JP2014080360A - 針状炭酸ストロンチウム微粉末 - Google Patents
針状炭酸ストロンチウム微粉末 Download PDFInfo
- Publication number
- JP2014080360A JP2014080360A JP2013204634A JP2013204634A JP2014080360A JP 2014080360 A JP2014080360 A JP 2014080360A JP 2013204634 A JP2013204634 A JP 2013204634A JP 2013204634 A JP2013204634 A JP 2013204634A JP 2014080360 A JP2014080360 A JP 2014080360A
- Authority
- JP
- Japan
- Prior art keywords
- strontium carbonate
- acicular
- particles
- acicular strontium
- fine powder
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
【解決手段】長径の平均長さが150nm以下であって、平均アスペクト比が1.5以上であり、長径の長さが200nm以上の針状粒子の含有率が個数基準で5%以下にある針状炭酸ストロンチウム粒子の微粉末であって、針状炭酸ストロンチウム粒子の表面が、側鎖にポリオキシアルキレン基を有するポリカルボン酸もしくはその無水物と、ポリオキシアルキレン基及び炭化水素基を有するアミンとで処理されていることを特徴とする針状炭酸ストロンチウム微粉末。
【選択図】なし
Description
(1)アミンのHLBが4〜10の範囲にある。
(2)アミンがポリオキシエチレン−ステアリルアミンである。
(3)針状炭酸ストロンチウム粒子の平均アスペクト比が2以上でかつ5以下である。
(4)針状炭酸ストロンチウム粒子の平均長さが10nm以上である。
(5)アミンの量がポリカルボン酸もしくはその無水物の量を1質量部としたときに1.1〜5.0質量部の範囲にある。
(1)針状炭酸ストロンチウム粒子水性スラリーの製造
水温10℃の純水3Lに水酸化ストロンチウム八水和物(特級試薬、純度:96%以上)366gを投入し、混合して濃度5.6質量%の水酸化ストロンチウム水性懸濁液を調製した。この水酸化ストロンチウム水性懸濁液に、DL−酒石酸(特級試薬、純度:99%以上)を加えて撹拌して該水性懸濁液中に溶解させた。ついで水酸化ストロンチウム水性懸濁液の液温を10℃に維持しつつ、撹拌を続けながら、該水性懸濁液に二酸化炭素ガスを3.75L/分の流量(水酸化ストロンチウム1gに対して22mL/分の流量)にて、該水性懸濁液のpHが7になるまで吹き込んで、炭酸ストロンチウム粒子を生成させた後、さらに30分間撹拌を続けて、炭酸ストロンチウム粒子水性懸濁液を得た。得られた炭酸ストロンチウム粒子水性懸濁液をステンレスタンクに入れて、該水性懸濁液を80℃の温度にて24時間加熱処理して炭酸ストロンチウム粒子を針状に成長させ、その後、室温まで放冷して、針状炭酸ストロンチウム粒子水性スラリーを製造した。
針状炭酸ストロンチウム粒子水性スラリー(濃度:5.8質量%)3500gをホモミキサー(プライミクス株式会社製、T.K.ホモミキサーMarkII)に投入し、該ホモミキサーの撹拌羽根を7.85m/秒の周速で回転させて撹拌しながら、該水性スラリーに、側鎖にポリオキシアルキレン基を有するポリカルボン酸の無水物(マリアリムKM−0521、日油株式会社製)を12.2g(炭酸ストロンチウム粒子100質量部に対して6質量部)添加して、該ポリマーを水性スラリーに溶解させ、ついでポリオキシエチレン−ステアリルアミン(ナイミーンS204、HLB=8.0、日油株式会社製)を30.5g(炭酸ストロンチウム粒子100質量部に対して15質量部)添加し、その後1時間撹拌混合を続けた。撹拌混合後の炭酸ストロンチウム粒子水性スラリーを120〜130℃に加熱したステンレス板の上に噴霧し、水性スラリーを乾燥して、炭酸ストロンチウム微粉末を得た。
得られた炭酸ストロンチウム微粉末を電子顕微鏡を用いて観察した結果、該微粉末は針状粒子の微粉末であることが確認された。また、針状粒子の表面をフーリエ変換赤外分光測定装置(FT−IR)を用いて1回反射ATR法(ダイヤモンド45°、分解能4cm-1)にて分析した。その結果、側鎖にポリオキシアルキレン基を有するポリカルボン酸無水物に起因する赤外吸収ピークとポリオキシエチレン−ステアリルアミンとに起因する赤外吸収ピークとが検出された。
針状炭酸ストロンチウム微粉末の電子顕微鏡画像から1000個の粒子の長径とアスペクト比とを測定し、それらの平均と長径の長さが200nm以上の針状粒子の含有率とを求めた。その結果、長径の平均が64nmで、アスペクト比の平均が2.7であって、長径の長さが200nm以上の針状粒子の含有率は0.1%以下(1000個中で0個)であった。また、得られた針状炭酸ストロンチウム微粉末のBET比表面積を測定したところ、74.0m2/gであった。
針状炭酸ストロンチウム微粉末0.2gを塩化メチレン20gに投入し、超音波ホモジナイザーを用いて5分間分散処理して、炭酸ストロンチウム粒子濃度が1質量%の針状炭酸ストロンチウム粒子分散液を調製した。
針状炭酸ストロンチウム粒子分散液中の炭酸ストロンチウム粒子の粒度分布を、動的光散乱法にて測定した。粒度分布のD90(篩下の累積粒度分布が90%となる粒子径)と標準偏差のデータを下記の表1に示す。
針状炭酸ストロンチウム粒子分散液の光透過率を、分光光度計を用いて測定した。塩化メチレン中に大きな凝集粒子が生成していると分散液の光透過率は低下する。波長が400nm、500nm、600nm、700nm及び800nmの光の透過率を下記の表1に示す。
実施例1の(2)針状炭酸ストロンチウム粒子の表面処理において、針状炭酸ストロンチウム粒子水性スラリーに、側鎖にポリオキシアルキレン基を有するポリカルボン酸の無水物を添加し、次いでポリオキシエチレン−ステアリルアミンを添加する代わりに、親水性基と疎水性基とを含み、更に水中でアニオンを形成する基を有する界面活性剤(カオーセラ8110、花王株式会社)を20.3g(炭酸ストロンチウム粒子100質量部に対して10質量部)を添加したこと、即ち側鎖にポリオキシアルキレン基を有するポリカルボン酸の無水物を添加せずに、親水性基と疎水性基とを含み、更に水中でアニオンを形成する基を有する界面活性剤のみを添加したこと以外は、実施例1と同様にして針状炭酸ストロンチウム微粉末を製造した。得られた針状炭酸ストロンチウム微粉末について、塩化メチレン中での分散性を実施例1と同様に針状炭酸ストロンチウム粒子分散液の粒度分布と光透過率を測定することによって評価した。その結果を下記の表1に示す。
────────────────────────────────────────
粒度分布 光透過率(%)
────────────── ────────────────────
D90(nm) 標準偏差(%) 400nm 500nm 600nm 700nm 800nm
────────────────────────────────────────
実施例1 243.3 63.7 5.5 17.6 30.4 40.7 49.2
────────────────────────────────────────
比較例1 1691 304.1 0.4 0.8 1.2 1.6 1.4
────────────────────────────────────────
実施例1の(2)針状炭酸ストロンチウム粒子の表面処理において、針状炭酸ストロンチウム粒子水性スラリーに、ポリオキシエチレン−ステアリルアミンを添加しなかったこと、即ち側鎖にポリオキシアルキレン基を有するポリカルボン酸の無水物(マリアリムKM−0521)12.2g(炭酸ストロンチウム粒子100質量部に対して6質量部)のみを添加したこと以外は、実施例1と同様にしてポリカルボン酸の無水物で処理された針状炭酸ストロンチウム微粉末を製造した。得られた針状炭酸ストロンチウム微粉末を塩化メチレンに投入したところ、針状炭酸ストロンチウム粒子は塩化メチレン中に沈降してしまい、塩化メチレン中に分散できなかった。
(1)針状炭酸ストロンチウム粒子水性スラリーの製造
二酸化炭素ガスの流量を0.5L/分(水酸化ストロンチウム1gに対して2.9mL/分の流量)としたこと、炭酸ストロンチウム粒子水性懸濁液を95℃の温度で12時間加熱処理して炭酸ストロンチウム粒子を針状に成長させたこと以外は、実施例1の(1)と同様にして針状炭酸ストロンチウム粒子水性スラリーを製造した。
針状炭酸ストロンチウム粒子水性スラリーに、ポリカルボン酸の無水物(マリアリムKM−0521)を12.2g添加する代わりに、側鎖にポリオキシアルキレン基を有するポリカルボン酸の無水物(マリアリムSC−0505K、日油株式会社製)を16.24g(炭酸ストロンチウム粒子100質量部に対して8質量部)添加したこと、ポリオキシエチレン−ステアリルアミン(ナイミーンS204、HLB=8.0)の添加量(30.5g)を、46.69g(炭酸ストロンチウム100質量部に対して23質量部)としたこと以外は、実施例1の(2)と同様にして針状炭酸ストロンチウム粒子の表面処理を行なった。
実施例1の(3)に記載の方法により、針状炭酸ストロンチウム微粉末の粒子サイズとBET比表面積を測定した。その結果、長径の平均が32nmでアスペクト比の平均が2.3であって、長径の長さが200nm以上の針状粒子の含有率が個数基準で0.1%以下(1000個中0個)であり、さらに長径の長さが100nm以上の針状粒子の含有率は0.1%以下(1000個中0個)であった。また得られた針状炭酸ストロンチウム微粉末のBET比表面積を測定したところ、98.0m2/gであった。
実施例2の(2)針状炭酸ストロンチウム粒子の表面処理において、HLB値が8.0のポリオキシエチレン−ステアリルアミンを46.69g添加する代わりに、HLB値が5.0のポリオキシエチレン−ステアリルアミン(ナイミーンS202、日油株式会社製)を48.72g(炭酸ストロンチウム100質量部に対して24質量部)添加したこと以外は、実施例2と同様にして針状炭酸ストロンチウム微粉末を製造した。
実施例2の(2)針状炭酸ストロンチウム粒子の表面処理において、針状炭酸ストロンチウム粒子水性スラリーに、側鎖にポリオキシアルキレン基を有するポリカルボン酸の無水物を添加し、次いでポリオキシエチレン−ステアリルアミンを添加する代わりに親水性基と疎水性基を含み、さらに水中でアニオンを形成する基を有する界面活性剤(カオーセラ8110、花王株式会社)を48.72g(炭酸ストロンチウム粒子100質量部に対し24質量部)添加したこと、即ち側鎖にポリオキシアルキレン基を有するポリカルボン酸の無水物を添加せずに、親水性基と疎水性基とを含み、更に水中でアニオンを形成する基を有する界面活性剤のみを添加したこと以外は、実施例2と同様にして針状炭酸ストロンチウム微粉末を製造した。
(1)針状炭酸ストロンチウム微粉末の塩化メチレン中での分散性の評価
実施例2、3及び比較例3にて製造した針状炭酸ストロンチウム微粉末について、実施例1の(4)と同様にして針状炭酸ストロンチウム粒子分散液を調製し、得られた針状炭酸ストロンチウム粒子分散液について、炭酸ストロンチウム粒子の粒度分布と光透過率とを測定した。粒度分布のD50(篩下の累積粒度分布が50%となる粒子径)、D90と標準偏差のデータを下記の表2に示す。波長が400nm、500nm、600nm、700nm及び800nmの光の透過率を下記の表2に示す。
────────────────────────────────────────
粒度分布 光透過率(%)
───────────────── ──────────────────
D50(nm) D90(nm) 標準偏差(%) 400nm 500nm 600nm 700nm 800nm
────────────────────────────────────────
実施例2 49.8 87.7 18.9 22.2 40.5 54.1 64.2 71.2
実施例3 61.6 151.3 37.4 8.0 21.7 36.2 47.4 57.3
────────────────────────────────────────
比較例3 199.2 365.4 99.5 0.3 1.2 2.8 4.7 6.9
────────────────────────────────────────
実施例2及び3にて製造した針状炭酸ストロンチウム微粉末について、シクロヘキサン中での分散性を下記のようにして評価した。
試料の針状炭酸ストロンチウム微粉末0.2gをシクロヘキサン20gに投入し、超音波ホモジナイザーを用いて5分間分散処理して、炭酸ストロンチウム粒子濃度が1質量%の針状炭酸ストロンチウム粒子分散液を調製した。調製した針状炭酸ストロンチウム粒子分散液を直ちに、ガラス製容器(容量:9mL)に入れて15分間静置し、静置後の分散液を目視で観察した。その結果を下記の表3に示す。
────────────────────────────────────────
シクロヘキサン中での分散性の評価
────────────────────────────────────────
実施例2 針状炭酸ストロンチウム粒子は均一に分散したが、粒子の一部が沈殿した。
実施例3 針状炭酸ストロンチウム粒子は均一に分散し、粒子は全く沈殿しなかった。
────────────────────────────────────────
Claims (9)
- 長径の平均長さが150nm以下であって、平均アスペクト比が1.5以上であり、長径の長さが200nm以上の針状粒子の含有率が個数基準で5%以下にある針状炭酸ストロンチウム粒子の微粉末であって、針状炭酸ストロンチウム粒子の表面が、側鎖にポリオキシアルキレン基を有するポリカルボン酸もしくはその無水物と、ポリオキシアルキレン基及び炭化水素基を有するアミンとで処理されていることを特徴とする針状炭酸ストロンチウム微粉末。
- アミンのHLBが4〜10の範囲にある請求項1に記載の針状炭酸ストロンチウム微粉末。
- アミンがポリオキシエチレン−ステアリルアミンである請求項1に記載の針状炭酸ストロンチウム微粉末。
- 平均アスペクト比が2以上でかつ5以下である請求項1に記載の針状炭酸ストロンチウム微粉末。
- 平均長さが10nm以上である請求項1に記載の針状炭酸ストロンチウム微粉末。
- 水性媒体中に、長径の平均長さが150nm以下、平均アスペクト比が1.5以上、長径の長さが200nm以上の針状粒子の含有率が個数基準で5%以下にある針状炭酸ストロンチウム粒子が分散されてなる水性スラリーを用意する工程;該水性スラリーと側鎖にポリオキシアルキレン基を有するポリカルボン酸もしくはその無水物とを混合して、該ポリカルボン酸もしくはその無水物で処理された針状炭酸ストロンチウム粒子が分散されている水性スラリーを得る工程;さらに該ポリカルボン酸もしくはその無水物による処理がなされた針状炭酸ストロンチウム粒子が分散されている水性スラリーとポリオキシアルキレン基及び炭化水素基を有するアミンとを混合して、該アミンによる二回目の処理がなされた針状炭酸ストロンチウム粒子が分散されている水性スラリーを得る工程;そして該二回目の処理がなされた針状炭酸ストロンチウム粒子が分散されている水性スラリーを乾燥する工程を含む請求項1に記載の針状炭酸ストロンチウム微粉末の製造方法。
- アミンのHLBが4〜10の範囲にある請求項6に記載の製造方法。
- アミンがポリオキシエチレン−ステアリルアミンである請求項6に記載の製造方法。
- 水性スラリーと混合するアミンの量が、水性スラリーと混合したポリカルボン酸もしくはその無水物の量を1質量部としたときに1.1〜5.0質量部の範囲にある請求項6に記載の製造方法。