JP2009029964A - 吸水性を有するフィルム - Google Patents
吸水性を有するフィルム Download PDFInfo
- Publication number
- JP2009029964A JP2009029964A JP2007196438A JP2007196438A JP2009029964A JP 2009029964 A JP2009029964 A JP 2009029964A JP 2007196438 A JP2007196438 A JP 2007196438A JP 2007196438 A JP2007196438 A JP 2007196438A JP 2009029964 A JP2009029964 A JP 2009029964A
- Authority
- JP
- Japan
- Prior art keywords
- film
- mass
- water
- resin composition
- particle size
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
【解決手段】(A)ポリエチレン系樹脂組成物100質量部、および(B)吸水性フィラー5〜200質量部を含む吸水性樹脂組成物の層から成るフィルムであって、ポリエチレン系樹脂組成物(A)は、(A−1)下記(i)〜(iv)の特性を有するエチレン系重合体99〜60質量%、(i)DSC融解曲線における最も高い温度側のピークトップ融点(Tm)が110℃以上である、(ii)DSC融解曲線における融解熱量(ΔH)が90〜180J/gである、(iii)110℃における結晶化度(Xc110)が10〜60%である、および(iv)MFR(190℃、21.18N)が0.1g/10分以上10g/10分未満である、および、(A−2)酸変性樹脂1〜40質量%を含み、ここで、成分(A−1)と成分(A−2)の量の合計が100質量%であり、吸水性フィラー(B)は、30μm以下の粒子径(D99)および20μm以下の粒子径(D50)を有するところのフィルム。
【選択図】なし
Description
(A)ポリエチレン系樹脂組成物100質量部、および
(B)吸水性フィラー5〜200質量部
を含む吸水性樹脂組成物の層から成るフィルムであって、ポリエチレン系樹脂組成物(A)は、
(A−1)下記(i)〜(iv)の特性を有するエチレン系重合体99〜60質量%、
(i)DSC融解曲線における最も高い温度側のピークトップ融点(Tm)が110℃以上である、
(ii)DSC融解曲線における融解熱量(ΔH)が90〜180J/gである、
(iii)110℃における結晶化度(Xc110)が10〜60%である、および
(iv)MFR(190℃、21.18N)が0.1g/10分以上10g/10分未満である
および、
(A−2)酸変性樹脂1〜40質量%
を含み、ここで、成分(A−1)と成分(A−2)の量の合計が100質量%であり、
吸水性フィラー(B)は、30μm以下の粒子径(D99)および20μm以下の粒子径(D50)を有する、ここでD99およびD50はそれぞれ、粒子径分布において粒子径の小さい方から累積して99質量%および50質量%になる点における粒子径を言う、ところのフィルムである。
本発明におけるポリエチレン系樹脂組成物は、エチレン系重合体(A−1)および酸変性樹脂(A−2)を含む。
エチレン系重合体は、十分な耐熱性およびフィラー受容性を有するように、下記(i)〜(iv)を満たすことが必要である。
(i)DSC融解曲線における最も高い温度側のピークトップ融点(Tm)が110℃以上である、
(ii)DSC融解曲線における融解熱量(ΔH)が90〜180J/gである、
(iii)110℃における結晶化度(Xc110)が10〜60%である、および
(iv)MFR(190℃、21.18N)が0.1g/10分以上10g/10分未満である。
酸変性樹脂は、疎水性であるエチレン系重合体(A−1)と親水性である吸水性フィラー(B)との混和性を改良して吸水性フィラーの分散を促進し、製膜したときにフィルムにブツなどの欠点が発生しないようにするための成分である。
吸水性フィラーは、吸水性を有し、溶剤に溶出しない安定的なものであればどのようなものでも良い。例えば、硫酸マグネシウム、酸化アルミニウム、シリカゲル、石灰、焼成ハイドロタルサイトおよびモレキュラーシーブが挙げられ、これらを、単独で、または2種以上の組み合わせで使用することができる。
(1)DSC融解曲線における最も高い温度側のピークトップ融点(Tm)が125℃以上である、および
(2)120℃における結晶化度(Xc120)が55%以上である。
上記ピークトップ融点は、より好ましくは130℃以上、さらに好ましくは135℃以上であり、上記結晶化度は、より好ましくは60%以上、さらに好ましくは65%以上である。
吸水性樹脂組成物の層から成るフィルムの製造:
表1に示す配合量(質量部)の成分をドライブレンドし、これを(株)モリヤマの20L加圧ニーダーにより溶融混練して吸水性樹脂組成物を得た後、造粒機によりペレット化した。排出温度(溶融混練温度)は220℃であり、造粒はホットカット法で行った。次いで、得られたペレットを、株式会社池貝製のPCM−46二軸押出機と東芝機械株式会社製のTダイを用いて製膜し、膜厚50μmのフイルムを得た。得られたフイルムは、露点温度−50℃以下にしたガス置換型グローブボックス(アズワン株式会社のSG−1000)の中に保管した。なお、製膜は、Tダイ出口樹脂温度200℃、チルロール温度40℃および引取速度10m/分の条件で真空ベントを使用して行った。得られたフィルムについて、下記(1)〜(6)の評価試験を行った。結果を表1に示す。
A4サイズに裁断したフィルム5枚を目視で観察し、以下の基準で判定した。
○:発泡および穴開きがなく、直径0.1mm以上のブツもない
△:発泡および穴開きがなく、直径0.5mm以上のブツもないが、直径0.1mm〜0.5mm未満のブツが1〜10個ある
×:発泡または穴開きがあり、直径0.5mm以上のブツもある
フィルム幅の中心付近についてマシン方向に2cm毎に20個所の膜厚を測定し、その標準偏差が1.5μm以下を「○」、1.5μmを超えて3.0μm以下を「△」、3.0μmを超えるものを「×」とした。
ジメチルカーボネート(DMC)/ジエチルカーボネート(DEC)/エチレンカーボネート(EC)=1/1/1(容積比)に水を極少量混合し、試験液とした。この試験液中の水分量をカールフィッシャー容量滴定装置(平沼産業株式会社のAQ-300)により測定した(初期の水分量)。次いで、この試験液30g中に450cm2のフィルムを浸漬し、25℃×48時間保管後の試験液中の水分量を同様に測定した。なお、以上の操作を、アイ・エイ・シー株式会社のエアードライヤーQD20−75により露点温度−50℃以下にしたガス置換型グローブボックス(アズワン株式会社のSG−1000)中で25℃で行った。
内容積400cm3の透明防湿袋に6000cm2のフィルムと上記グローブボックス中で状態調節した神栄株式会社のハンディタイプ温湿度計Hygropalm1を入れてヒートシールにより封止し、封止直後(初期)、25℃×15分後および25℃×2時間後の絶対湿度を測定した。測定は25℃で行った。
株式会社東洋精機製作所のHG−100型ヒートシール試験機を用い、80〜130℃の所定のシール温度でフィルムをそのマシン方向がT字剥離試験の引張方向になるように融着した(4秒間、圧力0.2MPa)。次いで、T字剥離試験を、株式会社東洋精機製作所のAE−CT型引張試験機を使用し、引剥幅25mm、引剥速度100mm/分、引剥角度180°で行った。より高いシール温度まで○判定になるものが耐熱性の良いフィルムである。
○:全くあるいは殆ど融着していない(引剥強度<0.1N/25mm)
△:僅かに融着している(引剥強度0.1〜2.0N/25mm)
×:融着している(引剥強度>2.0N/25mm)
フィルムをマシン方向が引張方向になるようにしてJIS5号ダンベル型試験片に打抜き、株式会社東洋精機製作所のAE−CT型引張試験機を使用して測定を行った(引張速度200mm/分、標線間距離40mm)。
KF271:日本ポリエチレン(株)製、直鎖状低密度ポリエチレン、Tm=127℃、ΔH=127J/g、Xc110=26%、Xc120=23%、MFR=2.4g/10分、密度913kg/m3
SP2040:プライムポリマー(株)製、直鎖状低密度ポリエチレン、Tm=117℃、ΔH=147J/g、Xc110=28%、MFR=4.0g/10分、密度920kg/m3
UF240:日本ポリエチレン(株)製、直鎖状低密度ポリエチレン、Tm=123℃、ΔH=136J/g、Xc110=47%、MFR=2.1g/10分、密度920kg/m3
SP2520:プライムポリマー(株)製、直鎖状低密度ポリエチレン、Tm=121℃、ΔH=154J/g、Xc110=38%、Xc120=19%、MFR=1.7g/10分、密度928kg/m3
F−730NV:プライムポリマー(株)製、プロピレンランダムコポリマー、Tm=139℃、Xc120=66%、MFR=7g/10分
SP4530:プライムポリマー(株)製、高密度ポリエチレン、Tm=132℃、ΔH=185J/g、Xc110=80%、Xc120=72%、MFR=2.8g/10分、密度942kg/m3
KS571:日本ポリエチレン(株)製、超低密度ポリエチレン、Tm=96℃、ΔH=110J/g、Xc110=0%、MFR=12.0g/10分、密度907kg/m3
KF360:日本ポリエチレン(株)製、超低密度ポリエチレン、Tm=111℃、ΔH=92J/g、Xc110=5%、MFR=3.5g/10分、密度898kg/m3
20200J:プライムポリマー(株)製、直鎖状低密度ポリエチレン、Tm=120℃、ΔH=137J/g、Xc110=43%、MFR=18.5g/10分、密度918kg/m3
アドマーXE070:三井化学(株)製、無水マレイン酸変性エチレン系重合体、MFR=3 g/10分
モレキュラーシーブ:ユニオン昭和(株)製のモレキュラーシーブ4Aパウダー、D99=9.9μm、D50=2.5μm
硫酸マグネシウム−1:馬居化成工業(株)製の乾燥硫酸マグネシウムSN−00の粉砕物、D99=3.5μm、D50=1.3μm
硫酸マグネシウム−2:馬居化成工業(株)製の乾燥硫酸マグネシウムSN−00、D99=118μm、D50=24μm
LBT−77:堺化学工業(株)製のポリエチレンワックス
ポリオレフィン層を外層として有するフィルムの製造:
実施例1で得られた吸水性樹脂組成物を、真空ベントを設けたGT−40−24−A型押出機(単軸タイプ、プラスチック工学研究所(株)製)から、表2に示すポリオレフィンをUT−32−24−A型押出機(単軸タイプ、プラスチック工学研究所(株)製)から押出してスタックプレートタイプの2種3層Tダイ(プラスチック工学研究所(株)製)により下記条件で、吸湿性樹脂組成物の層の両面にポリオレフィンの層を有する、全厚50μmの三層フィルムを製造した。ポリオレフィン層/吸水性樹脂組成物層/ポリオレフィン層の厚み比は1:8:1にした。得られたフィルムについて、上記(1)〜(6)の評価試験を行った。ただし、上記(3)の試験に関しては、25℃×48時間保管後に測定を行う代わりに、25℃×240時間保管後に測定を行った。また、上記(4)の試験に関しては、25℃×2時間後に測定を行う代わりに、25℃×96時間後に測定を行った。結果を表2に示す。
Tダイ出口樹脂温度220℃
引取速度15m/分
チルロール温度40℃
Claims (9)
- (A)ポリエチレン系樹脂組成物100質量部、および
(B)吸水性フィラー5〜200質量部
を含む吸水性樹脂組成物の層から成るフィルムであって、ポリエチレン系樹脂組成物(A)は、
(A−1)下記(i)〜(iv)の特性を有するエチレン系重合体99〜60質量%、
(i)DSC融解曲線における最も高い温度側のピークトップ融点(Tm)が110℃以上である、
(ii)DSC融解曲線における融解熱量(ΔH)が90〜180J/gである、
(iii)110℃における結晶化度(Xc110)が10〜60%である、および
(iv)MFR(190℃、21.18N)が0.1g/10分以上10g/10分未満である
および、
(A−2)酸変性樹脂1〜40質量%
を含み、ここで、成分(A−1)と成分(A−2)の量の合計が100質量%であり、
吸水性フィラー(B)は、30μm以下の粒子径(D99)および20μm以下の粒子径(D50)を有する、ここでD99およびD50はそれぞれ、粒子径分布において粒子径の小さい方から累積して99質量%および50質量%になる点における粒子径を言う、ところのフィルム。 - 請求項1記載のフィルムの両面にポリオレフィンの層が積層されたフィルム。
- ポリオレフィンが下記(1)〜(2)
(1)DSC融解曲線における最も高い温度側のピークトップ融点(Tm)が125℃以上である、および
(2)120℃における結晶化度(Xc120)が55%以上である
を満たす、請求項2記載のフィルム。 - 請求項1〜3のいずれか1項記載のフィルムを食品の包装材のために使用する方法。
- 請求項1〜3のいずれか1項記載のフィルムを二次電池用外装材のために使用する方法。
- 請求項1〜3のいずれか1項記載のフィルムを二次電池用吸湿材のために使用する方法。
- 請求項1〜3のいずれか1項記載のフィルムを履物の中敷きのために使用する方法。
- 請求項1〜3のいずれか1項記載のフィルムを衣類のカバーのために使用する方法。
- 請求項1〜3のいずれか1項記載のフィルムを検査薬の包装材のために使用する方法。