JP6770475B2 - 親水性ポリウレタンフォームとその製造方法 - Google Patents
親水性ポリウレタンフォームとその製造方法 Download PDFInfo
- Publication number
- JP6770475B2 JP6770475B2 JP2017070636A JP2017070636A JP6770475B2 JP 6770475 B2 JP6770475 B2 JP 6770475B2 JP 2017070636 A JP2017070636 A JP 2017070636A JP 2017070636 A JP2017070636 A JP 2017070636A JP 6770475 B2 JP6770475 B2 JP 6770475B2
- Authority
- JP
- Japan
- Prior art keywords
- isocyanate
- polyurethane foam
- polyol component
- mass
- parts
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
インク保持体は、親水性ポリウレタンフォームにインクを吸収させた状態でインクカートリッジに収容されている。
官能基数3〜4、分子量60〜500、水酸基価330〜2000mgKOH/gの架橋剤として、グリセリン、トリメチロールプロパン、1,2,4−ブタントリオール、2−メチル−2,3,4−ブタントリオール、トリエタノールアミン、ペンタエリスリトール等を挙げることができ、一種または複数併用してもよい。
架橋剤の配合量は、ポリオール成分100質量部に対して2〜6質量部が好ましい。
前記発泡は、スラブ発泡あるいはモールド発泡のいずれでもよい。スラブ発泡は、混合したポリウレタンフォーム用組成物をベルトコンベア上に吐出し、大気圧下、常温で発泡させる方法であり、一方、モールド発泡は、混合したポリウレタンフォーム用組成物をモールド(成形型)に充填してモールド内で発泡させる方法である。
・プレポリマー:ポリエーテルポリオール(*1)/イソシアネート(*2)=2モル/1モル混合液を金属触媒の存在下において、80℃で約2時間反応させて合成した水酸基末端プレポリマー、水酸基価33mgKOH/g、粘度17000mPa・s(30℃)。使用したポリエーテルポリオール(*1)は、分子量3000、官能基数3、水酸基価56mgKOH/g、品番;GP−3000、三洋化成工業株式会社製である。使用したイソシアネート(*2)は、2,4−TDI80%と2,6−TDI20%の混合物、品番;T−80、日本ポリウレタン社製である。
・ポリオール:ポリエーテルポリオール、分子量3000、官能基数3、水酸基価56mgKOH/g、品番;GP−3050NS、三洋化成工業株式会社製
・イソシアネート(MDI);ポリメリックMDI、品番S−6510、NCO%29.4、ハンツマン社製
・イソシアネート(TDI);2,4−TDI80%と2,6−TDI20%の混合物、品番;T−80、NCO%48.2、日本ポリウレタン社製
・架橋剤A;グリセリン、官能基数3、分子量92、水酸基価1829mgKOH/g
・架橋剤B;エチレンジアミンを開始剤としてプロピレンオキサイドを付加したもの、官能基数4、分子量450、水酸基価499mgKOH/g
・架橋剤C;エチレングリコール、官能基数2、分子量62、水酸基価1810mgKOH/g
・整泡剤A;シリコーン整泡剤、品番:SH−193、東レ・ダウコーニング社製
・整泡剤B;シリコーン整泡剤、品番:SZ−1346E、東レ・ダウコーニング社製
・アミン触媒A:品番;カオーライザーNo.25、花王社製
・アミン触媒B:品番;NE−300、エアープロダクト社製
・スズ触媒:ジブチルスズジラウレート、品番;MRH−110、城北化学工業社製
比較例1は、プレポリマーに代えてポリオールを使用した例、比較例2はイソシアネートとしてTDIを使用した例、比較例3は架橋剤を配合しない例、比較例4はシリコーン系整泡剤Aを配合した例、比較例5はシリコーン系整泡剤Bを配合した例、比較例6は官能基数2の架橋剤Cを配合した例である。
インク吸収性に関する評価は、インクジェットプリンター用インクの1ccを各試験体の表面上方5cmの位置から注射器で滴下し、試験体の表面に滴下したインクが試験体内に吸い込まれるまでの時間を測定し、測定結果が2秒未満の場合を「〇」、2〜3秒未満の場合を「△」、3秒以上の場合を「×」とした。
インクへの溶出性については、ポリウレタンフォームのエタノール抽出によって得られた抽出物に対してFT−IRによるオルガノポリシロキサンの分析によって行った。抽出残渣の分析によりオルガノポリシロキサンの吸収スペクトルの有無により判断し、スペクトルがない場合「○」、スペクトルがあった場合「×」とした。「○」の場合、インクへのオルガノシロキサンの溶出がないと考えられ、「×」の場合、インクへの溶出を引き起こす恐れがあると考えられる。
総合評価は、各評価が全て「〇」の場合に総合評価「〇」とし、各評価に一つでも「△」または「×」が存在する場合に総合評価「×」とした。
一方、プレポリマーに代えてポリオールを使用した比較例1は、フォームがダウンし、インク吸収性及びインクへの溶出について評価できず、総合評価が「×」であった。
イソシアネートとしてTDIを用いた比較例2は、フォームにセル荒れがあり、インク吸収性及びインクへの溶出について評価できず、総合評価が「×」であった。
架橋剤を配合しない比較例3は、フォームがダウンし、インク吸収性及びインクへの溶出について評価できず、総合評価が「×」であった。
シリコーン系整泡剤Aを配合した比較例4は、フォームのガス抜けが悪く、インク吸収性「×」、インクへの溶出がなく「〇」、総合評価「×」であった。
シリコーン系整泡剤Bを配合した比較例5は、インク吸収性「×」及びインクへの溶出性「×」であり、総合評価「×」であった。
官能基数2の架橋剤Cを配合した比較例6は、フォームがダウンし、インク吸収性及びインクへの溶出について評価できず、総合評価が「×」であった。
Claims (4)
- ポリオール成分、イソシアネート、発泡剤、触媒、架橋剤を含み、シリコーン系整泡剤を含まないポリウレタンフォーム用組成物から得られた親水性ポリウレタンフォームであって、
前記ポリオール成分は該ポリオール成分の100質量部中にポリエーテルポリオールとイソシアネートの反応により得られた水酸基末端プレポリマーを80〜100質量部含み、
前記架橋剤は官能基数が3〜4であり、
前記イソシアネートはMDI系イソシアネートであり、
イソシアネートインデックスは100〜120であることを特徴とする親水性ポリウレタンフォーム。 - 前記架橋剤の量は、前記ポリオール成分100質量部に対して3〜5質量部であることを特徴とする請求項1に記載の親水性ポリウレタンフォーム。
- ポリオール成分、イソシアネート、発泡剤、触媒、架橋剤を含み、シリコーン系整泡剤を含まないポリウレタンフォーム用組成物を用い、前記ポリオール成分と前記イソシアネートの反応により親水性ポリウレタンフォームを製造する方法において、
前記ポリオール成分は該ポリオール成分の100質量部中にポリエーテルポリオールとイソシアネートの反応により得られた水酸基末端プレポリマーを80〜100質量部含み、
前記架橋剤は官能基数が3〜4であり、
前記イソシアネートはMDI系イソシアネートであり、
イソシアネートインデックスは100〜120であることを特徴とする親水性ポリウレタンフォームの製造方法。 - 前記架橋剤の量は、前記ポリオール成分100質量部に対して3〜5質量部であることを特徴とする請求項3に記載の親水性ポリウレタンフォームの製造方法。