流側のキャストロール(チルロール)に表1に記載の面圧でタッチロールを接触させた。タッチロールは特開平11−235747号公報の実施例1に記載のもの(二重抑えロールと記載のあるもの、但し薄肉金属外筒厚みは2mmとした)を用い、タッチ圧3MPa、キャストロールとタッチロールの温度差3℃で使用した。
この後、巻き取り直前に両端(全幅の各5cm)をトリミングした後、両端に幅10mm、高さ20μmの厚みだし加工(ナーリング)をつけた。また、製膜幅は2.0mとし、40m/分で3000m巻き取った。製膜後の未延伸フィルムの膜厚が40μmの実施例1のアクリルフィルムを得た。
(偏光子の作成)
厚さ80μmのポリビニルアルコールフィルムを、5重量%(重量比:ヨウ素/ヨウ化カリウム=1/10)のヨウ素水溶液中で染色した。次いで、3重量%のホウ酸および2重量%ヨウ化カリウムを含む水溶液に浸漬し、さらに4重量%のホウ酸および3重量%のヨウ化カリウムを含む水溶液中で6.0倍まで延伸した後、5重量%のヨウ化カリウム水溶液に浸漬した。その後、40℃のオーブンで3分間乾燥を行い、厚さ30μmの偏光子を得た。
セルロース系樹脂(イーストマンケミカル社製、セルロースアセテートプロピオネート)を酢酸ブチルに希釈(固形分濃度7.5重量%)した溶液を調製した。この溶液を、前記アクリルフィルムの片面に塗布し、100℃のオーブンで3分間乾燥させ、セルロース系樹脂層付きの偏光子保護フィルムを得た。セルロース系樹脂層の乾燥厚みは0.8μmであった。
アセトアセチル基変性したポリビニルアルコール樹脂100重量部(アセチル化度13%)に対してメチロールメラミン20重量部を含む水溶液を、濃度0.5重量%になるように調整したポリビニルアルコール系接着剤水溶液を調製した。
上記偏光子の片面に上記偏光子保護フィルムのセルロース系樹脂層の面が、もう一方の面にはけん化処理されたトリアセチルセルロース(TAC)フィルム(富士フィルム(株)製フジタックT−40、厚み40μm)が接するように、上記で調製したポリビニルアルコール系接着剤水溶液を用いて貼り合わせた。その後、70℃で10分間乾燥させて本発明の実施例1の偏光板を得た。
アクリル樹脂、添加剤、アクリル樹脂粉体サイズ、アクリルサイズ粉体添加量、キャストロールとタッチロールの温度差、タッチ圧、製膜速度、未延伸フィルム幅を下記表1に記載のとおりとした以外は実施例1と同様にして、実施例2〜21および比較例1〜5のアクリルフィルム、実施例2〜21および比較例1〜5の偏光板を作成した。なお、実施例7〜15では可塑剤としてアデカスタブFP−700(商品名、株式会社アデカ製、240℃加熱1時間前後の揮散量1.2%)を下記表1記載の量を添加した。また、実施例11〜20および比較例5では紫外線吸収剤としてアデカスタブLA−31(商品名、株式会社アデカ製、240℃加熱1時間前後の揮散量1.5%)を下記表1記載の量を添加した。また、実施例16〜19ではマット剤としてアエロジルR972(商品名、日本アエロジル株式会社製、240℃加熱1時間前後の揮散量0%)を下記表1記載の量を添加した。また、実施例15および比較例5ではタッチロールを用いずに直接キャストロール上で固化し、アクリルフィルムを製膜した。さらに、前記実施例10および16〜19では下記表1記載の倍率で未延伸アクリルフィルムをTg+22℃で延伸した。また、膜厚は下記表1に記載のとおりであった。
なお、本発明の実施例21は安定剤アデカスダブAO−40(商品名、株式会社アデカ製、240℃加熱1時間前後の揮散量33%)1.0重量%を添加する以外、実施例1と全く同様にして実施したものである。
実施例1〜21および比較例1〜5のアクリルフィルムのフィルム面内の添加剤濃度分布、および横ダンを前記測定法にしたがって測定し、その結果を下記表1に示す。また、実施例1〜21および比較例1〜5の偏光板をIPS型液晶表示装置(26型IPS液晶テレビモニター(26C3500)、東芝(株)製)に組み込まれていた偏光板の代わりに組み込み、本発明の液晶表示装置の画像にじみを前記測定法に従って測定した。その結果を下記表1に示す。
前記未延伸、延伸アクリルフィルムを用いた本発明の偏光板を、特開平10−48420号公報の実施例1に記載の液晶表示装置、特開平9−26572号公報の実施例1に記載のディスコティック液晶分子を含む光学的異方性層、ポリビニルアルコールを塗布した配向膜、特開2000−154261号公報の図2〜9に記載の20インチVA型液晶表示装置、特開2000−154261号公報の図10〜15に記載の20インチOCB型液晶表示装置に用いたところ良好な特性が得られた。
(1)表面処理
上記延伸、未延伸のアクリルフィルムに下記条件でコロナ放電処理を行った。
電極:VETAPONE社製 Coron−Plus
ジェネレーター:CP1C
出力:900W
フィルム搬送速度:6m/分
これらの熱可塑性フィルム上に、下記の組成の塗布液を#16のワイヤーバーコーターで28mL/m2塗布した。60℃の温風で60秒、さらに90℃の温風で150秒乾燥した。
(2−1)配向膜塗布液組成
下記の変性ポリビニルアルコール 20質量部
水 360質量部
メタノール 120質量部
グルタルアルデヒド(架橋剤) 1.0質量部
配向膜上に、下記塗布液を、#3.2のワイヤーバーを1171回転でフィルムの搬送方向と同じ方向に回転させて、30m/分で搬送されている上記ロールフィルムの配向膜面に連続的に塗布した。室温から100℃に連続的に加温する工程で、溶媒を乾燥させ、その後、135℃の乾燥ゾーンで、ディスコティック液晶化合物層にあたる膜面風速がフィルム搬送方向に平行に1.5m/secとなるようにし、約90秒間加熱し、ディスコティック液晶化合物を配向させた。次に、80℃の乾燥ゾーンに搬送させて、フィルムの表面温度が約100℃の状態で、紫外線照射装置(紫外線ランプ:出力160W/cm、発光長1.6m)により、照度600mWの紫外線を4秒間照射し、架橋反応を進行させ、ディスコティック液晶化合物をその配向に固定した。その後、室温まで放冷し、円筒状に巻き取ってロール状の形態にした。光学異方性層の厚みは1.3μmであった。
また、得られた光学補償シートの弾性率を測定したところ2.4MPaであった。
下記の組成物を、97質量部のメチルエチルケトンに溶解して塗布液を調製した。
下記のディスコティック液晶性化合物(1) 41.01質量部
エチレンオキサイド変成トリメチロールプロパントリアクリレート
(V#360、大阪有機化学(株)製 4.06質量部
セルロースアセテートブチレート
(CAB551−0.2、イーストマンケミカル社製) 0.34質量部
セルロースアセテートブチレート
(CAB531−1、イーストマンケミカル社製) 0.11質量部
下記フルオロ脂肪族基含有ポリマー1 0.56質量部
下記フルオロ脂肪族基含有ポリマー2 0.06質量部
光重合開始剤(イルガキュアー907、チバガイギー社製) 1.35質量部
増感剤(カヤキュアーDETX、日本化薬(株)製) 0.45質量部
上記光学異方性層を塗設したアクリルフィルムを、上記偏光板作成方法と同様にして偏光板を作成した。
TN型液晶パネルを使用した液晶表示装置(MDT−191S、三菱電(株)製)に設けられている一対の偏光板を剥がし、代わりに上記の作製した偏光板を、光学補償シートが液晶セル側となるように粘着剤を介して、観察者側およびバックライト側に一枚ずつ貼り付けた。観察者側の偏光板の透過軸と、バックライト側の偏光板の透過軸とは、Oモードとなるように配置した。本発明を実施したものは像の歪みのない良好な特性を示した。
本発明の未延伸・延伸アクリルフィルムを発明協会公開技報(公技番号2001−1745)の実施例47に従い低反射フィルムを作製したところ、良好な光学性能が得られた。
Claims (15)
- 添加剤を少なくとも一種含有し、該添加剤のフィルム面内における添加剤濃度分布が0.01%〜3%であることを特徴とするアクリルフィルム。
- 前記添加剤が、安定剤、紫外線吸収剤、可塑剤およびマット剤からなる群より選ばれる少なくとも一種であることを特徴とする請求項1に記載のアクリルフィルム。
- 前記添加剤が安定剤または紫外線吸収剤であることを特徴とする請求項1または2に記載のアクリルフィルム。
- 前記アクリルフィルムが、ラクトン環単位、無水マレイン酸単位、グルタル酸無水物単位の少なくとも1種の単位を含み、厚みが20μm〜85μmであることを特徴とする請求項1〜3のいずれか一項に記載のアクリルフィルム。
- 前記アクリルフィルムの幅が1.5m〜4.0mであることを特徴とする請求項1〜4のいずれか一項に記載のアクリルフィルム。
- アクリル樹脂のペレットを押出し機に投入して溶融させてメルトを得る工程と、
前記ダイからメルトを押出す工程と、
前記ダイから押出されたメルトを固化して製膜する工程と、を含むアクリルフィルムの製造方法において、
前記アクリル樹脂のペレットを押出し機に投入して溶融させてメルトを得る工程において、前記ペレットとともに直径30μm〜1mmのアクリル樹脂粉体を前記押出機に投入し、かつ、前記アクリル樹脂粉体の添加量が、前記ペレットに対して0.01質量%〜10質量%であることを特徴とするアクリルフィルムの製造方法。 - 製膜速度が10m/分〜70m/分であることを特徴とする請求項6に記載のアクリルフィルムの製造方法。
- 前記ダイから押出されたメルトを固化して製膜する工程において、キャストロール上にメルトを流延し、前記キャストロールより1〜30℃低い温度に設定されたタッチロールをメルトを流延した前記キャストロールに0.1MP〜10MPの圧力で押圧することを特徴とする請求項6または7に記載のアクリルフィルムの製造方法。
- 前記ペレットを押出し機に投入して溶融させてメルトを得る工程において、添加剤含有量が異なる複数種のペレットを押出し機に投入して溶融する工程を含み、かつ、前記複数種のペレットのうち最も添加剤含有量が少ないペレットと最も添加剤含有量が多いペレットの間の添加剤含有量の比が1.1〜10倍であることを特徴とする請求項6〜8のいずれか一項に記載のアクリルフィルムの製造方法。
- 製膜後のフィルムを少なくとも一方向に1.1倍〜3.5倍の倍率で延伸する工程を含むことを特徴とする請求項6〜9のいずれか一項に記載のアクリルフィルムの製造方法。
- 請求項6〜10のいずれか一項に記載の製造方法で製造したことを特徴とする請求項1〜5のいずれか一項に記載のアクリルフィルム。
- 請求項1〜5および11のいずれか一項に記載のアクリルフィルムを用いた偏光板。
- 請求項1〜5および11のいずれか一項に記載のアクリルフィルムを用いた光学補償フィルム。
- 請求項1〜5および11のいずれか一項に記載のアクリルフィルムを用いた反射防止フィルム。
- 請求項1〜5および11のいずれか一項に記載のアクリルフィルムを用いた液晶表示装置。