JP2008144020A - 積層防汚塗膜、基材の防汚方法、積層防汚塗膜付き基材およびプライマー組成物 - Google Patents
積層防汚塗膜、基材の防汚方法、積層防汚塗膜付き基材およびプライマー組成物 Download PDFInfo
- Publication number
- JP2008144020A JP2008144020A JP2006332019A JP2006332019A JP2008144020A JP 2008144020 A JP2008144020 A JP 2008144020A JP 2006332019 A JP2006332019 A JP 2006332019A JP 2006332019 A JP2006332019 A JP 2006332019A JP 2008144020 A JP2008144020 A JP 2008144020A
- Authority
- JP
- Japan
- Prior art keywords
- coating film
- laminated
- primer
- antifouling coating
- base material
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
クロム化合物を用いることなく、基材表面、特にプロペラ表面を長期間防汚する方法を提供すること。
【解決手段】エポキシ樹脂(A)と硬化剤(B)とを含有するプライマー組成物から形成されたプライマー塗膜(P)と、該プライマー塗膜(P)の表面に形成された防汚塗膜(Q)とからなることを特徴とする積層防汚塗膜、ならびに
基材の表面を、基材/前記プライマー塗膜(P)/前記防汚塗膜(Q)の順序となるように、前記積層防汚塗膜で被覆することを特徴とする基材の防汚方法。
【選択図】なし
Description
さらに本発明は、クロム化合物を含有せず、長期間の防汚性に優れた積層防汚塗膜付き基材(特にプロペラ)を提供することを目的としている。
れたプライマー塗膜の形成に好適なプライマー組成物を提供することを目的としている。
前記粒子(C)は、好ましくは鱗片状のアルミニウム粒子(C1)である。
本発明の基材の防汚方法は、基材の表面を、基材/前記プライマー塗膜(P)/前記防汚塗膜(Q)の順序となるように、本発明の積層防汚塗膜で被覆することを特徴としている。
前記基材としては、プロペラが好ましい。
本発明のプライマー組成物は、エポキシ樹脂(A)、硬化剤(B)および鱗片状のアルミニウム粒子(C1)を含有することを特徴としている。
さらに本発明の積層防汚塗膜付き基材は、長期間の防汚性に優れている。
[積層防汚塗膜]
本発明の積層防汚塗膜は、エポキシ樹脂(A)と硬化剤(B)とを含有するプライマー組成物から形成されたプライマー塗膜(P)と、該プライマー塗膜(P)の表面に形成された防汚塗膜(Q)とからなることを特徴としている。
前記プライマー組成物は、エポキシ樹脂(A)および硬化剤(B)を含有している。
(A)エポキシ樹脂:
前記エポキシ樹脂(A)としては、ビスフェノールA型のジグリシジルエーテル、ビスフェノールF型のジグリシジルエーテル、ビスフェノール類のアルキレンオキシド付加物のジグリシジルエーテル、ダイマー酸ジグリシジルエステル、ダイマー酸変性BPA型エポキシこれらビスフェノール型エポキシ樹脂の水添物、フェノールノボラックエポキシ樹脂、ならびにエポキシ樹脂をリン原子に結合した水酸基を少なくとも1つ有する化合物で変性して得られる樹脂(A2)(以下「変性エポキシ樹脂(A2)」ともいう。)などが挙げられる。この変性エポキシ樹脂(A2)の詳細については後述する。なお、本明細書においては、変性エポキシ樹脂(A2)以外のエポキシ樹脂を「エポキシ樹脂(A1)」ともいう。
ビスフェノールF型のジグリシジルエーテルとしては、例えば、ビスフェノールFジグリシジルエーテル等のビスフェノールF型ジグリシジルエーテルが挙げられる。
常温で半固型状のものであれば、「E−834−85X(T)(商品名)」(大竹明新(株)エポキシ当量230〜270)、「エピコート834(商品名)」(ジャパンエポキシレジン(株)製、エポキシ当量230〜270)、「エポトートYD134(商品名)」(東都化成(株)製、エポキシ当量230〜270)、「エポトートYD−172(商品名)」(東都化成(株)製、エポキシ当量600〜700)などを挙げることができ、
常温で固型状のものであれば、「エピコート1001(商品名)」(ジャパンエポキシレジン(株)製、エポキシ当量450〜500)などを挙げることができる。
前記エポキシ樹脂(A1)のエポキシ当量は、好ましくは160〜500、さらに好ましくは160〜300である。エポキシ当量が上記範囲にあると、得られるプライマー塗膜(P)と基材(特にプロペラ)との付着力が優れると共に、前記プライマー組成物を塗装する際の作業性が良好である。
変性エポキシ樹脂(A2)としては、プライマー組成物から形成される塗膜が強靱かつ柔軟性であり基材(特にプロペラ)に対する付着力に優れる点で、前記ビスフェノール型エポキシ樹脂をリン酸化合物で変性してなる変性エポキシ樹脂が好ましい。さらに塗装作業性、乾燥性等を考慮すると、このビスフェノール型エポキシ樹脂の中でも、ビスフェノールA型のジグリシジルエーテルが特に好ましく、市販品であれば「E−834―85X(T)(商品名)」(大竹明新(株)製、エポキシ当量230〜270)を好適に使用できる。
前記硬化剤(B)としては、アミン系硬化剤を使用することができ、このアミン系硬化剤の中でも、フェノール類と、ホルマリンと、アミン化合物とのマンニッヒ縮合反応で形成されたマンニッヒ変性アミン類(b1)、ケチミン類(b2)および脂肪族ポリアミン類(b3)が好ましく、マンニッヒ変性アミン類(b1)が特に好ましい。硬化剤(B)としてマンニッヒ変性アミン類(b1)を用いると、本発明の組成物の硬化速度、低温硬化性が優れる。
前記マンニッヒ変性アミン類(b1)は、フェノール類と、ホルムアルデヒドと、アミン化合物とのマンニッヒ(脱水)縮合反応で形成されるが、このフェノール類としては、不飽和置換基含有フェノール、飽和置換基含有フェノールが挙げられる。
このような不飽和置換基含有フェノールとしては、具体的には、例えば、カルダノール(cardanol)、イソプロペニルフェノール、ジイソプロペニルフェノール、ブテニルフェノール、イソブテニルフェノール、シクロヘキセニルフェノール、
モノスチレン化フェノール(C6H5−CH=CH−C6H4−OH)、
ジスチレン化フェノール((C6H5−CH=CH)2−C6H3−OH)、
などが挙げられる。
1価フェノールが挙げられ、
ハロゲン化フェノールとしては、クロルフェノール等の1価フェノールが挙げられる。
アミン化合物としては、芳香環の立体障害及び塩基性が劣ることより常温での硬化が困難な芳香族アミンに比べ、常温で硬化可能な脂肪族アミンが望ましく、例えばアルキレンポリアミン、ポリアルキレンポリアミン、脂環族ポリアミン、芳香環を含む脂肪族アミン類等が挙げられ、
より具体的には、前記アルキレンポリアミンとしては、例えば、式:H2N−R1−NH2
(R1:炭素数1〜10の炭化水素基側鎖を1個または複数個有していてもよい主鎖炭素
数1〜12の二価炭化水素基)で表され、例えば、メチレンジアミン、エチレンジアミン、1,2−ジアミノプロパン、1,3−ジアミノプロパン、1,4−ジアミノブタン、1,5−ジアミノペンタン、1,6−ジアミノヘキサン、1,7−ジアミノヘプタン、1,8−ジアミノオクタン、1,9−ジアミノノナン、1,10−ジアミノデカン等が用いられる。
m:1〜10の整数、n:2〜10、好ましくは2〜6の整数)で表され、より具体的には、例えば、ジエチレントリアミン、ジプロピレントリアミン、トリエチレンテトラミン、トリプロピレンテトラミン、テトラエチレンペンタミン、テトラプロピレンペンタミン、ペンタエチレンヘキサミン、ノナエチレンデカミン、トリメチルヘキサメチレンジアミン等が挙げられる。
本発明では、これらのアミン化合物は、1種または2種以上組み合わせて用いることができる。
エアー・プロダクツ社製:アンカミン2432(NV43.5%、アミン価387)、アンカミン2089M(NV100%、アミン価368)、
コグニスジャパン社製:バーサミンF20(NV100%、アミン価400〜480)、バーサミンI−368(NV100%、アミン価370〜400)、バーサミンM−1(NV100%、アミン価375〜425)、
シェル社製:エピキュアー3549(NV100%)、エピキュアー3378(NV74.5%)、
Witco社製:TL0712(NV94.3%、アミン価705)、
旭電化(株)製:アデカハードナーEH342M(NV40.2%、アミン価307)、アデカハードナーEH342M17(NV33.3%、アミン価386)、アデカハードナーEH350(NV52.8%、アミン価385)、アデカハードナーEH351(NV46.9%、アミン価306)、
三和化学工業(株):サンマイドW−3000(NV100%、アミン価340)、サンマイドW−1000(NV100%、アミン価340)、サンマイドW−500(NV100%、アミン価280)、サンマイドCX−102(NV89.8%、アミン価288)、
大都産業(株):ダイトクラールSK900FCB(NV100%、アミン価385)、
大日本インキ化学工業(株):ラッカマイドV6−221(NV100%、アミン価420)
などが挙げられる。これらのマンニッヒ変性アミン類(b1)は、1種単独でまたは2種以上を組み合わせて用いることができる。
ケチミン類(ケチミン硬化剤)(b2)は、特許第3327833号公報に記載されているような、ジエチレントリアミン(DETA)、トリエチレンテトラミン(TETA)、ジエチルアミノプロピルアミン(DEAPA)、m−キシリレンジアミン(MXDA)
、変性脂肪族ポリアミンなどの脂肪族ポリアミンと、メチルエチルケトン(MEK)、イソブチルメチルケトン(MIBK)といったケトンとの反応によって製造される硬化剤である。
脂肪族ポリアミン類(b3)
前記脂肪族ポリアミン類(b3)としては、たとえば、アルキレンポリアミン、ポリアルキレンポリアミン、その他の脂肪族系ポリアミン類などが挙げられる。
R1:炭素数1〜10の炭化水素基側鎖を1個または複数個有していてもよい主鎖炭素数
1〜12の二価炭化水素基)で表され、例えば、メチレンジアミン、エチレンジアミン、1,2−ジアミノプロパン、1,3−ジアミノプロパン、1,4−ジアミノブタン、1,5−ジアミノペンタン、1,6−ジアミノヘキサン、1,7−ジアミノヘプタン、1,8−ジアミノオクタン、1,9−ジアミノノナン、1,10−ジアミノデカン等が用いられる。
m:1〜10の整数、n:2〜10、好ましくは2〜6の整数)で表され、より具体的には、例えば、ジエチレントリアミン、ジプロピレントリアミン、トリエチレンテトラミン、トリプロピレンテトラミン、テトラエチレンペンタミン、テトラプロピレンペンタミン、ペンタエチレンヘキサミン、ノナエチレンデカミン、トリメチルヘキサメチレンジアミン等が挙げられる。
これら脂肪族ポリアミン類(b3)のアミノ基の活性水素当量(g/equiv)は、一概に決定されないが、通常80〜250の脂肪族ポリアミン類(b3)が用いられる。
硬化剤(B)の配合量が上記範囲にあると、該組成物から形成される塗膜は、金属基材(特にプロペラ)への付着性、耐水性に優れる。
前記プライマー組成物が水中で用いられる金属製基材の塗装に適用される場合には、該プライマー組成物には、水中での耐食性が該基材金属よりも劣る金属の粒子が含まれることが好ましい。このような金属の粒子を用いることにより、金属性基材の耐食性を向上させることができる。
金属粒子(C)の配合量が上記範囲にあると、該組成物から得られる塗膜は金属基材(特に銅合金製のプロペラ)への付着性及び防食性に優れる。
本発明の組成物は、エポキシ樹脂(A)、硬化剤(B)、金属粉子(C)および前記変性エポキシ樹脂およびエポキシ樹脂の混合物(D)以外にも、体質顔料、着色顔料、防錆顔料、揺変剤などを、本発明の目的を逸脱しない範囲で含有していてもよい。
体質顔料は、本発明の組成物の固形分100重量部あたり、好ましくは5〜70重量部、さらに好ましくは20〜50重量部用いられる。
前記揺変剤としては、有機、無機、複合系があり、有機系では水添ひまし油系、アマイド系、酸化ポリエチレン系、植物油重合油系、界面活性剤系の揺変剤が、無機系ではシリカやベントナイト等の揺変剤が、複合系ではアマイド/ポリエチレン系の揺変剤などが挙げられる。この遥変剤として、上市されているものとしては、例えば、「エロジール200」(日本アエロジル(株)製)、「ディスパロン4200−20」(楠本化成(株)製、酸化ポリエチレン系)などが挙げられる。
さらに本発明の組成物は溶剤(D)を含有していてもよい。溶剤(D)としては、例えば、トルエン、キシレン、メチルエチルケトン、メチルイソブチルケトン、ブチルアセテート、プロピレングリコールモノメチルエーテル等の有機溶剤が挙げられる。
(プライマー組成物)
本発明のプライマー組成物は、前記エポキシ樹脂(A)と、前記硬化剤(B)とを含有し、好ましくは前記金属粒子(C)をさらに含有し、さらに前記溶剤(D)等を含有していていもよい。このプライマー組成物は、船舶等のプロペラ表面に防汚塗膜の下塗り塗膜であるプライマー塗膜を形成するための“プロペラ用プライマー組成物”として好適に使用することができる。
本発明の積層防汚塗膜は、前記プライマー組成物から形成されたプライマー塗膜(P)と、該プライマー塗膜(P)の表面に形成された防汚塗膜(Q)とからなる。
数1〜12の非置換または置換の1価炭化水素基を示し、複数のR1、Rは、それぞれ互
いに同一でも異なっていてもよく、nは5以上の整数を示し、aは0、1または2を示す。)で示される化合物であることが望ましく、上記式[α]中のWが水酸基であり、かつaが2である場合には、このような前記オルガノポリシロキサン(A)と前記疎水性シリカ(B)とに加えて、さらに、(C)式[I]:R1 bSiX4-b(式[I]中、R1は炭素数1〜8の非置換または置換の1価炭化水素基を示し、Xは加水分解性基を示し、bは0または1を示す。)で示されるオルガノシランまたはその部分加水分解物を含有することが望ましい。
基材上に、本発明の積層防汚塗膜は、基材/前記プライマー塗膜(P)/防汚塗膜(Q)の順序となるように形成される。この基材としては、水中構造物、船舶外板、漁網および漁具などが挙げられ、中でもプロペラ、特に銅合金製のプロペラが好ましい。このプロペラの詳細については後述する。
本発明の基材の防汚方法は、基材の表面を、基材/前記プライマー塗膜(P)/前記防汚塗膜(Q)の順序となるように、本発明の積層防汚塗膜で被覆することを特徴としている。基材の表面に、前記プライマー塗膜(P)を形成し、該プライマー塗膜(P)の表面に前記防汚塗膜(Q)を形成することにより、基材を前記積層防汚塗膜で被覆することができる。前記プライマー組成物および前記防汚塗料の塗装方法は、特に限定されず、従来公知の塗装方法を採用することができる。
このプロペラの材料としては、高力黄銅鋳物(JIS記号CAC301)、アルミニウム青銅鋳物(JIS記号CAC703)などの銅合金;アルミニウム;ステンレスなどが挙げられる。
このように、本発明の積層防汚塗膜や基材の防汚方法によれば、基材表面、特にプロペラ表面への、アオサ、フジツボ、アオノリ、セルプラ、カキ、フサコケムシ等の水棲生物の付着を長期間防止できる。
以下、本発明について実施例に基づいてさらに具体的に説明するが、本発明は、係る実施例により何ら限定されるものではない。
[合成例1]
リン酸変性エポキシ樹脂(PCEX−1)の合成:
攪拌機、コンデンサー、温度計、滴下装置、窒素導入管、加熱ジャケットおよび冷却ジャケットを備えた反応容器に、エポキシ樹脂(商品名:エポトート170、東都化成(株)製、エポキシ当量180〜190、不揮発分100重量%)850重量部を仕込み、こ
れらを窒素雰囲気下で、100℃となるまで加熱しながら攪拌した。100℃を保持しながら、上記樹脂中に、滴下装置からジメチルフォスフェート150重量部を1時間かけて滴下した。次いで、100℃でさらに4.5時間攪拌を行った後、冷却し、リン酸変性エポキシ樹脂(PCEX−1)を得た。
リン酸変性エポキシ樹脂(PCEX−2)の合成:
滴下成分およびその量を表1に記載されたように変えた他は合成例1と同様にして、リン酸変性エポキシ樹脂(PCEX−2)を製造した。
主剤成分の調製:
エポキシ樹脂(商品名:E−834−85X(T) 大竹明新(株) エポキシ当量230〜270) 13重量部、
リン酸亜鉛(商品名:LFボウセイZP-N) 3.5重量部、
黄色酸化鉄(商品名:タロックスLCXLO) 5重量部
酸化チタン(商品名:チタンR-5N) 3.5重量部、
タルク(商品名:TTKタルク) 22重量部、
スゾライトマイカ(商品名:スゾライトマイカ200−HK) 3.5重量部
酸化ポリエチレンワックス(商品名:ASA D-120) 1重量部、
有機ベントナイト(商品名:ベントン27の重量NV10%プレゲル)7重量部
ヒュームドシリカ(商品名:エロジール#200) 0.5部
メチルイソブチルケトン 5重量部、
キシレン 16重量部および
プロピレングリコールモノメチルエーテル 4重量部
を混合し主剤成分を調製した。
マーニッヒ型硬化剤(商品名:ラッカマイドV6−221) 3.0重量部及び1−ブタノール 3重量部を混合し硬化剤成分を調製した。
1.室内試験;
<試験板の作成>
上記の主剤成分と硬化剤成分とを混合し、プライマー組成物を調製した。この組成物を、サンドペーパーにより面粗しされた70×150×10mmのアルミニウム青銅鋳物(JIS記号CAC703)板の表面にスキマ400μmのアプリケーターを用いて塗装し、室内で室温(約20℃)にて1日間かけて硬化させプライマー塗膜(プライマー層)を形成した。
以下の方法で試験を行った。
[プライマー塗膜とアルミニウム青銅鋳物板との付着性]
上記試験板を、25℃の海水を入れた恒温槽に90日間静置浸漬した後に、プライマー塗膜とアルミニウム青銅鋳物板との付着性を、以下の(1)、(2)の手順(ナイフテスト)で評価した。
(1)塗膜表面に、互いに30度の角度で交わりプロペラに達する長さ約40mmの2本の切り傷をつける。この切り傷は、カッターナイフを、スチール製定規等に当て、その刃先を塗膜表面に対して35〜45度の範囲の一定の角度に保ちながら、約0.5秒間かけて等速で引くことで形成される。
(2)次に2本の切り傷の交差する箇所のプライマー塗膜とアルミニウム青銅鋳物板との層間にナイフの刃先を挿入し、刃先を積層方向に動かす。その時に塗膜がアルミニウム青銅鋳物板上に残存せず面状に容易にハガレが発生する場合はアルミニウム青銅鋳物板とプライマー塗膜との付着性が不良であり、層間剥離と判断する。また、アルミニウム青銅鋳物板表面にプライマー塗膜が残存し塗膜内での破壊が認められる場合はアルミニウム青銅鋳物板とプライマー塗膜との付着性が良好であり、凝集破壊と判断する。
5:凝集破壊のみが生じ、層間剥離は生じなかった。
3:層間剥離および凝集破壊がほぼ同面積で生じた。
2:大部分で層間剥離が生じ、一部で凝集破壊が生じた。
[プライマー塗膜と防汚塗膜との付着性]
上記試験板を、25℃の海水を入れた恒温槽に90日間静置浸漬した後に、プライマー塗膜と防汚塗膜との付着性を、ナイフテストにて評価した。ナイフテストは、プライマー塗膜と防汚塗膜との層間にナイフの刃を挿入した以外は前記同様の方法で行った。防汚塗膜がプライマー塗膜上に残存せず面状に容易にハガレが発生する場合はプライマー塗膜と防汚塗膜との付着性が不良であり、層間剥離と判断する。また、プライマー塗膜表面に防汚塗膜が残存、プライマー塗膜または防汚塗膜内での破壊が認められる場合はプライマー塗膜と防汚塗膜との付着性が良好であり、凝集破壊と判断する。
5:凝集破壊のみが生じ、層間剥離は生じなかった。
3:層間剥離と凝集破壊がほぼ同面積で生じた。
2:大部分で層間剥離が生じ、ごく一部で凝集破壊が生じた。
試験結果を表2に示す。
2.実船試験;
<試験塗装船概要>
実船試験では、下記の船を使用した。
サイズ:全長17.01m、19ton
プロペラ:パワーツールにより面粗しされたアルミニウム青銅鋳物(JIS規格CAC703)プロペラ
<積層塗膜の形成>
上記の主剤成分と硬化剤成分とを混合し、プロペラ用エポキシプライマー組成物を調製した。この組成物を、上記船のプロペラ表面に、刷毛により、乾燥膜厚が約100μmになるように塗装し、屋外(気温約20℃)にて3時間かけて硬化させ、プライマー塗膜(プライマー層)を形成した。
上記のようにプロペラ表面にプライマー塗膜および防汚塗膜が形成された前記の船を、船速24〜30ノット、稼働率20%の条件で6ヶ月運行させた後、目視及びナイフテストにて評価を行った。
4:剥離面積は5%未満であった。
3:剥離面積が5%以上〜15%未満であった。
1:剥離面積が35%以上であった。
試験結果を表2に示す。
主剤成分および硬化剤成分中の、配合成分および配合量を表2に記載のように変更した以外は実施例1と同様にして、積層塗膜を形成した。各積層塗膜についての試験結果を表2に示す。
Claims (16)
- エポキシ樹脂(A)と硬化剤(B)とを含有するプライマー組成物から形成されたプライマー塗膜(P)と、該プライマー塗膜(P)の表面に形成された防汚塗膜(Q)とからなることを特徴とする積層防汚塗膜。
- 前記プライマー組成物が、イオン化傾向が銅よりも大きい金属(ただしクロムを除く。)の粒子(C)をさらに含有することを特徴とする請求項1に記載の積層防汚塗膜。
- 前記エポキシ樹脂(A)が、リン原子に結合した水酸基を少なくとも1つ有する化合物でエポキシ樹脂を変性してなる樹脂(A2)を含有することを特徴とする請求項1または2に記載の積層防汚塗膜。
- 前記プライマー組成物が、前記エポキシ樹脂(A)の固形分100重量部に対して、前記硬化剤(B)を1〜80重量部、および前記イオン化傾向が銅よりも大きい金属(ただしクロムを除く。)の粒子(C)を1〜400重量部含有することを特徴とする請求項2または3に記載の積層防汚塗膜。
- 前記プライマー組成物が、前記エポキシ樹脂(A)の固形分100重量部に対して、前記硬化剤(B)を5〜50重量部、および前記イオン化傾向が銅よりも大きい金属(ただしクロムを除く。)の粒子(C)を5〜300重量部含有することを特徴とする請求項2または3に記載の積層防汚塗膜。
- 前記金属が亜鉛、アルミニウムおよびマグネシウムからなる群から選ばれた少なくとも1種の金属であることを特徴とする請求項2〜5のいずれかに記載の積層防汚塗膜。
- 前記金属がアルミニウムであることを特徴とする請求項6に記載の積層防汚塗膜。
- 前記粒子(C)が鱗片状のアルミニウム粒子(C1)であることを特徴とする請求項2〜7のいずれかに記載の積層防汚塗膜。
- 前記防汚塗膜(Q)が、シリコーン樹脂またはシリコーン樹脂含有組成物を硬化させてなる塗膜であることを特徴とする請求項1〜8のいずれかに記載の積層防汚塗膜。
- 基材の表面を、基材/前記プライマー塗膜(P)/前記防汚塗膜(Q)の順序となるように、請求項1〜9のいずれかに記載の積層防汚塗膜で被覆することを特徴とする基材の防汚方法。
- 基材の表面に前記プライマー塗膜(P)を形成し、該プライマー塗膜(P)の表面に前記防汚塗膜(Q)を形成することを特徴とする請求項10に記載の基材の防汚方法。
- 前記基材が、プロペラであることを特徴とする請求項10または11に記載の基材の防汚方法。
- 基材の表面が、基材/前記プライマー塗膜(P)/前記防汚塗膜(Q)の順序となるように、請求項1〜9のいずれかに記載の積層防汚塗膜で被覆されてなる、積層防汚塗膜付き基材。
- 前記基材が、プロペラであることを特徴とする請求項13に記載の積層防汚塗膜付き基材。
- エポキシ樹脂(A)、硬化剤(B)および鱗片状のアルミニウム粒子(C1)を含有するプライマー組成物。
- 前記エポキシ樹脂(A)が、リン原子に結合した水酸基を少なくとも1つ有する化合物でエポキシ樹脂を変性してなる樹脂(A2)を含有することを特徴とする請求項15に記載のプライマー組成物。