JP2015063468A - ハイドロゲル粒子 - Google Patents
ハイドロゲル粒子 Download PDFInfo
- Publication number
- JP2015063468A JP2015063468A JP2013196650A JP2013196650A JP2015063468A JP 2015063468 A JP2015063468 A JP 2015063468A JP 2013196650 A JP2013196650 A JP 2013196650A JP 2013196650 A JP2013196650 A JP 2013196650A JP 2015063468 A JP2015063468 A JP 2015063468A
- Authority
- JP
- Japan
- Prior art keywords
- mass
- less
- hydrogel particles
- hydrogel
- crystalline
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
本実施形態に係るハイドロゲル粒子は、非架橋型ハイドロゲルの連続相とその連続相内に分散した分散相とを備える。そして、分散相は、脂肪酸グリセライドA1及び炭素数14〜22の高級アルコールA2(以下「高級アルコールA2」と略す。)を含む固体脂Aと、ビフェニル骨格を有する結晶性美白剤B(以下「結晶性美白剤B」と略す。)を含有する。本実施形態に係るハイドロゲル粒子は、例えば、化粧料、主には美白化粧料に配合されて用いられるものである。
連続相は、非架橋型ハイドロゲルで構成されており、ゲル形成剤と水とを含有する。
分散相は、固体脂Aと結晶性美白剤Bとを含有する。また、分散相は、液体油Cを更に含有してもよい。この場合、分散相において、固体脂A及び液体油Cは油脂成分を構成する。
固体脂Aは、融点が35℃以上の油脂であり、脂肪酸グリセライドA1及び高級アルコールA2を含む。尚、固体脂Aは、ハイドロゲル粒子からの結晶性美白剤Bの漏出抑制効果を阻害しない範囲で、それら以外の、例えば、炭素数14〜22でない高級アルコールや固形パラフィン等を含んでいてもよい。
脂肪酸グリセライドA1は、下記一般式(I)で表される化合物を含むことが好ましい。
(式中、X及びYは、各々独立して、OH又はOCOR2を示し、R1及びR2は、各々独立して、炭素数13〜21の飽和炭化水素基、好ましくは炭素数13〜21の直鎖状飽和炭化水素基を示す)
一般式(I)の脂肪酸グリセライドA1は、X及びYのいずれもがOCOR2である脂肪酸トリグリセライドを含んでもよいが、ハイドロゲル粒子からの結晶性美白剤Bの漏出を抑制する観点から、X及びYのいずれもがOHである脂肪酸モノグリセライド並びにX及びYのいずれか一方がOHで且つ他方がOCOR2である脂肪酸ジグリセライドのうち少なくとも一方を含むことが好ましく、脂肪酸モノグリセライドを含むことがより好ましい。また、同様の観点から、一般式(I)の脂肪酸グリセライドA1は、R1及びR2が、各々独立して、炭素数16又は18の飽和炭化水素基であることが好ましく、炭素数18の飽和炭化水素基であることがより好ましい。飽和炭化水素基は、直鎖状及び分岐鎖状のいずれであってもよいが、直鎖状であることが好ましい。
高級アルコールA2は、分子中に含まれる炭素数が14〜22の鎖式アルコールである。高級アルコールA2は、ハイドロゲル粒子からの結晶性美白剤Bの漏出を抑制する観点から、分子中に含まれる炭素数が好ましくは16〜22、より好ましくは16〜18である。また、高級アルコールA2は、直鎖状又は分岐鎖状の飽和一価アルコールであることが好ましく、更に、直鎖状であることがより好ましい。
本出願における「結晶性美白剤B」とは、ビフェニル骨格を有する結晶性化合物であって、チロシナーゼ活性阻害効果及び/又はメラニン生成抑制効果を奏するものをいう。結晶性であることは、X線回折によりピークを有することで、結晶状態を確認できる。かかる結晶性美白剤Bとしてはマグノリグナンが好ましい。
液体油Cは、融点が35℃未満の油脂であり、難溶性の結晶性美白剤Bを安定に配合する観点及び化粧料等に適用した場合の皮膚上での延ばしやすさの観点から、下記一般式(i)で表される脂肪族ジカルボン酸エステルを含むことが好ましい。
連続相は、非架橋型ハイドロゲルのゲル化剤及び水以外に、特開2000-126586号公報に記載の糖類、多価アルコール、水溶性高分子化合物、水溶性香料等の水溶性有機化合物の成分を含有してもよい。
以下、本実施形態に係るハイドロゲル粒子の製造方法について説明する。
まず、分散相成分液として、脂肪酸グリセライドA1及び高級アルコールA2を含む固体脂A並びに結晶性美白剤Bを加熱混合して十分に溶解させた混合液を調製する。分散相が液体油Cを含む場合には、分散相成分液に液体油Cを含める。また、連続相成分液として、ゲル形成剤及びイオン交換水を混合し、その溶解温度以上の温度に加熱して十分に溶解させた混合液を調製する。
続いて、分散液を調製した後、その分散液を一般的な滴下法、噴霧法、又は攪拌法により液滴にして冷却固化させることによりハイドロゲル粒子を製造する。
本実施形態に係るハイドロゲル粒子を配合することにより、美白効果を有する美白化粧料を得ることができる。乳化液に用いる場合、w/o型、o/w型のいずれの化粧料にも適用することが可能であるが、ハイドロゲル粒子の分散安定性の観点から、o/w型の化粧料に用いることが好ましい。本実施形態に係るハイドロゲル粒子は、化粧水等の水溶性溶媒を主成分とする化粧料にも適用することが可能である。
(式中、X及びYは、各々独立して、OH又はOCOR2を示し、R1及びR2は、各々独立して、炭素数13〜21の飽和炭化水素基を示す)
<9>前記一般式(I)の脂肪酸グリセライドは、好ましくはX及びYのいずれもがOHである脂肪酸モノグリセライド並びにX及びYのいずれか一方がOHで且つ他方がOCOR2である脂肪酸ジグリセライドのうち少なくとも一方を含み、より好ましくは脂肪酸モノグリセライドを含む、前記<8>に記載のハイドロゲル粒子。
以下の実施例1〜10並びに比較例1及び2のハイドロゲル粒子を作製した。それぞれの構成について表1〜3にも示す。
脂肪酸グリセライドA1として(a1)ステアリン酸グリセライド(花王社製 商品名:レオドールMS−60、ステアリン酸モノグリセライド60質量%、ステアリン酸ジグリセライド40質量%)、高級アルコールA2として(a2−1)セチルアルコール(花王社製 商品名:カルコール6098、分子内炭素数16)及び(a2−2)ステアリルアルコール(花王社製 商品名:カルコール8098、分子内炭素数18)、高結晶性美白剤Bとして(b)ジプロピルビフェニルジオール(長谷川香料社製 商品名:マグノリグナン)、並びに液体油Cとして(c)セバシン酸ジイソプロピル(日本サーファクタント工業社製 商品名:N−DIS)を含む分散相成分液を調製した。このとき、得られるハイドロゲル粒子におけるそれぞれの含有量が、(a1)ステアリン酸グリセライド4質量%、(a2−1)セチルアルコール1.2質量%、(a2−2)ステアリルアルコール0.8質量%、(b)ジプロピルビフェニルジオール3質量%、及び(c)セバシン酸ジイソプロピル21質量%となるように配合を行った。
得られるハイドロゲル粒子における(a1)ステアリン酸グリセライドの含有量が3.0質量%、(a2−1)セチルアルコールの含有量が1.8質量%、及び(a2−2)ステアリルアルコールの含有量が1.2質量%となるように配合を行ったことを除いて実施例1と同一構成のハイドロゲル粒子を作製し、これを実施例2とした。
得られるハイドロゲル粒子における(a1)ステアリン酸グリセライドの含有量が2.0質量%、(a2−1)セチルアルコールの含有量が2.4質量%、及び(a2−2)ステアリルアルコールの含有量が1.6質量%となるように配合を行ったことを除いて実施例1と同一構成のハイドロゲル粒子を作製し、これを実施例3とした。
高級アルコールA2として(a2−2)ステアリルアルコールのみを用い、得られるハイドロゲル粒子における(a1)ステアリン酸グリセライドの含有量が3.0質量%、及び(a2−2)ステアリルアルコールの含有量が3.0質量%となるように配合を行ったことを除いて実施例1と同一構成のハイドロゲル粒子を作製し、これを実施例4とした。
高級アルコールA2として(a2−3)ベヘニルアルコール(花王社製、商品名:カルコール8098、分子内炭素数22)を用い、得られるハイドロゲル粒子における(a2−3)ベヘニルアルコールの含有量が2.0質量%となるように配合を行ったことを除いて実施例1と同一構成のハイドロゲル粒子を作製し、これを実施例5とした。
得られるハイドロゲル粒子における(a1)ステアリン酸グリセライドの含有量が3.0質量%、及び(a2−3)ベヘニルアルコールの含有量が3.0質量%となるように配合を行ったことを除いて実施例5と同一構成のハイドロゲル粒子を作製し、これを実施例6とした。
得られるハイドロゲル粒子における(a1)ステアリン酸グリセライドの含有量が2.0質量%、及び(a2−3)ベヘニルアルコールの含有量が4.0質量%となるように配合を行ったことを除いて実施例5と同一構成のハイドロゲル粒子を作製し、これを実施例7とした。
得られるハイドロゲル粒子における(a1)ステアリン酸グリセライドの含有量が1.5質量%、(a2−1)セチルアルコールの含有量が0.75質量%、及び(a2−2)ステアリルアルコールの含有量が0.75質量%となるように配合を行い、且つ分散相成分液と連続相成分液とを質量比27:73の割合で混合したことを除いて実施例1と同一構成のハイドロゲル粒子を作製し、これを実施例8とした。
得られるハイドロゲル粒子における(a1)ステアリン酸グリセライドの含有量が5.0質量%、(a2−1)セチルアルコールの含有量が2.5質量%、及び(a2−2)ステアリルアルコールの含有量が2.5質量%となるように配合を行い、且つ分散相成分液と連続相成分液とを質量比34:66の割合で混合したことを除いて実施例1と同一構成のハイドロゲル粒子を作製し、これを実施例9とした。
高級アルコールA2として(a2−4)ミリスチルアルコール(花王社製、商品名:カルコール4098、分子内炭素数14)を用い、得られるハイドロゲル粒子における(a1)ステアリン酸グリセライドの含有量が3.0質量%、及び(a2−4)ミリスチルアルコールの含有量が3.0質量%となるように配合を行ったことを除いて実施例1と同一構成のハイドロゲル粒子を作製し、これを実施例10とした。
高級アルコールA2を用いず、得られるハイドロゲル粒子における(a1)ステアリン酸グリセライドの含有量が3.0質量%となるように配合を行い、且つ分散相成分液と連続相成分液とを質量比27:73の割合で混合したことを除いて実施例1と同一構成のハイドロゲル粒子を作製し、これを比較例1とした。
脂肪酸グリセライドA1を用いず、高級アルコールA2として(a2−2)ステアリルアルコールを用い、得られるハイドロゲル粒子における(a2−2)ステアリルアルコールの含有量が3.0質量%となるように配合を行い、且つ分散相成分液と連続相成分液とを質量比27:73の割合で混合したことを除いて実施例1と同一構成のハイドロゲル粒子を作製し、これを比較例2とした。
実施例1〜10及び比較例1〜2のそれぞれのハイドロゲル粒子について、ハイドロゲル粒子50質量%、フェノキシエタノール(東邦化学社製 商品名:ハイソルブEPH)0.2質量%、エタノール10質量%、及び精製水49.8質量%の組成比となるスラリー状の化粧料を調製した。
表4は試験結果を示す。尚、表4中、「>7ヶ月」は、保存開始から7ヶ月経過した時点で結晶性美白剤の結晶の析出が認められないことを意味し、同様に、「>2ヶ月」は、保存開始から2ヶ月経過した時点で結晶性美白剤の結晶の析出が認められないことを意味する。
Claims (12)
- 非架橋型ハイドロゲルの連続相と、前記連続相内に分散した分散相とを備え、
前記分散相は、脂肪酸グリセライド及び炭素数14〜22の高級アルコールを含む固体脂と、ビフェニル骨格を有する結晶性美白剤とを含有する、ハイドロゲル粒子。 - 前記高級アルコールの炭素数が16〜22である、請求項1に記載のハイドロゲル粒子。
- 前記分散相における前記高級アルコールの含有量が2〜25質量%である、請求項1又は2に記載のハイドロゲル粒子。
- 前記分散相における前記高級アルコールの含有量に対する前記脂肪酸グリセライドの含有量の質量比(脂肪酸グリセライド/高級アルコール)が0.2〜4である、請求項1〜3の何れかに記載のハイドロゲル粒子。
- 前記分散相における前記脂肪酸グリセライド及び前記高級アルコールの合計の含有量に対する前記結晶性美白剤の含有量の質量比(結晶性美白剤/(脂肪酸グリセライド+高級アルコール))が0.1〜3である、請求項1〜4の何れかに記載のハイドロゲル粒子。
- 前記脂肪酸グリセライドが、下記一般式(I)で表される化合物を含む、請求項1〜5の何れかに記載のハイドロゲル粒子。
R1COOCH2(CHX)CH2Y (I)
(式中、X及びYは、各々独立して、OH又はOCOR2を示し、R1及びR2は、各々独立して、炭素数13〜21の飽和炭化水素基を示す) - 前記結晶性美白剤が2,2’−ジヒドロキシ−5,5’−ジ−n−プロピルビフェニルを含む、請求項1〜6の何れかに記載のハイドロゲル粒子。
- 前記分散相が液体油を更に含有する、請求項1〜7の何れかに記載のハイドロゲル粒子。
- 請求項1〜9の何れかに記載のハイドロゲル粒子を含有する、美白化粧料。
- 脂肪酸グリセライド及び炭素数14〜22の高級アルコールを含む固体脂、ビフェニル骨格を有する結晶性美白剤、ゲル形成剤、及び水を含有する分散液を、滴下法、噴霧法、又は撹拌法により液滴にして冷却固化させて得られる、請求項1〜9の何れかに記載のハイドロゲル粒子。
- 脂肪酸グリセライド及び炭素数14〜22の高級アルコールを含む固体脂、ビフェニル骨格を有する結晶性美白剤、ゲル形成剤、及び水を含有する分散液を、滴下法、噴霧法、又は撹拌法により液滴にして冷却固化させる、請求項1〜9の何れかに記載のハイドロゲル粒子の製造方法。