JP2005268055A - スクリーン印刷用導電ペースト - Google Patents
スクリーン印刷用導電ペースト Download PDFInfo
- Publication number
- JP2005268055A JP2005268055A JP2004079082A JP2004079082A JP2005268055A JP 2005268055 A JP2005268055 A JP 2005268055A JP 2004079082 A JP2004079082 A JP 2004079082A JP 2004079082 A JP2004079082 A JP 2004079082A JP 2005268055 A JP2005268055 A JP 2005268055A
- Authority
- JP
- Japan
- Prior art keywords
- conductive paste
- modified polyvinyl
- polyvinyl acetal
- viscosity
- acetal resin
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
【解決手段】 変性ポリビニルアセタール樹脂をバインダー樹脂とする導電ペーストであって、前記変性ポリビニルアセタール樹脂は、E型粘度計を用いて25℃において剪断速度60s−1の条件で測定した粘度が6.0Pa・sとなるように調整したα−テルピネオール溶液において、E型粘度計を用いて25℃において剪断速度60s−1の条件で測定した粘度η60と、剪断速度600s−1の条件で測定した粘度η600との比(η60/η600)が2.0〜5.0であるスクリーン印刷用導電ペースト。
【選択図】 なし
Description
そのうちの、積層セラミックコンデンサは、一般に次のような工程を経て製造されている。
まず、ポリビニルブチラール樹脂やポリ(メタ)アクリル酸エステル系樹脂等のバインダー樹脂を有機溶剤に溶解した溶液に可塑剤、分散剤等を添加した後、セラミック原料粉末を加え、ボールミル等の混合装置により均一に混合し、脱泡後に一定粘度を有するセラミックスラリー組成物を得る。このスラリー組成物をドクターブレード、リバースロールコーター等を用いて、離型処理したポリエチレンテレフタレートフィルム、またはSUSプレート等の支持体面に流延して、これを加熱等により、溶剤等の揮発分を溜去させた後、支持体から剥離してセラミックグリーンシートを得る。
しかし、近年積層セラミックコンデンサには更なる高容量化が求められており、より一層の多層化、薄膜化が検討されている。このように極めて薄膜化が進んだ積層セラミックコンデンサを、従来のエチルセルロースをバインダー樹脂とした導電ペーストを用いて製造した場合、ポリビニルアセタール樹脂をバインダー樹脂として用いたセラミックグリーンシートとの接着性が劣るため、いわゆるデラミネーションと呼ばれる層間剥離が発生しやすく、また、エチルセルロース自体の熱分解性が劣るため、上記積層体を脱脂処理した場合、焼成後にカーボン成分が残留し、電気特性を損なうといった問題点があった。
本発明は、変性ポリビニルアセタール樹脂をバインダー樹脂とする導電ペーストであって、前記変性ポリビニルアセタール樹脂は、E型粘度計を用いて25℃において剪断速度60s−1の条件で測定した粘度が6.0Pa・sとなるように調整したα−テルピネオール溶液において、1Hz、応力1000Paにおける位相角が87°〜90°であるスクリーン印刷用導電ペーストである。
本発明は、変性ポリビニルアセタール樹脂をバインダー樹脂とする導電ペーストであって、前記変性ポリビニルアセタール樹脂は、E型粘度計を用いて25℃において剪断速度60s−1の条件で測定した粘度が6.0Pa・sとなるように調整したα−テルピネオール溶液において、25℃において剪断速度を600s−1から60s−1に変化させたときに、E型粘度計を用いて測定した剪断速度600s−1ときの粘度η600と、剪断速度を60s−1に変化させてから10秒後の粘度η60との比(η600→60/η600)が1.9以上であるスクリーン印刷用導電ペーストである。
以下に本発明を詳述する。
本発明者らは、更に鋭意検討の結果、特定の性質を有する変性ポリビニルアセタール樹脂をバインダー樹脂として用いることにより、塗工性、版離れ性及び形状保持性のそれぞれに優れた導電ペーストが得られることを見出し、本発明を完成するに至った。
η60/η600が2.0未満であると、塗工時の粘度が低すぎて均一に塗り広げられなかったり、版のパターン内に入った導電ペーストの粘度が高すぎてパターン内に均一に広がらなかったりする。5.0を超えると、塗工時の粘度が高すぎて均一に塗り広げられなかったりする。好ましい下限は2.3、好ましい上限は3.0である。
なお、位相角は一定周波数を印加しながら測定する動的粘弾性測定法により測定することができる。また、1Hz、応力1000Paにおける位相角としたのは、通常の工程において版の剥離の際にペーストに印加される応力を考慮したものである。
η600→60/η600が1.9未満であると、版を剥離した際の導電ペーストの粘度が低すぎて、パターン形状を保持できない。好ましくは2.0以上である。
上記変性ポリビニルアルコールは、ビニルエステルとα−オレフィンとを共重合した共重合体をケン化することにより得ることができる。この場合に用いるビニルエステルとしては、例えば、蟻酸ビニル、酢酸ビニル、プロピオン酸ビニル、ピバリン酸ビニル等が挙げられ、なかでも経済的な観点から酢酸ビニルが好適である。また、上記エチレン性不飽和単量体に由来する成分を含有する変性ポリビニルアセタール樹脂を得る場合には、更にエチレン性不飽和単量体を共重合させる。また、チオール酢酸、メルカプトプロピオン酸等のチオール化合物の存在下で、酢酸ビニル等のビニルエステル系単量体とα−オレフィンとを共重合し、それをケン化することによって得られる末端変性ポリビニルアルコールも用いることができる。
なお、本明細書において、アセタール化度の計算方法としては、変性ポリビニルアセタール樹脂のアセタール基が2個の水酸基からアセタール化されて形成されていることから、アセタール化された2個の水酸基を数える方法を採用してアセタール化度のモル%を計算する。
上記金属材料としては充分な導電性を示すものであれば特に限定されず、例えば、ニッケル、パラジウム、白金、金、銀、銅やこれらの合金等からなる微粒子等が挙げられる。これらの金属材料は、単独で用いてもよく、2種以上を併用してもよい。
上記有機溶剤としては、上記バインダー樹脂を溶解できるものであれば特に限定されず、例えば、α−テルピネオール、ブチルカルビトール等のカルビトール類;ブチルセロソルブ等のセロソルブ類;ターピネオールアセタート等が挙げられる。
更に、本発明のスクリーン印刷用導電ペーストは、本発明の効果を損なわない範囲で、可塑剤、潤滑剤、分散剤、帯電防止剤等の従来公知の添加剤を含有してもよい。
重合度1700、エチレン含有量4モル%、ケン化度99モル%の変性ポリビニルアルコール193gを純水2900gに加え、90℃の温度で約2時間攪拌し溶解させた。この溶液を28℃に冷却し、濃度35重量%の塩酸20gとn−ブチルアルデヒド115gとを添加し、液温を20℃に下げてこの温度を保持してアセタール化反応を行い、反応生成物を析出させた。その後、液温を30℃、5時間保持して反応を完了させ、常法により中和、水洗及び乾燥を経て、変性ポリビニルアセタール樹脂の白色粉末を得た。
アルデヒドとしてn−ブチルアルデヒドとアセトアルデヒドとの混合物(重量比6:1)を用いた以外は実施例1と同様の方法により変性ポリビニルアセタール樹脂を得た。得られた変性ポリビニルアセタール樹脂のアセタール化度は76モル%であった。
得られた変性ポリビニルアセタール樹脂を用いた以外は実施例1と同様の方法によりビヒクル及びスクリーン印刷用導電ペーストを調製した。
アルデヒドとしてn−ブチルアルデヒドとアセトアルデヒドとの混合物(重量比1:2)を用いた以外は実施例1と同様の方法により変性ポリビニルアセタール樹脂を得た。得られた変性ポリビニルアセタール樹脂のアセタール化度は71モル%であった。
得られた変性ポリビニルアセタール樹脂を用いた以外は実施例1と同様の方法によりビヒクル及びスクリーン印刷用導電ペーストを調製した。
アルデヒドとしてアセトアルデヒドを用いた以外は実施例1と同様の方法により変性ポリビニルアセタール樹脂を得た。得られた変性ポリビニルアセタール樹脂のアセタール化度は73モル%であった。
得られた変性ポリビニルアセタール樹脂を用いた以外は実施例1と同様の方法によりビヒクル及びスクリーン印刷用導電ペーストを調製した。
バインダー樹脂として、ポリビニルブチラール樹脂(積水化学工業製、エスレックB「BH−S」)を用いた以外は実施例1と同様の方法によりビヒクル及びスクリーン印刷用導電ペーストを調製した。
バインダー樹脂として、エチルセルロース(ダウ社製、「STD−100」)を用いた以外は実施例1と同様の方法によりビヒクル及びスクリーン印刷用導電ペーストを調製した。
試験例1〜6で調製したビヒクル及びスクリーン印刷用導電ペーストについて、以下の方法により評価を行った。
結果を表1に示した。)
(1−1)η60/η600の測定
得られたビヒクルについて、E型粘度計を用いて25℃において剪断速度60s−1の条件で粘度η60を、剪断速度600s−1の条件で粘度η600を測定し、比(η60/η600)を求めた。
ポリビニルブチラール樹脂(積水化学工業製、エスレックB「BM−S」、重合度800)10重量部を、トルエン30重量部とエタノール15重量部との混合溶剤に加え、攪拌溶解し、更に、可塑剤としてジブチルフタレート3重量部を加え、攪拌溶解した。得られた樹脂溶液に、セラミック粉末としてチタン酸バリウム(堺化学工業製「BT−01(平均粒径0.3μm)」)100重量部を加え、ボールミルで48時間混合してセラミックスラリー組成物を得た。得られたスラリー組成物を、離型処理したポリエステルフィルム上に、乾燥後の厚みが約5μmになるように塗布し、常温で1時間風乾し、熱風乾燥機、80℃で3時間、続いて120℃で2時間乾燥させてセラミックグリーンシートを得た。
〇:印刷面のスクリーン印刷用導電ペーストに擦れが全く認められない
×:印刷面のスクリーン印刷用導電ペーストに擦れが認められた
(2−1)位相角の測定
得られたビヒクルについて、E型粘度計を用いて、1Hz、応力1000Paの条件で位相角を測定した。
(1−2)と同様の方法によりスクリーン印刷用導電ペーストをセラミックグリーンシート上にスクリーン印刷し、印刷面を目視又は拡大顕微鏡で観察し、下記の基準により版離れ性を評価した。
〇:印刷面の糸状のスクリーン印刷用導電ペーストが全く認められない
×:印刷面の糸状のスクリーン印刷用導電ペーストが認められた
(3−1)η600→60/η600の測定
得られたビヒクルについて、25℃において剪断速度を600s−1から60s−1に変化させたときに、E型粘度計を用いて剪断速度600s−1ときの粘度η600及び剪断速度を60s−1に変化させてから10秒後の粘度η60を測定し、比(η600→60/η600)を求めた。
(1−2)と同様の方法によりスクリーン印刷用導電ペーストをセラミックグリーンシート上にスクリーン印刷し、印刷面を目視又は拡大顕微鏡で観察し、下記の基準により形状保持性を評価した。
〇:印刷面のスクリーン印刷用導電ペーストにタレが全く認められない
×:印刷面のスクリーン印刷用導電ペーストにタレが認められた
(1−2)と同様の方法により作製したセラミックグリーンシートを5cm角の大きさに切断し、これにスクリーン印刷用導電ペーストをスクリーン印刷たものを100枚積重ね、温度70℃、圧力150kg/cm2、10分間の熱圧着条件で圧着して、セラミックグリーンシート積層体を得た。
得られたセラミックグリーンシート積層体を窒素雰囲気で、昇温速度3℃/分で450℃まで昇温し、5時間保持後、更に昇温速度5℃/分で1350℃まで昇温し、10時間保持してセラミック焼結体を得た。この焼結体を常温まで冷却した後、半分に割り、ちょうど50層付近のシートの状態を電子顕微鏡で観察し、セラミック層と導電層とのデラミネーションの有無観察し、以下の基準により接着性を評価した。
○:デラミネーションなし
×:デラミネーションあり
一方、変性ポリビニルアセタールをバインダー樹脂した試験例1、2、3又は4で作製したスクリーン印刷用導電ペーストは接着性に優れるうえ、試験例3で作製したスクリーン印刷用導電ペーストは塗工性に優れ、試験例4で作製したスクリーン印刷用導電ペーストは版離れ性に優れ、更に、試験例1及び2で作製したスクリーン印刷用導電ペーストは塗工性、版離れ性及び形状保持性の全てにおいて優れていた。
Claims (4)
- 変性ポリビニルアセタール樹脂をバインダー樹脂とする導電ペーストであって、
前記変性ポリビニルアセタール樹脂は、E型粘度計を用いて25℃において剪断速度60s−1の条件で測定した粘度が6.0Pa・sとなるように調整したα−テルピネオール溶液において、E型粘度計を用いて25℃において剪断速度60s−1の条件で測定した粘度η60と、剪断速度600s−1の条件で測定した粘度η600との比(η60/η600)が2.0〜5.0である
ことを特徴とするスクリーン印刷用導電ペースト。 - 変性ポリビニルアセタール樹脂をバインダー樹脂とする導電ペーストであって、
前記変性ポリビニルアセタール樹脂は、E型粘度計を用いて25℃において剪断速度60s−1の条件で測定した粘度が6.0Pa・sとなるように調整したα−テルピネオール溶液において、1Hz、応力1000Paにおける位相角が87°以上である
ことを特徴とするスクリーン印刷用導電ペースト。 - 変性ポリビニルアセタール樹脂をバインダー樹脂とする導電ペーストであって、
前記変性ポリビニルアセタール樹脂は、E型粘度計を用いて25℃において剪断速度60s−1の条件で測定した粘度が6.0Pa・sとなるように調整したα−テルピネオール溶液において、25℃において剪断速度を600s−1から60s−1に変化させたときに、E型粘度計を用いて測定した剪断速度600s−1ときの粘度η600と、剪断速度を60s−1に変化させてから10秒後の粘度η60との比(η600→60/η600)が1.9以上である
ことを特徴とするスクリーン印刷用導電ペースト。 - 変性ポリビニルアセタール樹脂は、下記一般式(1)、(2)、(3)及び(4)で表される構造単位からなるものであることを特徴とする請求項1、2又は3記載のスクリーン印刷用導電ペースト。