JP2012046670A - ゴム組成物の製造方法、ゴム組成物及びそれを用いたタイヤ - Google Patents
ゴム組成物の製造方法、ゴム組成物及びそれを用いたタイヤ Download PDFInfo
- Publication number
- JP2012046670A JP2012046670A JP2010191141A JP2010191141A JP2012046670A JP 2012046670 A JP2012046670 A JP 2012046670A JP 2010191141 A JP2010191141 A JP 2010191141A JP 2010191141 A JP2010191141 A JP 2010191141A JP 2012046670 A JP2012046670 A JP 2012046670A
- Authority
- JP
- Japan
- Prior art keywords
- resin
- rubber composition
- rubber
- mass
- producing
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
【解決手段】ゴム成分、樹脂、補強用充填剤及び架橋剤を含むゴム組成物の製造方法であって、前記樹脂を前記ゴム成分に添加してマスターバッチを作製する第一工程と、該マスターバッチに前記補強用充填剤を混練りして充填マスターバッチを作製する第二工程と、該充填マスターバッチに前記架橋剤を混練りする第三工程とを有するゴム組成物の製造方法である。
【選択図】なし
Description
しかしながら、これらの方法においても、前記高弾性化としては不十分であった。
すなわち本発明は、
〔1〕 ゴム成分、樹脂、補強用充填剤及び架橋剤を含むゴム組成物の製造方法であって、
前記樹脂を前記ゴム成分に添加してマスターバッチを作製する第一工程と、該マスターバッチに前記補強用充填剤を混練りして充填マスターバッチを作製する第二工程と、該充填マスターバッチに前記架橋剤を混練りする第三工程とを有するゴム組成物の製造方法、
〔2〕 前記第一工程が、ドライマスターバッチを作製する工程である〔1〕に記載のゴム組成物の製造方法、
〔3〕 前記樹脂が、熱硬化性樹脂である〔1〕または〔2〕に記載のゴム組成物の製造方法、
〔4〕 前記熱硬化性樹脂が、フェノール系熱硬化性樹脂である〔3〕に記載のゴム組成物の製造方法、
〔5〕 前記フェノール系熱硬化性樹脂が、ノボラック型フェノール樹脂、ノボラック型クレゾール樹脂、ノボラック型キシレノール樹脂、ノボラック型レゾルシノール樹脂及びこれらの樹脂をオイルで変性した樹脂、並びに、ノボラック型レゾルシン樹脂及びレゾール型フェノール樹脂を含む樹脂組成物から選ばれる少なくとも1種である〔4〕に記載のゴム組成物の製造方法、
〔6〕 前記フェノール系熱硬化性樹脂が、メチレン供与体を該フェノール系熱硬化性樹脂全量に対して0.1質量%以上80質量%以下含む〔4〕または〔5〕に記載のゴム組成物の製造方法、
〔7〕 前記ノボラック型レゾルシン樹脂が、レゾルシンとアルデヒド類とをモル比(アルデヒド類/レゾルシン)0.4以上0.8以下で反応させて得られるものである〔5〕に記載のゴム組成物の製造方法、
〔8〕 前記レゾール型フェノール系樹脂におけるジメチレンエーテル基量が、フェノール類に由来する芳香環同士を結合しているアルデヒド類に由来する全結合基量に対して、20モル%以上80モル%以下である〔5〕に記載のゴム組成物の製造方法、
〔9〕 前記樹脂のオイル変性に用いるオイルが、ロジン油、トール油、カシュー油、リノール酸、オレイン酸及びリノレイン酸から選ばれる少なくとも1種のオイルである〔5〕に記載のゴム組成物の製造方法、
〔10〕 前記樹脂の配合量が、ゴム成分100質量部に対して2質量部以上50質量部以下である〔1〕〜〔9〕のいずれかに記載のゴム組成物の製造方法、
〔11〕 前記補強用充填剤の配合量が、前記ゴム成分100質量部に対して5質量部以上200質量部以下である〔1〕〜〔10〕のいずれかに記載のゴム組成物の製造方法、
〔12〕 〔1〕〜〔11〕のいずれかに記載のゴム組成物の製造方法により得られるゴム組成物、及び、
〔13〕 〔12〕に記載のゴム組成物を用いたタイヤ、
を提供するものである。
<ゴム組成物の製造方法及びゴム組成物>
本実施形態のゴム組成物の製造方法は、ゴム成分、樹脂、補強用充填剤及び架橋剤を含むゴム組成物の製造方法であって、前記樹脂を前記ゴム成分に添加してマスターバッチを作製する第一工程と、該マスターバッチに前記補強用充填剤を混練りして充填マスターバッチを作製する第二工程と、該充填マスターバッチに前記架橋剤を混練りする第三工程とを有するものである。
本実施形態のゴム組成物の製造方法に使用可能なゴム成分としては、天然ゴム(NR)及び種々の合成ゴムから選択される少なくとも1種が挙げられる。上記合成ゴムの具体例としては、ポリイソプレンゴム(IR)、スチレン・ブタジエン共重合ゴム(SBR)、ポリブタジエンゴム(BR)、ブチルゴム(IIR)、ハロゲン化ブチルゴム(Br−IIR、Cl−IIR)、エチレン−プロピレン−ジエンゴム(EPDM)、架橋ポリエチレンゴム、クロロプレンゴム及びニトリルゴム等が挙げられる。これらのゴム成分は、一種単独で用いてもよいし、二種以上を混合して用いてもよく、これらのいずれを用いても後述する熱硬化性樹脂の硬化等により、高弾性でかつ破断伸びが大きいといった本実施形態の特有の効果が得られる。
また上記のうちでは、天然ゴム(NR)、スチレン・ブタジエン共重合ゴム(SBR)、ポリブタジエンゴム(BR)などのジエン系ゴムを用いることが、より高弾性でかつ破断伸びが大きい特性を有するゴム組成物が得られる点から好ましい。
本実施形態のゴム組成物には、樹脂が含有される。該樹脂は特に制限されないが、熱硬化性樹脂が好ましく用いられる。該熱硬化性樹脂としては、例えば、メラミン樹脂(メラミン−フォルムアルデヒド樹脂)、ユリア樹脂(尿素−フォルムアルデヒド樹脂)、ポリカーボネート樹脂、フェノール系熱硬化性樹脂、エポキシ樹脂、不飽和ポリエステル樹脂、アクリル樹脂、グアナミン樹脂、ポリウレタン樹脂等を挙げることができ、その他、これら樹脂に匹敵する硬度を有する樹脂も使用することが可能である。
また、上記フェノール系熱硬化性樹脂のオイル変性に用いる好適なオイルとしては、ロジン油、トール油、カシュー油、リノール酸、オレイン酸及びリノレイン酸から選ばれる少なくとも1種のオイルが挙げられる。
これらの中でも、硬化速度が速く、より高弾性化したゴム組成物が得られるという点から、ヘキサメチレンテトラミン、ヘキサメトキシメチルメラミンの使用が望ましい。
上記含有量は、より好ましくは5質量%以上70質量%以下であり、さらに好ましくは10質量%以上60質量%以下である。
前記ノボラック型レゾルシン樹脂等単独では、末端にメチロール基がないので硬化剤なしで硬化することができない。一方、レゾール型フェノール系樹脂は末端等にメチロール基を有するので、硬化剤がなくても硬化することができる。ただし、レゾール型フェノール系樹脂単独では樹脂の硬化性が遅く、ゴムの加硫時に樹脂の硬化が十分に進行しないので、ノボラック型レゾルシン樹脂及びレゾール型フェノール系樹脂を含む樹脂組成物とすることで、硬化剤を用いることなくゴム組成物における弾性率を増大させ、しかも大きな破断時伸びをも得ることができる。
これらのフェノール類の中でも、経済的に有利なフェノール、クレゾール類、及びビスフェノールAから選ばれるものが好ましい。
これらのアルデヒド類の中でも、反応性が優れ、安価であるホルムアルデヒド、パラホルムアルデヒドから選ばれるものが好ましい。
前記合成する際に用いる触媒としては、例えば、水酸化ナトリウム、水酸化リチウム、水酸化カリウムなどのアルカリ金属の水酸化物;カルシウム、マグネシウム、バリウムなどアルカリ土類金属の酸化物及び水酸化物;炭酸ナトリウム、アンモニア水、トリエチルアミン、ヘキサメチレンテトラミンなどのアミン類;酢酸マグネシウムや酢酸亜鉛などの二価金属塩;などの物質を単独または2種以上併用することができる。
各結合基量は、測定されたスペクトルからアセトンのピーク(2.04ppm)を基準に、各々メチレン基(約3.8ppm)、ジメチレンエーテル基(約4.5ppm)、メチロール基(約5.0ppm)とし、これらピークの積分強度比を、メチレン基、メチロール基については1/2倍、ジメチレンエーテル基については1/4倍とした値の比率より、アルデヒド類に由来する全結合基量(メチレン基量、ジメチレンエーテル基量及びメチロール基量の和)に対するジメチレンエーテル基量の比率(モル%)を算出した。
これらのレゾルシン類の中でも、経済的に有利なレゾルシン及びメチルレゾルシン類から選ばれるものが好ましい。
ノボラック型レゾルシン樹脂の含有量を上記範囲とすることにより、本実施形態における樹脂成分の硬化性を向上させることができ、高弾性で発熱性の低いゴム組成物を得ることができる。
前記充填剤の添加量としては、樹脂組成物100質量部に対して、充填剤を1質量部以上40質量部以下で使用するのが好ましい。これにより、ゴム組成物の弾性率や破断時伸びを阻害することなく、樹脂組成物の放置によるブロッキング性を改善することができる。
本実施形態のゴム組成物における前記樹脂の配合量は、前記ゴム成分100質量部に対して2質量部以上50質量部以下とすることが好ましい。配合量が上記範囲にあると、ゴム組成物の柔軟性が損なわれることなく高弾性なゴム組成物を得ることができる。
上記配合量は、3質量部以上45質量部以下とすることがより好ましく、5質量部以上40質量部以下とすることがさらに好ましく、10質量部以上30質量部以下が特に好ましい。
本実施形態における補強用充填剤としては、従来ゴム組成物に用いられているもののうちから適宜選択して用いることができる。具体的には例えば、カーボンブラック、シリカ及び下記一般式(I)で表される無機化合物を挙げることができる。
nM・xSiOy・zH2O ・・・ (I)
上記式中、Mは、アルミニウム、マグネシウム、チタン、カルシウムおよびジルコニウムからなる群から選ばれる金属、これらの金属の酸化物または水酸化物、およびそれらの水和物、またはこれらの金属の炭酸塩から選ばれる少なくとも一種であり、n、x、yおよびzは、それぞれ1〜5の整数、0〜10の整数、2〜5の整数および0〜10の整数である。
これら補強用充填剤は、一種を単独で用いても、二種以上を混合して用いてもよい。
また、前記シリカは特に限定されないが、湿式シリカ、乾式シリカ、コロイダルシリカが好ましい。これらは単独に又は混合して使用することができる。
また、一般式(I)で表される無機化合物としては、Mがアルミニウム金属、アルミニウムの酸化物又は水酸化物、それらの水和物、及びアルミニウムの炭酸塩から選ばれる少なくとも一種のものが好ましい。
中でも補強用充填剤としては、カーボンブラック、シリカ及び水酸化アルミニウムが好ましい。
上記配合量は、10質量部以上180質量部以下とすることがより好ましく、20質量部以上150質量部以下とすることがさらに好ましい。
本実施形態における架橋剤は、加硫剤および加硫促進剤を含む概念である。加硫剤としては、硫黄、硫黄含有化合物等が挙げられる。その配合量は、通常ゴム組成物に配合される範囲内とすることができ、例えば、前記ゴム成分100質量部に対し、硫黄分として0.1質量部以上10質量部以下が好ましく、より好適には1質量部以上5質量部以下である。
また、加硫促進剤としては、例えば、1,3−ジフェニルグアニジン、ジベンゾチアジルジスルフィド、N−t−ブチル−2−ベンゾチアジルスルフェンアミド、N−シクロヘキシル−2−ベンゾチアゾリルスルフェンアミド、N,N’−ジシクロヘキシル−2−ベンゾチアゾリルスルフェンアミド、2−メルカプトベンゾチアゾール等が挙げられる。加硫促進剤の配合量についても、通常ゴム組成物に配合される範囲内とすることができ、例えば、前記ゴム成分100質量部に対し、0.1質量部以上7質量部以下とすることが好ましく、より好適には1質量部以上5質量部以下である。
本実施形態のゴム組成物の製造方法においては、その他、ゴム業界で一般に使用されている配合剤、例えば、プロセスオイル、老化防止剤、軟化剤、酸化亜鉛、ステアリン酸、オゾン劣化防止剤、着色剤、帯電防止剤、滑剤、酸化防止剤、カップリング剤、発泡剤、発泡助剤等を、本発明の目的を害しない範囲で適宜配合することができる。これら配合剤としては、市販品を好適に使用することができる。
更に、前記老化防止剤としては、例えば3C(N−イソプロピル−N’−フェニル−p−フェニレンジアミン、6C[N−(1,3−ジメチルブチル)−N'−フェニル−p−フェニレンジアミン]、AW(6−エトキシ−2,2,4−トリメチル−1,2−ジヒドロキノリン)、ジフェニルアミンとアセトンの高温縮合物等を挙げることができる。その使用量は、ゴム成分100質量部に対して、0.1質量部以上6.0質量部以下が好ましく、更に好ましくは0.3質量部以上5.0質量部以下である。
本実施形態のゴム組成物の製造方法は、前述の第一工程、第二工程及び第三工程を有する。
−第一工程−
本工程は、前記樹脂を前記ゴム成分に添加してマスターバッチを作製する工程である。本実施形態では、ゴム組成物における樹脂の分散性を高めるため、さらには樹脂による補強用充填剤表面の被覆をなるべく避けるために、補強用充填剤の混合前に予めゴム成分及び樹脂のマスターバッチ(ゴム・樹脂複合体)を作製する。
上記ゴム成分及び樹脂を含むマスターバッチを製造する方法については特に制限はなく、ウェットマスターバッチまたはドライマスターバッチによって得ることができる。ここで、ウェットマスターバッチとは溶媒等を用いて原料成分を液状として混合したマスターバッチであり、ドライマスターバッチとは原料成分を固体状のまま機械的に混合したマスターバッチである。混合後の乾燥等の後処理が不要であること、後工程を連続的に行うことができることなどから、ドライマスターバッチが好ましい。
(ドライマスターバッチの場合)
ゴム成分及び樹脂を含むドライマスターバッチは、通常、ブロッック状の天然ゴムや合成ゴムとフェノール系熱硬化性樹脂などの熱硬化性樹脂とを混練りすることによって得ることができる(ゴム・樹脂作製工程)。代表的な混練機(第一混練機)としては、ロール、接線式(非噛合式)インターナルミキサー(以下接線式バンバリーミキサーと称することがある)、または二軸混練押出機が挙げられるが、ブロック状のゴムの噛み込みがよいロールや接線式バンバリーミキサーが好ましい。
また、ゴム成分及び樹脂を含むウェットマスターバッチの製法については後に詳述するが、用いる混練機としては、脱水乾燥、充填剤のゴム成分への分散が同時に可能な二軸混練押出機が好ましい。また、スクイザや遠心吸水機、エクスパンジョン、乾燥機を組み合わせてもよい。
次に、上記ゴム成分及び樹脂を含むウェットマスターバッチの作製方法について説明する。
この場合には、(a)ゴム配合材料を液状とする工程、(a’)これらを混合する工程、(a”)混合液を凝固処理する工程、(b)前記(a)工程で形成された凝固物を取り出す工程、及び(c)前記(b)工程で取り出された凝固物を第一混練機を用いて捏和し乾燥させると共に樹脂を分散させる工程、を経ることが好適である。
この工程は、ゴム配合材料を液状のゴム液とする工程である。
当該(a)工程において用いられるゴム液としては、天然ゴムラテックス及び/または合成ゴムラテックス、あるいは溶液重合による合成ゴムの有機溶媒溶液などを挙げることができるが、これらの中で、得られるウェットマスターバッチの性能や製造しやすさなどの観点から、天然ゴムラテックス及び/または合成ゴムラテックスが好適である。
・(a’)工程
この工程は、前記(a)工程で得られた液状のゴム材料と樹脂とを混合する工程である。
本実施形態におけるウェットマスターバッチの作製方法においては、上記ゴム液に、前述の樹脂の中から選ばれる少なくとも一種の樹脂を、ホモミキサー等を用いて分散させる。具体的には、例えば、ホモミキサー中に液状の熱硬化性樹脂を入れ、攪拌しながら、ラテックスを滴下する方法や、逆にラテックスを攪拌しながら、これに液状の熱硬化性樹脂を滴下する方法がある。また、一定の流量割合をもった熱硬化性樹脂液流とラテックス流とを、激しい水力攪拌の条件下で混合する方法などを用いることもできる。
・(a”)工程−
この工程は、前記混合工程で得られた混合液を凝固処理する工程である。具体的には、前記のようにして得られた熱硬化性樹脂を含むゴム液を凝固処理して、凝固物を形成させる。この凝固方法としては、従来公知の方法、例えば蟻酸、硫酸などの酸や、塩化ナトリウムなどの塩の凝固剤を熱や攪拌などによるせん断力を与えることによって行われる。また、複数の手段を組み合わせてもよい。
(b)工程は、前記(a)工程で形成された凝固物を、従来公知の固液分離手段を用いて取り出し、充分に洗浄する工程である。洗浄は、通常水洗法が採用される。
(c)工程は、前記(b)工程で取り出され、充分に洗浄された凝固物を第一混練機を用いて機械的せん断力をかけながら捏和し乾燥させると共に充填剤を分散させる工程である。
上記(c)工程においては、混練機を用いて機械的せん断力をかけながら捏和し乾燥させるため、工業的生産性の観点から、連続的に操作することが好ましい。単軸スクリュを備える装置を用いることもできるが、同方向回転、あるいは異方向回転の多軸混練押出機を用いることがより好ましく、特に二軸混練押出機を用いることが好ましい。
本工程は、前記の第一工程で得られたマスターバッチに前記補強用充填剤を混練りして充填マスターバッチを作製する工程である。具体的には、前述のマスターバッチ(ドライ・ウェット)に対して、第二混練機を用いて、さらに補強用充填剤を混合することが好適である。
前記第二混練機としては、2本のローターが互いに噛み合っている噛合式インターナルミキサー(以下、噛合式バンバリミキサーと称することがある)接線式バンバリミキサー、オープンロール及びニーダーの中から選ばれるいずれかであることが好ましい。
また、通常、二軸押出混練機に代表される連続式の混練機(連続式混練装置)はバンバリミキサーに代表されるバッチ式の混練機(バッチ式混練装置)に比べて単位体積当りの配合量のバラツキが大きく、補強用充填剤をゴム組成物中に均一に分散させるためにはバンバリミキサーのようなバッチ式の混練機が好ましい。
なお、この第二工程の時点で、補強用充填剤に加え架橋剤を除く前記ゴム用配合剤を加えてもよい。また、上記ウェットマスターバッチに関する、第一混練機及び第二混練機については、前述の説明と同様である。
本工程は、前記の第二工程で得られた充填マスターバッチに前記架橋剤を混練りする工程である。
混練りに用いる好適な混練機等は、前記第二工程で用いられるものと基本的に同様である。また、用いる架橋剤種や混練り条件などによっては、前記第二工程と第三工程とを1つの工程として行ってもよい。
本実施形態のタイヤは、前記のゴム組成物を用いたものである。すなわち、本実施形態のタイヤは、前記ゴム組成物をタイヤ構成部材のいずれかに含有させてなる。該タイヤ構成部材としては、例えば、トレッド、アンダートレッド、サイドウォール、カーカスコーティングゴム、ベルトコーティングゴム、ビードフィラーゴム、チェーファー、ビードコーティングゴム、クッションゴム等が挙げられる。
このようにして得られた本実施形態の空気入りタイヤは、補強性、耐摩耗性などに優れ、かつ軽量化が図られている。
(レゾール型フェノール樹脂)
攪拌装置、還流冷却器及び温度計を備えた反応装置に、フェノール1000部及び37%ホルムアルデヒド水溶液1294部を加え(モル比(ホルムアルデヒド/フェノール)=1.50)、さらに酢酸亜鉛5部を加えた。1時間還流させ、反応によって生じる水の真空除去を行い、90℃になった時点でさらに1時間反応させ、常温(25℃)で固形のレゾール型フェノール樹脂1145部を得た。
このレゾール型フェノール樹脂について、前述の条件で1H−NMRにて解析した結果、アルデヒドに由来する全結合基量に対するジメチレンエーテル基量は、45モル%であった。
攪拌装置、還流冷却器及び温度計を備えた反応装置に、レゾルシン1000部及びシュウ酸3部を加えた。内温が100℃になるまで加熱して、温度到達後、37%ホルムアルデヒド水溶液369部を30分間かけて逐添した(モル比(ホルムアルデヒド/フェノール)=0.50)。その後1時間還流させ、反応によって生じる水の常圧除去、真空除去を170℃になるまで行い、常温で固形のノボラック型レゾルシン樹脂1040部を得た。
上記で得られた各ノボラック型レゾルシン樹脂及びレゾール型フェノール系樹脂を、混合質量比(ノボラック型レゾルシン樹脂/レゾール型フェノール系樹脂)が30/70となるように混合し、衝撃式粉砕機により粉砕して、粉末状の樹脂組成物(1)を得た。
第1表に示す配合処方に従い、天然ゴムと各種フェノール系熱硬化性樹脂とを、8インチのオープンロールを用いて80℃にて混練して、ドライマスターバッチ(1)〜(5)を作製した(第一工程)。
1)天然ゴム:RSS#3
2)カーボンブラック:旭カーボン(株)製、旭#70(N330)
3)ノボラック型フェノール樹脂:住友ベークライト(株)製、スミライトレジン「PR50235」
4)カシュー変性フェノール樹脂:住友ベークライト(株)製、スミライトレジン「PR12686」
5)フェノール系樹脂組成物:樹脂組成物の製造で得た樹脂組成物(1)
下記表2に示す配合処方のうち、亜鉛華、加硫促進剤及び硫黄を除く成分を、バンバリーミキサーを使用して混練りし、充填マスターバッチを得た(第二工程)。次に、8インチのオープンロールを用いて、この充填マスターバッチに亜鉛華、加硫促進剤及び硫黄を添加して混練りし、未加硫のゴム組成物を得た(第三工程)。次いで、厚さ2mmにシーティングした後、145℃で30分間加硫した。得られた加硫ゴムに対して以下の方法での各特性を評価した。
得られた加硫ゴムを、JISダンベル状3号形に打ち抜いたサンプルについて、JISK6251に準拠して25℃で引っ張り試験を行い、破断時伸びと破断強度とを測定した。結果を表2に示す。
得られた加硫ゴムについて、東洋精機社製スぺクトロメータを用い、初期荷重100g、歪み2%、測定周波数50Hz、測定温度60℃にて動的弾性率E’を測定した。結果を表2に示す。
実施例1において、ゴム組成物として、表2に示した各配合処方からなるものを各々用いた以外は、実施例1と同様にして加硫ゴムを作製し、同様の評価を行った。
結果を表2にまとめて示す。
1)天然ゴム:RSS#3
2)ノボラック型フェノール樹脂:住友ベークライト(株)製、スミライトレジン「PR50235」
3)カシュー変性フェノール樹脂:住友ベークライト(株)製、スミライトレジン「PR12686」
4)フェノール系樹脂組成物:樹脂組成物の製造で得た樹脂組成物(1)
5)カーボンブラック:旭カーボン(株)製、旭#70(N330)
6)老化防止剤:N−(1,3−ジメチルブチル)−N’−フェニル−p−フェニレンジアミン、大内新興化学工業社製、商品名「ノクラック6C」
7)サイテック(株)製、商品名「CYREZ964RPC」
8)加硫促進剤:N−シクロヘキシル−2−ベンゾチアジルスルフェンアミド、大内新興化学工業社製、商品名「ノクセラーCZ」
9)硫黄:フレキシス社製、商品名「CRYSTEX HS OT 10」
Claims (13)
- ゴム成分、樹脂、補強用充填剤及び架橋剤を含むゴム組成物の製造方法であって、
前記樹脂を前記ゴム成分に添加してマスターバッチを作製する第一工程と、該マスターバッチに前記補強用充填剤を混練りして充填マスターバッチを作製する第二工程と、該充填マスターバッチに前記架橋剤を混練りする第三工程とを有するゴム組成物の製造方法。 - 前記第一工程が、ドライマスターバッチを作製する工程である請求項1に記載のゴム組成物の製造方法。
- 前記樹脂が、熱硬化性樹脂である請求項1または2に記載のゴム組成物の製造方法。
- 前記熱硬化性樹脂が、フェノール系熱硬化性樹脂である請求項3に記載のゴム組成物の製造方法。
- 前記フェノール系熱硬化性樹脂が、ノボラック型フェノール樹脂、ノボラック型クレゾール樹脂、ノボラック型キシレノール樹脂、ノボラック型レゾルシノール樹脂及びこれらの樹脂をオイルで変性した樹脂、並びに、ノボラック型レゾルシン樹脂及びレゾール型フェノール樹脂を含む樹脂組成物から選ばれる少なくとも1種である請求項4に記載のゴム組成物の製造方法。
- 前記フェノール系熱硬化性樹脂が、メチレン供与体を該フェノール系熱硬化性樹脂全量に対して0.1質量%以上80質量%以下含む請求項4または5に記載のゴム組成物の製造方法。
- 前記ノボラック型レゾルシン樹脂が、レゾルシンとアルデヒド類とをモル比(アルデヒド類/レゾルシン)0.4以上0.8以下で反応させて得られるものである請求項5に記載のゴム組成物の製造方法。
- 前記レゾール型フェノール系樹脂におけるジメチレンエーテル基量が、フェノール類に由来する芳香環同士を結合しているアルデヒド類に由来する全結合基量に対して、20モル%以上80モル%以下である請求項5に記載のゴム組成物の製造方法。
- 前記樹脂のオイル変性に用いるオイルが、ロジン油、トール油、カシュー油、リノール酸、オレイン酸及びリノレイン酸から選ばれる少なくとも1種のオイルである請求項5に記載のゴム組成物の製造方法。
- 前記樹脂の配合量が、ゴム成分100質量部に対して2質量部以上50質量部以下である請求項1〜9のいずれかに記載のゴム組成物の製造方法。
- 前記補強用充填剤の配合量が、前記ゴム成分100質量部に対して5質量部以上200質量部以下である請求項1〜10のいずれかに記載のゴム組成物の製造方法。
- 請求項1〜11のいずれかに記載のゴム組成物の製造方法により得られるゴム組成物。
- 請求項12に記載のゴム組成物を用いたタイヤ。