JP2010157447A - 酸化錫層を有する白色導電性無機粉末とその製造方法 - Google Patents
酸化錫層を有する白色導電性無機粉末とその製造方法 Download PDFInfo
- Publication number
- JP2010157447A JP2010157447A JP2008335477A JP2008335477A JP2010157447A JP 2010157447 A JP2010157447 A JP 2010157447A JP 2008335477 A JP2008335477 A JP 2008335477A JP 2008335477 A JP2008335477 A JP 2008335477A JP 2010157447 A JP2010157447 A JP 2010157447A
- Authority
- JP
- Japan
- Prior art keywords
- inorganic powder
- white
- powder
- conductive
- stannous
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
【解決手段】酸化第二錫表面層を有する白色無機粉末に、第一錫イオン含有溶液を加えてペーストにし、または、酸化第二錫表面層を有する白色無機粉末と第一錫イオン溶液をスラリーにし、該スラリーまたは該スラリーを乾燥したものを、非酸化性の第一錫イオン可溶性溶媒雰囲気下で加熱して酸化第二錫を還元し、導電性酸化錫層を形成し、白色無機粉末表面に導電性酸化錫層を有し、粉末体積抵抗が104Ω・cm以下であることを特徴とする導電性無機粉末を製造する方法、およびその導電性無機粉末。
【選択図】なし
Description
〔1〕白色無機粉末表面に導電性酸化錫層を有し、粉末体積抵抗が104Ω・cm以下であることを特徴とする白色導電性無機粉末。
〔2〕粉末の色調が、Lab表色系においてL値が70以上である上記[1]の白色導電性無機粉末。
〔3〕白色無機粉末表面の酸化第二錫層に第一錫イオンを接触させて酸化第二錫を還元することによって導電性酸化錫層を形成することを特徴とする白色導電性無機粉末の製造方法。
〔4〕酸化第二錫表面層を有する白色無機粉末に、第一錫イオン含有溶液を加えてペーストにすることによって酸化第二錫を還元して導電性酸化錫層を形成する上記[3]の製造方法。
〔5〕酸化第二錫表面層を有する白色無機粉末と第一錫イオン溶液をスラリーにし、該スラリーまたは該スラリーを乾燥したものを、非酸化性の第一錫イオン可溶性溶媒雰囲気下で加熱して酸化第二錫を還元し、導電性酸化錫層を形成する上記[3]の製造方法。
〔6〕上記[1]または上記[2]の白色導電性無機粉末を分散してなる分散液。
〔7〕上記[1]または上記[2]の白色導電性無機粉末を含有する膜組成物。
本発明の白色導電性無機粉末は、白色無機粉末表面に導電性酸化錫層を有し、粉末体積抵抗が104Ω・cm以下であることを特徴とする白色導電性無機粉末である。
〔イ〕酸化第二錫表面層を有する白色無機粉末に、第一錫イオン含有溶液を加えてペーストにすることによって酸化第二錫を還元して酸素欠陥を形成する方法。
〔ロ〕酸化第二錫表面層を有する白色無機粉末と第一錫イオン溶液をスラリーにし、該スラリーまたは該スラリーを乾燥したものを、非酸化性の第一錫イオン可溶性溶媒雰囲気下で加熱して酸化第二錫を還元して酸素欠陥を形成する方法。
SnO2 + 4HCl → SnCl2 + 2H2O + Cl2
本発明の白色導電性無機粉末は、第一錫イオンの可溶性溶媒中あるいは可溶性溶媒雰囲気下で、酸化第二錫表面層に第一錫イオンを接触させて還元させることによって製造することができる。
酸化チタン粉末(ルチル型)150gを水1Lに分散させ、90℃に加温した。塩化第二錫50%溶液100g(0.19mol)と、1N水酸化ナトリウム溶液とを同時に撹拌下にpH3〜4を保ちながら30分で滴下した。これを濾別回収し、乾燥後に大気中600℃で1時間熱処理し、粉末表面に酸化第二錫層を有する酸化チタン粉末を得た。
これを塩化第一錫二水塩4.3g(0.019mol%=10mol%)をイオン交換水200mlに溶解した第一錫イオン溶液に加えて乳鉢で練り、ペースト化した。これを90℃で乾燥して導電性無機粉末を得た。塩化第一錫を2.1g(5mol%)、1.1g(2.5mol%)に変えた以外は上記操作と同様にしてペーストを作成し、乾燥して導電性無機粉末を得た。これらの粉末体積抵抗を測定した。また粉末のL値を測定した。この結果を表1に示す。
酸化チタン粉末(ルチル型)150gを水1Lに分散させ、90℃に加温した。塩化第二錫50%溶液100g(0.19mol)と、1N水酸化ナトリウム溶液とを同時に撹拌下にpH3〜4を保ちながら30分で滴下した。これを濾別回収し、乾燥後に大気中600℃で1時間熱処理し、粉末表面に酸化第二錫層を有する酸化チタン粉末を得た。
これを、50%ホウフッ化第一錫溶液11.1g(0.019mol%=10mol%)をイオン交換水200mlに溶解した第一錫イオン溶液に加えて乳鉢で練り、ペースト化した。これを90℃で乾燥して導電性無機粉末を得た。また、50%ホウフッ化第一錫溶液をおのおの5.6g(5mol%)、2.8g(2.5mol%)に変えた以外は上記操作と同様にしてペーストを作成し、乾燥して導電性無機粉末を得た。これらの粉末体積抵抗を測定した。また粉末のL値を測定した。この結果を表2に示す。
酸化チタン粉末(ルチル型)150gを水1Lに分散させ、90℃に加温した。塩化第二錫50%溶液100g(0.19mol)と、1N水酸化ナトリウム溶液とを同時に撹拌下にpH3〜4を保ちながら30分で滴下した。これを濾別回収し、乾燥後に大気中600℃で1時間熱処理し、粉末表面に酸化第二錫層を有する酸化チタン粉末を得た。
これを、フッ化第一錫3.0g(0.019mol%=10mol%)をイオン交換水200mlに溶解した第一錫イオン溶液に加えて乳鉢で練り、ペースト化した。これを90℃で乾燥して導電性無機粉末を得た。フッ化第一錫をおのおの1.5g(5mol%)、0.7g(2.5mol%)に変えた以外は上記操作と同様にしてペーストを作成し、乾燥して導電性無機粉末を得た。これらの粉末体積抵抗を測定した。また粉末のL値を測定した。この結果を表3に示す。
酸化チタン粉末(ルチル型)150gを水1Lに分散させ、90℃に加温した。塩化第二錫50%溶液100g(0.19mol)と、1N水酸化ナトリウム溶液とを同時に撹拌下にpH3〜4を保ちながら30分で滴下した。これを濾別回収し、乾燥後に大気中600℃で1時間熱処理し、粉末表面に酸化第二錫層を有する酸化チタン粉末を得た。
これを、硫酸第一錫4.1g(0.019mol%=10mol%)をイオン交換水200mlに溶解した第一錫イオン溶液に加えて乳鉢で練り、ペースト化した。これを90℃で乾燥して導電性無機粉末を得た。硫酸第一錫をおのおの2.0g(5mol%)、1.0g(2.5mol%)に変えた以外は上記操作と同様にしてペーストを作成し、乾燥して導電性無機粉末を得た。これらの粉末体積抵抗を測定した。また粉末のL値を測定した。この結果を表4に示す。
Claims (7)
- 白色無機粉末表面に導電性酸化錫層を有し、粉末体積抵抗が104Ω・cm以下であることを特徴とする白色導電性無機粉末。
- 粉末の色調が、Lab表色系においてL値が70以上である請求項1の白色導電性無機粉末。
- 白色無機粉末表面の酸化第二錫層に第一錫イオンを接触させて酸化第二錫を還元することによって導電性酸化錫層を形成することを特徴とする白色導電性無機粉末の製造方法。
- 酸化第二錫表面層を有する白色無機粉末に、第一錫イオン含有溶液を加えてペーストにすることによって酸化第二錫を還元して導電性酸化錫層を形成する請求項3の製造方法。
- 酸化第二錫表面層を有する白色無機粉末と第一錫イオン溶液をスラリーにし、該スラリーまたは該スラリーを乾燥したものを、非酸化性の第一錫イオン可溶性溶媒雰囲気下で加熱して酸化第二錫を還元し、導電性酸化錫層を形成する請求項3の製造方法。
- 請求項1または請求項2の白色導電性無機粉末を分散してなる分散液。
- 請求項1または請求項2の白色導電性無機粉末を含有する膜組成物。