JP2015199965A - ポリウレタンフォームおよびそれを用いたシール材 - Google Patents
ポリウレタンフォームおよびそれを用いたシール材 Download PDFInfo
- Publication number
- JP2015199965A JP2015199965A JP2015114470A JP2015114470A JP2015199965A JP 2015199965 A JP2015199965 A JP 2015199965A JP 2015114470 A JP2015114470 A JP 2015114470A JP 2015114470 A JP2015114470 A JP 2015114470A JP 2015199965 A JP2015199965 A JP 2015199965A
- Authority
- JP
- Japan
- Prior art keywords
- polyurethane foam
- polyol
- mass
- foam
- catalyst
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
前記ポリオールがダイマー酸ポリオールであり、前記イソシアネート中のジフェニルメタンジイソシアネートの比率が55〜75質量%であり、かつ、前記ポリウレタンフォーム原料が、前記ポリオール100質量部に対し、架橋剤を1〜3質量部にて含むことを特徴とするものである。本発明においては、前記ポリウレタンフォームの、通気性が5cc/cm2/sec.以下であり、セル数が65個/inch以上であることが好ましい。
本発明のトナーシール材は、画像形成装置内において、トナーの漏出を防止するために用いられるものであって、ポリオール、イソシアネート、触媒および整泡剤を含むポリウレタンフォーム原料を発泡させて形成される。
下記の表中に示すポリウレタンフォーム原料を、ワンショット法により混合、発泡させて、ポリウレタンフォームを得た。得られた各ポリウレタンフォームにつき、下記に従い評価を行った結果を、下記の表中に併せて示す。
得られた各ポリウレタンフォームの通気性を、JIS L 1004のフラジール型により、フォーム厚さを10mmとして、測定した。通気性が、1cc/cm2/sec.以下の場合を◎とし、1cc/cm2/sec.を超える場合を×とした。
得られた各ポリウレタンフォームを用いて、20mm×200mm×10mm厚のトナーシール材を作製し、印字性能を評価した。印字性能は、印刷時での印字抜けがない場合を◎とし、ある場合を×とした。
得られた各ポリウレタンフォームにつき、発泡性を評価した。発泡性は、良好にフォームが形成され、健康泡がある場合を◎、良好にフォームは形成されているが健康泡がない場合を○、フォーム内にクラックがあるなどフォーム形成に不具合が生じた場合を△、フォームが形成されない場合を×とした。
得られた各ポリウレタンフォームにつき、JIS K6400−5.3に準拠して、伸び率を評価した。伸び率が、80%以上である場合を◎、70%以上80%未満である場合を○、70%未満である場合を×とした。
得られた各ポリウレタンフォームブロックの成長方向により水平裁断した試験片を、実体顕微鏡により観察して、長さ1inchの範囲にあるセル数を計測し、3点の測定値の平均値を求めた。フォーム外観性は、セル数が、65個/inch以上である場合を◎、60〜64個/inchである場合を○、59個/inch以下である場合を×とした。
*2)TDI,三井化学ポリウレタン(株)製,「コスモネートT80」
*3)MDI,住化バイエルウレタン(株)製,「44V20」(クルードMDI)
*4)反応性アミン,エアープロダクツジャパン(株)製,「DABCO NE300」
*5)シリコーン,モメンティブ・パフォーマンス・マテリアルズ・ジャパン合同会社製,「NIAX SILICONE L−5340」
*6)架橋剤,三井化学(株)製,「アクトコールT880」
Claims (3)
- ポリオール、イソシアネート、触媒および整泡剤を含むポリウレタンフォーム原料を発泡させてなるポリウレタンフォームであって、
前記ポリオールがダイマー酸ポリオールであり、前記イソシアネート中のジフェニルメタンジイソシアネートの比率が55〜75質量%であり、かつ、前記ポリウレタンフォーム原料が、前記ポリオール100質量部に対し、架橋剤を1〜3質量部にて含むことを特徴とするポリウレタンフォーム。 - 前記ポリウレタンフォームの、通気性が5cc/cm2/sec.以下であり、セル数が65個/inch以上である請求項1記載のポリウレタンフォーム。
- 請求項1または2記載のポリウレタンフォームを用いてなることを特徴とするシール材。