ES8602955A1 - Metodo de fabricacion de una chapa de acero con estructura de fase doble laminada en frio con excelente embutibilidad. - Google Patents

Metodo de fabricacion de una chapa de acero con estructura de fase doble laminada en frio con excelente embutibilidad.

Info

Publication number
ES8602955A1
ES8602955A1 ES530701A ES530701A ES8602955A1 ES 8602955 A1 ES8602955 A1 ES 8602955A1 ES 530701 A ES530701 A ES 530701A ES 530701 A ES530701 A ES 530701A ES 8602955 A1 ES8602955 A1 ES 8602955A1
Authority
ES
Spain
Prior art keywords
steel sheet
cold rolled
manufacturing
same
phase structure
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired
Application number
ES530701A
Other languages
English (en)
Spanish (es)
Other versions
ES530701A0 (es
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
JFE Steel Corp
Original Assignee
Kawasaki Steel Corp
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Kawasaki Steel Corp filed Critical Kawasaki Steel Corp
Publication of ES530701A0 publication Critical patent/ES530701A0/es
Publication of ES8602955A1 publication Critical patent/ES8602955A1/es
Expired legal-status Critical Current

Links

Classifications

    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/06—Ferrous alloys, e.g. steel alloys containing aluminium
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D8/00—Modifying the physical properties of ferrous metals or ferrous alloys by deformation combined with, or followed by, heat treatment
    • C21D8/02—Modifying the physical properties of ferrous metals or ferrous alloys by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips
    • C21D8/04—Modifying the physical properties of ferrous metals or ferrous alloys by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips to produce plates or strips for drawing, e.g. for deep-drawing
    • C21D8/0447—Modifying the physical properties of ferrous metals or ferrous alloys by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips to produce plates or strips for drawing, e.g. for deep-drawing characterised by the heat treatment
    • C21D8/0473—Final recrystallisation annealing
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/12—Ferrous alloys, e.g. steel alloys containing tungsten, tantalum, molybdenum, vanadium, or niobium
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D2211/00—Microstructure comprising significant phases
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D2211/00—Microstructure comprising significant phases
    • C21D2211/005—Ferrite
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D8/00—Modifying the physical properties of ferrous metals or ferrous alloys by deformation combined with, or followed by, heat treatment
    • C21D8/02—Modifying the physical properties of ferrous metals or ferrous alloys by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips
    • C21D8/04—Modifying the physical properties of ferrous metals or ferrous alloys by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips to produce plates or strips for drawing, e.g. for deep-drawing
    • C21D8/0421—Modifying the physical properties of ferrous metals or ferrous alloys by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips to produce plates or strips for drawing, e.g. for deep-drawing characterised by the working steps
    • C21D8/0426—Hot rolling
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D9/00—Heat treatment, e.g. annealing, hardening, quenching or tempering, adapted for particular articles; Furnaces therefor
    • C21D9/52—Heat treatment, e.g. annealing, hardening, quenching or tempering, adapted for particular articles; Furnaces therefor for wires; for strips ; for rods of unlimited length

Landscapes

  • Chemical & Material Sciences (AREA)
  • Engineering & Computer Science (AREA)
  • Mechanical Engineering (AREA)
  • Materials Engineering (AREA)
  • Metallurgy (AREA)
  • Organic Chemistry (AREA)
  • Physics & Mathematics (AREA)
  • Thermal Sciences (AREA)
  • Crystallography & Structural Chemistry (AREA)
  • Heat Treatment Of Sheet Steel (AREA)
  • Heat Treatment Of Steel (AREA)
  • Heat Treatment Of Strip Materials And Filament Materials (AREA)
ES530701A 1984-02-18 1984-03-16 Metodo de fabricacion de una chapa de acero con estructura de fase doble laminada en frio con excelente embutibilidad. Expired ES8602955A1 (es)

Applications Claiming Priority (1)

Application Number Priority Date Filing Date Title
JP59027995A JPS60174852A (ja) 1984-02-18 1984-02-18 深絞り性に優れる複合組織冷延鋼板とその製造方法

Publications (2)

Publication Number Publication Date
ES530701A0 ES530701A0 (es) 1985-12-01
ES8602955A1 true ES8602955A1 (es) 1985-12-01

Family

ID=12236401

Family Applications (1)

Application Number Title Priority Date Filing Date
ES530701A Expired ES8602955A1 (es) 1984-02-18 1984-03-16 Metodo de fabricacion de una chapa de acero con estructura de fase doble laminada en frio con excelente embutibilidad.

Country Status (6)

Country Link
US (2) US4615749A (enExample)
EP (1) EP0152665B1 (enExample)
JP (1) JPS60174852A (enExample)
CA (1) CA1229750A (enExample)
DE (1) DE3468906D1 (enExample)
ES (1) ES8602955A1 (enExample)

Families Citing this family (38)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPS60197847A (ja) * 1984-03-19 1985-10-07 Kawasaki Steel Corp 高加工性常温非時効性複合組織熱延鋼帯の製造方法
CA1305911C (en) * 1986-12-30 1992-08-04 Teruo Tanaka Process for the production of a strip of a chromium stainless steel of a duplex structure having high strength and elongation as well as reduced plane anisotropy
DE3787961T2 (de) * 1986-12-30 1994-05-19 Nisshin Steel Co., Ltd., Tokio/Tokyo Verfahren zur Herstellung von rostfreien Chromstahlband mit Zweiphasen-Gefüge mit hoher Festigkeit und hoher Dehnung und mit niedriger Anisotropie.
US4889566A (en) * 1987-06-18 1989-12-26 Kawasaki Steel Corporation Method for producing cold rolled steel sheets having improved spot weldability
JPH01263662A (ja) * 1988-04-15 1989-10-20 Fuji Xerox Co Ltd 記録装置およびその消耗部品
DE3917071C1 (enExample) * 1988-10-22 1990-04-19 Thyssen Edelstahlwerke Ag, 4000 Duesseldorf, De
JPH06104862B2 (ja) * 1989-03-06 1994-12-21 川崎製鉄株式会社 焼付け硬化性及び常温非時効性に優れた加工用冷延鋼板の製造方法
JPH06102816B2 (ja) * 1990-03-28 1994-12-14 川崎製鉄株式会社 加工性、常温非時効性及び焼付け硬化性に優れる複合組織冷延鋼板とその製造方法
JP3365632B2 (ja) * 1991-03-15 2003-01-14 新日本製鐵株式会社 成形性の良好な高強度冷延鋼板と溶融亜鉛メッキ高強度冷延鋼板およびそれらの製造方法
JPH05112845A (ja) * 1991-03-30 1993-05-07 Nippon Steel Corp 成形後の面形状性が良好で優れた耐デント性を有する深絞り用高強度冷延鋼板
JPH083136B2 (ja) * 1991-04-25 1996-01-17 住友金属工業株式会社 塗装焼付硬化性高張力薄鋼板とその製造法
JP2818319B2 (ja) * 1991-04-26 1998-10-30 川崎製鉄株式会社 常温非時効型絞り用高張力冷延鋼板及びその製造方法
CA2067043C (en) * 1991-04-26 1998-04-28 Susumu Okada High strength cold rolled steel sheet having excellent non-aging property at room temperature and suitable for drawing and method of producing the same
EP0559225B1 (en) * 1992-03-06 1999-02-10 Kawasaki Steel Corporation Producing steel sheet having high tensile strength and excellent stretch flanging formability
CA2097900C (en) * 1992-06-08 1997-09-16 Saiji Matsuoka High-strength cold-rolled steel sheet excelling in deep drawability and method of producing the same
KR940702231A (ko) * 1992-06-22 1994-07-28 미노루 다나까 우수한 소부 경화성, 비시효 특성 및 성형성을 가진 냉간압연 강판 및 열침지 피복 냉간압연 강판, 및 그의 제조방법(cold rolled steel sheet and hot dip ainc-coated cold rolled steel sheet having excellent bake hardenability, non-aging properties and formability, and process for producing same)
US5690755A (en) * 1992-08-31 1997-11-25 Nippon Steel Corporation Cold-rolled steel sheet and hot-dip galvanized cold-rolled steel sheet having excellent bake hardenability, non-aging properties at room temperature and good formability and process for producing the same
KR0121737B1 (ko) * 1992-08-31 1997-12-04 다나까 미노루 소부 경화성, 상온 비시효성 및 가공성이 우수한 냉연강판 및 용융아연 도금 냉연강판 및 그의 제조방법
JPH07179946A (ja) * 1993-12-24 1995-07-18 Kawasaki Steel Corp 耐二次加工ぜい性に優れる高加工性高張力冷延鋼板の製造方法
KR100308003B1 (ko) * 1994-02-15 2001-11-30 에모토 간지 고강도합금화용융아연도금강판
CN1115422C (zh) * 1999-08-11 2003-07-23 日本钢管株式会社 磁屏蔽用钢板及其制造方法
JP3958921B2 (ja) 2000-08-04 2007-08-15 新日本製鐵株式会社 塗装焼付硬化性能と耐常温時効性に優れた冷延鋼板及びその製造方法
JP4519373B2 (ja) * 2000-10-27 2010-08-04 Ｊｆｅスチール株式会社 成形性、歪時効硬化特性および耐常温時効性に優れた高張力冷延鋼板およびその製造方法
US20040047756A1 (en) * 2002-09-06 2004-03-11 Rege Jayanta Shantaram Cold rolled and galvanized or galvannealed dual phase high strength steel and method of its production
US8337643B2 (en) 2004-11-24 2012-12-25 Nucor Corporation Hot rolled dual phase steel sheet
US7442268B2 (en) * 2004-11-24 2008-10-28 Nucor Corporation Method of manufacturing cold rolled dual-phase steel sheet
US7959747B2 (en) * 2004-11-24 2011-06-14 Nucor Corporation Method of making cold rolled dual phase steel sheet
BRPI0607715B1 (pt) * 2005-03-30 2014-12-16 Nippon Steel & Sumitomo Metal Corp "equipamento para produção de tira de aço laminada a quente revestida por imersão a quente".
US9290835B2 (en) 2005-10-05 2016-03-22 Nippon Steel & Summitomo Metal Corporation Cold-rolled steel sheet excellent in paint bake hardenability and ordinary-temperature non-aging property and method of producing the same
US11155902B2 (en) 2006-09-27 2021-10-26 Nucor Corporation High strength, hot dip coated, dual phase, steel sheet and method of manufacturing same
US7608155B2 (en) * 2006-09-27 2009-10-27 Nucor Corporation High strength, hot dip coated, dual phase, steel sheet and method of manufacturing same
CA2701903C (en) 2007-10-10 2017-02-28 Nucor Corporation Complex metallographic structured steel and method of manufacturing same
CN102015155B (zh) * 2008-03-19 2013-11-27 纽科尔公司 使用铸辊定位的带材铸造设备
US20090236068A1 (en) 2008-03-19 2009-09-24 Nucor Corporation Strip casting apparatus for rapid set and change of casting rolls
US20090288798A1 (en) * 2008-05-23 2009-11-26 Nucor Corporation Method and apparatus for controlling temperature of thin cast strip
DE102011117572A1 (de) 2011-01-26 2012-08-16 Salzgitter Flachstahl Gmbh Höherfester Mehrphasenstahl mit ausgezeichneten Umformeigenschaften
CN104120220B (zh) * 2014-07-29 2016-11-23 东北大学 一种汽车用双相钢的热处理方法
CN118600328A (zh) 2016-08-24 2024-09-06 香港大学 双相钢及其制造方法

Family Cites Families (16)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US3988173A (en) * 1972-04-03 1976-10-26 Nippon Steel Corporation Cold rolled steel sheet having excellent workability and method thereof
JPS5157623A (en) * 1974-11-18 1976-05-20 Nippon Kokan Kk Takaitosoyakitsukekokaseitosugureta hijikoseiomotsukochoryokureienkohanno seizohoho
JPS5178730A (en) * 1974-12-30 1976-07-08 Nippon Steel Corp Fueraitosoto kyureihentaisoyorinaru fukugososhikikohanno seizohoho
JPS5849627B2 (ja) * 1979-02-27 1983-11-05 川崎製鉄株式会社 非時交性冷延鋼板の製造方法
JPS5747828A (en) * 1980-09-05 1982-03-18 Kobe Steel Ltd Production of high strength hot rolled steel plate
US4496400A (en) * 1980-10-18 1985-01-29 Kawasaki Steel Corporation Thin steel sheet having improved baking hardenability and adapted for drawing and a method of producing the same
US4426235A (en) * 1981-01-26 1984-01-17 Kabushiki Kaisha Kobe Seiko Sho Cold-rolled high strength steel plate with composite steel structure of high r-value and method for producing same
US4410372A (en) * 1981-06-10 1983-10-18 Nippon Steel Corporation Process for producing deep-drawing, non-ageing, cold rolled steel strips having excellent paint bake-hardenability by continuous annealing
JPS5825436A (ja) * 1981-08-10 1983-02-15 Kawasaki Steel Corp 遅時効性、異方性小なる深絞り用冷延鋼板の製造方法
JPS5867827A (ja) * 1981-09-18 1983-04-22 Nippon Steel Corp 深紋り用冷延鋼板の製造方法
JPS5852430A (ja) * 1981-09-19 1983-03-28 Sumitomo Metal Ind Ltd 絞り用亜鉛めつき鋼板の製造法
JPS5852440A (ja) * 1981-09-21 1983-03-28 Nippon Steel Corp 高い深絞り性を有し、プレス加工性の優れた遅時効性高強度冷延鋼板の連続焼鈍による製造方法
JPS58110659A (ja) * 1981-12-25 1983-07-01 Nippon Kokan Kk <Nkk> 深絞り用亜鉛めつき鋼板およびその製造方法
JPS6045689B2 (ja) * 1982-02-19 1985-10-11 川崎製鉄株式会社 プレス成形性にすぐれた冷延鋼板の製造方法
JPS58210125A (ja) * 1982-06-01 1983-12-07 Sumitomo Metal Ind Ltd 直接焼入法による強靭高張力鋼板の製造法
JPS60197846A (ja) * 1984-03-19 1985-10-07 Kawasaki Steel Corp 人工時効硬化性と深絞り性に優れるフエライト単相混合粒組織冷延鋼板

Also Published As

Publication number Publication date
CA1229750A (en) 1987-12-01
US4615749A (en) 1986-10-07
ES530701A0 (es) 1985-12-01
DE3468906D1 (en) 1988-02-25
EP0152665B1 (en) 1988-01-20
EP0152665A1 (en) 1985-08-28
JPH032224B2 (enExample) 1991-01-14
JPS60174852A (ja) 1985-09-09
US4708748A (en) 1987-11-24

Similar Documents

Publication Publication Date Title
GB2155951B (en) Bearing steel
CA2172441A1 (en) Hot-rolled steel sheet and method for forming hot-rolled steel sheet having low yield ratio, high strength and excellent toughness
CA2182813A1 (en) Method of making dual phase steel plate
DE3468906D1 (en) A cold rolled dual-phase structure steel sheet having an excellent deep drawability and a method of manufacturing the same
CA2097900A1 (en) High-strength cold-rolled steel sheet excelling in deep drawability and method of producing the same
CA2067043A1 (en) High strength cold rolled steel sheet having excellent non-aging property at room temperature and suitable for drawing and method of producing the same
EP0262874A3 (en) Cold-rolled steel sheets and method for producing cold-rolled steel sheets
AU585694B2 (en) Steel
JPS5684422A (en) Production of precipitation hardening type high-tension cold rolled steel plate
JPS55141526A (en) Production of high tension cold-rolled steel plate for deep drawing
JPS56166331A (en) Manufacture of cold rolled steel plate with superior press workability
TW327651B (en) Material for a magnetic shield, process for producing the same, and a color tube using such a material
GR3033166T3 (en) Process for producing steel strip for deep drawing and redrawing of steel cans
JPS5538979A (en) Manufacture of low yield point, high tensile hot rolled steel plate with superior workability
JPS6425946A (en) Steel plate having excellent workability and toughness as well as having good hardenability and its production
JPS6434599A (en) Steel for pressure vessel with 40-60kg class tensile strength
JPS5723025A (en) Manufacture of hot-rolled high tensile steel plate having excellent local ductility
JPS6479347A (en) High strength hot rolled steel plate having drastically excellent cold workability and its manufacture
JPS6455339A (en) Production of grain-oriented silicon iron alloy thin band
JPS57192225A (en) Production of drawable cold-rolled steel sheet having baking-hardenability
JPS5465115A (en) Boron-added high tensile steel with superior low temperature toughness
GB1512632A (en) Grain-oriented steel
JPS57188652A (en) High-strength austenite steel with superior cold work hardenability
JPS5531123A (en) Manufacture of hot rolled steel plate of composite structure having superior corrosion resistance, low yield ratio and high strength
JPS56166330A (en) Manufacture of cold rolled steel plate for deep drawing by continuous annealing

Legal Events

Date Code Title Description
FD1A Patent lapsed

Effective date: 20020401